Method of forming shallow diffusion layers in a semiconductor substrate in the vicinity of a gate electrode
Assignee: Renesas Electronics Corp
•
Filing: 1996-11-12
•
Granted: 1999-06-22
•
Expires: 2016-11-12
Abstract
Abstract A method of forming shallow diffusion layers in a semiconductor substrate is provided wherein the shallow diffusion layers are positioned in the vicinity of edge portions of a gate electrode and laterally extend from source/drain diffusion layers having a bottom level deeper than the shallow diffusion layers. The above method comprises the following steps. Crystal defects are selectively formed at least in predetermined shallow regions positioned in a surface region of the semiconductor substrate and in the vicinity of the edge portions of the gate electrode. The predetermined shallow regions are laterally in contact with impurity-introduced deep regions having been formed. The predetermined shallow regions have a bottom level shallower than the impurity-introduced deep regions. Subsequently, the semiconductor substrate is subjected to a heat treatment not only to cause a vertical diffusion of an impurity from the impurity-introduced regions so as to selectively form the source/drain diffusion layers but also to cause a rate-increased lateral diffusion of the impurity from the impurity-introduced regions through the predetermined shallow regions so as to selectively form the shallow diffusion layers.
Inventors
- 👤 Akira Mineji
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 08:56
CPC Classifications
H; H10; H10P; H10P30/00; H10P30/20; H10P30/202; H10P30/204; H10D; H10D30/00; H10D30/01; H10D30/021; H10D30/0223; H10D30/0227; H10D64/00; H10D64/20; H10D64/23; H10D64/251; H10D64/258; H10D64/259; H10P30/208; H10P30/225; H10P32/00; H10P32/10; H10P32/12; H10P32/1204; H10P32/14; H10P32/1408; H10P32/1414; H10P32/17; H10P32/171
Claims Analysis
Total Claims: 73
Claim 1
Independent Claim
199 words
A method of forming shallow diffusion layers in a semiconductor substrate, said shallow diffusion layers being positioned in the vicinity of edge portions of a gate electrode, said shallow diffusion layers laterally extending from source/drain diffusion layers having a bottom level deeper than said shallow diffusion layers, and said method comprising the steps of: selectively forming crystal defects, by ion-implantation without amorphizing the semiconductor substrate at a dose rate from 1×10 14 cm -2 to about 5×10 14 cm -2 , at least in predetermined shallow regions positioned in a surface region of said semiconductor substrate and in the vicinity of said edge portions of said gate electrode, said predetermined shallow regions being laterally in contact with impurity-introduced deep regions having been formed, and said predetermined shallow regions having a bottom level shallower than said impurity-introduced deep regions; and subjecting said semiconductor substrate to a heat treatment not only to cause a vertical diffusion of an impurity from said impurity-introduced regions so as to selectively form said source/drain diffusion layers but also to cause a rate-increased lateral diffusion of said impurity from said impurity-introduced regions through said predetermined shallow regions so as to selectively form said shallow diffusion layers.
Claim 2
Independent Claim
199 words
A method of forming shallow diffusion layers in a semiconductor substrate, said shallow diffusion layers being positioned in the vicinity of edge portions of a gate electrode, said shallow diffusion layers laterally extending from source/drain diffusion layers having a bottom level deeper than said shallow diffusion layers, and said method comprising the steps of: selectively forming crystal defects, by ion-implantation without amorphizing the semiconductor substrate at a dose rate from 1×10 14 cm -2 to about 5×10 14 cm -2 , at least in predetermined shallow regions positioned in a surface region of said semiconductor substrate and in the vicinity of said edge portions of said gate electrode, said predetermined shallow regions being laterally in contact with impurity-introduced deep regions having been formed, and said predetermined shallow regions having a bottom level shallower than said impurity-introduced deep regions; and subjecting said semiconductor substrate to a heat treatment not only to cause a vertical diffusion of an impurity from said impurity-introduced regions so as to selectively form said source/drain diffusion layers but also to cause a rate-increased lateral diffusion of said impurity from said impurity-introduced regions through said predetermined shallow regions so as to selectively form said shallow diffusion layers.
Claim 3
Dependent Claim
21 words
The method as claimed in claim 1, wherein said crystal defects are formed by subjecting said substrate to a plasma atmosphere.
