Abstract
Abstract A method of shaping three-dimensional products by manipulating an expanded polytetrafluoroethylene tubular body into a desired three-dimensional conformation. The present invention entails radially expanding a longitudinally expanded polytetrafluoroethylene (ePTFE) tube to form a radially expanded ePTFE (rePTFE) tube, engaging the rePTFE tube circumferentially about a shaping mandrel, heating the assembly to a temperature below the crystalline melt point temperature, or sintering temperature, of polytetrafluoroethylene to radially shrink the diameter of the rePTFE tube into intimate contact with the shaping mandrel, and heating the assembly to a temperature above the crystalline melt point temperature of polytetrafluoroethylene to amorphously lock the microstructure of the shaped polytetrafluoroethylene body.
Inventors
- 👤 Tarun J. Edwin
- 👤 Scott Randall
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 11:49
CPC Classifications
A; A61; A61F; A61F2/00; A61F2/02; A61F2/04; A61F2/06; B; B29; B29C; B29C55/00; B29C55/22; B29C55/26; B29C61/00; B29C61/02; B29C61/025; A61F2/07; A61F2002/061; A61F2002/065; A61F2002/075; B29K; B29K2027/00; B29K2027/12; B29K2027/18; B29L; B29L2031/00; B29L2031/753; B29L2031/7532; B29L2031/7534
Claims Analysis
Total Claims: 26
Claim 1
Independent Claim
220 words
A method for shaping expanded polytetrafluorocthylene tubes into a shaped three-dimensional article, comprising the steps of: (a) extruding an admixture of polytetrafluoroethylenc resin and lubricant into a tubular extrudate; (b) drying the tubular extrudate to remove at least a major fraction of the lubricant; (c) longitudinally expanding the tubular extridate forming a longitudinally expanded tubular extrudate with a polytetrafluoroethylene microstructure having a plurality of nodes interconnected by fibrils; (d) at least partially sintering the longitudinally expanded tubular extrudate forming an at least partially sintered longitudinally expanded tubular extrudate having a dimensional stability greater than the longitudinally expanded tubular extrudate; (e) radially expanding the at least partially sintered tubular extrudate at a temperature greater than ambient but below the crystalline melt point of polytetrafluoroethylene forming a radially expanded at least partially sintered longitudinally expanded tubular extrudate with a diameter greater than that of the at least partially sintered longitudinally expanded tubular extrudate; (f) engaging the radially expanded at least partially sintered tubular extrudate circumferentially about a shaping mandrel, the shaping mandrel having a shaped three-dimensional conformation; and (g) heating the shaping mandrel and the radially expanded at least partially sintered tubular extrudate, shrinking the radially expanded at least partially sintered tubular extrudate into intimate contact with the shaping mandrel so that said extrudate adopts the three-dimensional conformation of the shaping mandrel.
Claim 2
Independent Claim
220 words
A method for shaping expanded polytetrafluorocthylene tubes into a shaped three-dimensional article, comprising the steps of: (a) extruding an admixture of polytetrafluoroethylenc resin and lubricant into a tubular extrudate; (b) drying the tubular extrudate to remove at least a major fraction of the lubricant; (c) longitudinally expanding the tubular extridate forming a longitudinally expanded tubular extrudate with a polytetrafluoroethylene microstructure having a plurality of nodes interconnected by fibrils; (d) at least partially sintering the longitudinally expanded tubular extrudate forming an at least partially sintered longitudinally expanded tubular extrudate having a dimensional stability greater than the longitudinally expanded tubular extrudate; (e) radially expanding the at least partially sintered tubular extrudate at a temperature greater than ambient but below the crystalline melt point of polytetrafluoroethylene forming a radially expanded at least partially sintered longitudinally expanded tubular extrudate with a diameter greater than that of the at least partially sintered longitudinally expanded tubular extrudate; (f) engaging the radially expanded at least partially sintered tubular extrudate circumferentially about a shaping mandrel, the shaping mandrel having a shaped three-dimensional conformation; and (g) heating the shaping mandrel and the radially expanded at least partially sintered tubular extrudate, shrinking the radially expanded at least partially sintered tubular extrudate into intimate contact with the shaping mandrel so that said extrudate adopts the three-dimensional conformation of the shaping mandrel.
