Assignee: Dow Silicones Corp
•
Filing: 1997-11-13
•
Granted: 1999-08-17
•
Expires: 2017-11-13
Abstract
Abstract The viscosity of a solvent is modified by thickening the solvent with a silicone latex. A silicone latex having a plurality of crosslinked polysiloxane particles is first prepared by mixing the siloxane polymer, a surfactant, and water; emulsifying the mixture to a gel phase; diluting the emulsion with water; adding a cure package (i.e., a catalyst, a crosslinker, or both, or a self catalytic crosslinker); and then without removing the water from the latex and after the particles of siloxane polymer in the latex have been cured, mixing the latex and solvent to thicken the solvent, forming viscous liquids, gels, and pastes. Water in the latex thickened solvent composition can be stabilized by adding a silicone polyether during mixing of the latex and the solvent. These stabilized latex thickened solvent compositions have beneficial properties such as clarity, shelf stability, and ease of preparation; and therefore have wide areas of application, especially as additives in antiperspirants, deodorants, and other personal care applications.
Inventors
- 👤 James Anderson Beck
- 👤 Vicky Sue Cobb
- 👤 Cassie Emelia Cuthbert
- 👤 Eric Jude Joffre
- 👤 Virginia Kay O'Neil
- 👤 Burt Michael Wrolson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 22:25
CPC Classifications
A; A61; A61K; A61K8/00; A61K8/18; A61K8/72; A61K8/84; A61K8/89; A61K8/891; A61K8/894; A61K8/02; A61K8/04; A61K8/042; A61K8/895; A61Q; A61Q19/00; C; C08; C08J; C08J3/00; C08J3/02; C08J3/03; C08J3/09; C08J2383/00; C08J2383/04
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
309 words
A method of modifying the viscosity of a solvent, the method comprising (I) adding a silicone latex containing water and a plurality of cured crosslinked polysiloxane particles to a solvent after the particles have been cured and without removing the water from the latex; (II) mixing the latex containing the water and the cured particles, and the solvent together to thicken the solvent; and (III) stabilizing water in the latex thickened solvent by adding a silicone polyether during step (II); the latex prepared by a method comprising: (A) mixing (i) 100 weight parts of a siloxane polymer having a viscosity of greater than 5,000 mPa.s but less than 500,000 mPa.s at 25° C., (ii) 0.5-10 weight parts of a surfactant, and (iii) 0.5-25 weight parts of water, (B) emulsifying the mixture into a gel phase having a siloxane polymer content of at least 80% by weight; (C) diluting the emulsion with further water to a siloxane polymer content of at least 75% by weight, (D) adding 0.00001-20 weight parts catalyst either before or after the emulsification, or before or after the dilution; (E) adding 0.1-20 weight parts crosslinker either before or after the emulsification, or before or after the dilution; (F) or in place of adding (D) and (E), adding 1-5 weight parts self catalytic crosslinker either before or after the emulsification, or before or after the dilution; the silicone polyether having the formula MD 10-1 ,000 D' 1-100 M where M represents monofunctional unit R 3 SiO 1/2 , D represents difunctional unit R 2 SiO 2/2 , and D' represents difunctional unit RR'SiO 2/2 , in which R is an alkyl group containing 1-6 carbon atoms or an aryl group, and R' is oxyalkylene unit EO 10-100 PO 0-100 in which EO represents --(CH 2 CH 2 O)-- and PO represents --(CH 2 CH(CH 3 )O)--, respectively.
Claim 2
Independent Claim
309 words
A method of modifying the viscosity of a solvent, the method comprising (I) adding a silicone latex containing water and a plurality of cured crosslinked polysiloxane particles to a solvent after the particles have been cured and without removing the water from the latex; (II) mixing the latex containing the water and the cured particles, and the solvent together to thicken the solvent; and (III) stabilizing water in the latex thickened solvent by adding a silicone polyether during step (II); the latex prepared by a method comprising: (A) mixing (i) 100 weight parts of a siloxane polymer having a viscosity of greater than 5,000 mPa.s but less than 500,000 mPa.s at 25° C., (ii) 0.5-10 weight parts of a surfactant, and (iii) 0.5-25 weight parts of water, (B) emulsifying the mixture into a gel phase having a siloxane polymer content of at least 80% by weight; (C) diluting the emulsion with further water to a siloxane polymer content of at least 75% by weight, (D) adding 0.00001-20 weight parts catalyst either before or after the emulsification, or before or after the dilution; (E) adding 0.1-20 weight parts crosslinker either before or after the emulsification, or before or after the dilution; (F) or in place of adding (D) and (E), adding 1-5 weight parts self catalytic crosslinker either before or after the emulsification, or before or after the dilution; the silicone polyether having the formula MD 10-1 ,000 D' 1-100 M where M represents monofunctional unit R 3 SiO 1/2 , D represents difunctional unit R 2 SiO 2/2 , and D' represents difunctional unit RR'SiO 2/2 , in which R is an alkyl group containing 1-6 carbon atoms or an aryl group, and R' is oxyalkylene unit EO 10-100 PO 0-100 in which EO represents --(CH 2 CH 2 O)-- and PO represents --(CH 2 CH(CH 3 )O)--, respectively.