Claim 4
Dependent Claim
30 words
The method as claimed in claim 1, wherein said semiconductor substrate is a silicon substrate and said crystal defects are formed by an ion-implantation of silicon into said silicon substrate.
Claim 5
Dependent Claim
25 words
The method as claimed in claim 3, wherein said ion-implantation of silicon is carried out at a dose of about 1×10 14 cm -2 .
Claim 6
Dependent Claim
37 words
The method as claimed in claim 1, wherein said semiconductor substrate is a silicon substrate and said crystal defects are formed by subjecting said surface of said silicon substrate to an ion-implantation to cause interstitial silicon atoms.
Claim 7
Dependent Claim
31 words
The method as claimed in claim 1, wherein said ion-implantation is with an ion selected from the group consisting of N, F, Sb, In, P, As, Ga, He, Ne and Ar.
Claim 8
Dependent Claim
23 words
The method as claimed in claim 1, wherein said heat treatment is carried out at a temperature in the range of 700-900° C.
Claim 9
Dependent Claim
27 words
The method as claimed in claim 1, wherein said heat treatment is a rapid thermal anneal carried out at a temperature in the range of 900-1150° C.
Claim 10
Dependent Claim
21 words
The method as claimed in claim 1, wherein said shallow diffusion layers have a depth in the range of 10-70 nanometers.
Claim 11
Independent Claim
197 words
A method of forming shallow diffusion layers in a semiconductor substrate, said shallow diffusion layers being positioned in the vicinity of edge portions of a gate electrode, said shallow diffusion layers laterally extending from source/drain diffusion layers having a bottom level deeper than said shallow diffusion layers, and said method comprising the steps of: selectively forming crystal defects, by ion-implantation without amorphizing the semiconductor substrate at a dose rate from 1×10 14 cm -2 to about 5×10 14 cm -2 , at least in predetermined shallow regions positioned in a surface region of said semiconductor substrate and in the vicinity of said edge portions of said gate electrode; selectively forming impurity-introduced deep regions laterally in contact with said predetermined shallow regions, and said impurity-introduced deep regions having a bottom level deeper than said predetermined shallow regions; and subjecting said semiconductor substrate to a heat treatment not only to cause a vertical diffusion of an impurity from said impurity-introduced regions so as to selectively form said source/drain diffusion layers but also to cause a rate-increased lateral diffusion of said impurity from said impurity-introduced regions through said predetermined shallow regions so as to selectively form said shallow diffusion layers.
Claim 12
Independent Claim
197 words
A method of forming shallow diffusion layers in a semiconductor substrate, said shallow diffusion layers being positioned in the vicinity of edge portions of a gate electrode, said shallow diffusion layers laterally extending from source/drain diffusion layers having a bottom level deeper than said shallow diffusion layers, and said method comprising the steps of: selectively forming crystal defects, by ion-implantation without amorphizing the semiconductor substrate at a dose rate from 1×10 14 cm -2 to about 5×10 14 cm -2 , at least in predetermined shallow regions positioned in a surface region of said semiconductor substrate and in the vicinity of said edge portions of said gate electrode; selectively forming impurity-introduced deep regions laterally in contact with said predetermined shallow regions, and said impurity-introduced deep regions having a bottom level deeper than said predetermined shallow regions; and subjecting said semiconductor substrate to a heat treatment not only to cause a vertical diffusion of an impurity from said impurity-introduced regions so as to selectively form said source/drain diffusion layers but also to cause a rate-increased lateral diffusion of said impurity from said impurity-introduced regions through said predetermined shallow regions so as to selectively form said shallow diffusion layers.
Claim 13
Dependent Claim
21 words
The method as claimed in claim 10, wherein said crystal defects are formed by subjecting said substrate to a plasma atmosphere.
Claim 14
Dependent Claim
29 words
The method as claimed in claim 10, wherein said semiconductor substrate is a silicon substrate and said crystal defects are formed by ion-implantation of silicon into said silicon substrate.
Claim 15
Dependent Claim
32 words
The method as claimed in claim 12, wherein said ion-implantation of silicon is carried out at a dose lower than a critical dose over which crystal silicon is made into amorphous silicon.
