Abstract
Abstract A silicon layer containing microcrystal is formed on a semiconductor substrate 10 having an amorphous silicon layer 61 a formed on the surface thereof (t 1 and t 2 ). Continuously, HSGs (hemispherical grains) are formed, in the same furnace, on the silicon layer 61 a using microcrystal on the silicon layer 61 a as a nucleus (t 2 and t 3 ). Further, a source gas containing impurities is introduced into the furnace to diffuse impurities into the HSGs (t 3 and t 4 ), wherein a lower electrode is formed. Also, during the processes from t 1 through t 4 , the partial pressure of water and oxygen in the furnace is set to 1×10 −6 Torr or less. Furthermore, during the processes from t 1 through t 4 , the temperature in the furnace is set to 550 through 600° C.
Inventors
- 👤 Fumiki Aiso
- 👤 Toshiyuki Hirota
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 01:28
CPC Classifications
H; H10; H10B; H10B12/00; H10D; H10D1/00; H10D1/60; H10D1/68; H10D1/692; H10D1/711; H10D1/712; H10D1/01; H10D1/041; H10D1/042; H10D1/716
Claims Analysis
Total Claims: 45
Claim 1
Independent Claim
235 words
A method for producing capacitor elements constructed of a lower electrode, a dielectric body layer and an upper electrode, which are formed on a semiconductor substrate, comprising: a first silicon layer forming step for forming a first amorphous silicon layer at an appointed area on the semiconductor substrate, a lower electrode surface rinsing step for rinsing the surface of said first silicon layer, a nucleus forming step for selectively forming a second amorphous silicon layer including microcrystal on the surface of said first silicon layer, an HSG forming step for growing HSGs (hemispherical Grains) using microcrystal included in said second silicon layer as a nucleus by annealing said first and second silicon layer at a low pressure or in the atmosphere of an inactive gas, and forming HSGs on the surface of said first silicon layer, an impurity diffusing step for forming a lower electrode by annealing while said HSGs are being exposed to a source gas including impurities and thermally diffusing said impurities in said HSGS, a dielectric body layer forming step for forming a dielectric body layer on said first silicon layer having said HSGs on the surface thereof, and an upper electrode forming step for forming an upper electrode on said dielectric body layer, wherein the partial pressure of oxygen and water is maintained at 1×10 −6 Torr or less at least between said HSG forming step and said impurity diffusing step.
Claim 2
Independent Claim
235 words
A method for producing capacitor elements constructed of a lower electrode, a dielectric body layer and an upper electrode, which are formed on a semiconductor substrate, comprising: a first silicon layer forming step for forming a first amorphous silicon layer at an appointed area on the semiconductor substrate, a lower electrode surface rinsing step for rinsing the surface of said first silicon layer, a nucleus forming step for selectively forming a second amorphous silicon layer including microcrystal on the surface of said first silicon layer, an HSG forming step for growing HSGs (hemispherical Grains) using microcrystal included in said second silicon layer as a nucleus by annealing said first and second silicon layer at a low pressure or in the atmosphere of an inactive gas, and forming HSGs on the surface of said first silicon layer, an impurity diffusing step for forming a lower electrode by annealing while said HSGs are being exposed to a source gas including impurities and thermally diffusing said impurities in said HSGS, a dielectric body layer forming step for forming a dielectric body layer on said first silicon layer having said HSGs on the surface thereof, and an upper electrode forming step for forming an upper electrode on said dielectric body layer, wherein the partial pressure of oxygen and water is maintained at 1×10 −6 Torr or less at least between said HSG forming step and said impurity diffusing step.
Claim 3
Dependent Claim
46 words
A method for producing a capacitor element as set forth in claim 1 , wherein said nucleus forming step, said HSG forming step, and said impurity diffusing step are carried out in the same reaction chamber of a low pressure chemical vapor deposition apparatus (LPCVD apparatus).
Claim 4
Dependent Claim
44 words
A method for producing a capacitor element as set forth in claim 2 , wherein said nucleus forming step and said HSG forming step is to make the partial pressure of the remaining PH3 gas in the reaction chamber lower than 1×10 −4 Torr.
