Method for making dynamic random access memory cells using a novel stacked capacitor process
Assignee: Taiwan Semiconductor Manufacturing Co TSMC Ltd
•
Filing: 1997-10-23
•
Granted: 1999-07-20
•
Expires: 2017-10-23
Abstract
Abstract A method is described for making an array of DRAM cells having increased capacitance. The method forms a planar insulating layer over FETs in an array of cells. Node contact openings are etched to each FET. A thick first polysilicon layer is deposited to fill the node contact openings and provide a planar polysilicon surface on the insulating layer. A thin silicon nitride layer is deposited on the first polysilicon layer, and both are patterned leaving portions having essentially vertical sidewalls over the contact openings. Polysilicon oxide sidewalls are formed on the first polysilicon layer by thermal oxidation. The nitride layer prevents oxidation of the top of the polysilicon. The nitride is removed and the polysilicon is selectively etched (recessed) leaving polysilicon oxide sidewalls. A second polysilicon layer is deposited over the oxide sidewalls and etched back to form inner and outer sidewall spacers. The oxide sidewalls and portions of the planar insulating layer are etched, lifting off the outer polysilicon sidewall spacers to provide a capacitor bottom electrode having vertical sidewalls. A thin capacitor dielectric layer is formed on the bottom electrodes and a third polysilicon layer is deposited and patterned to form the top electrodes and to complete the array of stacked capacitors on the DRAM device.
Inventors
- 👤 Horng-Huei Tseng
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 03:31
CPC Classifications
H; H10; H10B; H10B12/00; H10B12/01; H10B12/02; H10B12/03; H10B12/033; H10B12/30; H10B12/31; H10B12/318
Claims Analysis
Total Claims: 25
Claim 1
Independent Claim
332 words
A method for fabricating stacked capacitors having a high capacitance comprising the steps of: forming field oxide areas on a semiconductor substrate while leaving device areas for fabrication of semiconductor devices; forming device structures in and on said device areas of said semiconductor substrate; depositing a first insulating layer over said device areas and said field oxide areas; depositing a second insulating layer on said first insulating layer; planarizing said second insulating layer; forming contact openings in said first and second insulating layers to said device areas where electrical contacts are desired for said stacked capacitors; and forming said stacked capacitors by, depositing a first polysilicon layer over said device areas and said field oxide areas, and said first polysilicon layer contacting said device areas in said contact openings; forming a third insulating layer on said first polysilicon layer; patterning by anisotropic etching said third insulating layer and said first polysilicon layer to said second insulating layer leaving portions of said third insulating layer and said first polysilicon layer over said contact openings; forming polysilicon oxide sidewalls by thermal oxidation on sidewalls of said portions of said first polysilicon layer while said third insulating layer prevents oxidation of the top surface of said portions of said first polysilicon layer; etching selectively said third insulating layer and said portions of said first polysilicon layer leaving said polysilicon oxide sidewalls and recessing said portions of said first polysilicon layer over said contact openings; depositing a second polysilicon layer; anisotropically etching back said second polysilicon layer to form outer polysilicon spacers and inner polysilicon spacers on said polysilicon oxide sidewalls; isotropically etching said polysilicon oxide sidewalls and concurrently etching portions of said second insulating layer to lift off said outer polysilicon spacers and to form bottom electrodes having vertical sidewalls formed from said inner polysilicon spacers for said stacked capacitors; forming a capacitor dielectric layer on said bottom electrodes; depositing and patterning a third polysilicon layer to form top electrodes to complete said stacked capacitors.
Claim 2
Independent Claim
332 words
A method for fabricating stacked capacitors having a high capacitance comprising the steps of: forming field oxide areas on a semiconductor substrate while leaving device areas for fabrication of semiconductor devices; forming device structures in and on said device areas of said semiconductor substrate; depositing a first insulating layer over said device areas and said field oxide areas; depositing a second insulating layer on said first insulating layer; planarizing said second insulating layer; forming contact openings in said first and second insulating layers to said device areas where electrical contacts are desired for said stacked capacitors; and forming said stacked capacitors by, depositing a first polysilicon layer over said device areas and said field oxide areas, and said first polysilicon layer contacting said device areas in said contact openings; forming a third insulating layer on said first polysilicon layer; patterning by anisotropic etching said third insulating layer and said first polysilicon layer to said second insulating layer leaving portions of said third insulating layer and said first polysilicon layer over said contact openings; forming polysilicon oxide sidewalls by thermal oxidation on sidewalls of said portions of said first polysilicon layer while said third insulating layer prevents oxidation of the top surface of said portions of said first polysilicon layer; etching selectively said third insulating layer and said portions of said first polysilicon layer leaving said polysilicon oxide sidewalls and recessing said portions of said first polysilicon layer over said contact openings; depositing a second polysilicon layer; anisotropically etching back said second polysilicon layer to form outer polysilicon spacers and inner polysilicon spacers on said polysilicon oxide sidewalls; isotropically etching said polysilicon oxide sidewalls and concurrently etching portions of said second insulating layer to lift off said outer polysilicon spacers and to form bottom electrodes having vertical sidewalls formed from said inner polysilicon spacers for said stacked capacitors; forming a capacitor dielectric layer on said bottom electrodes; depositing and patterning a third polysilicon layer to form top electrodes to complete said stacked capacitors.
