USRE30854E
Expired / Lapsed
US
⏱️ 0.0 years remaining
Free machining Cu--Ni--Sn alloys
Assignee: AT&T Inc
•
Filing: 1980-09-22
•
Granted: 1982-01-26
•
Expires: 2000-09-22
Abstract
Abstract Cu-Ni-Sn alloys are disclosed which are particularly suited to undergo shaping by machining such as drilling, and lathing. In addition to Cu, Ni, and Sn, these alloys contain specified small amounts of Te, Se, Pb, or MnS. When articles are formed by machining of alloys having such specified composition, clogging of the machining tool and overheating of workpiece and machining tool are effectively prevented.
Inventors
- 👤 John T. Plewes
- 👤 Philip R. White
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 11:41
CPC Classifications
C; C22; C22C; C22C9/00; C22C9/06
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
173 words
Article of manufacture comprising a copper based alloy which is shaped by machining, an aggregate amount of at least 90 weight percent of said alloy consisting of Cu, Ni, Sn, and at least one additive, said aggregate amount having a Ni content in the range of three weight percent to 30 weight percent, said aggregate amount having a Sn content in a range of three weight percent to an upper limit which is a linear function of said Ni content, said upper limit being ten weight percent when said Ni content is three weight percent and said upper limit being 12 weight percent when said Ni content is 30 weight percent, and CHARACTERIZED IN THAT said additive is .[.selected from the group consisting of Se in the range of 0.1-0.5 weight percent of said aggregate amount, Te in the range of 0.1-0.5 weight percent of said aggregate amount, Pb in the range of 0.1-0.2 weight percent of said aggregate amount, and.]. MnS in the range of 0.2-2.0 weight percent of said aggregate amount.
Claim 2
Dependent Claim
173 words
Article of manufacture comprising a copper based alloy which is shaped by machining, an aggregate amount of at least 90 weight percent of said alloy consisting of Cu, Ni, Sn, and at least one additive, said aggregate amount having a Ni content in the range of three weight percent to 30 weight percent, said aggregate amount having a Sn content in a range of three weight percent to an upper limit which is a linear function of said Ni content, said upper limit being ten weight percent when said Ni content is three weight percent and said upper limit being 12 weight percent when said Ni content is 30 weight percent, and CHARACTERIZED IN THAT said additive is .[.selected from the group consisting of Se in the range of 0.1-0.5 weight percent of said aggregate amount, Te in the range of 0.1-0.5 weight percent of said aggregate amount, Pb in the range of 0.1-0.2 weight percent of said aggregate amount, and.]. MnS in the range of 0.2-2.0 weight percent of said aggregate amount.
Claim 3
Dependent Claim
64 words
Article of claim 1 in which said additive is .[.selected from the group consisting of Se in the range of 0.15-0.2 weight percent of said aggregate amount, Te in the range of 0.15-0.2 weight percent of said aggregate amount, Pb in the range of 0.11-0.15 weight percent of said aggregate amount, and.]. MnS in the range of 0.5-1.5 weight percent of said aggregate amount.
Claim 4
Dependent Claim
117 words
Article of claim 1 in which not more than 0.1 weight percent of said alloy is Mo, not more than 0.35 weight percent of said alloy is Nb, not more than 0.3 weight percent of said alloy is Ta, not more than 0.5 weight percent of said alloy is V, not more than 7 weight percent of said alloy is Fe, not more than 1 weight percent of said alloy is Mg, not more than 5 weight percent of said alloy is Mn, not more than 10 weight percent of said alloy is Zn, not more than 0.2 weight percent of said alloy is Zr, and not more than 1 weight percent of said alloy is Cr.
Claim 5
Dependent Claim
51 words
Article of claim 1 in which not more than 0.2 weight percent of said alloy is Co, not more than 0.1 weight percent of said alloy is Al, not more than 0.01 weight percent of said alloy is P, and not more than 0.05 weight percent of said alloy is Si.
Claim 6
Dependent Claim
26 words
Article of claim 1 in which said alloy prior to machining is hot worked, warm worked, or cold worked, and in which said additive is MnS.