Claim 5
Dependent Claim
52 words
A method for producing a capacitor element as set forth in claim 2 , wherein after said semiconductor substrate is removed from said reaction chamber after said impurity diffusion step, a gas including silane or disilane is introduced into said reaction chamber to reduce the normal PH3 gas in said reaction chamber.
Claim 6
Dependent Claim
71 words
A method for producing a capacitor element as set forth in claim 2 , wherein, while the minimum temperature on the inner wall of said reaction chamber is maintained at 60° C. or more, a step for progressive removing remaining PH3 gas adsorbed on a low temperature portion of the corresponding reaction chamber to reduce the amount of the remaining PH 3 gas in the corresponding reaction chamber is further provided.
Claim 7
Dependent Claim
116 words
A method for producing a capacitor element as set forth in claim 2 , wherein a step is provided, where a series of actions are repeated an appointed number of times, in which after said impurity diffusing step, an inactive gas is introduced into said reaction chamber after said semiconductor substrate is removed from said reaction chamber, the pressure of said reaction chamber is increased and is kept for an appointed period of time,.and subsequently the pressure is reduced, the low temperature portion in said reaction chamber is heated to progressively remove PH 3 gas adsorbed on the low temperature portion in said reaction chamber, and the remaining PH3 gas in said reaction chamber is reduced.
Claim 8
Dependent Claim
30 words
A method for producing a capacitor element as set forth in claim 1 , wherein said impurity diffusing step is carried out at a temperature from 550 through 600° C.
Claim 9
Dependent Claim
33 words
A method for producing a capacitor element as set forth in claim 1 , wherein the annealing temperature in the HSG forming step is substantially equal to that in the impurity diffusing step.
Claim 10
Dependent Claim
36 words
A method for producing a capacitor element as set forth in claim 1 , wherein an etching step for etching the surface area of the HSGs is further provided before said dielectric body layer forming step.
Claim 11
Dependent Claim
34 words
A method for producing a capacitor element as set forth in claim 9 , wherein said etching is performed to a depth from 1 nm through 5 nm from the surface of said HSGs.
Claim 12
Dependent Claim
42 words
A method for producing a capacitor element as set forth in claim 1 , wherein a step for lowering the concentration of impurities on the surface of said HSGs by annealing with reduced pressure is further provided after the impurity diffusing step.
Claim 13
Dependent Claim
44 words
A method for producing a capacitor element as set forth in claim 11 , wherein the concentration of impurities on the surface of said HSGs before the dielectric body layer forming step is set to a value lower than 3×10 20 atoms/cm 3 .
Claim 14
Dependent Claim
26 words
A method for producing a capacitor element as set forth in claim 1 , wherein the impurities contained in said source gas is PH 3 .
Claim 15
Dependent Claim
84 words
A method for producing a capacitor element as set forth in claim 1 , wherein said first silicon forming step is further provided, before the nucleus forming step, with a step for forming the first silicon layer on the inner wall of a recess held by an insulation layer formed on said semiconductor substrate and for removing at least a part of said insulation layer so that the first silicon layer formed on the inner wall of the recess protrudes from the corresponding recess.
Claim 16
Independent Claim
274 words
A method for producing capacitor elements constructed of a lower electrode, a dielectric body layer, and an upper electrode, which are formed on a semiconductor substrate, comprising a first silicon layer forming step for forming a first amorphous silicon layer on the entire surface including the inner wall of a recess on an insulation layer having said recess at an appointed part, a lower electrode rinsing step for rinsing and cleaning the surface of said first silicon layer, a nucleus forming step for forming a second amorphous silicon layer including microcrystal on the surface of said first silicon layer, an HSG forming step for growing HSGs (hemispherical Grains) using microcrystal included in said second silicon layer as a nucleus by annealing said first and second silicon layer at a low pressure or in the atmosphere of an inactive gas, and forming HSGs on the surface of said first silicon layer, an impurity diffusing step for forming a lower electrode by annealing while said HSGs are being exposed to a source gas including impurities and thermally diffusing said impurities in said HSGs, a lower electrode forming step for forming a lower electrode in said recess by etching back said first silicon layer having said HSGS on the surface thereof, a dielectric body layer forming step for forming a dielectric body layer on the surface of said lower electrode, and an upper electrode forming step for forming an upper electrode on the surface of said dielectric body layer, wherein the partial pressure of oxygen and water is maintained at 1×10 −6 Torr or less at least between said HSG forming step and said impurity diffusing step.