Claim 16
Dependent Claim
25 words
The method as claimed in claim 12, wherein said ion-implantation of silicon is carried out at a dose of about 1×10 14 cm -2 .
Claim 17
Dependent Claim
31 words
The method as claimed in claim 10, wherein said ion-implantation is with an ion selected from the group consisting of N, F, Sb, In, P, As, Ga, He, Ne and Ar.
Claim 18
Dependent Claim
23 words
The method as claimed in claim 10, wherein said heat treatment is carried out at a temperature in the range of 700-900° C.
Claim 19
Dependent Claim
27 words
The method as claimed in claim 10, wherein said heat treatment is a rapid thermal anneal carried out at a temperature in the range of 900-1150° C.
Claim 20
Dependent Claim
21 words
The method as claimed in claim 10, wherein said shallow diffusion layers have a depth in the range of 10-70 nanometers.
Claim 21
Independent Claim
223 words
A method of forming a MOS field effect transistor comprising the steps of: selectively forming a gate electrode on a gate insulation film which is formed on a surface of a silicon substrate; selectively forming crystal defects, by ion-implantation without amorphizing the semiconductor substrate at a dose rate from 1×10 14 cm -2 to about 5×10 4 cm -2 , in predetermined shallow regions positioned in a surface region of said semiconductor substrate by using said gate electrode as a mask; selectively forming side wall oxide films at opposite sides of said gate electrode; selectively forming impurity-introduced deep regions having a bottom level deeper than said predetermined shallow regions by an ion implantation using said gate electrode and said side wall oxide films as masks; and subjecting said semiconductor substrate to a heat treatment not only to cause a vertical diffusion of an impurity from said impurity-introduced regions so as to selectively form source/drain diffusion layers but also to cause a rate-increased lateral diffusion of said impurity from said impurity-introduced regions through said predetermined shallow regions so as to selectively form shallow diffusion layers in said semiconductor substrate under said side wall oxide films, so that said shallow diffusion layers laterally extend from said source/drain diffusion layers and that said shallow diffusion layers have a bottom level shallower than said source/drain diffusion layers.
Claim 22
Independent Claim
223 words
A method of forming a MOS field effect transistor comprising the steps of: selectively forming a gate electrode on a gate insulation film which is formed on a surface of a silicon substrate; selectively forming crystal defects, by ion-implantation without amorphizing the semiconductor substrate at a dose rate from 1×10 14 cm -2 to about 5×10 4 cm -2 , in predetermined shallow regions positioned in a surface region of said semiconductor substrate by using said gate electrode as a mask; selectively forming side wall oxide films at opposite sides of said gate electrode; selectively forming impurity-introduced deep regions having a bottom level deeper than said predetermined shallow regions by an ion implantation using said gate electrode and said side wall oxide films as masks; and subjecting said semiconductor substrate to a heat treatment not only to cause a vertical diffusion of an impurity from said impurity-introduced regions so as to selectively form source/drain diffusion layers but also to cause a rate-increased lateral diffusion of said impurity from said impurity-introduced regions through said predetermined shallow regions so as to selectively form shallow diffusion layers in said semiconductor substrate under said side wall oxide films, so that said shallow diffusion layers laterally extend from said source/drain diffusion layers and that said shallow diffusion layers have a bottom level shallower than said source/drain diffusion layers.
Claim 23
Dependent Claim
29 words
The method as claimed in claim 19, wherein said side wall oxide films are formed at a temperature below a critical temperature over which said crystal defects are recovered.
Claim 24
Dependent Claim
24 words
The method as claimed in claim 20, wherein said side wall oxide films are formed at a temperature in the range of 200-450° C.
Claim 25
Dependent Claim
21 words
The method as claimed in claim 19, wherein said crystal defects are formed by ion-implantation of silicon into said silicon substrate.
Claim 26
Dependent Claim
25 words
The method as claimed in claim 22, wherein said ion-implantation of silicon is carried out at a dose of about 1×10 14 cm -2 .
Claim 27
Dependent Claim
29 words
The method as claimed in claim 19, wherein said crystal defects are formed by subjecting said surface of said silicon substrate to an ion-implantation to cause interstitial silicon atoms.
Claim 28
Dependent Claim
31 words
The method as claimed in claim 19, wherein said ion-implantation is with an ion selected from the group consisting of N, F, Sb, In, P, As, Ga, He, Ne and Ar.
