Method of manufacturing an intracutaneous microneedle array
Assignee: Corium LLC
•
Filing: 2000-05-26
•
Granted: 2002-09-17
•
Expires: 2020-05-26
Abstract
Abstract A microneedle array is manufactured using a mold preparation procedure that begins by placing an optical mask over a layer of PMMA material, exposing the PMMA material to x-rays, then developing using a photoresist process. The remaining PMMA material is then electroplated with metal. Once the metal has reached an appropriate thickness, it is detached to become a metal mold that is used in a microembossing procedure, in which the metal mold is pressed against a heated layer of plastic material. Once the mold is pressed down to its proper distance, the plastic material is cooled until solidified, and the mold is then detached, thereby leaving behind an array of microneedles.
Inventors
- 👤 Faiz Feisal Sherman
- 👤 Vadim Vladimirovich Yuzhakov
- 👤 Vladimir Gartstein
- 👤 Grover David Owens
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 09:11
CPC Classifications
B; B29; B29C; B29C51/00; B29C51/08; B29C51/082; A; A61; A61M; A61M37/00; A61M37/0015; B26; B26F; B26F1/00; B26F1/24; B29C33/00; B29C33/0033; B29C33/42; B29C37/00; B29C37/0053; B29C45/00; B29C45/17; B29C45/26; B29C45/2628; B81; B81C; B81C1/00; B81C1/00015; B81C1/00023; B81C1/00111; A61M2037/0023; A61M2037/003; A61M2037/0053; B29C59/00; B29C59/02; B29C59/022; B29C2059/023; B29L; B29L2031/00; B29L2031/753; B29L2031/7544; B29L2031/756; B81B; B81B2201/00; B81B2201/05; B81B2201/055; B81C2201/00; B81C2201/03; B81C2201/036
Claims Analysis
Total Claims: 26
Claim 1
Independent Claim
145 words
A method of preparing a mold for manufacturing a microneedle array, comprising: providing a photoresist material, in contact with a temporary substrate; placing a mask layer upon said photoresist material, said mask layer having a predetermined pattern, at least a portion of said mask layer comprising a material that prevents high energy radiation from passing therethrough; exposing said combination photoresist material/mask layer to high energy radiation; removing said mask layer, and chemically developing exposed portions of said photo-resist material, thereby removing portions of the photoresist material and leaving behind a pattern of said photoresist material that represents a three-dimensional structure emulating a plurality of microneedles that are to be later formed; electroplating said patterned photoresist material with a metallic substance; and detaching said metallic substance from said patterned photoresist material, said metallic substance thereby forming a microneedle array mold; wherein said mask layer comprises gold.
Claim 2
Independent Claim
145 words
A method of preparing a mold for manufacturing a microneedle array, comprising: providing a photoresist material, in contact with a temporary substrate; placing a mask layer upon said photoresist material, said mask layer having a predetermined pattern, at least a portion of said mask layer comprising a material that prevents high energy radiation from passing therethrough; exposing said combination photoresist material/mask layer to high energy radiation; removing said mask layer, and chemically developing exposed portions of said photo-resist material, thereby removing portions of the photoresist material and leaving behind a pattern of said photoresist material that represents a three-dimensional structure emulating a plurality of microneedles that are to be later formed; electroplating said patterned photoresist material with a metallic substance; and detaching said metallic substance from said patterned photoresist material, said metallic substance thereby forming a microneedle array mold; wherein said mask layer comprises gold.
Claim 3
Dependent Claim
15 words
The method as recited in claim 1 , wherein said electroplating metallic substance comprises nickel.
Claim 4
Independent Claim
166 words
A method of preparing a mold for manufacturing a microneedle array, comprising: providing a photoresist material, in contact with a temporary substrate; placing a mask layer upon said photoresist material, said mask layer having a predetermined pattern, at least a portion of said mask layer comprising a material that prevents high energy radiation from passing therethrough; exposing said combination photoresist material/mask layer to high energy radiation; removing said mask layer, and chemically developing exposed portions of said photo-resist material, thereby removing portions of the photoresist material and leaving behind a pattern of said photoresist material that represents a three-dimensional structure emulating a plurality of microneedles that are to be later formed; electroplating said patterned photoresist material with a metallic substance; and detaching said metallic substance from said patterned photoresist material, said metallic substance thereby forming a microneedle array mold; wherein said patterned photoresist material is chemically coated before the step of electroplating to aid in later detachment of the metallic substance from the patterned photoresist material.