Claim 17
Independent Claim
274 words
A method for producing capacitor elements constructed of a lower electrode, a dielectric body layer, and an upper electrode, which are formed on a semiconductor substrate, comprising a first silicon layer forming step for forming a first amorphous silicon layer on the entire surface including the inner wall of a recess on an insulation layer having said recess at an appointed part, a lower electrode rinsing step for rinsing and cleaning the surface of said first silicon layer, a nucleus forming step for forming a second amorphous silicon layer including microcrystal on the surface of said first silicon layer, an HSG forming step for growing HSGs (hemispherical Grains) using microcrystal included in said second silicon layer as a nucleus by annealing said first and second silicon layer at a low pressure or in the atmosphere of an inactive gas, and forming HSGs on the surface of said first silicon layer, an impurity diffusing step for forming a lower electrode by annealing while said HSGs are being exposed to a source gas including impurities and thermally diffusing said impurities in said HSGs, a lower electrode forming step for forming a lower electrode in said recess by etching back said first silicon layer having said HSGS on the surface thereof, a dielectric body layer forming step for forming a dielectric body layer on the surface of said lower electrode, and an upper electrode forming step for forming an upper electrode on the surface of said dielectric body layer, wherein the partial pressure of oxygen and water is maintained at 1×10 −6 Torr or less at least between said HSG forming step and said impurity diffusing step.
Claim 18
Dependent Claim
46 words
A method for producing a capacitor element as set forth in claim 15 , wherein said nucleus forming step, said HSG forming step, and said impurity diffusing step are carried out in the same reaction chamber of a low pressure chemical vapor deposition apparatus (LPCVD apparatus).
Claim 19
Dependent Claim
44 words
A method for producing a capacitor element as set forth in claim 16 , wherein said nucleus forming step and said HSG forming step is to make the partial pressure of the remaining PH3 gas in the reaction chamber lower than 1×10 −4 Torr.
Claim 20
Dependent Claim
52 words
A method for producing a capacitor element as set forth in claim 16 , wherein after said semiconductor substrate is removed from said reaction chamber after said impurity diffusion step, a gas including silane or disilane is introduced into said reaction chamber to reduce the normal PH3 gas in said reaction chamber.
Claim 21
Dependent Claim
71 words
A method for producing a capacitor element as set forth in claim 16 , wherein, while the minimum temperature on the inner wall of said reaction chamber is maintained at 60° C. or more, a step for progressive removing remaining PH3 gas adsorbed on a low temperature portion of the corresponding reaction chamber to reduce the amount of the remaining PH 3 gas in the corresponding reaction chamber is further provided.
Claim 22
Dependent Claim
117 words
A method for producing a capacitor element as set forth in claim 16 , wherein a step is provided, where a series of actions are repeated an appointed number of times, in which after said impurity diffusing step, an inactive gas is introduced into said reaction chamber after said semiconductor substrate is removed from said reaction chamber, the pressure of said reaction chamber is increased and is kept for an appointed period of time, and subsequently the pressure is reduced, the low temperature portion in said reaction chamber is heated to progressively remove PH 3 gas adsorbed on the low temperature portion in said reaction chamber, and the remaining PH3 gas in said reaction chamber is reduced.
Claim 23
Dependent Claim
30 words
A method for producing a capacitor element as set forth in claim 15 , wherein said impurity diffusing step is carried out at a temperature from 550 through 600° C.
Claim 24
Dependent Claim
33 words
A method for producing a capacitor element as set forth in claim 15 , wherein the annealing temperature in the HSG forming step is substantially equal to that in the impurity diffusing step.
