Metal interconnection and method for making
Assignee: Kawasaki Microelectronics Inc
•
Filing: 1997-01-30
•
Granted: 1999-10-26
•
Expires: 2017-01-30
Abstract
Abstract A metal interconnection is prepared by forming an underlying metal film of high melting point metal such as Ti and/or high melting point metal compound such as TiN layers above a semiconductor substrate, plasma etching the surface of the underlying metal film in a gas atmosphere containing chloride, and forming an interconnecting metal film such as Al, Cu, Au and Ag on the underlying metal film. Alternatively, a metal interconnection is prepared by forming an insulating film above a semiconductor substrate, forming connection holes in the insulating film, forming an underlying metal film such as TiN on the insulating film and the bottom and side wall of the connection holes by a CVD process under controlled conditions, and forming an interconnecting metal film such as Al on the underlying metal film. The TiN film has (111) preferential orientation and the aluminum film has (111) preferential orientation, smooth surface and effective coverage. The thus fabricated metal interconnection has improved reliability including electromigration immunity when used in semiconductor devices and finding advantageous use in miniaturized semiconductor devices.
Inventors
- 👤 Hiroshi Shinriki
- 👤 Takeshi Kaizuka
- 👤 Nobuyuki Takeyasu
- 👤 Tomohiro Ohta
- 👤 Eiichi Kondoh
- 👤 Hiroshi Yamamoto
- 👤 Tomoharu Katagiri
- 👤 Tadashi Nakano
- 👤 Yumiko Kawano
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 01:36
CPC Classifications
H; H10; H10W; H10W20/00; H10W20/01; H10W20/031; H10W20/032; H10W20/033; H10W20/035; H10P; H10P14/00; H10P14/40; H10P14/42; H10P14/43; H10P50/00; H10P50/20; H10P50/26; H10P50/264; H10P50/266; H10P50/267; H10W20/036; H10W20/047; H10W20/048; H10W20/054; H10W20/056; H10W20/40; H10W20/41; H10W20/425
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
218 words
A metal interconnection structures, comprising: an insulating film formed over a semiconductor substrate; at least one connection hole in the insulating film; an underlying metal film including a first layer composed mainly of a refractory metal which has a cubic or hexagonal crystal structure formed on the insulating film and on a side wall of the connection hole and a second layer composed mainly of a refractory metal compound which has a cubic crystal structure formed on the first layer; and an interconnecting metal film containing predominantly a component selected from the group consisting of Al, Cu, Au and Ag on the underlying metal film, wherein said first layer of said underlying metal film on the insulating film has a (111) preferential orientation when said refractory metal has the cubic crystal structure or a (002) preferential orientation when said refractory metal has the hexagonal crystal structure; said second layer and said interconnecting metal film over the insulating film each has a (111) preferential orientation; said connection hole has an aspect ratio of at least 1; and a thickness of said second layer over the side wall of the connection hole is at least 0.5 times of a thickness of said second layer over the insulating film, or said connection hole is filled up with the underlying metal film.
Claim 2
Dependent Claim
218 words
A metal interconnection structures, comprising: an insulating film formed over a semiconductor substrate; at least one connection hole in the insulating film; an underlying metal film including a first layer composed mainly of a refractory metal which has a cubic or hexagonal crystal structure formed on the insulating film and on a side wall of the connection hole and a second layer composed mainly of a refractory metal compound which has a cubic crystal structure formed on the first layer; and an interconnecting metal film containing predominantly a component selected from the group consisting of Al, Cu, Au and Ag on the underlying metal film, wherein said first layer of said underlying metal film on the insulating film has a (111) preferential orientation when said refractory metal has the cubic crystal structure or a (002) preferential orientation when said refractory metal has the hexagonal crystal structure; said second layer and said interconnecting metal film over the insulating film each has a (111) preferential orientation; said connection hole has an aspect ratio of at least 1; and a thickness of said second layer over the side wall of the connection hole is at least 0.5 times of a thickness of said second layer over the insulating film, or said connection hole is filled up with the underlying metal film.
