Biodegradable filter material and method for its manufacture
Assignee: BioTec Biologische Naturverpackungen GmbH and Co KG
•
Filing: 1996-09-27
•
Granted: 2000-05-16
•
Expires: 2016-09-27
Abstract
Abstract There is provided a biodegradable filter tow or filter material from renewable raw materials for the use as a tobacco smoke filter element of cigarettes, cigars or pipes as well as a method for preparing it, wherein fibers, films or foams prepared in an extrusion method from biopolymers based on thermoplastic starch or its polymer compositions are processed to the filter tow or filter material according to the present invention. The advantages of this invention reside in the use of mainly renewable raw materials, a fast and complete biodegradability of the natural biopolymer filter material, a pollutant-reducing flavor-increasing filtering effect and an economically favorable preparation method.
Inventors
- 👤 Juergen Loercks
- 👤 Harald Schmidt
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 13:35
CPC Classifications
A; A24; A24D; A24D3/00; A24D3/06; A24D3/067; A24D3/068; A24D3/08; Y; Y10; Y10S; Y10S264/00; Y10S264/48
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
158 words
A method for manufacturing biodegradable filter elements comprising: (a) continuously supplying a mixture to an extruder, the mixture consisting essentially of a starch-based polymer selected from the group consisting of native starches, modified starches, and thermoplastic starch polymers, at least one synthetic polymer selected from the group consisting of polyvinyl alcohol, polyester amides, polyester urethanes, aliphatic polyesters, aromatic polyesters, and copolymers of aliphatic polyesters and aromatic polyesters, optionally a flow auxiliary, and optionally a blowing agent, wherein the starch-based polymer supplied to the extruder comprises starch that has been initially predried to below its natural water content; (b) heating and kneading the mixture under conditions so as to form a thermoplastic melt; (c) extruding the thermoplastic melt through a die to form an extrudate of the thermoplastic melt; (d) causing the extrudate to develop a porous configuration; (e) compressing the extrudate and forming an endless filter rod; and (f) wrapping the filter rod and forming single filter elements.
Claim 2
Independent Claim
158 words
A method for manufacturing biodegradable filter elements comprising: (a) continuously supplying a mixture to an extruder, the mixture consisting essentially of a starch-based polymer selected from the group consisting of native starches, modified starches, and thermoplastic starch polymers, at least one synthetic polymer selected from the group consisting of polyvinyl alcohol, polyester amides, polyester urethanes, aliphatic polyesters, aromatic polyesters, and copolymers of aliphatic polyesters and aromatic polyesters, optionally a flow auxiliary, and optionally a blowing agent, wherein the starch-based polymer supplied to the extruder comprises starch that has been initially predried to below its natural water content; (b) heating and kneading the mixture under conditions so as to form a thermoplastic melt; (c) extruding the thermoplastic melt through a die to form an extrudate of the thermoplastic melt; (d) causing the extrudate to develop a porous configuration; (e) compressing the extrudate and forming an endless filter rod; and (f) wrapping the filter rod and forming single filter elements.
Claim 3
Dependent Claim
18 words
A method according to claim 1, wherein steps (c) and (d) are part of a single continuous process.
Claim 4
Dependent Claim
36 words
A method according to claim 1, wherein steps (a) through (c) yield a thermoplastic starch polymer granulate which is subsequently processed in a single-shaft extruder to yield the filter elements according to steps (a) through (f).
Claim 5
Dependent Claim
18 words
A method according to claim 1, wherein steps (a) through (c) are performed using a double shaft extruder.
Claim 6
Dependent Claim
29 words
A method according to claim 1, wherein the extrudate formed in step (c) is in a form selected from the group consisting of filaments, a film, and a foam.
Claim 7
Dependent Claim
65 words
A method according to claim 1, wherein the die utilized in step (c) has a die configuration selected from the group consisting of a die having more than 100 die orifices for the extrusion of filaments, a die having from 1 to 2 die orifices for the extrusion of films, and a die having from 1 to 40 die orifices for the extrusion of foams.
Claim 8
Dependent Claim
51 words
A method according to claim 1, wherein the die is configured for the extrusion of films, is selected from the group consisting of a film die, a tubular die, and a double tubular die, and yields a film selected from the group consisting of a flat film and a brown film.
Claim 9
Dependent Claim
15 words
A method according to claim 1, wherein the extruder includes a plurality of temperature zones.
Claim 10
Dependent Claim
31 words
A method according to claim 8, wherein step (a) is carried out in first and second temperature zones and wherein step (b) is carried out in third to sixth temperature zones.
Claim 11
Dependent Claim
59 words
A method according to claim 8, wherein the extruder includes six temperature zones having approximately the following temperature profiles: Zone 1: 25-45° C. Zone 2: 70-110° C. Zone 3: 110-160° C. Zone 4: 150-220° C. Zone 5: 180-220° C. Zone 6: 180-220° C. wherein the thermoplastic melt is extruded at a temperature of approximately 180-220° C. as a foam.
