Silicon thin film, group of silicon single crystal grains and formation process thereof, and semiconductor device, flash memory cell and fabrication process thereof
Assignee: Japan Display West Inc
•
Filing: 1997-05-21
•
Granted: 2001-02-20
•
Expires: 2017-05-21
Abstract
Abstract A process of forming a silicon thin film includes the steps of: irradiating a pulsed rectangular ultraviolet beam on an amorphous or polycrystalline silicon layer formed on a base body, to thereby form a silicon thin film composed of a group of silicon single crystal grains which are each approximately rectangular-shaped and which are arranged in a grid pattern on the base body. In this process, the moved amount of a ultraviolet beam irradiating position in a period from completion of an irradiation of the rectangular ultraviolet beam to starting of the next irradiation of the rectangular ultraviolet beam is specified at 40 mum or less, and a ratio of the moved amount to a width of the rectangular ultraviolet beam measured in the movement direction thereof is in a range of 0.1 to 5%. Further, a selected orientation of the silicon single crystal grains to the surface of the base body is approximately the <100> direction.
Inventors
- 👤 Takashi Noguchi
- 👤 Yasuhiro Kanaya
- 👤 Masafumi Kunii
- 👤 Yuji Ikeda
- 👤 Setsuo Usui
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 07:52
CPC Classifications
H; H10; H10P; H10P14/00; H10P14/20; H10P14/38; H10P14/3802; H10P14/3808; H10P14/3816; B; B82; B82Y; B82Y10/00; H10D; H10D30/00; H10D30/01; H10D30/021; H10D30/031; H10D30/0312; H10D30/0316; H10D30/0321; H10D30/60; H10D30/67; H10D30/6729; H10D30/673; H10D30/6732; H10D30/674; H10D30/6741; H10D30/6743; H10D30/6745; H10D64/00; H10D64/01; H10D64/031; H10D64/035; H10P14/29; H10P14/2901; H10P14/2902; H10P14/2905; H10P14/2921; H10P14/2922; H10P14/32; H10P14/3202; H10P14/3238; H10P14/3241; H10P14/3242; H10P14/3244; H10P14/3248; H10P14/34; H10P14/3402; H10P14/3404; H10P14/3411; H10P14/3451; H10P14/3452; H10P14/3456; H10P14/3458; H10P14/3466; H10P14/382; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24355; Y10T428/24372
Claims Analysis
Total Claims: 25
Claim 1
Independent Claim
181 words
A process of forming a silicon thin film, comprising the steps of: irradiating a pulsed rectangular ultraviolet beam on an amorphous or polycrystalline silicon layer formed on a base body, to thereby form a silicon thin film composed of a group of silicon single crystal grains on said base body; moving the beam with the moved amount of an ultraviolet beam irradiating position in a period from completion of an irradiation pulse of said rectangular ultraviolet beam to starting of the next irradiation pulse of said rectangular ultraviolet beam being in a range of 4 μm to 20 μm, and a ratio of said moved amount to a width of said rectangular ultraviolet beam measured in the movement direction thereof being in a range of 0.1 to 5%, to form a silicon thin film composed of a group of silicon single crystal grains which are each approximately rectangular-shaped and which are arranged in a grid pattern on said base body, a selected orientation of said silicon single crystal grains to the surface of said base body being approximately the <100> direction.
Claim 2
Dependent Claim
181 words
A process of forming a silicon thin film, comprising the steps of: irradiating a pulsed rectangular ultraviolet beam on an amorphous or polycrystalline silicon layer formed on a base body, to thereby form a silicon thin film composed of a group of silicon single crystal grains on said base body; moving the beam with the moved amount of an ultraviolet beam irradiating position in a period from completion of an irradiation pulse of said rectangular ultraviolet beam to starting of the next irradiation pulse of said rectangular ultraviolet beam being in a range of 4 μm to 20 μm, and a ratio of said moved amount to a width of said rectangular ultraviolet beam measured in the movement direction thereof being in a range of 0.1 to 5%, to form a silicon thin film composed of a group of silicon single crystal grains which are each approximately rectangular-shaped and which are arranged in a grid pattern on said base body, a selected orientation of said silicon single crystal grains to the surface of said base body being approximately the <100> direction.
Claim 3
Dependent Claim
32 words
A process of forming a silicon thin film according to claim 1 , wherein a length of one side of said silicon single crystal grain approximately rectangular-shaped is 0.05 μm or more.
Claim 4
Dependent Claim
34 words
A process of forming a silicon thin film according to claim 1 , wherein an average thickness of said silicon thin film is in a range of 1×10 −8 m to 1×10 −7 m.
Claim 5
Dependent Claim
25 words
A process of forming a silicon thin film according to claim 1 , wherein said base body is made of silicon oxide or silicon nitride.
Claim 6
Dependent Claim
52 words
A process of forming a silicon thin film according to claim 1 , wherein opposed sides of said silicon single crystal grain approximately rectangular-shaped are approximately in parallel to the movement direction of the ultraviolet beam irradiating position or intersect the movement direction of the ultraviolet beam irradiating position at approximately 45°.
