Method of fabricating a salicide layer of a device electrode
Assignee: United Microelectronics Corp
•
Filing: 1997-03-11
•
Granted: 1999-11-09
•
Expires: 2017-03-11
Abstract
Abstract Salicide (self-aligned silicide) structures are formed using a process that does not form oxide spacer structures alongside polysilicon gate electrodes and wiring lines. A shaped polysilicon electrode is formed having protrusions extending beyond the sidewalls of the electrode. LDD source/drain regions are formed by ion implantation using only the polysilicon gate electrode as a mask, thereby forming LDD source drain/regions without using spacer oxide regions. Physical vapor deposition is used to deposit a metal layer having discontinuities at or adjacent the protrusions. A first rapid thermal anneal is performed to cause the metal to form a metal silicide over the polysilicon electrode. Unreacted metal is etched and then a second rapid thermal anneal is performed to convert the metal silicide to its lowest resistivity phase. Gate electrodes and wiring lines having this structure generally are formed having lower stress in the silicide layers, producing salicide structures having lower resistance than gate electrodes and wiring lines formed using conventional salicide techniques.
Inventors
- 👤 Water Lur
- 👤 Tony Lin
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 05:45
CPC Classifications
H; H10; H10D; H10D30/00; H10D30/01; H10D30/021; H10D30/0223; H10D30/0227; H10D30/0212; H10D64/00; H10D64/01; H10D64/011; H10D64/0111; H10D64/0112; H10D64/013; H10D64/01302; H10D64/01304; H10D64/01306; H10D64/01308; H10D64/0131; H10D64/01324; H10P; H10P14/00; H10P14/40; H10P14/412; H10P14/414; H10D64/20; H10D64/27; H10D64/311; H10D64/411; H10D64/511; H10D64/517; H10D64/518
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
178 words
A method of making a semiconductor device, comprising the steps of: providing a semiconductor substrate and providing a layer of insulating material over at least a portion of the semiconductor substrate; providing a first layer of a first material over the layer of insulating material; providing a second layer of a second material over the first layer of the first material; patterning the first and second layers to form an opening in the first and second layers that exposes a portion of the layer of insulating material; laterally etching the second layer from within the opening such that the opening becomes wider at the second layer and above the first layer; forming a shaped polysilicon structure over the layer of insulating material and within the opening, the shaped polysilicon structure having protrusions extending laterally over surfaces of the first layer and the semiconductor substrate; removing the first layer and the second layer; depositing a metal layer on the shaped polysilicon structure; and annealing the semiconductor device to produce a layer of metal silicide on the shaped polysilicon structure.
Claim 2
Independent Claim
178 words
A method of making a semiconductor device, comprising the steps of: providing a semiconductor substrate and providing a layer of insulating material over at least a portion of the semiconductor substrate; providing a first layer of a first material over the layer of insulating material; providing a second layer of a second material over the first layer of the first material; patterning the first and second layers to form an opening in the first and second layers that exposes a portion of the layer of insulating material; laterally etching the second layer from within the opening such that the opening becomes wider at the second layer and above the first layer; forming a shaped polysilicon structure over the layer of insulating material and within the opening, the shaped polysilicon structure having protrusions extending laterally over surfaces of the first layer and the semiconductor substrate; removing the first layer and the second layer; depositing a metal layer on the shaped polysilicon structure; and annealing the semiconductor device to produce a layer of metal silicide on the shaped polysilicon structure.
Claim 3
Dependent Claim
15 words
The method of claim 1, wherein the metal layer is deposited by physical vapor deposition.
Claim 4
Dependent Claim
34 words
The method of claim 1, wherein the metal layer is deposited in such a manner that there is a discontinuity in the deposited metal layer at or near the protrusions of the polysilicon structure.
Claim 5
Dependent Claim
32 words
The method of claim 1, wherein the step of annealing the semiconductor device consists of a rapid thermal anneal performed at a temperature within the range of 600° C. to 750° C.
Claim 6
Dependent Claim
19 words
The method of claim 4, wherein the rapid thermal anneal is performed at a temperature of about 700° C.
Claim 7
Dependent Claim
19 words
The method of claim 4, wherein the rapid thermal anneal continues for a time between 10 to 120 seconds.