Claim 3
Dependent Claim
31 words
The method according to claim 1 , wherein said step of at least partially sintering the longitudinally expanded tubular extrudate results in a crystalline conversion factor of 1 within said extrudate.
Claim 4
Dependent Claim
33 words
The method according to claim 1 , wherein the step of at least partially sintering the longitudinally expanded tubular extrudate results in a crystalline conversion value between 0.10 and 0.85 within said extrudate.
Claim 5
Dependent Claim
35 words
The method according to claim 1 , further comprising a step of fully sintering following the step of shrinking the radially expanded at least partially sintered tubular extrudate into intimate contact with the shaping mandrel.
Claim 6
Dependent Claim
60 words
The method according to claim 1 , wherein the step of heating the shaping mandrel comprises exposing the shaping mandrel and the radially expanded at least partially sintered tubular extrudate to a temperature below the crystalline melt point of polytetrafluoroethylene but above the temperature at which the step of radially expanding the at lest partially sintered tubular extrudate is conducted.
Claim 7
Independent Claim
189 words
A method for shaping expanded polytetrafluoroethylene tubes into a shaped three-dimensional article, comprising the steps of: extruding a mixture of polytetrafluorocthylene resin particles and lubricant to form a tubular extrudate; drying the tubular extrudate to remove at least a major fraction of the lubricant; longitudinally expanding the tubular extrudate to form an expanded polytetrafluoroethylene extridate having a microstructure of a plurality of nodes interconnected by fibrils; at least partially sintering the expanded polytetrafluoroethylene extrudate to form a sintered expanded extrudate having a dimensional stability greater than the expanded polytetrafluoroethylene extrudate; radially expanding the sintered expanded extrudate at a temperature greater than ambient but below the crystalline melt point of polytetrafluoroethylene forming a radially expanded sintered extrudate with a diameter greater than a diameter of the sintered expanded extrudate; engaging the radially expanded sintered extrudate circumferentially about a shaping mandrel, the shaping mandrel having a shaped three-dimensional conformation; heating the shaping mandrel and the radially expanded sintered extrudate to shrink the radially expanded sintered extrudate into intimate contact with the shaping mandrel so that said extrudate adopts the three-dimensional conformation of the shaping mandrel; and sintering the heat shrunken extrudate.
Claim 8
Independent Claim
189 words
A method for shaping expanded polytetrafluoroethylene tubes into a shaped three-dimensional article, comprising the steps of: extruding a mixture of polytetrafluorocthylene resin particles and lubricant to form a tubular extrudate; drying the tubular extrudate to remove at least a major fraction of the lubricant; longitudinally expanding the tubular extrudate to form an expanded polytetrafluoroethylene extridate having a microstructure of a plurality of nodes interconnected by fibrils; at least partially sintering the expanded polytetrafluoroethylene extrudate to form a sintered expanded extrudate having a dimensional stability greater than the expanded polytetrafluoroethylene extrudate; radially expanding the sintered expanded extrudate at a temperature greater than ambient but below the crystalline melt point of polytetrafluoroethylene forming a radially expanded sintered extrudate with a diameter greater than a diameter of the sintered expanded extrudate; engaging the radially expanded sintered extrudate circumferentially about a shaping mandrel, the shaping mandrel having a shaped three-dimensional conformation; heating the shaping mandrel and the radially expanded sintered extrudate to shrink the radially expanded sintered extrudate into intimate contact with the shaping mandrel so that said extrudate adopts the three-dimensional conformation of the shaping mandrel; and sintering the heat shrunken extrudate.
