Method for making a more reliable storage capacitor for dynamic random access memory (DRAM)
Assignee: Taiwan Semiconductor Manufacturing Co TSMC Ltd
•
Filing: 1998-08-07
•
Granted: 2000-08-22
•
Expires: 2018-08-07
Abstract
Abstract A modified method for forming stacked capacitors for DRAMs which circumvents oxide erosion due to misalignment is described. A planar silicon oxide (SiO 2 ) first insulating layer is formed over device areas. First openings are etched for capacitor node contacts. A polysilicon layer is deposited and etched back to form node contacts in the first openings, which are generally recessed due to overetching to completely remove the polysilicon on the insulating surface. A Si 3 N 4 etch-stop layer is deposited to protect the exposed sidewalls in the first openings. A disposable second SiO 2 insulating layer is deposited and second openings are etched over and to the node contacts for forming bottom electrodes. A conformal second polysilicon layer is deposited and chemically/mechanically polished back to form the bottom electrodes in the second openings. The second insulating layer is removed by wet etching to the etch-stop layer. When the second openings are misaligned over the node contact openings, the Si 3 N 4 on the sidewalls protects the SiO 2 first insulating layer from being eroded over the devices on the substrate. The capacitors are now completed by forming an inter-electrode dielectric layer on the bottom electrodes, and depositing and patterning a third polysilicon layer for top electrodes.
Inventors
- 👤 Yung-Kuan Hsiao
- 👤 Cheng-Ming Wu
- 👤 Yu-Hua Lee
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 13:05
CPC Classifications
H; H10; H10B; H10B12/00; H10B12/01; H10B12/02; H10B12/03; H10B12/033; H10B12/05
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
257 words
A method for fabricating stacked capacitors for memory devices comprising the steps of: providing a semiconductor substrate having device areas with semiconductor devices; forming a planar first insulating layer over said device areas on said substrate; selectively etching first openings for capacitor node contacts in said first insulating layer to said device areas; depositing a conductively doped first polysilicon layer to fill said first openings, and etching back said first polysilicon layer to form polysilicon plugs in said first openings; depositing a blanket etch-stop layer on said first insulating layer and over said polysilicon plugs in said first openings and over the sidewalls of any exposed said first insulating layer when said polysilicon plugs are overetched; depositing a second insulating layer on said etch-stop layer; selectively etching second openings, over and wider than said first openings, in said second insulating layer and in said etch-stop layer to said polysilicon plugs; depositing a conformal second polysilicon layer over and in said second openings and contacting said polysilicon plugs; polishing back said second polysilicon layer to said second insulating layer to form bottom electrodes in said second openings; isotropically etching said second insulating layer selectively to said etch-stop layer to leave free-standing said bottom electrodes, while said etch-stop layer on said sidewalls of said first insulating layer protect said first insulating layer from etching when said second openings are misaligned to said first openings; depositing an interelectrode dielectric layer on said bottom electrodes; depositing and patterning a third polysilicon layer to form top electrodes and completing said stacked capacitors.
Claim 2
Independent Claim
257 words
A method for fabricating stacked capacitors for memory devices comprising the steps of: providing a semiconductor substrate having device areas with semiconductor devices; forming a planar first insulating layer over said device areas on said substrate; selectively etching first openings for capacitor node contacts in said first insulating layer to said device areas; depositing a conductively doped first polysilicon layer to fill said first openings, and etching back said first polysilicon layer to form polysilicon plugs in said first openings; depositing a blanket etch-stop layer on said first insulating layer and over said polysilicon plugs in said first openings and over the sidewalls of any exposed said first insulating layer when said polysilicon plugs are overetched; depositing a second insulating layer on said etch-stop layer; selectively etching second openings, over and wider than said first openings, in said second insulating layer and in said etch-stop layer to said polysilicon plugs; depositing a conformal second polysilicon layer over and in said second openings and contacting said polysilicon plugs; polishing back said second polysilicon layer to said second insulating layer to form bottom electrodes in said second openings; isotropically etching said second insulating layer selectively to said etch-stop layer to leave free-standing said bottom electrodes, while said etch-stop layer on said sidewalls of said first insulating layer protect said first insulating layer from etching when said second openings are misaligned to said first openings; depositing an interelectrode dielectric layer on said bottom electrodes; depositing and patterning a third polysilicon layer to form top electrodes and completing said stacked capacitors.
Claim 3
Dependent Claim
26 words
The method of claim 1, wherein said first insulating layer is silicon oxide, and has a thickness of between about 500 and 5000 Angstroms after planarizing.
Claim 4
Dependent Claim
44 words
The method of claim 1, wherein said first polysilicon layer is doped with conductive impurities to a concentration of between about 1.0 E 17 and 1.0 E 21 atoms/cm 3 , and is deposited to a thickness of between about 2000 and 5000 Angstroms.
Claim 5
Dependent Claim
23 words
The method of claim 1, wherein said etch-stop layer is silicon nitride and has a thickness of between about 50 and 1000 Angstroms.
Claim 6
Dependent Claim
26 words
The method of claim 1, wherein said second insulating layer is silicon oxide and is deposited to a thickness of between about 3000 and 18000 Angstroms.
Claim 7
Dependent Claim
43 words
The method of claim 1, wherein said second polysilicon layer is conductively doped in-situ to a concentration of between about 1.0 E 19 and 1.0 E 21 atoms/cm 3 , and is deposited to a thickness of between about 300 and 2000 Angstroms.