Claim 5
Independent Claim
166 words
A method of preparing a mold for manufacturing a microneedle array, comprising: providing a photoresist material, in contact with a temporary substrate; placing a mask layer upon said photoresist material, said mask layer having a predetermined pattern, at least a portion of said mask layer comprising a material that prevents high energy radiation from passing therethrough; exposing said combination photoresist material/mask layer to high energy radiation; removing said mask layer, and chemically developing exposed portions of said photo-resist material, thereby removing portions of the photoresist material and leaving behind a pattern of said photoresist material that represents a three-dimensional structure emulating a plurality of microneedles that are to be later formed; electroplating said patterned photoresist material with a metallic substance; and detaching said metallic substance from said patterned photoresist material, said metallic substance thereby forming a microneedle array mold; wherein said patterned photoresist material is chemically coated before the step of electroplating to aid in later detachment of the metallic substance from the patterned photoresist material.
Claim 6
Independent Claim
270 words
A method of preparing a mold for manufacturing a microneedle array, comprising: providing a photoresist material, in contact with a temporary substrate; placing a mask layer upon said photoresist material, said mask layer having a predetermined pattern, at least a portion of said mask layer comprising a material that prevents high energy radiation from passing therethrough; exposing said combination photoresist material/mask layer to high energy radiation; removing said mask layer, and chemically developing exposed portions of said photo-resist material, thereby removing portions of the photoresist material and leaving behind a pattern of said photoresist material that represents a three-dimensional structure emulating a plurality of microneedles that are to be later formed; electroplating said patterned photoresist material with a metallic substance; and detaching said metallic substance from said patterned photoresist material, said metallic substance thereby forming a microneedle array mold; wherein said method of preparing a mold for manufacturing a microneedle array further comprises a microembossing procedure, comprising: placing a plastic material upon a temperature-controlled surface and, by use of said temperature-controlled surface, heating said plastic material to substantially its elastic working temperature, said plastic material having a first substantially planar surface touching said temperature-controlled surface and a second substantially planar surface on its opposite side; pressing said microneedle array mold against the second substantially planar surface of said plastic material, thereby forming a three-dimensional pattern comprising a microneedle array in said plastic material; by use of said temperature-controlled surface, cooling said patterned plastic material below its deformable temperature; and de-molding, by removing said microneedle array mold from contact with said patterned plastic material, thereby leaving behind a plastic microneedle array.
Claim 7
Independent Claim
270 words
A method of preparing a mold for manufacturing a microneedle array, comprising: providing a photoresist material, in contact with a temporary substrate; placing a mask layer upon said photoresist material, said mask layer having a predetermined pattern, at least a portion of said mask layer comprising a material that prevents high energy radiation from passing therethrough; exposing said combination photoresist material/mask layer to high energy radiation; removing said mask layer, and chemically developing exposed portions of said photo-resist material, thereby removing portions of the photoresist material and leaving behind a pattern of said photoresist material that represents a three-dimensional structure emulating a plurality of microneedles that are to be later formed; electroplating said patterned photoresist material with a metallic substance; and detaching said metallic substance from said patterned photoresist material, said metallic substance thereby forming a microneedle array mold; wherein said method of preparing a mold for manufacturing a microneedle array further comprises a microembossing procedure, comprising: placing a plastic material upon a temperature-controlled surface and, by use of said temperature-controlled surface, heating said plastic material to substantially its elastic working temperature, said plastic material having a first substantially planar surface touching said temperature-controlled surface and a second substantially planar surface on its opposite side; pressing said microneedle array mold against the second substantially planar surface of said plastic material, thereby forming a three-dimensional pattern comprising a microneedle array in said plastic material; by use of said temperature-controlled surface, cooling said patterned plastic material below its deformable temperature; and de-molding, by removing said microneedle array mold from contact with said patterned plastic material, thereby leaving behind a plastic microneedle array.
