Electrical stress control

Claim 2

An electrical stress- controlling composition, comprising: (a) a polymeric matrix, and (b) a particulate filler comprising doped zinc oxide varistor powder; wherein (i) the particles of the filler are calcined at a temperature between 800° C. and 1400° C., and subsequently broken up such that substantially all of the particles retain their original shape, (ii) at least 85% of the weight of the filler comprises zinc oxide, (iii) more than 50% by weight of the filler particles have a maximum dimension of between 5 and 100 micrometers such that the composition has a specific impedance that decreases by at least a factor of 10 when subjected to an electric field increase of less than 5 kV/cm at a region within an electrical field range of 5 kV/cm to 50 kV/cm, (iv) the filler comprises between 5% and 60% of the volume of the total composition; and (v) the particles of the filler are generally spherical.

Claim 3

A composition according to claim 1, wherein all the particles of the filler have a maximum dimension of less than 100 micrometers.

Claim 4

A composition according to claim 1 or claim 2, wherein not more than 15% by weight of the filler particles have a maximum dimension less than 15 micrometers.

Claim 5

A composition according to claim 1 or claim 2, wherein the filler particles are calcined at a temperature between 950° C. and 1250° C.

Claim 6

A composition according to claim 1 or claim 2, wherein at least 90% of the weight of the filler comprises zinc oxide.

Claim 7

A composition according to claim 1 or claim 2, wherein more than 50% by weight of the filler particles have a maximum dimension of between 25 and 75 micrometers.

Claim 8

A composition according to claim 1 or claim 2, wherein the filler comprises between 10% and 40% of the volume of the total composition.

Claim 9

A layer of material comprising a stress-controlling composition in accordance with claim 1 or claim 2.

Claim 10

A joint or termination of an electric power cable having applied thereto a layer of material according to claim 8.

Claim 11

A composition according to claim 1 wherein the specific impedence of the composition is substantially unchanged when subjected to an electrical field range of less than 5 kV/cm.

Claim 12

An electrical stress-controlling composition, comprising: a polymeric matrix; and a plurality of filler particles comprising: (a) a zinc oxide varistor powder; and (b) a dopant layer on particles of the zinc oxide varistor powder, the dopant layer being selected from the group consisting of Bi 2 O 3 , Cr 2 O 3 , Sb 2 O 3 , Co 2 O 3 , MnO 3 , Al 2 O 3 , CoO, Co 3 O 4 , MnO, MnO 2 , SiO 2 , and trace amounts of lead, iron, boron and aluminum; wherein (i) the filler particles are calcined at a temperature of between about 800° C. and about 1400° C., and subsequently broken up such that substantially all of the filler particles retain their original shape; (ii) at least about 85% of the weight of the filler particles comprises zinc oxide; (iii) more than about 50% by weight of the filler particles have a maximum dimension of between about 5 and about 100 micrometers; and (iv) the filler particles comprise between about 5% and about 60% of the volume of the electrical stress-controlling composition.

Claim 13

An electrical stress-controlling composition, comprising: a polymeric matrix; and a plurality of filler particles comprising: (a) a zinc oxide varistor powder; and (b) a dopant layer on particles of the zinc oxide varistor powder, the dopant layer being selected from the group consisting of Bi 2 O 3 , Cr 2 O 3 , Sb 2 O 3 , Co 2 O 3 , MnO 3 , Al 2 O 3 , CoO, Co 3 O 4 , MnO, MnO 2 , SiO 2 , and trace amounts of lead, iron, boron and aluminum; wherein (i) the filler particles are calcined at a temperature of between about 800° C. and about 1400° C., and subsequently broken up such that substantially all of the filler particles retain their original shape; (ii) at least about 85% of the weight of the filler particles comprises zinc oxide; (iii) more than about 50% by weight of the filler particles have a maximum dimension of between about 5 and about 100 micrometers; and (iv) the filler particles comprise between about 5% and about 60% of the volume of the electrical stress-controlling composition.

Claim 14

A composition according to claim 11 wherein the composition has a specific impedance that decreases by at least about a factor of 10 when subjected to an electric field increase of less than about 5 kV/cm at a region within an electrical field range of about 5 kV/cm to about 50 kV/cm.

Claim 15

A composition according to claim 12 wherein the specific impedence of the composition is substantially unchanged when subjected to an electrical field range of less than about 5 kV/cm.

Claim 16

A composition according to claim 12 wherein the dopant layer is selected from the group consisting of Bi 2 O 3 , Cr 2 O 3 , Sb 2 O 3 , Co 2 O 3 and MnO 3 .

Claim 17

A composition according to claim 12, wherein the particles of the filler have a maximum dimension of less than about 125 micrometers.

Claim 18

A composition according to claim 15, wherein not more than about 15% by weight of the filler particles have a maximum dimension of less than about 15 micrometers.

Claim 19

A composition according to claim 12 wherein the filler particles are calcined at a temperature of between about 950° C. and about 1250° C.

Claim 20

A composition according to claim 12, wherein at least about 90% of the filler particles by weight comprises zinc oxide.

Claim 21

A composition according to claim 12, wherein more than about 50% by weight of the filler particles have a maximum dimension of between about 25 and about 75 micrometers.