Claim 3
Dependent Claim
34 words
The method of claim 1, wherein said first insulating layer is composed of a silicon oxide layer and an upper silicon nitride layer having a total thickness of between about 1000 and 2000 Angstroms.
Claim 4
Dependent Claim
30 words
The method of claim 1, wherein said second insulating layer is a borophosphosilicate glass (BPSG) deposited by chemical vapor deposition and the thickness is between about 2000 and 8000 Angstroms.
Claim 5
Dependent Claim
22 words
The method of claim 1, wherein said first polysilicon layer is deposited to a thickness of between about 5000 and 10000 Angstroms.
Claim 6
Dependent Claim
24 words
The method of claim 1, where said third insulating layer is silicon nitride deposited to a thickness of between about 200 and 1000 Angstroms.
Claim 7
Dependent Claim
22 words
The method of claim 1, wherein said polysilicon oxide sidewalls are grown to a thickness of between about 100 and 1000 Angstroms.
Claim 8
Dependent Claim
18 words
The method of claim 1, wherein said second polysilicon layer is between about 500 and 2000 Angstroms thick.
Claim 9
Dependent Claim
28 words
The method of claim 1, wherein said capacitor dielectric layer is composed of a silicon oxide/silicon nitride/silicon oxide having a thickness of between about 10 and 1000 Angstroms.
Claim 10
Dependent Claim
20 words
The method of claim 1, wherein said third polysilicon layer has a thickness of between about 1000 and 2000 Angstroms.
Claim 11
Dependent Claim
21 words
The method of claim 1, wherein said first, second, and third polysilicon layers are conductively doped with an N type dopant.
Claim 12
Dependent Claim
17 words
The method of claim 1, wherein said isotropic etching is carried out in a hydrofluoric acid solution.
Claim 13
Independent Claim
371 words
A method for fabricating dynamic random access memory (DRAM) devices having stacked capacitors with high capacitance comprising the steps of: forming field oxide areas on a semiconductor substrate while leaving device areas for fabrication of field effect transistors; forming a gate oxide layer on said device areas; depositing and patterning an electrically conducting layer to form gate electrodes on said device areas; forming source/drain areas adjacent to said gate electrodes to form said field effect transistors; depositing a first insulating layer over said device areas and said field oxide areas; depositing a second insulating layer on said first insulating layer; planarizing said second insulating layer; forming contact openings in said first and second insulating layers to said device areas where electrical contacts are desired for said stacked capacitors; and forming said stacked capacitors by, depositing a first polysilicon layer over said device areas and said field oxide areas, and said first polysilicon layer contacting said device areas in said contact openings; forming a third insulating layer on said first polysilicon layer; patterning by anisotropic etching said third insulating layer and said first polysilicon layer to said second insulating layer leaving portions of said third insulating layer and said first polysilicon layer over said contact openings; forming polysilicon oxide sidewalls by thermal oxidation on sidewalls of said portions of said first polysilicon layer while said third insulating layer prevents oxidation of the top surface of said portions of said first polysilicon layer; etching selectively said third insulating layer and said portions of said first polysilicon layer leaving said polysilicon oxide sidewalls and recessing said portions of said first polysilicon layer over said contact openings; depositing a second polysilicon layer; anisotropically etching back said second polysilicon layer to form outer polysilicon spacers and inner polysilicon spacers on said polysilicon oxide sidewalls; isotropically etching said polysilicon oxide sidewalls and concurrently etching portions of said second insulating layer to lift off said outer polysilicon spacers and to form bottom electrodes having vertical sidewalls formed from said inner polysilicon spacers for said stacked capacitors; forming a capacitor dielectric layer on said bottom electrodes; depositing and patterning a third polysilicon layer to form top electrodes to complete said dynamic random access memory devices having said stacked capacitors.