Claim 3
Dependent Claim
24 words
The metal interconnection structure of claim 1, wherein said connection hole is filled up with the underlying metal film and the interconnecting metal film.
Claim 4
Dependent Claim
19 words
The metal interconnection structure of claim 1, wherein said connection hole is filled up with the underlying metal film.
Claim 5
Dependent Claim
121 words
The metal interconnection structure of claim 1, wherein the refractory metal of said first layer of said underlying metal film has a first atomic distance in a (111) plane when the metal has the cubic crystal structure or a (002) plane when the metal has the hexagonal crystal structure, the refractory metal compound of said second layer has a second atomic distance in a (111) plane, the component of said interconnecting metal film has a third atomic distance in a (111) plane, the ratio of the second atomic distance to the first atomic distance is from about 0.95 to about 1.05, and the ratio of the third atomic distance to the second atomic distance is from about 0.95 to about 1.05.
Claim 6
Dependent Claim
58 words
The metal interconnection structure of claim 1, wherein said refractory metal is selected from the group consisting of Ti, Ta, and Nb, said refractory metal compound is selected from the group consisting of TiN, VN, W 2 N, VC, W 2 C, and Mo 2 N, and said component of the interconnecting metal film is Al or Au.
Claim 7
Dependent Claim
29 words
The metal interconnection structure of claim 1, wherein said refractory metal is Ti, said refractory metal compound is TiN, and the component of the interconnecting metal film is Al.
Claim 8
Dependent Claim
21 words
The metal interconnection structure of claim 1, wherein said refractory metal compound of the second layer is a refractory metal nitride.
Claim 9
Dependent Claim
19 words
The metal interconnection structure of claim 1, wherein said refractory metal compound of the second layer is titanium nitride.
Claim 10
Dependent Claim
27 words
The metal interconnection structure of claim 1, wherein said second layer has an I(111)/I(200) peak intensity ratio of Cu K.sub.α X-ray diffraction of greater than about one.
Claim 11
Dependent Claim
28 words
The metal interconnection structure of claim 1, wherein said second layer has an I(111)/I(200) peak intensity ratio of Cu K.sub.α X-ray diffraction of not less than about 4.
Claim 12
Dependent Claim
28 words
The metal interconnection structure of claim 1, wherein said second layer has an I(111)/I(200) peak intensity ratio of Cu K.sub.α X-ray diffraction of not less than about 10.
Claim 13
Dependent Claim
15 words
The metal interconnection structure of claim 1, wherein said interconnecting metal film contains predominantly Al.
Claim 14
Dependent Claim
29 words
The metal interconnection structure of claim 1, wherein said interconnecting metal film has an I(111)/I(200) peak intensity ratio of Cu K.sub.α X-ray diffraction of not less than about 20.
Claim 15
Dependent Claim
29 words
The metal interconnection structure of claim 1, wherein said interconnecting metal film has an I(111)/I(200) peak intensity ratio of Cu K.sub.α X-ray diffraction of not less than about 2000.
Claim 16
Dependent Claim
40 words
The metal interconnection structure of claim 1, wherein the thickness of the second layer over the side wall of the connection hole is about the same as the thickness of the second layer over the surface of the insulating film.
Claim 17
Dependent Claim
26 words
The metal interconnection structure of claim 1, wherein said second layer of the underlying metal film prevents diffusion of the component of the interconnecting metal film.