Claim 7
Dependent Claim
179 words
A process of forming a group of silicon single crystal grains comprising: a step (a) of irradiating a pulsed rectangular ultraviolet beam on an amorphous or polycrystalline silicon layer formed on a base body, to thereby form a silicon thin film composed of a group of silicon single crystal grains which are each approximately rectangular-shaped and which are arranged in a grid pattern on said base body, a selected orientation of said silicon single crystal grains to the surface of said body being approximately the <100> direction; and a step (b) of separating adjacent ones of said silicon single crystal grains to each other; wherein the moved amount of an ultraviolet beam irradiating position in a period from completion of an irradiation pulse of said rectangular ultraviolet beam to starting of the next irradiation pulse of said rectangular ultraviolet beam being in a range of 4 μm to 20 μm, and a ratio of said moved amount to a width of said rectangular ultraviolet beam measured in the movement direction thereof being in a range of 0.1 to 5%.
Claim 8
Dependent Claim
179 words
A process of forming a group of silicon single crystal grains comprising: a step (a) of irradiating a pulsed rectangular ultraviolet beam on an amorphous or polycrystalline silicon layer formed on a base body, to thereby form a silicon thin film composed of a group of silicon single crystal grains which are each approximately rectangular-shaped and which are arranged in a grid pattern on said base body, a selected orientation of said silicon single crystal grains to the surface of said body being approximately the <100> direction; and a step (b) of separating adjacent ones of said silicon single crystal grains to each other; wherein the moved amount of an ultraviolet beam irradiating position in a period from completion of an irradiation pulse of said rectangular ultraviolet beam to starting of the next irradiation pulse of said rectangular ultraviolet beam being in a range of 4 μm to 20 μm, and a ratio of said moved amount to a width of said rectangular ultraviolet beam measured in the movement direction thereof being in a range of 0.1 to 5%.
Claim 9
Dependent Claim
65 words
A process of forming a group of silicon single crystal grains according to claim 6 , wherein said step (b) of separating adjacent ones of said silicon single crystal grains from each other comprises a step of oxidizing said silicon thin film formed in said step (a) to form a region made of silicon oxide between the adjacent ones of said silicon single crystal grains.
Claim 10
Dependent Claim
47 words
A process of forming a group of silicon single crystal grains according to claim 6 , wherein a length of one side of each of said approximately rectangular-shaped silicon single crystal grains in said silicon thin film formed in said step (a) is 0.05 μm or more.
Claim 11
Dependent Claim
42 words
A process of forming a group of silicon single crystal grains according to claim 6 , wherein an average thickness of said silicon thin film formed in said step (a) is in a range of ×10 −8 m to 1×10 −7 m.
Claim 12
Dependent Claim
28 words
A process of forming a group of silicon single crystal grains according to claim 6 , wherein said base body is made of silicon oxide or silicon nitride.
Claim 13
Dependent Claim
67 words
A process of forming a group of silicon single crystal grains according to claim 6 , wherein opposed sides of each of said approximately rectangular-shaped silicon single crystal grains in said silicon thin film formed in said step (a) are approximately in parallel to the movement direction of the ultraviolet beam irradiating position or intersect the movement direction of the ultraviolet beam irradiating position at approximately 45°.
Claim 14
Dependent Claim
196 words
A process of fabricating a semiconductor device, comprising the steps of: irradiating a pulsed rectangular ultraviolet beam on an amorphous or polycrystalline silicon layer formed on a base body, to form a silicon thin film composed of a group of silicon single crystal grains on said base body; and forming a source/drain region and a channel region in said silicon thin film or said silicon single crystal grains; wherein the moved amount of an ultraviolet beam irradiating position in a period from completion of an irradiation pulse of said rectangular ultraviolet beam to starting of the next irradiation pulse of said rectangular ultraviolet beam being in a range of 4 μm to 20 μm, and a ratio of said moved amount to a width of said rectangular ultraviolet beam measured in the movement direction thereof being in a range of 0.1 to 5%, whereby forming a silicon thin film composed of a group of silicon single crystal grains which are each approximately rectangular-shaped and which are arranged in a grid pattern on said base body, a selected orientation of said silicon single crystal grains to the surface of said base body being approximately the <100> direction.
Claim 15
Dependent Claim
196 words
A process of fabricating a semiconductor device, comprising the steps of: irradiating a pulsed rectangular ultraviolet beam on an amorphous or polycrystalline silicon layer formed on a base body, to form a silicon thin film composed of a group of silicon single crystal grains on said base body; and forming a source/drain region and a channel region in said silicon thin film or said silicon single crystal grains; wherein the moved amount of an ultraviolet beam irradiating position in a period from completion of an irradiation pulse of said rectangular ultraviolet beam to starting of the next irradiation pulse of said rectangular ultraviolet beam being in a range of 4 μm to 20 μm, and a ratio of said moved amount to a width of said rectangular ultraviolet beam measured in the movement direction thereof being in a range of 0.1 to 5%, whereby forming a silicon thin film composed of a group of silicon single crystal grains which are each approximately rectangular-shaped and which are arranged in a grid pattern on said base body, a selected orientation of said silicon single crystal grains to the surface of said base body being approximately the <100> direction.