Claim 8
Dependent Claim
16 words
The method as recited in claim 4 , wherein said plastic material comprises a biocompatible polymer.
Claim 9
Dependent Claim
17 words
The method as recited in claim 4 , further comprising: providing a vacuum during the molding process.
Claim 10
Dependent Claim
26 words
The method as recited in claim 4 , further comprising: forming a fluid-holding chamber on the second substantially planar surface side of said patterned microneedle array.
Claim 11
Independent Claim
101 words
A method of manufacturing a microneedle array, comprising: providing a microneedle array mold; providing a temperature-controlled mold chamber; providing a heated plastic material into said temperature-controlled mold chamber having its temperature raised substantially to its elastic working temperature, while causing said microneedle array mold to be held in an appropriate position until a microneedle array three-dimensional pattern is formed in said plastic material; by use of said temperature-controlled mold chamber, cooling said patterned plastic material below its deformable temperature; and de-molding, by removing said microneedle array mold from contact with said patterned plastic material, thereby leaving behind a plastic microneedle array.
Claim 12
Independent Claim
101 words
A method of manufacturing a microneedle array, comprising: providing a microneedle array mold; providing a temperature-controlled mold chamber; providing a heated plastic material into said temperature-controlled mold chamber having its temperature raised substantially to its elastic working temperature, while causing said microneedle array mold to be held in an appropriate position until a microneedle array three-dimensional pattern is formed in said plastic material; by use of said temperature-controlled mold chamber, cooling said patterned plastic material below its deformable temperature; and de-molding, by removing said microneedle array mold from contact with said patterned plastic material, thereby leaving behind a plastic microneedle array.
Claim 13
Dependent Claim
16 words
The method as recited in claim 8 , wherein said plastic material comprises a biocompatible polymer.
Claim 14
Dependent Claim
17 words
The method as recited in claim 8 , further comprising: providing a vacuum during the molding process.
Claim 15
Dependent Claim
51 words
The method as recited in claim 8 , wherein during said step of providing a heated plastic material into said temperature-controlled mold chamber, said microneedle array mold is pressed against a layer of said heated-plastic material that was previously placed in position upon a planar surface, thereby microembossing said plastic material.
Claim 16
Dependent Claim
48 words
The method as recited in claim 8 , wherein during said step of providing a heated plastic material into said temperature-controlled mold chamber, said microneedle array mold is already in its molding position and molten plastic material is injected into said mold chamber, thereby micromolding said plastic material.
Claim 17
Dependent Claim
23 words
The method as recited in claim 8 , further comprising: forming a fluid-holding chamber in said patterned microneedle array by way of micromachining.
Claim 18
Dependent Claim
25 words
The method as recited in claim 8 , further comprising: forming a fluid-holding chamber in said patterned microneedle array by way of oxygen plasma etching.
Claim 19
Dependent Claim
52 words
The method as recited in claim 8 , further comprising: forming at least one through-hole in a base member of said patterned microneedle array, in which said microneedle array comprises hollow microneedles, by burning a hole through said base member that is substantially concentric with at least one of said hollow microneedles.
Claim 20
Dependent Claim
58 words
The method as recited in claim 8 , further comprising: during the step of de-molding, controlling the cool-down temperature to generate shear forces along a surface of hollow microneedle shapes within said patterned microneedle array, such that upon removal of said microneedle array mold, at least one sharp point is formed at the tip of said hollow microneedles.
Claim 21
Independent Claim
246 words
A method of manufacturing a microneedle array, comprising: providing a laminate material comprising two layers of biocompatible plastic; providing a first mold having a plurality of projections that face against a surface of said laminate material; placing said laminate material upon a first temperature-controlled surface and, by use of said first temperature-controlled surface, heating said laminate material to substantially its elastic working temperature; pressing said first mold against one surface of said laminate material such that said plurality of projections extend completely through a first of the two layers of biocompatible plastic, thereby forming a plurality of through-holes in said first layer; by use of said first temperature-controlled surface, cooling said laminate material below its deformable temperature; detaching said two layers of biocompatible plastic, and retaining said first layer; placing said first layer of biocompatible plastic upon a second temperature-controlled surface and, by use of said second temperature-controlled surface, heating said first layer of biocompatible plastic to substantially its elastic working temperature; providing a second mold having a microneedle array pattern, and pressing said second mold against one surface of said first layer of biocompatible plastic, thereby forming a three-dimensional pattern comprising a microneedle array in said first layer of biocompatible plastic; by use of said second temperature-controlled surface, cooling said patterned biocompatible plastic below its deformable temperature; and de-molding, by removing said second mold from contact with said patterned biocompatible plastic, thereby leaving behind a plastic microneedle array that exhibits through-holes in its base element.
