US5972801A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for reducing defects in oxide layers on silicon carbide
Assignee: Wolfspeed Inc
•
Filing: 1995-11-08
•
Granted: 1999-10-26
•
Expires: 2015-11-08
Abstract
Abstract A method is disclosed for obtaining improved oxide layers and resulting improved performance from oxide based devices. The method comprises exposing an oxide layer on a silicon carbide layer to an oxidizing source gas at a temperature below the temperature at which SiC would begin to oxidize at a significant rate, while high enough to enable the oxidizing source gas to diffuse into the oxide layer, and while avoiding any substantial additional oxidation of the silicon carbide, and for a time sufficient to densify the oxide layer and improve the interface between the oxide layer and the silicon carbide layer.
Inventors
- 👤 Lori A. Lipkin
- 👤 David B. Slater, Jr.
- 👤 John W. Palmour
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 16:51
CPC Classifications
H; H10; H10D; H10D62/00; H10D62/80; H10D62/83; H10D62/832; H10D62/8325; H10D64/00; H10D64/01; H10D64/013; H10D64/01366; H10D48/00; H10D48/01; Y; Y10; Y10S; Y10S438/00; Y10S438/931
Claims Analysis
Total Claims: 38
Claim 1
Independent Claim
110 words
A method of obtaining oxide layers on silicon carbide and resulting improved performance from oxide based silicon carbide devices, the method comprising: preparing the surface of a silicon carbide layer for an oxidation layer; producing an oxide layer on the prepared silicon carbide surface; and thereafter exposing the oxide layer and the underlying silicon carbide layer to an oxidizing source gas at a temperature of between about 600 and 1000° C., and while avoiding any substantial additional oxidation of the silicon carbide under the oxide layer, and for a time sufficient to densify the oxide layer and improve the interface between the oxide layer and the underlying silicon carbide layer.
Claim 2
Independent Claim
110 words
A method of obtaining oxide layers on silicon carbide and resulting improved performance from oxide based silicon carbide devices, the method comprising: preparing the surface of a silicon carbide layer for an oxidation layer; producing an oxide layer on the prepared silicon carbide surface; and thereafter exposing the oxide layer and the underlying silicon carbide layer to an oxidizing source gas at a temperature of between about 600 and 1000° C., and while avoiding any substantial additional oxidation of the silicon carbide under the oxide layer, and for a time sufficient to densify the oxide layer and improve the interface between the oxide layer and the underlying silicon carbide layer.
Claim 3
Dependent Claim
30 words
A method according to claim 1 wherein the step of producing the oxide layer comprises thermally oxidizing the silicon carbide layer at temperatures of between about 1050° and 1300° C.
Claim 4
Dependent Claim
34 words
A method according to claim 1 wherein the step of producing the oxide layer comprises thermally oxidizing the carbon face of the silicon carbide layer at temperatures of between about 1000° and 1300° C.
Claim 5
Dependent Claim
34 words
A method according to claim 1 wherein the step of producing the oxide layer comprises thermally oxidizing the silicon face of the silicon carbide layer at temperatures if between about 1000° and 1400° C.
Claim 6
Dependent Claim
24 words
A method according to claim 1 wherein the step of producing the oxide layer comprises depositing an oxide layer on the silicon carbide layer.
Claim 7
Dependent Claim
20 words
A method according to claim 1 wherein the step of producing the oxide layer comprises sputter depositing the oxide layer.
Claim 8
Dependent Claim
20 words
A method according to claim 1 wherein the step of producing the oxide layer comprises plasma depositing the oxide layer.
Claim 9
Dependent Claim
19 words
A method according to claim 1 wherein the step of producing the oxide layer comprises producing an oxynitride layer.
Claim 10
Dependent Claim
32 words
A method according to claim 1 wherein the step of exposing the oxide and silicon carbide to the oxidizing source gas comprises exposing an oxide layer on a silicon carbide epitaxial layer.
Claim 11
Dependent Claim
31 words
A method according to claim 1 wherein the step of exposing the oxide and silicon carbide to the oxidizing source gas comprises exposing an oxide layer on a silicon carbide substrate.
Claim 12
Dependent Claim
45 words
A method according to claim 1 wherein the step of exposing the oxide and underlying silicon carbide layer to an oxidizing source gas comprises exposing the oxide and silicon carbide to an oxidizing source gas at a temperature of between about 800° and 1000° C.
Claim 13
Dependent Claim
53 words
A method according to claim 1 wherein the step of exposing the oxide and silicon carbide to an oxidizing source gas comprises exposing the oxide and silicon carbide to an oxygen-containing gas that does not otherwise interfere with the chemical, physical, or electronic characteristics of either of the oxide or silicon carbide layers.
Claim 14
Dependent Claim
58 words
A method according to claim 1 wherein the step of exposing the oxide and silicon carbide to an oxidizing source gas comprises exposing the oxide and silicon carbide to a gas selected from the group consisting of: oxygen, water vapor, oxygen in water vapor, water vapor a in carrier gas, compounds of nitrogen and oxygen, and mixtures thereof.
Claim 15
Independent Claim
124 words
A method of obtaining oxide layers on silicon carbide and resulting improved performance from oxide based silicon carbide devices, the method comprising: preparing the surface of a silicon carbide layer for an oxidation layer; thermally oxidizing the prepared layer of silicon carbide at a temperature of between about 1050° and 1100° C. to produce an oxide layer on the layer of silicon carbide; and thereafter exposing the oxide layer and the underlying silicon carbide layer to an oxidizing source gas at a temperature between about 600 and 1000° C., and while avoiding any substantial additional oxidation of the silicon carbide, and for a time sufficient to densify the oxide layer and improve the interface between the oxide layer and the underlying silicon carbide layer.