Claim 7
Dependent Claim
21 words
Article of claim 1 in which a predominantly spinodal structure is developed in said alloy.[.and in which said additive is MnS.]..
Claim 8
Dependent Claim
17 words
Article of claim 6 in which said spinodal structure is developed by homogenizing, cold working, and aging.
Claim 9
Dependent Claim
25 words
Article of claim 6 in which said alloy contains Mo, Nb, Ta, V, or Fe and in which said spinodal structure is developed by aging.
Claim 10
Dependent Claim
18 words
Article of claim 1 in which the ratio of Mn:S is in the range of 3:1 to 7:1.
Claim 11
Dependent Claim
16 words
Article of claim 9 in which said ratio is in the range of 5:1 to 6:1.
Claim 12
Dependent Claim
162 words
Copper based alloy of which an aggregate amount of at least 90 weight percent consists of Cu, Ni, Sn, and at least one additive, said aggregate amount having a Ni content in the range of three weight percent to 30 weight percent, said aggregate amount having a Sn content in a range of three weight percent to an upper limit which is a linear function of said Ni content, said upper limit being ten weight percent when said Ni content is three weight percent and said upper limit being 12 weight percent when said Ni content is 30 weight percent, and CHARACTERIZED IN THAT said additive is .[.selected from the group consisting of Se in the range of 0.1-0.5 weight percent of said aggregate amount, Te in the range of 0.1-0.5 weight percent of said aggregate amount, Pb in the range of 0.1-0.2 weight percent of said aggregate amount, and.]. MnS in the range of 0.2-2.0 weight percent of said aggregate amount.
Claim 13
Dependent Claim
162 words
Copper based alloy of which an aggregate amount of at least 90 weight percent consists of Cu, Ni, Sn, and at least one additive, said aggregate amount having a Ni content in the range of three weight percent to 30 weight percent, said aggregate amount having a Sn content in a range of three weight percent to an upper limit which is a linear function of said Ni content, said upper limit being ten weight percent when said Ni content is three weight percent and said upper limit being 12 weight percent when said Ni content is 30 weight percent, and CHARACTERIZED IN THAT said additive is .[.selected from the group consisting of Se in the range of 0.1-0.5 weight percent of said aggregate amount, Te in the range of 0.1-0.5 weight percent of said aggregate amount, Pb in the range of 0.1-0.2 weight percent of said aggregate amount, and.]. MnS in the range of 0.2-2.0 weight percent of said aggregate amount.
Claim 14
Dependent Claim
64 words
Alloy of claim 11 in which said additive is .[.selected from the group consisting of Se in the range of 0.15-0.2 weight percent of said aggregate amount, Te in the range of 0.15-0.2 weight percent of said aggregate amount, Pb in the range of 0.11-0.15 weight percent of said aggregate amount, and.]. MnS in the range of 0.5-1.5 weight percent of said aggregate amount.
Claim 15
Dependent Claim
76 words
Alloy of claim 11 containing not more than 0.1 weight percent Mo, not more than 0.35 weight percent Nb, not more than 0.3 weight percent Ta, not more than 0.5 weight percent V, not more than 7 weight percent Fe, not more than one weight percent Mg, not more than 5 weight percent Mn, not more than 10 weight percent Zn, not more than 0.2 weight percent Zr, and not more than 1 weight percent Cr.
Claim 16
Dependent Claim
34 words
Alloy of claim 11 containing not more than 0.2 weight percent Co, not more than 0.1 weight percent Al, not more than 0.01 weight percent P, and not more than 0.05 weight percent Si.
Claim 17
Dependent Claim
18 words
Alloy of claim 11 in which the ratio of Mn:S is in the range of 3:1 to 7:1.
Claim 18
Dependent Claim
16 words
Alloy of claim 15 in which said ratio is in the range of 5:1 to 6:1.
References Cited (Backward Citations)
US1816509A
Cited
GB466675A
Cited
US2117106A
Cited
US3940290A
Cited
US4046596A
Cited
US4012240A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-01-25 | 1985-07-27 | 1986-01-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-01-25 | 1989-07-27 | 1990-01-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-01-25 | 1993-07-27 | 1994-01-26 | $7700.00 | Window Closed / Lapsed |