US5830291A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method for producing bright stainless steel
Assignee: Jewel Acquisition LLC
•
Filing: 1996-10-08
•
Granted: 1998-11-03
•
Expires: 2016-10-08
Abstract
Abstract A method for producing bright stainless steel whereby a hot mill band having a dull oxide-free surface is first formed. The hot mill band is cold reduced to form a full hard coil having a shiny surface. The coil is subjected to continuous annealing at a temperature of 1500 DEG -1950 DEG F. in an oxygen-containing atmosphere sufficient to form a protective FeCr2O3 scale. The annealed coil is subjected to a mild non-etching pickling process to remove the black scale. The coil is then rolled on a temper mill having specially finished rolls to impart a surface pattern that replicates an abrasively polished surface.
Inventors
- 👤 Michael F. McGuire
- 👤 Kelley L. Senzarin-Kulik
- 👤 Anthony J. Denoi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 17:37
CPC Classifications
C; C21; C21D; C21D8/00; C21D8/02; C23; C23G; C23G1/00; C23G1/02; C23G1/08; C23G1/086; C21D8/0221; C21D8/0236; C21D8/0278
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
109 words
A method for producing bright stainless steel comprising: a) forming a hot mill band having a dull oxide free surface; b) cold reducing the hot mill band to form a full hard coil having a shiny surface; c) subjecting said full hard coil to a continuous anneal at a temperature of 1500°-1950° F. in an oxygen containing atmosphere sufficient to form a protective FeCr 2 O 3 scale; d) subjecting said annealed coil to a mild non-etching pickling process to remove the scale; and e) rolling said annealed coil on a temper mill having specially finished rolls configured to impart a surface pattern that replicates an abrasively polished surface.
Claim 2
Independent Claim
109 words
A method for producing bright stainless steel comprising: a) forming a hot mill band having a dull oxide free surface; b) cold reducing the hot mill band to form a full hard coil having a shiny surface; c) subjecting said full hard coil to a continuous anneal at a temperature of 1500°-1950° F. in an oxygen containing atmosphere sufficient to form a protective FeCr 2 O 3 scale; d) subjecting said annealed coil to a mild non-etching pickling process to remove the scale; and e) rolling said annealed coil on a temper mill having specially finished rolls configured to impart a surface pattern that replicates an abrasively polished surface.
Claim 3
Dependent Claim
47 words
The method of claim 1 wherein the mild non-etching pickling process includes air cooling the annealed coil to an intermediate temperature where it is subjected to a molten salt treatment and then air cooling to ambient temperature where the coil is subjected to a mild acid pickle.
Claim 4
Dependent Claim
16 words
The method of claim 2 wherein the intermediate temperature is between 800° F. and 1000° F.
Claim 5
Independent Claim
196 words
A method for producing bright stainless steel comprising: a) forming a hot mill band having a dull oxide free surface; b) cold reducing the hot mill band to form a full hard coil having a shiny surface; c) subjecting said full hard coil to a continuous anneal at a temperature of 1500°-1950° F. in an oxygen containing atmosphere sufficient to form a protective FeCr 2 O 3 scale: d) subjecting said annealed coil to a mild non-etching pickling process to remove the scale, wherein the mild non-etching pickling process includes air cooling the annealed coil to an intermediate temperature between 800° F. and 1000° F. where it is subjected to a molten salt treatment and then air cooling to ambient temperature where the coil is subjected to a mild acid pickle, and wherein the mild acid pickle includes subjecting said annealed coil to at least one of a nitric acid bath and rinse, a sulfuric acid bath and rinse with hydrofluoric concentration of 0.5% or less on either acid bath; and e) rolling said annealed coil on a temper mill having specially finished rolls configured to impart a surface pattern that replicates an abrasively polished surface.
Claim 6
Independent Claim
196 words
A method for producing bright stainless steel comprising: a) forming a hot mill band having a dull oxide free surface; b) cold reducing the hot mill band to form a full hard coil having a shiny surface; c) subjecting said full hard coil to a continuous anneal at a temperature of 1500°-1950° F. in an oxygen containing atmosphere sufficient to form a protective FeCr 2 O 3 scale: d) subjecting said annealed coil to a mild non-etching pickling process to remove the scale, wherein the mild non-etching pickling process includes air cooling the annealed coil to an intermediate temperature between 800° F. and 1000° F. where it is subjected to a molten salt treatment and then air cooling to ambient temperature where the coil is subjected to a mild acid pickle, and wherein the mild acid pickle includes subjecting said annealed coil to at least one of a nitric acid bath and rinse, a sulfuric acid bath and rinse with hydrofluoric concentration of 0.5% or less on either acid bath; and e) rolling said annealed coil on a temper mill having specially finished rolls configured to impart a surface pattern that replicates an abrasively polished surface.
