Tantalum tertiary amylimido tris (dimethylamide), a process for producing the same, a solution of starting material for mocvd using the same, and a method of forming a tantalum nitride film using the same
Abstract A stable compound having a vapor pressure higher by 1 order than that of Ta(NtBu)(NEt 2 ) 3 is provided as a starting material for forming a TaN film as a barrier film by the CVD method. There are further provided a process for producing the same and a method of forming a TaN film by using the same. The novel compound, tantalum tertiary amylimido tris(dimethylamide) [Ta(NtAm)(NMe 2 ) 3 ] has a vapor pressure of 1 Torr at 80° C., and its melting point is 36° C. This compound is obtained by allowing 1 mole of TaCl 5 , 4 moles of LiNMe 2 and 1 mole of LiNHtAm to react with one another in an organic solvent in the vicinity of room temperature, then separating byproducts by filtration, distilling the solvent away, and distilling the product in vacuo. This compound can be used as a starting material in CVD to form a cubic TaN film on a SiO 2 /Si substrate at 550° C. at 0.05 Torr.
A process for producing tantalum tertiary amylimido tris(dimethylamide), which comprises allowing 1 mole of tantalum pentachloride, 4 moles of lithium dimethylamide and 1 mole of lithium tertiary amylamide to react with one another in an organic solvent, then separating a byproduct lithium chloride by filtration, distilling the solvent away, and distilling the residue in vacuo.
Claim 4
Dependent Claim
55 words
A process for producing tantalum tertiary amylimido tris(dimethylamide), which comprises allowing 1 mole of tantalum pentachloride, 4 moles of lithium dimethylamide and 1 mole of lithium tertiary amylamide to react with one another in an organic solvent, then separating a byproduct lithium chloride by filtration, distilling the solvent away, and distilling the residue in vacuo.
Claim 5
Dependent Claim
21 words
A solution of starting material for MOCVD, comprising at least 10 wt % organic solvent added to tantalum tertiary amylimido tris(dimethylamide).
Claim 6
Dependent Claim
21 words
A solution of starting material for MOCVD, comprising at least 10 wt % organic solvent added to tantalum tertiary amylimido tris(dimethylamide).
Claim 7
Independent Claim
23 words
A method of forming a tantalum nitride film by the MOCVD method wherein tantalum tertiary amylimido tris(dimethylamide) is used as the starting material.
Claim 8
Independent Claim
23 words
A method of forming a tantalum nitride film by the MOCVD method wherein tantalum tertiary amylimido tris(dimethylamide) is used as the starting material.