Claim 12
Dependent Claim
59 words
A method according to claim 8, wherein the extruder includes six temperature zones having approximately the following temperature profiles: Zone 1: 25-45° C. Zone 2: 60-100° C. Zone 3: 90-120° C. Zone 4: 90-120° C. Zone 5: 90-120° C. Zone 6: 90-125° C. wherein the thermoplastic melt is extruded at a temperature of approximately 80-180° C. as a granulate.
Claim 13
Dependent Claim
59 words
A method according to claim 8, wherein the extruder includes six temperature zones having approximately the following temperature profiles: Zone 1: 25-45° C. Zone 2: 60-120° C. Zone 3: 100-190° C. Zone 4: 140-190° C. Zone 5: 140-190° C. Zone 6: 140-200° C. wherein the thermoplastic melt is extruded at a temperature of approximately 150-200° C. as a foam.
Claim 14
Dependent Claim
16 words
A method according to claim 1, wherein the thermoplastic melt is plasticized prior to being extruded.
Claim 15
Dependent Claim
21 words
A method according to claim 1, wherein the filter material is compressed to a strand transversely to its axis and wrapped.
Claim 16
Dependent Claim
20 words
A method according to claim 1, wherein the starch-based polymer supplied to the extruder is dried by degasification during processing.
Claim 17
Independent Claim
104 words
A method for manufacturing biodegradable filter elements comprising: (a) forming a thermoplastic starch/polymer melt comprising a blend of thermoplastic starch and at least one synthetic polymer, wherein the thermoplastic starch is formed by mixing starch and at least one plasticizer under conditions that result in the thermoplastic starch having a water content of less than 5%, wherein the synthetic polymer is selected from the group consisting of polyvinyl alcohol, polyester amides, polyester urethanes, aliphatic polyesters, aromatic polymers, and copolymers of aliphatic polyesters and aromatic polyesters; (b) extruding the thermoplastic starch/polymer melt to form an extrudate; and (c) processing the extrudate into a filter element.
Claim 18
Independent Claim
104 words
A method for manufacturing biodegradable filter elements comprising: (a) forming a thermoplastic starch/polymer melt comprising a blend of thermoplastic starch and at least one synthetic polymer, wherein the thermoplastic starch is formed by mixing starch and at least one plasticizer under conditions that result in the thermoplastic starch having a water content of less than 5%, wherein the synthetic polymer is selected from the group consisting of polyvinyl alcohol, polyester amides, polyester urethanes, aliphatic polyesters, aromatic polymers, and copolymers of aliphatic polyesters and aromatic polyesters; (b) extruding the thermoplastic starch/polymer melt to form an extrudate; and (c) processing the extrudate into a filter element.
Claim 19
Dependent Claim
15 words
A method according to claim 16, wherein the filter element is free of cellulose esters.
Claim 20
Independent Claim
95 words
A method for manufacturing biodegradable filter elements comprising: (a) continuously supplying a mixture to an extruder, the mixture consisting essentially of one or more renewable raw materials, at least one hydrophobic synthetic polymer selected from the group consisting of polyester urethanes, aliphatic polyesters, aromatic polyesters, and copolymers of aliphatic polyesters and aromatic polyesters, optionally a flow auxiliary, and optionally a blowing agent; (b) heating and kneading the mixture under conditions so as to form a thermoplastic melt; (c) extruding the thermoplastic melt to form an extrudate; and (d) processing the extrudate into a filter element.
Claim 21
Independent Claim
95 words
A method for manufacturing biodegradable filter elements comprising: (a) continuously supplying a mixture to an extruder, the mixture consisting essentially of one or more renewable raw materials, at least one hydrophobic synthetic polymer selected from the group consisting of polyester urethanes, aliphatic polyesters, aromatic polyesters, and copolymers of aliphatic polyesters and aromatic polyesters, optionally a flow auxiliary, and optionally a blowing agent; (b) heating and kneading the mixture under conditions so as to form a thermoplastic melt; (c) extruding the thermoplastic melt to form an extrudate; and (d) processing the extrudate into a filter element.
Claim 22
Dependent Claim
31 words
A method according to claim 18, wherein the renewable raw material consists essentially of a starch-based polymer selected from the group consisting of native starches, modified starches and thermoplastic starch polymers.
References Cited (Backward Citations)
DE1079521B
Cited
EP0285811A1
Cited
GB2205102A
Cited
WO1990005161A1
Cited
US5153037A
Cited
US4863655A
Cited
DE4013304A1
Cited
DE4013293A1
Cited
WO1992015209A1
Cited
DE4109603A1
Cited
DE4116404A1
Cited
WO1993002070A1
Cited
WO1993007771A1
Cited
EP0539191A1
Cited
EP0541050A2
Cited
EP0542155A2
Cited
US5402802A
Cited
EP0597478A1
Cited
EP0614620A2
Cited
DE4322966A1
Cited
EP0632970A2
Cited
EP0632969A2
Cited
EP0632968A2
Cited
EP0634113A2
Cited
EP0641525A2
Cited
US5497793A
Cited
US5396909A
Cited
EP0672772A2
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2003-05-16 | 2003-11-15 | 2004-05-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2007-05-16 | 2007-11-15 | 2008-05-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2011-05-16 | 2011-11-15 | 2012-05-16 | $7700.00 | Window Closed / Lapsed |