Claim 9
Independent Claim
191 words
A method for shaping expanded polytetrafluoroethylene tubes into a shaped three-dimensional article, comprising the steps of: extruding an admixture of polytetrafluoroethylene resin and lubricant into a tubular extrudate; longitudinally expanding the tubular extrudate forming a longitudinally expanded tubular extrudate with a polytetrafluoroethylene microstructure having a plurality of nodes interconnected by fibrils; at least partially sintering the longitudinally expanded tubular extrudate forming an at least partially sintered longitudinally expanded tubular extrudate having a dimensional stability greater than the longitudinally expanded tubular extrudate; radially expanding the at least partially sintered longitudinally expanded tubular extrudate at a temperature greater than ambient but below the crystalline melt point of polytetrafluoroethylene forming a radially expanded at least partially sintered extrudate with a diameter that is 200%-400% greater than that of the at least partially sintered longitudinally expanded tubular extrudate; engaging the radially expanded at least partially sintered extrudate circumferentially about a shaping mandrel, the shaping mandrel having a shaped three-dimensional conformation; and heating the shaping mandrel and the radially expanded at least partially sintered extrudate, shrinking said extrudate into intimate contact with the shaping mandrel so that said extrudate adopts the three-dimensional conformation of shaping mandrel.
Claim 10
Independent Claim
191 words
A method for shaping expanded polytetrafluoroethylene tubes into a shaped three-dimensional article, comprising the steps of: extruding an admixture of polytetrafluoroethylene resin and lubricant into a tubular extrudate; longitudinally expanding the tubular extrudate forming a longitudinally expanded tubular extrudate with a polytetrafluoroethylene microstructure having a plurality of nodes interconnected by fibrils; at least partially sintering the longitudinally expanded tubular extrudate forming an at least partially sintered longitudinally expanded tubular extrudate having a dimensional stability greater than the longitudinally expanded tubular extrudate; radially expanding the at least partially sintered longitudinally expanded tubular extrudate at a temperature greater than ambient but below the crystalline melt point of polytetrafluoroethylene forming a radially expanded at least partially sintered extrudate with a diameter that is 200%-400% greater than that of the at least partially sintered longitudinally expanded tubular extrudate; engaging the radially expanded at least partially sintered extrudate circumferentially about a shaping mandrel, the shaping mandrel having a shaped three-dimensional conformation; and heating the shaping mandrel and the radially expanded at least partially sintered extrudate, shrinking said extrudate into intimate contact with the shaping mandrel so that said extrudate adopts the three-dimensional conformation of shaping mandrel.
Claim 11
Dependent Claim
31 words
The method according to claim 7 , wherein said step of at least partially sintering the longitudinally expanded tubular extrudate results in a crystalline conversion factor of 1 within said extrudate.
Claim 12
Dependent Claim
33 words
The method according to claim 7 , wherein the step of at least partially sintering the longitudinally expanded tubular extrudate results in a crystalline conversion value between 0.10 and 0.85 within said extrudate.
Claim 13
Dependent Claim
35 words
The method according to claim 7 , further comprising a step of fully sintering following the step of shrinking the radially expanded at least partially sintered tubular extrudate into intimate contact with the shaping mandrel.
Claim 14
Dependent Claim
60 words
The method according to claim 7 , wherein the step of heating the shaping mandrel comprises exposing the shaping mandrel and the radially expanded at least partially sintered tubular extrudate to a temperature below the crystalline melt point of polytetrafluoroethylene but above the temperature at which the step of radially expanding the at least partially sintered tubular extrudate is conducted.