Claim 22

A composition according to claim 12, wherein the filler particles comprise between about 10% and about 40% of the volume of the composition.

Claim 23

An electrical stress control apparatus for an electrical power cable comprising: a cover configured to be placed over the electrical power cable; and an electrical stress-controlling composition positioned between the cover and the electrical power cable, the electrical stress-controlling composition comprising: (a) a polymeric matrix, and (b) a particulate filler comprising doped zinc oxide varistor powder; wherein (i) the particles of the filler are calcined at a temperature of between about 800° C. and about 1400° C., and subsequently broken up such that substantially all of the particles retain their original shape; (ii) at least about 85% of the weight of the filler particles comprises zinc oxide; (iii) more than about 50% by weight of the filler particles have a maximum dimension of between about 5 and about 100 micrometers; (iv) the composition has a specific impedance that decreases by at least about a factor of 10 when subjected to an electric field increase of less than about 5 kV/cm at a region within an electrical field range of about 5 kV/cm to about 50 kV/cm; (v) the filler particles comprise between about 5% and about 60% of the volume of the composition; and (vi) the filler particles are generally spherical.

Claim 24

An electrical stress control apparatus for an electrical power cable comprising: a cover configured to be placed over the electrical power cable; and an electrical stress-controlling composition positioned between the cover and the electrical power cable, the electrical stress-controlling composition comprising: (a) a polymeric matrix, and (b) a particulate filler comprising doped zinc oxide varistor powder; wherein (i) the particles of the filler are calcined at a temperature of between about 800° C. and about 1400° C., and subsequently broken up such that substantially all of the particles retain their original shape; (ii) at least about 85% of the weight of the filler particles comprises zinc oxide; (iii) more than about 50% by weight of the filler particles have a maximum dimension of between about 5 and about 100 micrometers; (iv) the composition has a specific impedance that decreases by at least about a factor of 10 when subjected to an electric field increase of less than about 5 kV/cm at a region within an electrical field range of about 5 kV/cm to about 50 kV/cm; (v) the filler particles comprise between about 5% and about 60% of the volume of the composition; and (vi) the filler particles are generally spherical.

Claim 25

An apparatus according to claim 21 wherein the specific impedence of the composition is substantially unchanged when subjected to an electrical field range of less than about 5 kV/cm.

Claim 26

An electrical stress control apparatus for an electrical power cable comprising: a cover configured to be placed over the electrical power cable; and an electrical stress-controlling composition positioned between the cover and the electrical power cable, the electrical stress-controlling composition comprising: a polymeric matrix; and a plurality of filler particles comprising: (a) a zinc oxide varistor powder; and (b) a dopant layer on particles of the zinc oxide varistor powder, the dopant layer being selected from the group consisting of Bi 2 O 3 , Cr 2 O 3 , Sb 2 O 3 , Co 2 O 3 , MnO 3 , Al 2 O 3 , CoO, Co 3 O 4 , MnO, MnO 2 , SiO 2 , and trace amounts of lead, iron, boron and aluminum; wherein (i) the filler particles are calcined at a temperature of between about 800° C. and about 1400° C., and subsequently broken up such that substantially all of the filler particles retain their original shape; (ii) at least about 85% of the weight of the filler particles comprises zinc oxide; (iii) more than about 50% by weight of the filler particles have a maximum dimension of between about 5 and about 100 micrometers; and (iv) the filler particles comprise between about 5% and about 60% of the volume of the electrical stress-controlling composition.

Claim 27

An electrical stress control apparatus for an electrical power cable comprising: a cover configured to be placed over the electrical power cable; and an electrical stress-controlling composition positioned between the cover and the electrical power cable, the electrical stress-controlling composition comprising: a polymeric matrix; and a plurality of filler particles comprising: (a) a zinc oxide varistor powder; and (b) a dopant layer on particles of the zinc oxide varistor powder, the dopant layer being selected from the group consisting of Bi 2 O 3 , Cr 2 O 3 , Sb 2 O 3 , Co 2 O 3 , MnO 3 , Al 2 O 3 , CoO, Co 3 O 4 , MnO, MnO 2 , SiO 2 , and trace amounts of lead, iron, boron and aluminum; wherein (i) the filler particles are calcined at a temperature of between about 800° C. and about 1400° C., and subsequently broken up such that substantially all of the filler particles retain their original shape; (ii) at least about 85% of the weight of the filler particles comprises zinc oxide; (iii) more than about 50% by weight of the filler particles have a maximum dimension of between about 5 and about 100 micrometers; and (iv) the filler particles comprise between about 5% and about 60% of the volume of the electrical stress-controlling composition.

Claim 28

An apparatus according to claim 23 wherein the composition has a specific impedance that decreases by at least about a factor of 10 when subjected to an electric field increase of less than about 5 kV/cm at a region within an electrical field range of about 5 kV/cm to about 50 kV/cm and wherein the specific impedence is substantially unchanged when subjected to an electrical field range of less than about 5 kV/cm.

Claim 29

An apparatus according to claim 24 wherein the specific impedence of the composition is substantially unchanged when subjected to an electrical field range of less than 5 kV/cm.