Claim 29
Dependent Claim
23 words
The method as claimed in claim 19, wherein said heat treatment is carried out at a temperature in the range of 700-900° C.
Claim 30
Dependent Claim
27 words
The method as claimed in claim 19, wherein said heat treatment is a rapid thermal anneal carried out at a temperature in the range of 900-1150° C.
Claim 31
Dependent Claim
21 words
The method as claimed in claim 19, wherein said shallow diffusion layers have a depth in the range of 10-70 nanometers.
Claim 32
Independent Claim
232 words
A method of forming a MOS field effect transistor comprising the steps of: selectively forming a gate electrode on a gate insulation film which is formed on a surface of a silicon substrate; selectively forming side wall oxide films at opposite sides of said gate electrode; selectively forming impurity-introduced deep regions by an ion implantation using gate electrode and said side wall oxide films as masks; removing said side wall oxide films; selectively forming crystal defects, by ion-implantation without amorphizing the semiconductor substrate at a dose rate from 1×10 14 cm -2 to about 5×10 14 cm -2 , in predetermined shallow regions positioned in a surface region of said semiconductor substrate by using said gate electrode as a mask, said predetermined shallow regions having a bottom level shallower than said impurity-introduced deep regions; and subjecting said semiconductor substrate to a heat treatment not only to cause a vertical diffusion of an impurity from said impurity-introduced regions so as to selectively form source/drain diffusion layers but also to cause a rate-increased lateral diffusion of said impurity from said impurity-introduced regions through said predetermined shallow regions so as to selectively form shallow diffusion layers in said semiconductor substrate under said side wall oxide films, so that said shallow diffusion layers laterally extend from said source/drain diffusion layers and that said shallow diffusion layers have a bottom level shallower than said source/drain diffusion layers.
Claim 33
Independent Claim
232 words
A method of forming a MOS field effect transistor comprising the steps of: selectively forming a gate electrode on a gate insulation film which is formed on a surface of a silicon substrate; selectively forming side wall oxide films at opposite sides of said gate electrode; selectively forming impurity-introduced deep regions by an ion implantation using gate electrode and said side wall oxide films as masks; removing said side wall oxide films; selectively forming crystal defects, by ion-implantation without amorphizing the semiconductor substrate at a dose rate from 1×10 14 cm -2 to about 5×10 14 cm -2 , in predetermined shallow regions positioned in a surface region of said semiconductor substrate by using said gate electrode as a mask, said predetermined shallow regions having a bottom level shallower than said impurity-introduced deep regions; and subjecting said semiconductor substrate to a heat treatment not only to cause a vertical diffusion of an impurity from said impurity-introduced regions so as to selectively form source/drain diffusion layers but also to cause a rate-increased lateral diffusion of said impurity from said impurity-introduced regions through said predetermined shallow regions so as to selectively form shallow diffusion layers in said semiconductor substrate under said side wall oxide films, so that said shallow diffusion layers laterally extend from said source/drain diffusion layers and that said shallow diffusion layers have a bottom level shallower than said source/drain diffusion layers.
Claim 34
Dependent Claim
22 words
The method as claimed in claim 29, wherein said crystal defects are formed by an ion-implantation of silicon into said silicon substrate.
Claim 35
Dependent Claim
25 words
The method as claimed in claim 30, wherein said ion-implantation of silicon is carried out at a dose of about 1×10 14 cm -2 .
Claim 36
Dependent Claim
29 words
The method as claimed in claim 29, wherein said crystal defects are formed by subjecting said surface of said silicon substrate to an ion-implantation to cause interstitial silicon atoms.
Claim 37
Dependent Claim
31 words
The method as claimed in claim 29, wherein said ion-implantation is with an ion selected from the group consisting of N, F, Sb, In, P, As, Ga, He, Ne and Ar.
Claim 38
Dependent Claim
23 words
The method as claimed in claim 29, wherein said heat treatment is carried out at a temperature in the range of 700-900° C.
Claim 39
Dependent Claim
27 words
The method as claimed in claim 29, wherein said heat treatment is a rapid thermal anneal carried out at a temperature in the range of 900-1150° C.
