Method for producing austenitic steel plate with excellent surface brightness and corrosion resistance
Assignee: JFE Steel Corp
•
Filing: 1998-09-18
•
Granted: 1999-11-02
•
Expires: 2018-09-18
Abstract
Abstract An austenite stainless steel plate having both excellent surface brightness and superior corrosion resistance, without polishing after finish annealing and pickling for descaling of the strip. The steel plate contains Si 0.02 to 0.2 wt % together with Si oxides at 1.0 wt % or less in the surface layer part in the 10 mu m depth from the surface. The depth of the intergranular groove in the surface layer part is 0.1 mu m or more to 0.5 mu m or less. Furthermore, the steel plate contains Al of 0.005 wt % or less and 0 of 0.006 wt % or less. The Al oxides are contained at 0.1 wt % or less in the surface layer part in the 10 mu m depth from the surface.
Inventors
- 👤 Kunio Fukuda
- 👤 Yoshikazu Kawabata
- 👤 Kazuhide Ishii
- 👤 Susumu Sato
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 12:48
CPC Classifications
C; C21; C21D; C21D8/00; C21D8/02; C23; C23G; C23G1/00; C23G1/02; C23G1/08; C23G1/086; C21D8/0221; C21D8/0226; C21D8/0236; C21D8/0247; C21D8/0273; C21D8/0278
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
163 words
A method for producing an austenite stainless steel plate, comprising descaling of slab after heating, hot rolling of the slab, annealing of the hot-rolled plate, pickling of the hot-rolled plate, cold rolling of the hot-rolled plate, finish annealing and pickling of the cold-rolled plate, employing slab containing Si of 0.2 wt % or less at the hot-rolling, finish annealing the cold-rolled plate so that the surface layer part of the 10 μm depth from the surface of the plate after pickling contains Si oxides at 1.0 wt % or less, solubilizing the surface of the cold-rolled plate at the pickling process after finish annealing in an acid mixture within the range of average solubilized weight loss represented by the following formula, so that the depth of the intergranular groove of the surface layer part might be 0.1 μm or more to 0.5 μm or less, 1.2+3×E≦D≦3.8+2×E wherein "D" represents the average solubilized level (g/m 2 ) and "E" represents Si concentration (wt %).
Claim 2
Independent Claim
163 words
A method for producing an austenite stainless steel plate, comprising descaling of slab after heating, hot rolling of the slab, annealing of the hot-rolled plate, pickling of the hot-rolled plate, cold rolling of the hot-rolled plate, finish annealing and pickling of the cold-rolled plate, employing slab containing Si of 0.2 wt % or less at the hot-rolling, finish annealing the cold-rolled plate so that the surface layer part of the 10 μm depth from the surface of the plate after pickling contains Si oxides at 1.0 wt % or less, solubilizing the surface of the cold-rolled plate at the pickling process after finish annealing in an acid mixture within the range of average solubilized weight loss represented by the following formula, so that the depth of the intergranular groove of the surface layer part might be 0.1 μm or more to 0.5 μm or less, 1.2+3×E≦D≦3.8+2×E wherein "D" represents the average solubilized level (g/m 2 ) and "E" represents Si concentration (wt %).
Claim 3
Dependent Claim
70 words
A method for producing an austenite stainless steel plate having excellent corrosion resistance and surface brightness according to claim 1, wherein the surface is solubilized by using an acid mixture of nitric acid and hydrofluoric acid of the composition satisfying the range represented by the following formula; 10≦A≦70 5≦B-0.67×C≦20 C≦50 wherein "A" is nitrate concentration (g/l); "B" is hydrofluorate concentration (g/l); and "C" is Fe concentration (g/l) in solvent medium.
Claim 4
Dependent Claim
37 words
A method for producing an austenite stainless steel plate having excellent corrosion resistance and surface brightness according to claim 1, wherein the slab temperature at starting time of hot rolling is about 1100° C. to 1200° C.
Claim 5
Dependent Claim
41 words
A method for producing an austenite stainless steel plate having excellent corrosion resistance and surface brightness according to claim 1, comprising subjecting slab to high-pressure descaling at a water injection pressure of 200 kgf/cm 2 or more prior to hot rolling.
Claim 6
Dependent Claim
62 words
A method for producing an austenite stainless steel plate having excellent corrosion resistance and surface brightness according to claim 1, further containing Al of 0.005 wt % or less and O of 0.006 wt % or less in the steel plate, wherein the Al oxides are contained at 0.1 wt % or less in the surface layer part of the steel plate.
Claim 7
Dependent Claim
49 words
A method for producing an austenite stainless steel plate having excellent corrosion resistance and surface brightness according to claim 1, further containing one or more selected from the group of V at 0.05 to 0.8 wt % and Co at 0.05 to 0.5 wt % in the steel plate.
References Cited (Backward Citations)
JPS5959900A
Cited
JPS6196092A
Cited
JPH0617271A
Cited
JPH0688300A
Cited
JPH0688297A
Cited
JPH06260164A
Cited
JPH06280064A
Cited
JPH0726350A
Cited
JPH07113187A
Cited
US5830291A
Cited
US5830291C1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2002-11-01 | 2003-05-03 | 2003-11-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2006-11-01 | 2007-05-03 | 2007-11-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2010-11-01 | 2011-05-03 | 2011-11-02 | $7700.00 | Window Closed / Lapsed |