Claim 18
Dependent Claim
165 words
A metal interconnection structure, comprising: an insulating film formed over a semiconductor substrate; at least one connection hole in the insulating film; an underlying metal film including a layer composed mainly of a refractory metal compound which has a cubic crystal structure formed on the insulating film and on a side wall of the connection hole; and an interconnecting metal film containing predominantly a component selected from the group consisting of Al, Cu, Au and Ag on the underlying metal film, wherein said layer of the underlying metal film on the insulating film and said interconnecting metal film over the insulating film each has a (111) preferential orientation; said connection hole has an aspect ratio of at least one; and a thickness of the layer of the underlying metal film on the side wall of the connection hole is at least 0.5 times of a thickness of the layer on the insulating film, or said connection hole is filled up with the underlying metal film.
Claim 19
Dependent Claim
165 words
A metal interconnection structure, comprising: an insulating film formed over a semiconductor substrate; at least one connection hole in the insulating film; an underlying metal film including a layer composed mainly of a refractory metal compound which has a cubic crystal structure formed on the insulating film and on a side wall of the connection hole; and an interconnecting metal film containing predominantly a component selected from the group consisting of Al, Cu, Au and Ag on the underlying metal film, wherein said layer of the underlying metal film on the insulating film and said interconnecting metal film over the insulating film each has a (111) preferential orientation; said connection hole has an aspect ratio of at least one; and a thickness of the layer of the underlying metal film on the side wall of the connection hole is at least 0.5 times of a thickness of the layer on the insulating film, or said connection hole is filled up with the underlying metal film.
Claim 20
Dependent Claim
76 words
The metal interconnection structure of claim 17, wherein said underlying metal film further includes a first layer composed mainly of a refractory metal which has a cubic or hexagonal crystal structure formed under the layer; and said first layer of the underlying metal film on the insulating film has a (111) preferential orientation when said refractory metal has the cubic crystal structure or a (002) preferential orientation when the refractory metal has the hexagonal crystal structure.
Claim 21
Dependent Claim
189 words
A metal interconnection structure, comprising: an insulating film formed over a semiconductor substrate; at least one connection hole in the insulating film; and an underlying metal film including a first layer composed mainly of a refractory metal which has a cubic or hexagonal crystal structure formed on the insulating film and on a side wall of the connection hole and a second layer composed mainly of a refractory metal compound which has a cubic crystal structure formed on the first layer, wherein said first layer of the underlying metal film has a (111) preferential orientation when said refractory metal has the cubic crystal structure or a (002) preferential orientation when the refractory metal has the hexagonal crystal structure; said second layer of the underlying metal film over the insulating film has a (111) preferential orientation; said connection hole has an aspect ratio of at least one; and a thickness of said second layer over the side wall of the connection hole is at least 0.5 times of a thickness of the second layer over the insulating film, or said connection hole is filled up with the underlying metal film.
Claim 22
Dependent Claim
189 words
A metal interconnection structure, comprising: an insulating film formed over a semiconductor substrate; at least one connection hole in the insulating film; and an underlying metal film including a first layer composed mainly of a refractory metal which has a cubic or hexagonal crystal structure formed on the insulating film and on a side wall of the connection hole and a second layer composed mainly of a refractory metal compound which has a cubic crystal structure formed on the first layer, wherein said first layer of the underlying metal film has a (111) preferential orientation when said refractory metal has the cubic crystal structure or a (002) preferential orientation when the refractory metal has the hexagonal crystal structure; said second layer of the underlying metal film over the insulating film has a (111) preferential orientation; said connection hole has an aspect ratio of at least one; and a thickness of said second layer over the side wall of the connection hole is at least 0.5 times of a thickness of the second layer over the insulating film, or said connection hole is filled up with the underlying metal film.
Claim 23
Dependent Claim
47 words
The metal interconnection structure of claim 19, further comprising an interconnecting metal film containing predominantly a component selected from the group consisting of Al, Cu, Au and Ag on the underlying metal film, wherein said interconnecting metal film over the insulating film has a (111) preferential orientation.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2002-10-25 | 2003-04-26 | 2003-10-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2006-10-25 | 2007-04-26 | 2007-10-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2010-10-25 | 2011-04-26 | 2011-10-26 | $7700.00 | Window Closed / Lapsed |