Method for producing thin-film solar cell and equipment for producing the same
Assignee: Solar Frontier KK
•
Filing: 1997-04-30
•
Granted: 2000-04-11
•
Expires: 2017-04-30
Abstract
Abstract A thin-film light absorbing layer which is regulated so as to have any desired gallium concentration and which is capable of attaining a high open-circuit voltage is formed by a simple method at a temperature lower than the softening point of the soda-lime float glass. A light absorbing layer is formed by forming a back electrode on a soda-lime float glass substrate, forming on the back electrode layer a stacked precursor film including a copper-gallium alloy layer and an indium layer by sputtering, and then heating the precursor film in an atmosphere of selenium and/or sulfur.
Inventors
- 👤 Katsumi Kushiya
- 👤 Muneyori Tachiyuki
- 👤 Takahisa Kase
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 07:35
CPC Classifications
H; H10; H10F; H10F10/00; H10F10/10; H10F10/16; H10F10/167; H10F71/00; H10F71/137; H10F77/00; H10F77/10; H10F77/12; H10F77/126; Y; Y02; Y02E; Y02E10/00; Y02E10/50; Y02E10/541; Y02P; Y02P70/00; Y02P70/50
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
195 words
A method for producing a thin-film light absorbing layer for a thin-film solar cell which comprises forming a stacked precursor film comprising a copper-gallium alloy layer and an indium layer on a metallic back electrode layer by sputtering, and then heating the precursor film in an atmosphere of at least one of selenium and sulfur to thereby form a light absorbing layer comprising a Cu-III-VI 2 chalcopyrite multi-element compound semiconductor, wherein said stacked precursor film which comprises a copper-gallium alloy layer and an indium layer is formed by depositing the copper-gallium alloy layer and the indium layer in this order on the metallic back electrode layer by sputtering using (1) copper-gallium alloy targets having different gallium contents, with the gallium content in each copper-gallium alloy target being from 1 to 40% by weight and (2) an indium or indium-selenium alloy target, wherein said thin-film light absorbing layer has a side closest to the metallic back electrode layer and a side closest to an interfacial layer in the solar cell and has a gallium concentration gradient that increases from the side closest to the interfacial layer to the side closest to the metallic back electrode layer.
Claim 2
Independent Claim
195 words
A method for producing a thin-film light absorbing layer for a thin-film solar cell which comprises forming a stacked precursor film comprising a copper-gallium alloy layer and an indium layer on a metallic back electrode layer by sputtering, and then heating the precursor film in an atmosphere of at least one of selenium and sulfur to thereby form a light absorbing layer comprising a Cu-III-VI 2 chalcopyrite multi-element compound semiconductor, wherein said stacked precursor film which comprises a copper-gallium alloy layer and an indium layer is formed by depositing the copper-gallium alloy layer and the indium layer in this order on the metallic back electrode layer by sputtering using (1) copper-gallium alloy targets having different gallium contents, with the gallium content in each copper-gallium alloy target being from 1 to 40% by weight and (2) an indium or indium-selenium alloy target, wherein said thin-film light absorbing layer has a side closest to the metallic back electrode layer and a side closest to an interfacial layer in the solar cell and has a gallium concentration gradient that increases from the side closest to the interfacial layer to the side closest to the metallic back electrode layer.
Claim 3
Dependent Claim
80 words
The method for producing a thin-film light absorbing layer for a thin-film solar cell as claimed in claim 1, wherein the gallium concentration gradient in the thin-film light absorbing layer is obtained by forming the stacked precursor film comprising a copper-gallium alloy layer and an indium layer by sputtering in such a manner that the structure of the copper-gallium alloy layer is changed and then heating the precursor film in an atmosphere of at least one of selenium and sulfur.
Claim 4
Dependent Claim
99 words
The method for producing a thin-film light absorbing layer for a thin-film solar cell as claimed in claim 1, wherein the gallium concentration gradient in the thin-film light absorbing layer is obtained by forming the stacked precursor film comprising a copper-gallium alloy layer and an indium layer by depositing a copper-gallium alloy layer having a high gallium content, a copper-gallium alloy layer having a low gallium content, and an indium layer in this order on the metallic back electrode layer by sputtering, and then heating the precursor film in an atmosphere of at least one of selenium and sulfur.
Claim 5
Dependent Claim
99 words
The method for producing a thin-film light absorbing layer for a thin-film solar cell as claimed in claim 1, wherein the gallium concentration gradient in the thin-film light absorbing layer is obtained by forming the stacked precursor film comprising a copper-gallium alloy layer and an indium layer by depositing a copper-gallium alloy layer having a low gallium content, a copper-gallium alloy layer having a high gallium content, and an indium layer in this order on the metallic back electrode layer by sputtering, and then heating this precursor film in an atmosphere of at least one of selenium and sulfur.
References Cited (Backward Citations)
US3985635A
Cited
US4335266A
Cited
US4465575A
Cited
US4798660A
Cited
US5439575A
Cited
US4915745A
Cited
US4915745B1
Cited
US5445973A
Cited
JPH04326526A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2003-04-11 | 2003-10-11 | 2004-04-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2007-04-11 | 2007-10-11 | 2008-04-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2011-04-11 | 2011-10-11 | 2012-04-11 | $7700.00 | Window Closed / Lapsed |