Claim 25
Dependent Claim
36 words
A method for producing a capacitor element as set forth in claim 15 , wherein an etching step for etching the surface area of the HSGs is further provided before said dielectric body layer forming step.
Claim 26
Dependent Claim
34 words
A method for producing a capacitor element as set forth in claim 23 , wherein said etching is performed to a depth from 1 nm through 5 nm from the surface of said HSGs.
Claim 27
Dependent Claim
42 words
A method for producing a capacitor element as set forth in claim 15 , wherein a step for lowering the concentration of impurities on the surface of said HSGs by annealing with reduced pressure is further provided after the impurity diffusing step.
Claim 28
Dependent Claim
45 words
A method for producing a capacitor element as set forth in claim 25 , wherein the concentration of impurities on the surface of said HSGs before the dielectric body layer forming step is set to a value lower than 3×10 20 atoms /cm 3 .
Claim 29
Dependent Claim
50 words
A method for producing a capacitor element as set forth in claim 15 , wherein a step for removing at least a part of the insulation layer so that the lower electrode in said recess protrudes from said insulation layer is further provided before said dielectric body layer forming step.
Claim 30
Dependent Claim
55 words
A method for producing a capacitor element as set forth in claim 15 , wherein a step for forming a protective material, which protects the inside of said recess when etching back in the corresponding lower electrode forming step, on said first silicon layer having said HSGs is provided before said lower electrode forming step.
Claim 31
Independent Claim
258 words
A method for producing capacitor elements constructed of a lower electrode, a dielectric body layer, and an upper electrode, which are formed on a semiconductor substrate, comprising: a first silicon layer forming step for forming a first amorphous silicon layer on the entire surface including the inner wall of a recess on an insulation layer having said recess at an appointed part, a nucleus forming step for forming a second amorphous silicon layer including microcrystal on the surface of said first silicon layer, an HSG forming step for growing HSGs (hemispherical Grains) using microcrystal included in said second silicon layer as a nucleus by annealing said first and second silicon layer at a low pressure or in the atmosphere of an inactive gas, and forming HSGs on the surface of said first silicon layer, an impurity diffusing step for forming a lower electrode by annealing while said HSGs are being exposed to a source gas including impurities and thermally diffusing said impurities in said HSGs, a lower electrode forming step for forming a lower electrode in said recess by etching back said first silicon layer having said HSGs on the surface thereof, a dielectric body layer forming step for forming a dielectric body layer on the surface of said lower electrode, and an upper electrode forming step for forming an upper electrode on the surface of said dielectric body layer, wherein the partial pressure of oxygen and water is maintained at 1×10 −6 Torr or less at least between said HSG forming step and said impurity diffusing step.
Claim 32
Independent Claim
258 words
A method for producing capacitor elements constructed of a lower electrode, a dielectric body layer, and an upper electrode, which are formed on a semiconductor substrate, comprising: a first silicon layer forming step for forming a first amorphous silicon layer on the entire surface including the inner wall of a recess on an insulation layer having said recess at an appointed part, a nucleus forming step for forming a second amorphous silicon layer including microcrystal on the surface of said first silicon layer, an HSG forming step for growing HSGs (hemispherical Grains) using microcrystal included in said second silicon layer as a nucleus by annealing said first and second silicon layer at a low pressure or in the atmosphere of an inactive gas, and forming HSGs on the surface of said first silicon layer, an impurity diffusing step for forming a lower electrode by annealing while said HSGs are being exposed to a source gas including impurities and thermally diffusing said impurities in said HSGs, a lower electrode forming step for forming a lower electrode in said recess by etching back said first silicon layer having said HSGs on the surface thereof, a dielectric body layer forming step for forming a dielectric body layer on the surface of said lower electrode, and an upper electrode forming step for forming an upper electrode on the surface of said dielectric body layer, wherein the partial pressure of oxygen and water is maintained at 1×10 −6 Torr or less at least between said HSG forming step and said impurity diffusing step.
Claim 33
Dependent Claim
52 words
A method for producing a capacitor element as set forth in claim 29 , wherein said first silicon layer forming step, said nucleus forming step, said HSG forming step, and said impurity diffusing step are carried out in the same reaction chamber of a low pressure chemical vapor deposition apparatus (LPCVD apparatus).