Claim 7
Dependent Claim
24 words
The method of claim 3 including a mild acid bath and maintaining an iron content of the nitric acid bath at or below 1%.
Claim 8
Dependent Claim
37 words
The method of claim 1 wherein the surface pattern following temper rolling is defined by an arithmetic roughness on the order of 2 to 50 micro inch and an 85° transverse surface gloss of 40 to 90%.
Claim 9
Dependent Claim
23 words
The method of claim 1 wherein the stainless steel is of the austenitic type and the annealing temperature is 1800° to 1950° F.
Claim 10
Dependent Claim
20 words
The method of claim 1 wherein the stainless steel is of the ferritic type and the composition includes ferrite stabilizers.
Claim 11
Dependent Claim
13 words
The method of claim 8 wherein the ferrite stabilizers include at least Ti.
Claim 12
Dependent Claim
17 words
The method of claim 1 wherein the atmosphere has an oxygen partial pressure of at least 0.1%.
Claim 13
Independent Claim
14 words
The method claim of 10 wherein the oxygen partial pressure is at least 2%.
Claim 14
Dependent Claim
18 words
The method of claim 1 wherein the air/fuel ratio used for combustion is at least 9.2 to 1.
Claim 15
Dependent Claim
25 words
The method of claim 1 wherein said coil is subject to a temper pass on a smooth roll prior to the specially finished roll pass.
Claim 16
Independent Claim
129 words
A method for producing bright stainless steel from a cold reduced, full hard coil, comprising the steps of: subjecting the full hard coil to a continuous anneal at a temperature of 1500°-1950° F. in an oxygen containing atmosphere to form an FeCr 2 O 3 containing scale on the annealed coil; pickling the annealed coil with a mild non-etching pickling process to remove the scale, wherein the pickling process includes treating the annealed coil with an acid bath including at least one of nitric and sulfuric acid, the acid bath having a hydrofluoric acid content of less than 0.5%; and rolling the descaled coil on a temper mill having specially finished rolls such that a surface pattern is imparted to the rolled coil which replicates an abrasively polished surface.
Claim 17
Independent Claim
129 words
A method for producing bright stainless steel from a cold reduced, full hard coil, comprising the steps of: subjecting the full hard coil to a continuous anneal at a temperature of 1500°-1950° F. in an oxygen containing atmosphere to form an FeCr 2 O 3 containing scale on the annealed coil; pickling the annealed coil with a mild non-etching pickling process to remove the scale, wherein the pickling process includes treating the annealed coil with an acid bath including at least one of nitric and sulfuric acid, the acid bath having a hydrofluoric acid content of less than 0.5%; and rolling the descaled coil on a temper mill having specially finished rolls such that a surface pattern is imparted to the rolled coil which replicates an abrasively polished surface.
Claim 18
Dependent Claim
21 words
The method as claimed in claim 14, wherein the steel is an austenitic steel and the annealing temperature is 1800°-1950° F.
Claim 19
Dependent Claim
20 words
The method as claimed in claim 15, wherein the atmosphere has an oxygen partial pressure of at least two percent.
Claim 20
Dependent Claim
37 words
The method as claimed in claim 14, wherein the steel is ferritic steel having at least one ferrite stabilizer selected from the group consisting of Ti, Nb, Ta and Zr and the annealing temperature is 1700°-1950° F.
Claim 21
Dependent Claim
33 words
The method as claimed in claim 14, including: cooling the annealed coil to an intermediate temperature; subjecting the annealed coil to a molten salt treatment; and cooling the annealed coil to ambient temperature.
References Cited (Backward Citations)
US1859698A
Cited
US1810612A
Cited
US1931134A
Cited
US1901039A
Cited
US2249556A
Cited
US2264859A
Cited
US2303343A
Cited
US2340461A
Cited
US2389838A
Cited
US2474674A
Cited
US2666003A
Cited
US2710271A
Cited
US2750301A
Cited
US2752274A
Cited
US2987429A
Cited
US3117897A
Cited
US3260619A
Cited
US3615909A
Cited
US3536601A
Cited
US3563074A
Cited
US3712833A
Cited
US4160677A
Cited
US4620884A
Cited
US4286986A
Cited
US4415415A
Cited
US4450058A
Cited
US4545826A
Cited
US4648914A
Cited
US4713154A
Cited
JPS62253732A
Cited
US4851092A
Cited
US5344509A
Cited
US5505786A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2001-11-02 | 2002-05-04 | 2002-11-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2005-11-02 | 2006-05-04 | 2006-11-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2009-11-02 | 2010-05-04 | 2010-11-03 | $7700.00 | Window Closed / Lapsed |