Claim 14
Independent Claim
371 words
A method for fabricating dynamic random access memory (DRAM) devices having stacked capacitors with high capacitance comprising the steps of: forming field oxide areas on a semiconductor substrate while leaving device areas for fabrication of field effect transistors; forming a gate oxide layer on said device areas; depositing and patterning an electrically conducting layer to form gate electrodes on said device areas; forming source/drain areas adjacent to said gate electrodes to form said field effect transistors; depositing a first insulating layer over said device areas and said field oxide areas; depositing a second insulating layer on said first insulating layer; planarizing said second insulating layer; forming contact openings in said first and second insulating layers to said device areas where electrical contacts are desired for said stacked capacitors; and forming said stacked capacitors by, depositing a first polysilicon layer over said device areas and said field oxide areas, and said first polysilicon layer contacting said device areas in said contact openings; forming a third insulating layer on said first polysilicon layer; patterning by anisotropic etching said third insulating layer and said first polysilicon layer to said second insulating layer leaving portions of said third insulating layer and said first polysilicon layer over said contact openings; forming polysilicon oxide sidewalls by thermal oxidation on sidewalls of said portions of said first polysilicon layer while said third insulating layer prevents oxidation of the top surface of said portions of said first polysilicon layer; etching selectively said third insulating layer and said portions of said first polysilicon layer leaving said polysilicon oxide sidewalls and recessing said portions of said first polysilicon layer over said contact openings; depositing a second polysilicon layer; anisotropically etching back said second polysilicon layer to form outer polysilicon spacers and inner polysilicon spacers on said polysilicon oxide sidewalls; isotropically etching said polysilicon oxide sidewalls and concurrently etching portions of said second insulating layer to lift off said outer polysilicon spacers and to form bottom electrodes having vertical sidewalls formed from said inner polysilicon spacers for said stacked capacitors; forming a capacitor dielectric layer on said bottom electrodes; depositing and patterning a third polysilicon layer to form top electrodes to complete said dynamic random access memory devices having said stacked capacitors.
Claim 15
Dependent Claim
34 words
The method of claim 12, wherein said first insulating layer is composed of a silicon oxide layer and an upper silicon nitride layer having a total thickness of between about 1000 and 2000 Angstroms.
Claim 16
Dependent Claim
30 words
The method of claim 12, wherein said second insulating layer is a borophosphosilicate glass (BPSG) deposited by chemical vapor deposition and the thickness is between about 2000 and 8000 Angstroms.
Claim 17
Dependent Claim
22 words
The method of claim 12, wherein said first polysilicon layer is deposited to a thickness of between about 5000 and 10000 Angstroms.
Claim 18
Dependent Claim
24 words
The method of claim 12, where said third insulating layer is silicon nitride deposited to a thickness of between about 200 and 1000 Angstroms.
Claim 19
Dependent Claim
22 words
The method of claim 12, wherein said polysilicon oxide sidewalls are grown to a thickness of between about 100 and 1000 Angstroms.
Claim 20
Dependent Claim
18 words
The method of claim 12, wherein said second polysilicon layer is between about 500 and 2000 Angstroms thick.
Claim 21
Dependent Claim
28 words
The method of claim 12, wherein said capacitor dielectric layer is composed of a silicon oxide/silicon nitride/silicon oxide having a thickness of between about 10 and 1000 Angstroms.
Claim 22
Dependent Claim
20 words
The method of claim 12, wherein said third polysilicon layer has a thickness of between about 1000 and 2000 Angstroms.
Claim 23
Dependent Claim
21 words
The method of claim 12, wherein said first, second, and third polysilicon layers are conductively doped with an N type dopant.
Claim 24
Dependent Claim
17 words
The method of claim 12, wherein said isotropic etching is carried out in a hydrofluoric acid solution.
Claim 25
Dependent Claim
37 words
The method of claim 12, wherein said electrically conducting layer is a polycide composed of an N doped polysilicon layer and a refractory metal silicide layer having a total thickness of between about 1500 and 3500 Angstroms.
References Cited (Backward Citations)
US5399518A
Cited
US5468670A
Cited
US5545582A
Cited
US5759888A
Cited
US5604146A
Cited
US5792688A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2002-07-19 | 2003-01-18 | 2003-07-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2006-07-19 | 2007-01-18 | 2007-07-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2010-07-19 | 2011-01-18 | 2011-07-20 | $7700.00 | Window Closed / Lapsed |