Silicidation with silicon buffer layer and silicon spacers
Assignee: Advanced Micro Devices Inc
•
Filing: 1998-11-05
•
Granted: 2000-08-08
•
Expires: 2018-11-05
Abstract
Abstract High integrity ultra-shallow source/drain junctions are formed employing cobalt silicide contacts. Field oxide regions, gates, spacers, and source/drain implants are initially formed. A layer of silicon is then deposited. A protective non-contuctive film is then formed and anisotropically etched to expose the silicon layer on the source/drain regions and the top surfaces of the gates, and to form protective spacers on the edges of the field oxide regions and on the side surfaces of the gates. A layer of cobalt is thereafter deposited and silicidation is performed, as by rapid thermal annealing, to form a low-resistance cobalt silicide while consuming the silicon film. The consumption of the silicon film during silicidation results in less consumption of substrate silicon, thereby enabling the formation of ultra-shallow source/drain junctions without junction leakage, allowing the formation of cobalt silicide contacts at optimum thickness and facilitating reliable device scaling.
Inventors
- 👤 Nick Kepler
- 👤 Karsten Wieczorek
- 👤 Larry Wang
- 👤 Paul Raymond Besser
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 03:32
CPC Classifications
H; H10; H10D; H10D30/00; H10D30/01; H10D30/021; H10D30/0223; H10D30/0227; H10D30/0212; H10D64/00; H10D64/01; H10D64/011; H10D64/0111; H10D64/0112; H10D64/013; H10D64/01302; H10D64/01304; H10D64/01306; H10D64/01308; H10D64/0131; H10D64/021; H10D64/20; H10D64/23; H10D64/251; H10D64/258; H10D64/259
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
164 words
A method of manufacturing a semiconductor device, which method comprises: forming conductive gates and dielectric field oxide regions on a main surface of a semiconductor substrate; implanting impurities into the substrate to form source/drain regions having a junction with the substrate; forming a silicon layer on the source/drain regions, field oxide regions, and side and top surfaces of the gates; forming a protective non-conductive layer on the silicon layer; anisotropically etching the protective non-conductive layer to expose the silicon layer on the source/drain regions and the top surfaces of the gates and to form protective spacers on the silicon layer on the side surfaces of the gates and on field oxide edges where the field oxide regions abut the main surface; forming a metal layer on the exposed silicon layer; and heating to form a metal silicide layer from the metal layer and the exposed silicon layer; wherein the metal silicide layer is formed above the junction and is spaced apart from the junction.
Claim 2
Independent Claim
164 words
A method of manufacturing a semiconductor device, which method comprises: forming conductive gates and dielectric field oxide regions on a main surface of a semiconductor substrate; implanting impurities into the substrate to form source/drain regions having a junction with the substrate; forming a silicon layer on the source/drain regions, field oxide regions, and side and top surfaces of the gates; forming a protective non-conductive layer on the silicon layer; anisotropically etching the protective non-conductive layer to expose the silicon layer on the source/drain regions and the top surfaces of the gates and to form protective spacers on the silicon layer on the side surfaces of the gates and on field oxide edges where the field oxide regions abut the main surface; forming a metal layer on the exposed silicon layer; and heating to form a metal silicide layer from the metal layer and the exposed silicon layer; wherein the metal silicide layer is formed above the junction and is spaced apart from the junction.
Claim 3
Dependent Claim
63 words
The method according to claim 1, wherein the step of heating to form a metal silicide layer includes: heating at a first temperature to form a first-phase metal silicide layer from the metal layer and the silicon layer; and heating at a second temperature to form a second-phase metal silicide layer having a resistivity lower than that of the first-phase metal silicide layer.
Claim 4
Dependent Claim
29 words
The method according to claim 2, wherein the metal layer comprises cobalt, the first-phase metal silicide layer comprises CoSi and the second-phase metal silicide layer comprises CoSi 2 .
Claim 5
Dependent Claim
48 words
The method according to claim 3, wherein the step of heating at the first temperature includes rapid thermal annealing at about 400° C. to about 550° C.; and the step of heating at the second temperature includes rapid thermal annealing at about 700° C. to about 900° C.
Claim 6
Dependent Claim
40 words
The method according to claim 3, wherein the step of heating at the first temperature includes rapid thermal annealing at about 470° C., and the step of heating at the second temperature includes rapid thermal annealing at about 825° C.
Claim 7
Dependent Claim
31 words
The method according to claim 2, comprising heating at the first temperature for an amount of time sufficient to substantially consume the silicon layer when forming the first-phase metal silicide layer.
Claim 8
Dependent Claim
38 words
The method according to claim 3, comprising depositing the metal layer at a thickness of about 100 Å to about 200 Å and depositing the silicon layer at a thickness of about 300 Å to about 600 Å.
Claim 9
Dependent Claim
30 words
The method according to claim 3, comprising depositing the metal layer at a thickness of about 100 Å and depositing the silicon layer at a thickness of about 300 Å.
Claim 10
Dependent Claim
39 words
The method according to claim 1, comprising: forming dielectric spacers on the side surfaces of the gates before forming the silicon layer; and forming the silicon layer, the protective non-conductive layer and the protective spacers on the dielectric spacers.
Claim 11
Dependent Claim
33 words
The method according to claim 3, comprising: forming the metal layer on the protective spacers; and etching to remove the metal layer from the protective spacers after forming the first-phase metal silicide layer.
Claim 12
Dependent Claim
21 words
The method according to claim 1, wherein the step of forming the silicon layer comprises forming a polysilicon layer by LPCVD.
Claim 13
Dependent Claim
22 words
The method according to claim 1, wherein the step of forming the silicon layer comprises forming an amorphous silicon layer by sputtering.
Claim 14
Dependent Claim
23 words
The method according to claim 1, comprising forming the protective non-conductive layer to a thickness of about 100 Å to about 1000 Å.
Claim 15
Dependent Claim
22 words
The method according to claim 1, wherein the step of forming the protective non-conductive layer comprises forming a layer of silicon dioxide.
Claim 16
Dependent Claim
14 words
The method according to claim 14, comprising forming the silicon dioxide layer by PECVD.
Claim 17
Dependent Claim
22 words
The method according to claim 1, wherein the step of forming the protective non-conductive layer comprises forming a layer of silicon nitride.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2003-08-08 | 2004-02-07 | 2004-08-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2007-08-08 | 2008-02-07 | 2008-08-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2011-08-08 | 2012-02-07 | 2012-08-08 | $7700.00 | Window Closed / Lapsed |