Claim 40
Dependent Claim
21 words
The method as claimed in claim 29, wherein said shallow diffusion layers have a depth in the range of 10-70 nanometers.
Claim 41
Independent Claim
248 words
A method of forming a MOS field effect transistor comprising the steps of: selectively forming a gate electrode on a gate insulation film which is formed on a surface of a silicon substrate; selectively forming side wall oxide films at opposite sides of said rate electrode; selectively forming impurity-introduced deep regions by an ion-implantation using said gate electrode and said side wall oxide films as masks; selectively forming crystal defects in predetermined shallow and deep regions by such an ion-implantation as to have atoms penetrate through said gate electrode and said side wall oxide films, said predetermined shallow region being positioned in a surface region of said semiconductor substrate under said gate electrode and said side wall oxide films, said predetermined shallow region having a bottom shallower than said impurity-introduced deep regions, said predetermined deep regions having bottoms positioned under said impurity-introduced deep regions; and subjecting said semiconductor substrate to a heat treatment not only to cause a rate-increased vertical diffusion of an impurity from said impurity-introduced regions through said predetermined deep regions so as to selectively form source/drain diffusion layers but also to cause a rate-increased lateral diffusion of said impurity from said impurity-introduced regions through said predetermined shallow region so as to selectively form shallow diffusion layers in said semiconductor substrate under said side wall oxide films, so that said shallow diffusion layers laterally extend from said source/drain diffusion layers and that said shallow diffusion layers have a bottom level shallower than said source/drain diffusion layers.
Claim 42
Independent Claim
248 words
A method of forming a MOS field effect transistor comprising the steps of: selectively forming a gate electrode on a gate insulation film which is formed on a surface of a silicon substrate; selectively forming side wall oxide films at opposite sides of said rate electrode; selectively forming impurity-introduced deep regions by an ion-implantation using said gate electrode and said side wall oxide films as masks; selectively forming crystal defects in predetermined shallow and deep regions by such an ion-implantation as to have atoms penetrate through said gate electrode and said side wall oxide films, said predetermined shallow region being positioned in a surface region of said semiconductor substrate under said gate electrode and said side wall oxide films, said predetermined shallow region having a bottom shallower than said impurity-introduced deep regions, said predetermined deep regions having bottoms positioned under said impurity-introduced deep regions; and subjecting said semiconductor substrate to a heat treatment not only to cause a rate-increased vertical diffusion of an impurity from said impurity-introduced regions through said predetermined deep regions so as to selectively form source/drain diffusion layers but also to cause a rate-increased lateral diffusion of said impurity from said impurity-introduced regions through said predetermined shallow region so as to selectively form shallow diffusion layers in said semiconductor substrate under said side wall oxide films, so that said shallow diffusion layers laterally extend from said source/drain diffusion layers and that said shallow diffusion layers have a bottom level shallower than said source/drain diffusion layers.
Claim 43
Dependent Claim
34 words
The method as claimed in claim 37, wherein said crystal defects are formed by an ion-implantation at a dose slightly lower than a critical dose over which crystal semiconductor is made into amorphous semiconductor.
Claim 44
Dependent Claim
29 words
The method as claimed in claim 37, wherein said crystal defects are formed by subjecting said surface of said silicon substrate to an ion-inplantation to cause interstitial silicon atoms.
Claim 45
Dependent Claim
30 words
The method as claimed in claim 39, wherein said ion is one selected from the group consisting of Ge, N, F, Sb, In, P, As, Ga, He, Ne and Ar.
Claim 46
Dependent Claim
23 words
The method as claimed in claim 37, wherein said heat treatment is carried out at a temperature in the range of 700-900° C.
Claim 47
Dependent Claim
27 words
The method as claimed in claim 37, wherein said heat treatment is a rapid thermal anneal carried out at a temperature in the range of 900-1150° C.
Claim 48
Dependent Claim
21 words
The method as claimed in claim 37, wherein said shallow diffusion layers have a depth in the range of 10-70 nanometers.
Claim 49
Dependent Claim
11 words
The method of claim 37, wherein said ion-implantation is with silicon.
Claim 50
Dependent Claim
32 words
The method as claimed in claim 44, wherein said ion-implantation of silicon is carried out at a dose in the range of 1×10 13 cm -2 to 5×10 14 cm -2 .