Claim 34
Dependent Claim
44 words
A method for producing a capacitor element as set forth in claim 30 , wherein said nucleus forming step and said HSG forming step is to make the partial pressure of the remaining PH3 gas in the reaction chamber lower than 1×10 −4 Torr.
Claim 35
Dependent Claim
52 words
A method for producing a capacitor element as set forth in claim 30 , wherein after said semiconductor substrate is removed from said reaction chamber after said impurity diffusion step, a gas including silane or disilane is introduced into said reaction chamber to reduce the normal PH3 gas in said reaction chamber.
Claim 36
Dependent Claim
71 words
A method for producing a capacitor element as set forth in claim 30 , wherein, while the minimum temperature on the inner wall of said reaction chamber is maintained at 60° C. or more, a step for progressive removing remaining PH3 gas adsorbed on a low temperature portion of the corresponding reaction chamber to reduce the amount of the remaining PH 3 gas in the corresponding reaction chamber is further provided.
Claim 37
Dependent Claim
117 words
A method for producing a capacitor element as set forth in claim 30 , wherein a step is provided, where a series of actions are repeated an appointed number of times, in which after said impurity diffusing step, an inactive gas is introduced into said reaction chamber after said semiconductor substrate is removed from said reaction chamber, the pressure of said reaction chamber is increased and is kept for an appointed period of time, and subsequently the pressure is reduced, the low temperature portion in said reaction chamber is heated to progressively remove PH 3 gas adsorbed on the low temperature portion in said reaction chamber, and the remaining PH3 gas in said reaction chamber is reduced.
Claim 38
Dependent Claim
30 words
A method for producing a capacitor element as set forth in claim 29 , wherein said impurity diffusing step is carried out at a temperature from 550 through 600° C.
Claim 39
Dependent Claim
33 words
A method for producing a capacitor element as set forth in claim 29 , wherein the annealing temperature in the HSG forming step is substantially equal to that in the impurity diffusing step.
Claim 40
Dependent Claim
36 words
A method for producing a capacitor element as set forth in claim 29 , wherein an etching step for etching the surface area of the HSGs is further provided before said dielectric body layer forming step.
Claim 41
Dependent Claim
34 words
A method for producing a capacitor element as set forth in claim 37 , wherein said etching is performed to a depth from 1 nm through 5 nm from the surface of said HSGs.
Claim 42
Dependent Claim
42 words
A method for producing a capacitor element as set forth in claim 29 , wherein a step for lowering the concentration of impurities on the surface of said HSGs by annealing with reduced pressure is further provided after the impurity diffusing step.
Claim 43
Dependent Claim
44 words
A method for producing a capacitor element as set forth in claim 39 , wherein the concentration of impurities on the surface of said HSGs before the dielectric body layer forming step is set to a value lower than 3×10 20 atoms/cm 3 .
Claim 44
Dependent Claim
50 words
A method for producing a capacitor element as set forth in claim 29 , wherein a step for removing at least a part of the insulation layer so that the lower electrode in said recess protrudes from said insulation layer is further provided before said dielectric body layer forming step.
Claim 45
Dependent Claim
55 words
A method for producing a capacitor element as set forth in claim 29 , wherein a step for forming a protective material, which protects the inside of said recess when etching back in the corresponding lower electrode forming step, on said first silicon layer having said HSGs is provided before said lower electrode forming step.
References Cited (Backward Citations)
JPH09298278A
Cited
JPH1070249A
Cited
JPH10303368A
Cited
US6228749B1
Cited
JPH11145392A
Cited
US6187623B1
Cited
US6218230B1
Cited
US5897352A
Cited
US5930625A
Cited
US6046083A
Cited
US5913119A
Cited
US20010030336A1
Cited
US6171955B1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2005-04-22 | 2005-10-22 | 2006-04-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2009-04-22 | 2009-10-22 | 2010-04-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2013-04-22 | 2013-10-22 | 2014-04-23 | $7700.00 | Window Closed / Lapsed |