Claim 16
Dependent Claim
31 words
A process of fabricating a semiconductor device according to claim 12 , wherein a length of one side of said silicon single crystal grain approximately rectangular-shaped is 0.05 μm or more.
Claim 17
Dependent Claim
33 words
A process of fabricating a semiconductor device according to claim 12 , wherein an average thickness of said silicon thin film is in a range of 1×10 −8 m to 1×10 −7 m.
Claim 18
Dependent Claim
24 words
A process of fabricating a semiconductor device according to claim 12 , wherein said base body is made of silicon oxide or silicon nitride.
Claim 19
Dependent Claim
51 words
A process of fabricating a semiconductor device according to claim 12 , wherein opposed sides of said silicon single crystal grain approximately rectangular-shaped are approximately in parallel to the movement direction of the ultraviolet beam irradiating position or intersect the movement direction of the ultraviolet beam irradiating position at approximately 45°.
Claim 20
Dependent Claim
193 words
A process of fabricating a flash memory cell, comprising: a step (a) of irradiating a pulsed rectangular ultraviolet beam on an amorphous or polycrystalline silicon layer formed on a tunnel oxide film, to form a silicon thin film composed of a croup of silicon single crystal grains which are each approximately rectangular-shaped and which are arranged in a grid pattern on said tunnel oxide film, a selected orientation of said silicon single crystal grains to the surface of said tunnel oxide film is approximately the <100> direction; and a step (b) of separating adjacent ones of said silicon single crystal grains to each other, whereby forming a floating gate composed of said group of silicon single crystal grains; wherein the moved amount of an ultraviolet beam irradiating position in a period from completion of an irradiation pulse of said rectangular ultraviolet beam to starting of the next irradiation pulse of said rectangular ultraviolet beam being in a range of 4 μm to 20 μm, and a ratio of said moved amount to a width of said rectangular ultraviolet beam measured in the movement direction thereof being in a range of 0.1 to 5%.
Claim 21
Dependent Claim
193 words
A process of fabricating a flash memory cell, comprising: a step (a) of irradiating a pulsed rectangular ultraviolet beam on an amorphous or polycrystalline silicon layer formed on a tunnel oxide film, to form a silicon thin film composed of a croup of silicon single crystal grains which are each approximately rectangular-shaped and which are arranged in a grid pattern on said tunnel oxide film, a selected orientation of said silicon single crystal grains to the surface of said tunnel oxide film is approximately the <100> direction; and a step (b) of separating adjacent ones of said silicon single crystal grains to each other, whereby forming a floating gate composed of said group of silicon single crystal grains; wherein the moved amount of an ultraviolet beam irradiating position in a period from completion of an irradiation pulse of said rectangular ultraviolet beam to starting of the next irradiation pulse of said rectangular ultraviolet beam being in a range of 4 μm to 20 μm, and a ratio of said moved amount to a width of said rectangular ultraviolet beam measured in the movement direction thereof being in a range of 0.1 to 5%.
Claim 22
Dependent Claim
62 words
A process of fabricating a flash memory cell according to claim 17 , wherein said step (b) of separating adjacent ones of said silicon single crystal grains from each other comprises a step of oxidizing said silicon thin film formed in said step (a) to form a region made of silicon oxide between the adjacent ones of said silicon single crystal grains.
Claim 23
Dependent Claim
44 words
A process of fabricating a flash memory cell according to claim 17 , wherein a length of one side of each of said approximately rectangular-shaped silicon single crystal grains in said silicon thin film formed in said step (a) is 0.05 μm or more.
Claim 24
Dependent Claim
39 words
A process of fabricating a flash memory cell according to claim 17 , wherein an average thickness of said silicon thin film formed in said step (a) is in a range of 1×10 −8 m to 1×10 −7 m.
Claim 25
Dependent Claim
65 words
A process of fabricating a flash memory cell according to claim 17 , wherein opposed sides of each of said approximately rectangular-shaped silicon single crystal grains in said silicon thin film formed in said steo (a) are approximately in parallel to the movement direction of the ultraviolet beam irradiating position or intersect the movement direction of the ultraviolet beam irradiating position at approximately 45° .
References Cited (Backward Citations)
US4059461A
Cited
US5122223A
Cited
US4768076A
Cited
US4933298A
Cited
US5365875A
Cited
US5304357A
Cited
US5904550A
Cited
US5496768A
Cited
US5591668A
Cited
US5756364A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2004-02-20 | 2004-08-21 | 2005-02-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2008-02-20 | 2008-08-21 | 2009-02-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2012-02-20 | 2012-08-21 | 2013-02-20 | $7700.00 | Window Closed / Lapsed |