Claim 16
Independent Claim
124 words
A method of obtaining oxide layers on silicon carbide and resulting improved performance from oxide based silicon carbide devices, the method comprising: preparing the surface of a silicon carbide layer for an oxidation layer; thermally oxidizing the prepared layer of silicon carbide at a temperature of between about 1050° and 1100° C. to produce an oxide layer on the layer of silicon carbide; and thereafter exposing the oxide layer and the underlying silicon carbide layer to an oxidizing source gas at a temperature between about 600 and 1000° C., and while avoiding any substantial additional oxidation of the silicon carbide, and for a time sufficient to densify the oxide layer and improve the interface between the oxide layer and the underlying silicon carbide layer.
Claim 17
Dependent Claim
24 words
A method according to claim 14 wherein the step of thermally oxidizing a silicon carbide layer comprises thermally oxidizing a silicon carbide epitaxial layer.
Claim 18
Dependent Claim
23 words
A method according to claim 14 wherein the step of thermally oxidizing a silicon carbide layer comprises thermally oxidizing a silicon carbide substrate.
Claim 19
Dependent Claim
40 words
A method according to claim 14 wherein the step of exposing the oxide and silicon carbide to an oxidizing source gas comprises exposing the oxide and silicon carbide to an oxidizing source gas at a temperature of about 950° C.
Claim 20
Dependent Claim
53 words
A method according to claim 14 wherein the step of exposing the oxide and silicon carbide to an oxidizing source gas comprises exposing the oxide and silicon carbide to an oxygen-containing gas that does not otherwise interfere with the chemical, physical, or electronic characteristics of either of the oxide or silicon carbide layers.
Claim 21
Dependent Claim
58 words
A method according to claim 14 wherein the step of exposing the oxide and silicon carbide to an oxidizing source gas comprises exposing the oxide and silicon carbide to a gas selected from the group consisting of: oxygen, water vapor, oxygen in water vapor, water vapor in a carrier gas, compounds of nitrogen and oxygen, and mixtures thereof.
Claim 22
Dependent Claim
33 words
A method according to claim 14 and further comprising the step of annealing the oxide layer in an argon atmosphere prior to the step of exposing the layers to an oxidizing source gas.
Claim 23
Dependent Claim
41 words
An improved silicon carbide and oxide structure comprising: a silicon carbide substrate; and an oxide layer on the silicon carbide substrate, said oxide layer having an interface state density less than 1.6×10 11 per square centimeter per electron-volt (cm -2 /eV).
Claim 24
Dependent Claim
41 words
An improved silicon carbide and oxide structure comprising: a silicon carbide substrate; and an oxide layer on the silicon carbide substrate, said oxide layer having an interface state density less than 1.6×10 11 per square centimeter per electron-volt (cm -2 /eV).
Claim 25
Dependent Claim
23 words
A silicon carbide and oxide structure according to claim 21 wherein said interface state density is less than 1.5×10 11 cm -2 /eV.
Claim 26
Dependent Claim
23 words
A silicon carbide and oxide structure according to claim 21 wherein said interface state density is less than 1.1×10 11 cm -2 /eV.
Claim 27
Dependent Claim
34 words
A silicon carbide and oxide structure according to claim 21 wherein said silicon carbide layer is a single crystal with a polytype selected from the group consisting of 2H, 3C, 4H, 6H, and 15R.
Claim 28
Dependent Claim
19 words
A silicon carbide and oxide structure according to claim 21 wherein said silicon carbide layer is an epitaxial layer.
Claim 29
Dependent Claim
18 words
A silicon carbide and oxide structure according to claim 21 wherein said silicon carbide layer is a substrate.
Claim 30
Dependent Claim
18 words
A silicon carbide and oxide structure according to claim 21 wherein said oxide layer is predominantly silicon dioxide.
Claim 31
Dependent Claim
35 words
An improved silicon carbide and oxide structure comprising: a silicon carbide substrate; and an oxide layer on the silicon carbide substrate, said oxide layer having an oxide charge less than 2.5×10 12 cm -2 .
Claim 32
Dependent Claim
35 words
An improved silicon carbide and oxide structure comprising: a silicon carbide substrate; and an oxide layer on the silicon carbide substrate, said oxide layer having an oxide charge less than 2.5×10 12 cm -2 .
Claim 33
Dependent Claim
22 words
A silicon carbide and oxide structure according to claim 28 wherein said oxide charge is less than 1.5×10 12 cm -2 .
Claim 34
Dependent Claim
22 words
A silicon carbide and oxide structure according to claim 28 wherein said oxide charge is less than 1.1×10 12 cm -2 .
Claim 35
Dependent Claim
33 words
A silicon carbide and oxide structure according to claim 28 wherein said silicon carbide layer is a single crystal with a polytype selected from the group consisting of 3C, 4H, 6H, and 15R.
Claim 36
Dependent Claim
19 words
A silicon carbide and oxide structure according to claim 28 wherein said silicon carbide layer is an epitaxial layer.
Claim 37
Dependent Claim
18 words
A silicon carbide and oxide structure according to claim 28 wherein said silicon carbide layer is a substrate.
Claim 38
Dependent Claim
18 words
A silicon carbide and oxide structure according to claim 28 wherein said oxide layer is predominantly silicon dioxide.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2002-10-25 | 2003-04-26 | 2003-10-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2006-10-25 | 2007-04-26 | 2007-10-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2010-10-25 | 2011-04-26 | 2011-10-26 | $7700.00 | Window Closed / Lapsed |