Method of making an electrode having a coating containing a platinum metal oxide thereon
Assignee: Chemnor Corp
•
Filing: 1975-08-05
•
Granted: 1976-05-18
•
Expires: 1995-08-05
Abstract
Abstract A method of making an electrode for use in an electrolytic process. The electrode has a core of a film-forming metal and a layer having at least a part of the outside portion of the thickness thereof of an electrolyte resistant and electrolysis product resistant material, which material contains as the material effective for carrying out electrolysis at least one oxide of at least one platinum metal taken from the group consisting of platinum, iridium, rhodium palladium, ruthenium and osmium. The method comprises forming the platinum metal on the core and then oxidizing it, forming the oxide and then applying it to the core, or forming the oxide directly on the core, for example, by heating a solution of a salt of the metal or electrolysis.
Inventors
- 👤 Henri Bernard Beer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 22:59
CPC Classifications
C; C25; C25B; C25B11/00; C25B11/04; C25B11/051; C25B11/073; C25B11/091; C25B11/093
Claims Analysis
Total Claims: 46
Claim 1
Independent Claim
100 words
A method of making an electrode comprising forming on at least part of the surface of a core of a film-forming metal a layer containing at least one platinum metal taken from the group consisting of platinum, iridium, rhodium, palladium, ruthenium, rhenium and osmium, and alloys of these metals, the amount of platinum metal being sufficient, when converted to the oxide thereof, to be effective for carrying out electrolysis, and subjecting the layer to oxidizing conditions which are sufficient to oxidize the metal of said layer until the layer is oxidized to a depth of at least about 0.054 micron.
Claim 2
Independent Claim
100 words
A method of making an electrode comprising forming on at least part of the surface of a core of a film-forming metal a layer containing at least one platinum metal taken from the group consisting of platinum, iridium, rhodium, palladium, ruthenium, rhenium and osmium, and alloys of these metals, the amount of platinum metal being sufficient, when converted to the oxide thereof, to be effective for carrying out electrolysis, and subjecting the layer to oxidizing conditions which are sufficient to oxidize the metal of said layer until the layer is oxidized to a depth of at least about 0.054 micron.
Claim 3
Dependent Claim
31 words
A method as claimed in claim 1 in which the core metal is a metal taken from the group consisting of titanium, tantalum, zirconium and niobium and alloys of said metals.
Claim 4
Dependent Claim
30 words
A method as claimed in claim 2 comprising oxidizing said core metal for forming an oxide layer on said core metal prior to applying the oxide of the platinum metal.
Claim 5
Dependent Claim
19 words
A method as claimed in claim 3 in which the oxide layer is formed on the core metal thermally.
Claim 6
Dependent Claim
28 words
A method as claimed in claim 1 in which the step of subjecting the layer to oxidizing conditions comprises applying to it a melt of an oxidizing salt.
Claim 7
Dependent Claim
57 words
A method as claimed in claim 5 in which the core is titanium, the metal of the layer is platinum, and the step of subjecting the layer to oxidizing conditions comprises immersing the core having the layer of platinum thereon into a melt of a material taken from the group consisting of sodium nitrate and potassium nitrate.
Claim 8
Dependent Claim
60 words
A method as claimed in claim 5 in which the core is zirconium, the metal of the layer is an alloy of platinum and palladium, and the step of subjecting the layer to oxidizing conditions comprises immersing the core having the layer thereon into a melt of a material taken from the group consisting of sodium nitrate and potassium nitrate.
Claim 9
Dependent Claim
55 words
A method as claimed in claim 5 in which the core is niobium, the metal of the layer is palladium, and the step of subjecting the layer to oxidizing conditions comprises immersing the core having the layer thereon into a melt of a material taken from the group consisting of sodium nitrate and potassium nitrate.
Claim 10
Dependent Claim
40 words
A method as claimed in claim 1 in which the platinum metal is taken from the group consisting of ruthenium and palladium, and the step of subjecting the layer to oxidizing conditions comprises heating it in an oxygen containing atmosphere.
Claim 11
Dependent Claim
47 words
A method as claimed in claim 9 in which the core is titanium and the metal is ruthenium, and the step of heating in an oxygen containing atmosphere comprises heating in an oxygen containing atmosphere having a partial pressure of oxygen substantially equal to that of air.
Claim 12
Dependent Claim
32 words
A method as claimed in claim 9 in which the core is tantalum and the metal is ruthenium, and the step of heating in a oxygen containing atmosphere comprises heating in air.
Claim 13
Dependent Claim
45 words
A method as claimed in claim 11 in which the step of forming the metal layer comprises applying to the core a solution of a salt which when heated will form on the core the metal, and then heating the core to form the metal.