Claim 15
Independent Claim
195 words
A method for shaping expanded polytetrafluoroethylene tubes into a shaped three-dimensional article, comprising the steps of: extruding a mixture of polytetrafluoroethylene resin particles and lubricant to form a tubular extrudate; drying the tubular extrudate to remove a major fraction of the lubricant; longitudinally expanding the tubular extrudate to form an expanded polytetrafluoroethylene extrudate having a microstructure of a plurality of nodes interconnected by fibrils; at least partially sintering the expanded polytctrafluoroethylene extrudate to form a sintered expanded extrudate having a dimensional stability greater than the expanded polytetrafluoroethylene extrudate; radially expanding the sintered expanded extrudate at a temperature greater than ambient but below the crystalline melt point of polytetrafluoroethylene within a constraining chamber to form a radially expanded sintered extrudate with a diameter greater than a diameter of the sintered expanded extrudate, shaped by and in intimate contact with an inner surface of the constraining chamber; engaging the radially expanded sintered extrudate circumferentially about a shaping mandrel, the shaping mandrel having a shaped three-dimensional conformation; heating the shaping mandrel and the radially expanded sintered extrudate, shrinking said extrudate so that said extrudate adopts the three-dimensional conformation of the shaping mandrel; and sintering the heat shrunken extrudate.
Claim 16
Independent Claim
195 words
A method for shaping expanded polytetrafluoroethylene tubes into a shaped three-dimensional article, comprising the steps of: extruding a mixture of polytetrafluoroethylene resin particles and lubricant to form a tubular extrudate; drying the tubular extrudate to remove a major fraction of the lubricant; longitudinally expanding the tubular extrudate to form an expanded polytetrafluoroethylene extrudate having a microstructure of a plurality of nodes interconnected by fibrils; at least partially sintering the expanded polytctrafluoroethylene extrudate to form a sintered expanded extrudate having a dimensional stability greater than the expanded polytetrafluoroethylene extrudate; radially expanding the sintered expanded extrudate at a temperature greater than ambient but below the crystalline melt point of polytetrafluoroethylene within a constraining chamber to form a radially expanded sintered extrudate with a diameter greater than a diameter of the sintered expanded extrudate, shaped by and in intimate contact with an inner surface of the constraining chamber; engaging the radially expanded sintered extrudate circumferentially about a shaping mandrel, the shaping mandrel having a shaped three-dimensional conformation; heating the shaping mandrel and the radially expanded sintered extrudate, shrinking said extrudate so that said extrudate adopts the three-dimensional conformation of the shaping mandrel; and sintering the heat shrunken extrudate.
Claim 17
Dependent Claim
36 words
The method according to claim 12 , further comprising a step of applying pressure to the radially expanded sintered extrudate to bring said extrudate into intimate contact with the shaping mandrel prior to the heating step.
Claim 18
Dependent Claim
30 words
The method according to claim 12 , wherein the step of at least partially sintering the expanded polytetrafluoroethylene extrudate results in a crystalline conversion factor of 1 within said extrudate.
Claim 19
Dependent Claim
32 words
The method according to claim 12 , wherein the step of at least partially sintering the expanded polytetrafluoroethylene extrudate results in a crystalline conversion value between 0.10 and 0.85 within said extrudate.
Claim 20
Dependent Claim
53 words
The method according to claim 12 , wherein the step of heating the shaping mandrel comprises exposing the shaping mandrel and the radially expanded sintered extrudate to a temperature below the crystalline melt point of polytetrafluoroethylene but above the temperature at which the step of radially expanding the sintered expanded extrudate is conducted.