Claim 8
Dependent Claim
22 words
The method of claim 1, wherein said isotropic etching of said second insulating layer is carried out in a hydrofluoric acid solution.
Claim 9
Dependent Claim
27 words
The method of claim 1, wherein said interelectrode dielectric layer is silicon oxide/silicon nitride/silicon oxide (ONO), and has a thickness of between about 30 and 200 Angstroms.
Claim 10
Dependent Claim
42 words
The method of claim 1, wherein said third polysilicon layer is doped with conductive impurities to a concentration of between about 1.0 E 19 and 1.0 E 21 atoms/cm 3 , and has a thickness of between about 500 and 2000 Angstroms.
Claim 11
Independent Claim
261 words
A method for fabricating stacked capacitors for memory devices comprising the steps of: providing a semiconductor substrate having device areas with semiconductor devices; forming a planar first insulating layer over said device areas on said substrate; selectively etching first openings for capacitor node contacts in said first insulating layer to said device areas; depositing a conductively doped first polysilicon layer to fill said first openings, and etching back said first polysilicon layer to form polysilicon plugs in said first openings; depositing a blanket etch-stop layer, composed of silicon nitride, on said first insulating layer and over said polysilicon plugs in said first openings and over the sidewalls of any exposed said first insulating layer when said polysilicon plugs are overetched; depositing a second insulating layer on said etch-stop layer; selectively etching second openings, over and wider than said first openings, in said second insulating layer and in said etch-stop layer to said polysilicon plugs; depositing a conformal second polysilicon layer over and in said second openings and contacting said polysilicon plugs; polishing back said second polysilicon layer to said second insulating layer to form bottom electrodes in said second openings; isotropically etching said second insulating layer selectively to said etch-stop layer to leave free-standing said bottom electrodes, while said etch-stop layer on said sidewalls of said first insulating layer protect said first insulating layer from etching when said second openings are misaligned to said first openings; depositing an interelectrode dielectric layer on said bottom electrodes; depositing and patterning a third polysilicon layer to form top electrodes and completing said stacked capacitors.
Claim 12
Independent Claim
261 words
A method for fabricating stacked capacitors for memory devices comprising the steps of: providing a semiconductor substrate having device areas with semiconductor devices; forming a planar first insulating layer over said device areas on said substrate; selectively etching first openings for capacitor node contacts in said first insulating layer to said device areas; depositing a conductively doped first polysilicon layer to fill said first openings, and etching back said first polysilicon layer to form polysilicon plugs in said first openings; depositing a blanket etch-stop layer, composed of silicon nitride, on said first insulating layer and over said polysilicon plugs in said first openings and over the sidewalls of any exposed said first insulating layer when said polysilicon plugs are overetched; depositing a second insulating layer on said etch-stop layer; selectively etching second openings, over and wider than said first openings, in said second insulating layer and in said etch-stop layer to said polysilicon plugs; depositing a conformal second polysilicon layer over and in said second openings and contacting said polysilicon plugs; polishing back said second polysilicon layer to said second insulating layer to form bottom electrodes in said second openings; isotropically etching said second insulating layer selectively to said etch-stop layer to leave free-standing said bottom electrodes, while said etch-stop layer on said sidewalls of said first insulating layer protect said first insulating layer from etching when said second openings are misaligned to said first openings; depositing an interelectrode dielectric layer on said bottom electrodes; depositing and patterning a third polysilicon layer to form top electrodes and completing said stacked capacitors.
Claim 13
Dependent Claim
26 words
The method of claim 10, wherein said first insulating layer is silicon oxide, and has a thickness of between about 500 and 5000 Angstroms after planarizing.
Claim 14
Dependent Claim
44 words
The method of claim 10, wherein said first polysilicon layer is doped with conductive impurities to a concentration of between about 1.0 E 17 and 1.0 E 21 atoms/cm 3 , and is deposited to a thickness of between about 2000 and 5000 Angstroms.
Claim 15
Dependent Claim
19 words
The method of claim 10, wherein said etch-stop layer has a thickness of between about 50 and 1000 Angstroms.
Claim 16
Dependent Claim
26 words
The method of claim 10, wherein said second insulating layer is silicon oxide and is deposited to a thickness of between about 3000 and 18000 Angstroms.
Claim 17
Dependent Claim
43 words
The method of claim 10, wherein said second polysilicon layer is conductively doped in-situ to a concentration of between about 1.0 E 19 and 1.0 E 21 atoms/cm 3 , and is deposited to a thickness of between about 300 and 2000 Angstroms.
Claim 18
Dependent Claim
22 words
The method of claim 10, wherein said isotropic etching of said second insulating layer is carried out in a hydrofluoric acid solution.
Claim 19
Dependent Claim
27 words
The method of claim 10, wherein said interelectrode dielectric layer is silicon oxide/silicon nitride/silicon oxide (ONO), and has a thickness of between about 30 and 200 Angstroms.
Claim 20
Dependent Claim
42 words
The method of claim 10, wherein said third polysilicon layer is doped with conductive impurities to a concentration of between about 1.0 E 19 and 1.0 E 21 atoms/cm 3 , and has a thickness of between about 500 and 2000 Angstroms.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2003-08-22 | 2004-02-21 | 2004-08-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2007-08-22 | 2008-02-21 | 2008-08-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2011-08-22 | 2012-02-21 | 2012-08-22 | $7700.00 | Window Closed / Lapsed |