Tires with colored indicia
Assignee: Goodyear Tire and Rubber Co
•
Filing: 1998-06-04
•
Granted: 2000-07-25
•
Expires: 2018-06-04
Abstract
Abstract This invention relates to a vulcanized rubber substrate such as, for example, a tire and a colored, crosslinked, non-black, non-staining, opaque, rubber composition layer therein such as, for example, a colored sidewall. In one preferred embodiment, the invention relates to such a tire wherein said white sidewall is partially colored with a contrasting color prior to vulcanization. The color is desirably applied after mixing with a plasticizer for the white sidewall composition. During vulcanization the color penetrates and colors the visible portion of the white sidewall composition.
Inventors
- 👤 Ramendra Nath Majumdar
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 18:59
CPC Classifications
B; B60; B60C; B60C13/00; B60C13/001; B29; B29D; B29D30/00; B29D30/06; B29D30/72; B29D2030/726
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
145 words
A process for coloring an opaque non-black rubber component of a pneumatic tire, said process comprising: a) compounding and mixing a non-black rubber compound including at least 50 PHR of a copolymer having at least 50 weight percent repeating units from a monoisoolefin of 4 to 7 carbon atoms; b) applying a dye mixed with at least one low molecular weight rubber plasticizing additive, wherein said additive is a liquid, at temperatures in the range of about 20° C. to about 120° C., to at least one external surface of said rubber compound prior to curing said rubber compound to form a colored rubber compound substantially without the use of a volatile organic solvent; c) assembling said colored rubber compound into an uncured pneumatic tire; and d) molding and crosslinking said pneumatic tire thereby producing a tire with at least one colored non-black rubber component.
Claim 2
Dependent Claim
145 words
A process for coloring an opaque non-black rubber component of a pneumatic tire, said process comprising: a) compounding and mixing a non-black rubber compound including at least 50 PHR of a copolymer having at least 50 weight percent repeating units from a monoisoolefin of 4 to 7 carbon atoms; b) applying a dye mixed with at least one low molecular weight rubber plasticizing additive, wherein said additive is a liquid, at temperatures in the range of about 20° C. to about 120° C., to at least one external surface of said rubber compound prior to curing said rubber compound to form a colored rubber compound substantially without the use of a volatile organic solvent; c) assembling said colored rubber compound into an uncured pneumatic tire; and d) molding and crosslinking said pneumatic tire thereby producing a tire with at least one colored non-black rubber component.
Claim 3
Dependent Claim
24 words
A process according to claim 1, wherein said dye is mixed with either a plasticizer for a rubber, or a wax, or combinations thereof.
Claim 4
Dependent Claim
26 words
A process according to claim 2, wherein a black rubber coverstrip is applied over said colored rubber compound before it is assembled into a pneumatic tire.
Claim 5
Dependent Claim
144 words
A process for coloring an opaque non-black rubber component of a pneumatic tire, said process comprising; a) compounding and mixing an opaque non-black rubber compound including at least 50 PHR of a copolymer having at least 50 weight percent repeating units from a monoisoolefin of 4 to 7 carbon atoms and a sufficient amount of white pigment to make the rubber compound opaque; b) applying a dye mixed with either a plasticizer for a rubber or a wax, or combinations thereof, to at least one external surface of said rubber compound prior to curing said rubber compound to form a colored rubber compound substantially without the use of a volatile organic solvent; c) assembling said colored rubber compound into an uncured pneumatic tire; and d) molding and crosslinking said pneumatic tire thereby producing a tire with at least one opaque non-black colored rubber component.
Claim 6
Dependent Claim
144 words
A process for coloring an opaque non-black rubber component of a pneumatic tire, said process comprising; a) compounding and mixing an opaque non-black rubber compound including at least 50 PHR of a copolymer having at least 50 weight percent repeating units from a monoisoolefin of 4 to 7 carbon atoms and a sufficient amount of white pigment to make the rubber compound opaque; b) applying a dye mixed with either a plasticizer for a rubber or a wax, or combinations thereof, to at least one external surface of said rubber compound prior to curing said rubber compound to form a colored rubber compound substantially without the use of a volatile organic solvent; c) assembling said colored rubber compound into an uncured pneumatic tire; and d) molding and crosslinking said pneumatic tire thereby producing a tire with at least one opaque non-black colored rubber component.
Claim 7
Dependent Claim
26 words
A process according to claim 4, wherein a black rubber coverstrip is applied over said colored rubber compound before it is assembled into a pneumatic tire.
Claim 8
Dependent Claim
22 words
A process according to claim 4, wherein said white pigment is TiO 2 present in an amount of at least 20 PHR.
Claim 9
Dependent Claim
51 words
A process according to claim 4, wherein opaque is defined as having less than a 2% change in the L value of a 1 mm thick specimen according to CIE 1976 L* scale when a black backup plate is substituted for a white backup plate for the sample in the test.
Claim 10
Dependent Claim
51 words
A process according to claim 4, wherein opaque is defined as having less than a 2% change in the L value of a 0.5 mm thick specimen according to CIE 1976 L* scale when a black backup plate is substituted for a white backup plate for the sample in the test.
Claim 11
Dependent Claim
24 words
A process according to claim 4, wherein the dye forms a dye penetration layer by only penetrating partially through said opaque non-black rubber component.
References Cited (Backward Citations)
US51848A
Cited
US1715209A
Cited
US1854601A
Cited
US1895088A
Cited
US3081276A
Cited
US3253634A
Cited
US3449201A
Cited
US3607498A
Cited
US3729041A
Cited
US3577261A
Cited
US4158378A
Cited
JPH01139883A
Cited
SU1527240A1
Cited
US4987192A
Cited
JPH0472335A
Cited
EP0744304A2
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2003-07-25 | 2004-01-24 | 2004-07-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2007-07-25 | 2008-01-24 | 2008-07-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2011-07-25 | 2012-01-24 | 2012-07-25 | $7700.00 | Window Closed / Lapsed |