Claim 14
Dependent Claim
42 words
A method as claimed in claim 1 in which the step of subjecting the layer to oxidizing conditions comprises heating it in an oxygen containing atmosphere which has a partial pressure of oxygen greater than the partial oxygen pressure of atmospheric air.
Claim 15
Dependent Claim
69 words
A method as claimed in claim 13 in which the core is titanium with 4% molybdenum, the step of forming the metal layer comprises applying to the core a solution of a salt of platinum which will form platinum when heated, and then heating the core to form platinum, and the step of heating in an oxygen containing atmosphere comprises heating in oxygen at a pressure of 8-15 atmospheres.
Claim 16
Independent Claim
86 words
A method of making an electrode comprising forming a material containing as a substance effective to carry out electrolysis at least one oxide of a platinum metal taken from the group consisting of platinum, iridium, rhodium, palladium, ruthenium, rhenium and osmium, and alloys of these metals, and applying the material to at least a part of the surface of a core of a film-forming metal to form a layer on said part of the surface of the core, which layer is at least 0.054 micron thick.
Claim 17
Independent Claim
86 words
A method of making an electrode comprising forming a material containing as a substance effective to carry out electrolysis at least one oxide of a platinum metal taken from the group consisting of platinum, iridium, rhodium, palladium, ruthenium, rhenium and osmium, and alloys of these metals, and applying the material to at least a part of the surface of a core of a film-forming metal to form a layer on said part of the surface of the core, which layer is at least 0.054 micron thick.
Claim 18
Dependent Claim
31 words
A method as claimed in claim 15 in which the core metal is a metal taken from the group consisting of titanium, tantalum, zirconium and niobium and alloys of said metals.
Claim 19
Dependent Claim
30 words
A method as claimed in claim 16 comprising oxidizing said core metal for forming an oxide layer on said core metal prior to applying the oxide of the platinum metal.
Claim 20
Dependent Claim
19 words
A method as claimed in claim 17 in which the oxide layer is formed on the core metal thermally.
Claim 21
Dependent Claim
47 words
A method as claimed in claim 15 in which the step of forming the material comprises melting a platinum metal oxide under pressure, and the step of applying the material to the core comprises applying the molten oxide to the core and then cooling the thus-coated core.
Claim 22
Dependent Claim
43 words
A method as claimed in claim 15 in which the step of forming the material comprises preparing a hot melt of the platinum metal oxide, and the step of applying the material to the core comprises spraying the hot melt onto the core.
Claim 23
Dependent Claim
57 words
A method as claimed in claim 15 in which the step of forming the material comprises forming a dispersion of the platinum metal oxide in a liquid carrier which is a liquid which can be evaporated without leaving any residue, and the step of applying the material to the core comprises contacting the core and the dispersion.
Claim 24
Dependent Claim
22 words
A method as claimed in claim 21 in which the step of applying the material comprises spraying the dispersion onto the core.
Claim 25
Dependent Claim
22 words
A method as claimed in claim 21 in which the step of applying the material comprises brushing the dispersion onto the core.
Claim 26
Dependent Claim
22 words
A method as claimed in claim 21 in which the step of applying the material comprises dipping the core into the dispersion.
Claim 27
Dependent Claim
22 words
A method as claimed in claim 21 in which the core is titanium and the dispersion is a dispersion of platinum oxide.
Claim 28
Dependent Claim
25 words
A method as claimed in claim 21 in which the core is niobium and the dispersion is a dispersion of rhodium oxide and iridium oxide.
Claim 29
Dependent Claim
30 words
A method as claimed in claim 21 which further comprises, after the dispersion is applied to the core, applying pressure to the dispersion for adhering the dispersion to the core.
Claim 30
Dependent Claim
41 words
A method as claimed in claim 15 in which the step of forming the material comprises preparing a plasma of the platinum metal oxide, and the step of applying the material to the core comprises spraying the plasma onto the core.
Claim 31
Dependent Claim
19 words
A method as claimed in claim 28 in which the core is titanium and the oxide is platinum dioxide.
Claim 32
Dependent Claim
61 words
A method as claimed in claim 15 in which the step of forming the material comprises preparing a dispersion of a platinum metal oxide and an oxide of a metal other than platinum in a liquid carrier which is evaporated without leaving any residue, and the step of applying the material to the core comprises contacting the core and the dispersion.
Claim 33
Dependent Claim
38 words
A method as claimed in claim 30 in which the core is 4% molybdenum and the balance titanium, and the platinum metal oxide is platinum oxide and the oxide of a metal other than platinum is manganese dioxide.