Claim 22
Independent Claim
246 words
A method of manufacturing a microneedle array, comprising: providing a laminate material comprising two layers of biocompatible plastic; providing a first mold having a plurality of projections that face against a surface of said laminate material; placing said laminate material upon a first temperature-controlled surface and, by use of said first temperature-controlled surface, heating said laminate material to substantially its elastic working temperature; pressing said first mold against one surface of said laminate material such that said plurality of projections extend completely through a first of the two layers of biocompatible plastic, thereby forming a plurality of through-holes in said first layer; by use of said first temperature-controlled surface, cooling said laminate material below its deformable temperature; detaching said two layers of biocompatible plastic, and retaining said first layer; placing said first layer of biocompatible plastic upon a second temperature-controlled surface and, by use of said second temperature-controlled surface, heating said first layer of biocompatible plastic to substantially its elastic working temperature; providing a second mold having a microneedle array pattern, and pressing said second mold against one surface of said first layer of biocompatible plastic, thereby forming a three-dimensional pattern comprising a microneedle array in said first layer of biocompatible plastic; by use of said second temperature-controlled surface, cooling said patterned biocompatible plastic below its deformable temperature; and de-molding, by removing said second mold from contact with said patterned biocompatible plastic, thereby leaving behind a plastic microneedle array that exhibits through-holes in its base element.
Claim 23
Dependent Claim
18 words
The method as recited in claim 17 , wherein said biocompatible plastic laminate material comprises a biocompatible polymer.
Claim 24
Dependent Claim
15 words
The method as recited in claim 17 , wherein said photoresist material comprises polymethylmethacrylate (PMMA).
Claim 25
Dependent Claim
18 words
The method as recited in claim 17 , wherein said first mold and said second mold comprise nickel.
Claim 26
Dependent Claim
17 words
The method as recited in claim 17 , further comprising: providing a vacuum during the molding processes.
References Cited (Backward Citations)
US3964482A
Cited
US4381963A
Cited
US5711761A
Cited
US4784737A
Cited
US4837049A
Cited
US5730714A
Cited
US5362307A
Cited
SU1667864A1
Cited
US5250023A
Cited
US5215088A
Cited
US5279544A
Cited
US5848991A
Cited
US5156591A
Cited
US5527288A
Cited
US5676850A
Cited
US5256360A
Cited
US5318557A
Cited
US5383512A
Cited
US5704520A
Cited
US5848990A
Cited
US5681580A
Cited
US5611806A
Cited
US5855801A
Cited
US5591139A
Cited
US5771890A
Cited
WO1996000109A1
Cited
US5498235A
Cited
US5551953A
Cited
US5800420A
Cited
US5820622A
Cited
US5807375A
Cited
WO1996037256A1
Cited
WO1996037155A1
Cited
WO1997003718A1
Cited
JPH0951878A
Cited
US5814020A
Cited
US5735273A
Cited
US5827183A
Cited
US5645977A
Cited
US5658515A
Cited
WO1997048442A1
Cited
WO1997048440A1
Cited
WO1997048441A1
Cited
WO1998000193A1
Cited
WO1999000155A1
Cited
WO1999029298A2
Cited
WO1999029364A1
Cited
WO1999029365A1
Cited
WO1999064580A1
Cited
US6334856B1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2005-09-16 | 2006-03-18 | 2006-09-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2009-09-16 | 2010-03-18 | 2010-09-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2013-09-16 | 2014-03-18 | 2014-09-17 | $7700.00 | Window Closed / Lapsed |