Claim 3
Dependent Claim
24 words
A method according to claim 1 in which the latex has a solids content of siloxane polymer of at least 90 percent by weight.
Claim 4
Dependent Claim
125 words
A method according to claim 1 in which the siloxane polymer has the formula X 3-n R n --YO--(R 1 2 SiO) z --Y--R n X 3-n where n is 0, 1, 2 or 3; z is an integer from 500-5,000; X is hydrogen, a vinyl group, or a hydroxyl group Y is a silicon atom, the group .tbd.Si--(CH 2 ) m --SiR 1 2 --, or the group .tbd.Si--(CH 2 ) m --SiR 1 2 OSiR 1 2 (CH 2 )m--SiR 1 2 --, where m is 1-8; R is selected from the group consisting of aliphatic alkyl, aminoalkyl, polyaminoalkyl, epoxyalkyl, alkenyl, and an aromatic group; and R 1 is selected from the group consisting of X, aliphatic alkyl, alkenyl, and an aromatic group.
Claim 5
Dependent Claim
70 words
A method according to claim 3 in which the siloxane polymer has at least two vinyl groups per molecule bonded to a silicon atom, the crosslinker having an average of at least two silicon-bonded hydrogen atoms and being a silicon hydride crosslinker present in an amount sufficient to provide at least one hydrogen atom for each vinyl group in the siloxane polymer, and the catalyst is a noble metal catalyst.
Claim 6
Dependent Claim
31 words
A method according to claim 1 in which the self catalyzing crosslinker has at least one catalytic leaving group selected from the group consisting of acetoxy, amide, acetamide, aminoxy, and oxime.
Claim 7
Dependent Claim
46 words
A method according to claim 5 in which the self catalyzing crosslinker is a compound of the formula ##STR3## where R is the same or a different alkyl group of 1-8 carbon atoms; a is zero or a positive integer, and b is greater than two.
Claim 8
Dependent Claim
28 words
A method according to claim 1 in which the surfactant is selected from the group consisting of nonionic surfactants, cationic surfactants, anionic surfactants, amphoteric surfactants, and mixtures thereof.
Claim 9
Dependent Claim
43 words
A method according to claim 1 in which the solvent is selected from the group consisting of aromatic hydrocarbons, aliphatic hydrocarbons, alcohols, aldehydes, ketones, amines, esters, ethers, glycols, glycol ethers, alkyl halides, aromatic halides, petroleum hydrocarbons, lubricating oils, fatty oils, and mixtures thereof.
Claim 10
Dependent Claim
14 words
A latex thickened solvent composition prepared according to the method described in claim 1.
Claim 11
Dependent Claim
80 words
A personal care product containing the latex thickened solvent composition of claim 9 selected from the group consisting of antiperspirants, deodorants, skin creams, skin care lotions, moisturizers, acne removers, wrinkle removers, facial cleansers, bath oils, perfumes, colognes, sachets, sunscreens, pre-shave lotions, after-shave lotions, shaving soaps, shaving lathers, hair shampoos, hair conditioners, hair sprays, mousses, permanents, depilatories, cuticle coats, make-ups, color cosmetics, foundations, blushes, lipsticks, eyeliners, mascaras, oil removers, cosmetic removers, delivery systems for oil and water soluble substances, and powders.
Claim 12
Dependent Claim
25 words
A method of treating hair or skin comprising applying to the hair or skin a composition containing the latex thickened solvent composition of claim 9.
References Cited (Backward Citations)
US5064894A
Cited
EP0739928A2
Cited
US5674937A
Cited
US5705562A
Cited
US5707613A
Cited
US5665804A
Cited
US5623017A
Cited
US5811487A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2002-08-16 | 2003-02-15 | 2003-08-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2006-08-16 | 2007-02-15 | 2007-08-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2010-08-16 | 2011-02-15 | 2011-08-17 | $7700.00 | Window Closed / Lapsed |