Claim 34
Dependent Claim
33 words
A method as claimed in claim 30 in which the core is titanium and the platinum metal oxide is platinum oxide and the oxide of a metal other than platinum is silicon dioxide.
Claim 35
Independent Claim
150 words
A method of making an electrode comprising forming a solution of a material containing a salt of at least one platinum metal taken from the group consisting of platinum, iridium, rhodium, palladium, ruthenium, rhenium and osmium, the amount of platinum metal salt being sufficient, when converted to the oxide of the platinum metal, to be effective for carrying out electrolysis, contacting at least part of the surface of a core of a film forming metal with the solution, and subjecting the solution to conditions for causing a layer to be formed on the part of the surface of the core which contains, as a material effective for carrying out electrolysis, the oxide of the platinum metal, said step of contacting comprising contacting said surface of said core with sufficient solution for forming, during the subjecting of the solution to said conditions, a layer which is at least 0.054 micron thick.
Claim 36
Independent Claim
150 words
A method of making an electrode comprising forming a solution of a material containing a salt of at least one platinum metal taken from the group consisting of platinum, iridium, rhodium, palladium, ruthenium, rhenium and osmium, the amount of platinum metal salt being sufficient, when converted to the oxide of the platinum metal, to be effective for carrying out electrolysis, contacting at least part of the surface of a core of a film forming metal with the solution, and subjecting the solution to conditions for causing a layer to be formed on the part of the surface of the core which contains, as a material effective for carrying out electrolysis, the oxide of the platinum metal, said step of contacting comprising contacting said surface of said core with sufficient solution for forming, during the subjecting of the solution to said conditions, a layer which is at least 0.054 micron thick.
Claim 37
Dependent Claim
31 words
A method as claimed in claim 33 in which the core metal is a metal taken from the group consisting of titanium, tantalum, zirconium and niobium and alloys of said metals.
Claim 38
Dependent Claim
25 words
A method as claimed in claim 34 comprising forming an oxide layer on said core metal prior to applying the oxide of the platinum metal.
Claim 39
Dependent Claim
19 words
A method as claimed in claim 35 in which the oxide layer is formed on the core metal thermally.
Claim 40
Dependent Claim
87 words
A method as claimed in claim 33 in which the step of forming the solution comprises forming a solution containing a salt of the platinum metal in an organic carrier, the step of contacting the surface of the core with the solution comprises coating the part of the surface of the core with the solution, and the step of subjecting the solution to conditions for causing the layer to be formed comprises heating the coated core in air to directly deposit the oxide of the platinum metal.
Claim 41
Dependent Claim
19 words
A method as claimed in claim 37 in which the core is titanium, and the platinum metal is palladium.
Claim 42
Dependent Claim
19 words
A method as claimed in claim 37 in which the core is tungsten and the platinum metal is ruthenium.
Claim 43
Dependent Claim
127 words
A method as claimed in claim 37 in which the core is tantalum and the platinum metals are palladium and iridium. .[.41. A method as claimed in claim 33 in which the step of forming the solution comprises forming an electrolyte of a salt of the platinum metal, the step of contacting the surface of the core with the solution comprises inserting the core into the solution, and the step of subjecting the solution to conditions for causing the layer to be formed comprises carrying out electrolysis using the immersed core as an electrode in the electrolyte..]. .[.42. A method as claimed in claim 41 in which the core is a metal taken from the group consisting of titanium and tantalum and the platinum metal is platinum..].
Claim 44
Dependent Claim
94 words
A method as claimed in claim 33 in which the step of forming the solution comprises forming a solution of a salt of the platinum metal and the salt of a metal other than a platinum metal in an organic carrier, the step of contacting the surface of the core with the solution, and the step of subjecting the solution to conditions for causing the layer to be formed comprises heating the coated core in air to deposit directly the oxide of the platinum metal and the oxide of the metal other than the
Claim 45
Dependent Claim
27 words
platinum metal. 44. A method as claimed in claim 43 in which the core is titanium and the platinum metal is iridium and the metal other than
Claim 46
Dependent Claim
33 words
platinum metal is manganese. 45. A method as claimed in claim 43 in which the core is titanium and the platinum metal is platinum and the metal other than platinum metal is chromium.
References Cited (Backward Citations)
US2987453A
Cited
US3177131A
Cited
US3213004A
Cited
US3055811A
Cited
US3254006A
Cited
US3254015A
Cited
US3191108A
Cited
US3282735A
Cited
US3357858A
Cited
US3368919A
Cited
US3428544A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-05-18 | 1979-11-17 | 1980-05-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-05-18 | 1983-11-17 | 1984-05-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-05-18 | 1987-11-17 | 1988-05-18 | $7700.00 | Window Closed / Lapsed |