Claim 21
Independent Claim
191 words
A method for shaping expanded polytetrafluoroethylene tubes into a shaped three-dimensional article, comprising the steps of: extruding an admixture of polytetrafluoroethylene resin and lubricant into a tubular extrudate; drying the tubular extrudate to remove at least a major fraction of the lubricant; longitudinally expanding the tubular extrudate to form an expanded polytetrafluoroethylene extrudate having a microstructure of a plurality of nodes interconnected by fibrils; at least partially sintering the expanded polytetrafluoroethylene extrudate to form a sintered expanded extrudate having a dimensional stability greater than the longitudinally expanded tubular extrudate; radially expanding the sintered expanded extrudate at a temperature greater than ambient but below the crystalline melt point of polytetrafluoroethylene to form a radially expanded sintered extrudate with a diameter greater than that of the sintered expanded extrudate; engaging the radially expanded sintered extrudate circumferentially about a shaping mandrel, the shaping mandrel having a shaped three-dimensional conformation; applying pressure to the radially expanded sintered extrudate, to bring said extrudate into intimate contact with the shaping mandrel; and heating the shaping mandrel and the radially expanded sintered extrudate, shrinking said extrudate so that said extrudate adopts the three-dimensional conformation of the shaping mandrel.
Claim 22
Independent Claim
191 words
A method for shaping expanded polytetrafluoroethylene tubes into a shaped three-dimensional article, comprising the steps of: extruding an admixture of polytetrafluoroethylene resin and lubricant into a tubular extrudate; drying the tubular extrudate to remove at least a major fraction of the lubricant; longitudinally expanding the tubular extrudate to form an expanded polytetrafluoroethylene extrudate having a microstructure of a plurality of nodes interconnected by fibrils; at least partially sintering the expanded polytetrafluoroethylene extrudate to form a sintered expanded extrudate having a dimensional stability greater than the longitudinally expanded tubular extrudate; radially expanding the sintered expanded extrudate at a temperature greater than ambient but below the crystalline melt point of polytetrafluoroethylene to form a radially expanded sintered extrudate with a diameter greater than that of the sintered expanded extrudate; engaging the radially expanded sintered extrudate circumferentially about a shaping mandrel, the shaping mandrel having a shaped three-dimensional conformation; applying pressure to the radially expanded sintered extrudate, to bring said extrudate into intimate contact with the shaping mandrel; and heating the shaping mandrel and the radially expanded sintered extrudate, shrinking said extrudate so that said extrudate adopts the three-dimensional conformation of the shaping mandrel.
Claim 23
Dependent Claim
39 words
The method according to claim 17 , wherein said step of radially expanding takes place within a constraining chamber, wherein the radially expanded sintered extrudate comes into intimate contact with an inner surface of the constraining chamber upon expanding.
Claim 24
Dependent Claim
30 words
The method according to claim 17 , wherein said step of at least partially sintering the expanded polytetrafluoroethylene extrudate results in a crystalline conversion factor of 1 within said extrudate.
Claim 25
Dependent Claim
32 words
The method according to claim 17 , wherein the step of at least partially sintering the expanded polytetrafluoroethylene extrudate results in a crystalline conversion value between 0.10 and 0.85 within said extrudate.
Claim 26
Dependent Claim
53 words
The method according to claim 17 , wherein the step of heating the shaping mandrel comprises exposing the shaping mandrel and the radially expanded sintered extrudate to a temperature below the crystalline melt point of polytetrafluoroethylene but above the temperature at which the step of radially expanding the sintered expanded extrudate is conducted.
References Cited (Backward Citations)
US3196194A
Cited
US4104394A
Cited
US4208745A
Cited
US4234535A
Cited
USRE31341E
Cited
US4596837A
Cited
US4714748A
Cited
US4760102A
Cited
US4647416A
Cited
US4671754A
Cited
US4655769A
Cited
US4830062A
Cited
US5071609A
Cited
US5061276A
Cited
US4816339A
Cited
US5171805A
Cited
US4957669A
Cited
US5387236A
Cited
US5152782A
Cited
US5084065A
Cited
US5123917A
Cited
US5143122A
Cited
US5376110A
Cited
US5234739A
Cited
EP0648869A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2004-03-19 | 2004-09-18 | 2005-03-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2008-03-19 | 2008-09-18 | 2009-03-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2012-03-19 | 2012-09-18 | 2013-03-20 | $7700.00 | Window Closed / Lapsed |