Additive printed circuit boards and method of manufacture
Assignee: MacDermid Inc
•
Filing: 1973-12-14
•
Granted: 1976-05-25
•
Expires: 1993-12-14
Abstract
Abstract Circuit boards for electronic equipment are produced in which the circuit-forming conductor metal is deposited on a suitably catalyzed and masked resin substrate by an all-additive electroless deposition technique, in which the characterizing feature is the use of a two-stage metal deposition to build up the desired total thickness of metal. In the first stage a fine grained, thin deposit of metal is produced on the substrate which is then water rinsed and immersed in a second metal bath having a sufficiently high rate of deposition to produce the desired total thickness of metal in a commercially practical period of time. Improved adhesion of plated metal to the resin substrate, both before and after thermal shock, is achieved by resort to this two-stage plating procedure.
Inventors
- 👤 John J. Grunwald
- 👤 Peter E. Kukanskis
- 👤 Elaine F. Jacovich
- 👤 Eugene D. D'Ottavio
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 20:00
CPC Classifications
H; H05; H05K; H05K3/00; H05K3/10; H05K3/18; H05K3/181; H05K3/187; C; C23; C23C; C23C18/00; C23C18/16; C23C18/1601; C23C18/1603; C23C18/1605; C23C18/1633; C23C18/1646; C23C18/165; C23C18/1651; H05K3/182; H05K3/184; H05K2201/00; H05K2201/03; H05K2201/0332; H05K2201/0335; H05K2201/0344
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
244 words
A method for producing printed circuit boards by an all-additive electroless plating procedure which eliminates the need for interrupting the plating operations to perform an adhesion-promoting baking step heretofore required to develop adequate adhesion, which comprises immersing a suitably-masked, catalyzed-surface substrate selected from the group consisting of paper or glass fiber reinforced phenolic, epoxy and polyester resins in a first electroless metal plating bath to produce thereon a first layer of said metal on the unmasked areas of said substrate, moving said substrate from said first bath through a water rinse immediately into at least one other electroless metal plating bath, to produce a metal composite of at least two layers of electroless metal on the unmasked portions of the substrate, wherein the thickness of the metal in the second layer always substantially exceeds that of the first layer, said metal plating baths each being selected from the group consisting of electroless nickel, cobalt and copper, and wherein, when copper is selected for the first electroless metal plating bath, such bath is adjusted to give a maximum deposition rate under ambient room temperature conditions of from around 0.03 to less than 0.10 mil per hour and wherein, when cobalt or nickel is selected for the first electroless metal plating bath, such bath is adjusted to give a maximum deposition rate of from around 0.02 to 0.3 mil per hour, the thickness of the deposit in either event being from about 0.005 to 0.2 mil.
Claim 2
Independent Claim
244 words
A method for producing printed circuit boards by an all-additive electroless plating procedure which eliminates the need for interrupting the plating operations to perform an adhesion-promoting baking step heretofore required to develop adequate adhesion, which comprises immersing a suitably-masked, catalyzed-surface substrate selected from the group consisting of paper or glass fiber reinforced phenolic, epoxy and polyester resins in a first electroless metal plating bath to produce thereon a first layer of said metal on the unmasked areas of said substrate, moving said substrate from said first bath through a water rinse immediately into at least one other electroless metal plating bath, to produce a metal composite of at least two layers of electroless metal on the unmasked portions of the substrate, wherein the thickness of the metal in the second layer always substantially exceeds that of the first layer, said metal plating baths each being selected from the group consisting of electroless nickel, cobalt and copper, and wherein, when copper is selected for the first electroless metal plating bath, such bath is adjusted to give a maximum deposition rate under ambient room temperature conditions of from around 0.03 to less than 0.10 mil per hour and wherein, when cobalt or nickel is selected for the first electroless metal plating bath, such bath is adjusted to give a maximum deposition rate of from around 0.02 to 0.3 mil per hour, the thickness of the deposit in either event being from about 0.005 to 0.2 mil.
Claim 3
Dependent Claim
26 words
A method as defined in claim 1, wherein said first metal deposit is electroless nickel or electroless cobalt, and the second metal layer is electroless copper.
Claim 4
Dependent Claim
56 words
A method as defined in claim 2, wherein the deposition of metal in said first electroless plating bath is discontinued when said first deposit has a thickness of not over 0.03 mil, and continuing the deposition of metal in said second electroless bath until the total thickness of metal composite is at least about 1.0 mil.
Claim 5
Dependent Claim
29 words
The method as defined in claim 3, wherein the deposition of said first layer of metal is discontinued when the thickness thereof has reached about 0.005 to 0.02 mil.
Claim 6
Dependent Claim
59 words
A method as defined in claim 3, wherein said first electroless metal plating bath is adjusted to produce a metal deposition rate of not over 0.3 mil per hour at ambient room temperature, and said second electroless plating bath is adjusted to produce a metal deposition rate of not less than 0.1 mil per hour at ambient room temperature.
Claim 7
Dependent Claim
56 words
A method as defined in claim 5, wherein said first electroless plating bath is adjusted to produce a metal deposition rate of from 0.03 to 0.1 mil per hour, and said second electroless plating bath is adjusted to produce a metal deposition rate of from about 0.1 to 0.2 mil per hour at ambient room temperature.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-05-25 | 1979-11-24 | 1980-05-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-05-25 | 1983-11-24 | 1984-05-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-05-25 | 1987-11-24 | 1988-05-25 | $7700.00 | Window Closed / Lapsed |