Claim 8
Dependent Claim
16 words
The method of claim 5, wherein the rapid thermal anneal continues for 20 to 60 seconds.
Claim 9
Dependent Claim
37 words
The method of claim 1, further comprising the step of etching the device in a solution of NH 4 OH, H 2 O 2 and H 2 O subsequent to the step of annealing the semiconductor device.
Claim 10
Dependent Claim
26 words
The method of claim 8, further comprising a second step of annealing the semiconductor device at a temperature of about 850° C. for about 20 seconds.
Claim 11
Dependent Claim
30 words
The method of claim 1, further comprising a second step of annealing the semiconductor device at a temperature of greater than 700° C. for about 10 to about 120 seconds.
Claim 12
Independent Claim
210 words
A method of forming a semiconductor device including a MOS transistor, the method of making the MOS transistor comprising the steps of: forming an insulator on a semiconductor substrate; forming a shaped polysilicon electrode on the insulator, the shaped polysilicon electrode having protrusions extending laterally over the semiconductor substrate, wherein the step of forming the shaped polysilicon electrode includes: depositing a first layer of masking material on the semiconductor device and a second layer of masking material on the first layer of masking material; forming an opening by removing a portion of the first and the second layers of masking material; laterally etching the second layer of masking material so that the opening is wider at the second layer than at the first layer; depositing polysilicon within the opening and over the second layer of masking material; removing excess polysilicon to expose an upper layer of masking material; and removing the first and second layers of masking material forming by ion implantation LDD source/drain regions within the substrate on either side of the shaped polysilicon electrode using the protrusions of the shaped polysilicon electrode as a mask for the ion implantation to define the LDD source/drain region dopant distribution; and forming a metal silicide layer over the shaped polysilicon electrode.
Claim 13
Independent Claim
210 words
A method of forming a semiconductor device including a MOS transistor, the method of making the MOS transistor comprising the steps of: forming an insulator on a semiconductor substrate; forming a shaped polysilicon electrode on the insulator, the shaped polysilicon electrode having protrusions extending laterally over the semiconductor substrate, wherein the step of forming the shaped polysilicon electrode includes: depositing a first layer of masking material on the semiconductor device and a second layer of masking material on the first layer of masking material; forming an opening by removing a portion of the first and the second layers of masking material; laterally etching the second layer of masking material so that the opening is wider at the second layer than at the first layer; depositing polysilicon within the opening and over the second layer of masking material; removing excess polysilicon to expose an upper layer of masking material; and removing the first and second layers of masking material forming by ion implantation LDD source/drain regions within the substrate on either side of the shaped polysilicon electrode using the protrusions of the shaped polysilicon electrode as a mask for the ion implantation to define the LDD source/drain region dopant distribution; and forming a metal silicide layer over the shaped polysilicon electrode.
Claim 14
Dependent Claim
31 words
The method of claim 11, further comprising the step of depositing a third layer of masking material on the second layer of masking material before the step of forming an opening.
Claim 15
Dependent Claim
20 words
The method of claim 12, wherein the first and third layers of masking material are formed of the same material.
Claim 16
Dependent Claim
15 words
The method of claim 13, wherein the second layer of masking material comprises silicon oxide.
Claim 17
Dependent Claim
19 words
The method of claim 12, wherein the polysilicon is deposited by chemical vapor deposition and is doped in situ.
Claim 18
Dependent Claim
48 words
The method of claim 11, wherein the step of forming a metal silicide layer comprises the steps of: depositing a layer of metal on the semiconductor device; annealing the semiconductor device to form metal silicide on the shaped polysilicon electrode; and etching unreacted metal from the semiconductor device.
Claim 19
Dependent Claim
22 words
The method of claim 16, wherein the deposited metal is selected from the group consisting of titanium, cobalt, nickel platinum and palladium.
References Cited (Backward Citations)
US4818715A
Cited
US5214305A
Cited
US5162884A
Cited
US5196357A
Cited
US5518942A
Cited
US5656546A
Cited
US5646056A
Cited
US5753559A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2002-11-08 | 2003-05-10 | 2003-11-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2006-11-08 | 2007-05-10 | 2007-11-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2010-11-08 | 2011-05-10 | 2011-11-09 | $7700.00 | Window Closed / Lapsed |