Method of making a hollow, interiorly coated glass body and a glass tube as a semi-finished product for forming the glass body
Assignee: Schott AG
•
Filing: 1999-01-19
•
Granted: 2001-03-13
•
Expires: 2019-01-19
Abstract
Abstract Numerous applications for hollow glass bodies made from low melting glass material require an increase in the chemical resistance of the interior surface of the glass body. In order to avoid a disadvantageous de-alkalizing process the hollow glass body must be provided with an interior coating in a comparatively expensive prior art process. In an improved process according to the invention a glass tube acting as a semifinished product from which the hollow glass body is made is provided with an interior coating of oxide material, preferably SiO2, Al2O3, TiO2 or mixtures thereof, having a predetermined coating thickness according to the required chemical resistance or working conditions for forming the glass body and then the hollow glass body is made from the glass tube. The coating is advantageously provided by means of a PICVD process.
Inventors
- 👤 Marten Walther
- 👤 Michael Spallek
- 👤 Burkhardt Danielzik
- 👤 Martin Heming
- 👤 Johannes Segner
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 02:00
CPC Classifications
C; C03; C03C; C03C17/00; C03C17/22; C03C17/23; C03C17/25; C03C17/256; C03C17/001; C03C17/003; C03C17/004; C03C17/245; C03C17/2456; C23; C23C; C23C18/00; C23C18/02; C23C18/12; C23C18/125; C23C18/1254; Y; Y10; Y10T; Y10T428/00; Y10T428/13; Y10T428/131; Y10T428/1314; Y10T428/1317
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
100 words
A glass tube made from low melting glass material and acting as a semi-finished product or intermediate for making a hollow, interiorly coated glass body with an interior coating increasing a chemical resistance of said hollow, interiorly coated glass body, said glass body being formed by shaping or working, wherein said glass tube has an interior surface and a coating of oxide material on said interior surface, and said coating has a predetermined coating thickness, whereby required shaping or working conditions for making said glass body from said glass tube and chemical resistance requirements for said glass body are met.
Claim 2
Dependent Claim
100 words
A glass tube made from low melting glass material and acting as a semi-finished product or intermediate for making a hollow, interiorly coated glass body with an interior coating increasing a chemical resistance of said hollow, interiorly coated glass body, said glass body being formed by shaping or working, wherein said glass tube has an interior surface and a coating of oxide material on said interior surface, and said coating has a predetermined coating thickness, whereby required shaping or working conditions for making said glass body from said glass tube and chemical resistance requirements for said glass body are met.
Claim 3
Dependent Claim
31 words
The glass tube as defined in claim 1 , wherein said coating thickness is in a range from 1 nm and 500 nm or from about 1 nm to 500 nm.
Claim 4
Dependent Claim
20 words
The glass tube as defined in claim 1 , wherein said coating thickness is between about 1 to 5 nm.
Claim 5
Dependent Claim
27 words
The glass tube as defined in claim 1 , wherein said oxide material comprises SiO 2 , Al 2 O 3 , TiO 2 or mixtures thereof.
Claim 6
Dependent Claim
68 words
The glass tube as defined in claim 1 , wherein said coating is provided on the interior surface of the glass tube by a method comprising a chemical vapor deposition process and including passing a mixture of a reaction gas and oxygen through the glass tube and forming a microwave discharge in the mixture in the glass tube, said reaction gas comprising hexamethyidisiloxane, tetramethyldisiloxane, titanium tetraisopropoxide or silazane.
Claim 7
Dependent Claim
159 words
A glass tube with an interior oxide coating, said glass tube with said interior oxide coating being made by a method comprising the steps of: a) providing a glass tube consisting of a low melting glass material and having an interior surface; and b) coating said interior surface of said glass tube provided in step a) with an oxide selected from the group consisting of SiO 2 , Al 2 O 3 and TiO 2 or with a mixture of at least two members selected from the group consisting of SiO 2 , Al 2 O 3 and TiO 2 to form the interior oxide coating with a thickness of from about 1 nm to 500 nm; whereby said glass tube with said interior oxide coating is an intermediate product for making a hollow, interiorly coated glass body from said glass tube by shaping or working so that said hollow, interiorly coated glass body has an increased chemical resistance.
Claim 8
Dependent Claim
159 words
A glass tube with an interior oxide coating, said glass tube with said interior oxide coating being made by a method comprising the steps of: a) providing a glass tube consisting of a low melting glass material and having an interior surface; and b) coating said interior surface of said glass tube provided in step a) with an oxide selected from the group consisting of SiO 2 , Al 2 O 3 and TiO 2 or with a mixture of at least two members selected from the group consisting of SiO 2 , Al 2 O 3 and TiO 2 to form the interior oxide coating with a thickness of from about 1 nm to 500 nm; whereby said glass tube with said interior oxide coating is an intermediate product for making a hollow, interiorly coated glass body from said glass tube by shaping or working so that said hollow, interiorly coated glass body has an increased chemical resistance.
Claim 9
Dependent Claim
20 words
The glass tube as defined in claim 6 , wherein said thickness is from about 1 nm to 5 nm.
Claim 10
Dependent Claim
43 words
The glass tube as defined in claim 6 , wherein said method comprises chemical vapor deposition (CVD) of said interior oxide coating on said interior surface from a gas phase by vacuum-assisted plasma enhanced chemical vapor deposition or plasma impulse chemical vapor deposition.
Claim 11
Dependent Claim
31 words
The glass tube as defined in claim 6 , wherein said method comprises depositing said oxide coating from a liquid phase according to a sol-gel process or from a supersatured solution.
References Cited (Backward Citations)
US3314772A
Cited
US4882209A
Cited
DE3924830A1
Cited
DE4008405C1
Cited
US5154943A
Cited
DE9404753U1
Cited
DE4438359A1
Cited
DE29609958U1
Cited
DE19629877C1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2004-03-12 | 2004-09-11 | 2005-03-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2008-03-12 | 2008-09-11 | 2009-03-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2012-03-12 | 2012-09-11 | 2013-03-13 | $7700.00 | Window Closed / Lapsed |