Claim 51
Dependent Claim
25 words
The method as claimed in claim 44, wherein said ion-implantation of silicon is carried out at a dose of about 1×10 14 cm -2 .
Claim 52
Independent Claim
239 words
A method of forming a MOS field effect transistor comprising the steps of: selectively forming a gate electrode on a gate insulation film which is formed on a surface of a silicon substrate; selectively forming side wall oxide films at opposite sides of said gate electrode; selectively forming impurity-introduced deep regions self-aligned by using said gate electrode and said side wall oxide films as masks; forming source/drain diffusion layers by activating said impurity-introduced deep regions; selectively forming crystal defects both in a predetermined shallow region and in said source/drain diffusion layers by such an ion-implantation as to have atoms penetrate through said gate electrode and said side wall oxide films, said predetermined shallow region being positioned in a surface region of said semiconductor substrate under said gate electrode and said side wall oxide films, said predetermined shallow region having a bottom shallower than said source/drain diffusion layers; and subjecting said semiconductor substrate to a heat treatment not only to cause a vertical diffusion of an impurity from said source/drain diffusion regions but also to cause a rate-increased lateral diffusion of said impurity from said source/drain diffusion layers through said predetermined shallow region so as to selectively form shallow diffusion layers in said semiconductor substrate under said side wall side films, so that said shallow diffusion layers laterally extend from said source/drain diffusion layers and that said shallow diffusion layers have a bottom level shallower than said source/drain diffusion layers.
Claim 53
Independent Claim
239 words
A method of forming a MOS field effect transistor comprising the steps of: selectively forming a gate electrode on a gate insulation film which is formed on a surface of a silicon substrate; selectively forming side wall oxide films at opposite sides of said gate electrode; selectively forming impurity-introduced deep regions self-aligned by using said gate electrode and said side wall oxide films as masks; forming source/drain diffusion layers by activating said impurity-introduced deep regions; selectively forming crystal defects both in a predetermined shallow region and in said source/drain diffusion layers by such an ion-implantation as to have atoms penetrate through said gate electrode and said side wall oxide films, said predetermined shallow region being positioned in a surface region of said semiconductor substrate under said gate electrode and said side wall oxide films, said predetermined shallow region having a bottom shallower than said source/drain diffusion layers; and subjecting said semiconductor substrate to a heat treatment not only to cause a vertical diffusion of an impurity from said source/drain diffusion regions but also to cause a rate-increased lateral diffusion of said impurity from said source/drain diffusion layers through said predetermined shallow region so as to selectively form shallow diffusion layers in said semiconductor substrate under said side wall side films, so that said shallow diffusion layers laterally extend from said source/drain diffusion layers and that said shallow diffusion layers have a bottom level shallower than said source/drain diffusion layers.
Claim 54
Dependent Claim
34 words
The method as claimed in claim 47, wherein said crystal defects are formed by an ion-implantation at a dose slightly lower than a critical dose over which crystal semiconductor is made into amorphous semiconductor.
Claim 55
Dependent Claim
29 words
The method as claimed in claim 47, wherein said crystal defects are formed by subjecting said surface of said silicon substrate to an ion-implantation to cause interstitial silicon atoms.
Claim 56
Dependent Claim
30 words
The method as claimed in claim 49, wherein said ion is one selected from the group consisting of Ge, N, F, Sb, In, P, As, Ga, He, Ne and Ar.
Claim 57
Dependent Claim
23 words
The method as claimed in claim 47, wherein said heat treatment is carried out at a temperature in the range of 700-900° C.
Claim 58
Dependent Claim
27 words
The method as claimed in claim 47, wherein said heat treatment is a rapid thermal anneal carried out at a temperature in the range of 900-1150° C.
Claim 59
Dependent Claim
21 words
The method as claimed in claim 47, wherein said shallow diffusion layers have a depth in the range of 10-70 nanometers.
Claim 60
Dependent Claim
11 words
The method of claim 47, wherein said ion-implantation is with silicon.
Claim 61
Dependent Claim
32 words
The method as claimed in claim 54, wherein said ion-implantation of silicon is carried out at a dose in the range of 1×10 13 cm -2 to 5×10 14 cm -2 .
Claim 62
Dependent Claim
25 words
The method as claimed in claim 54, wherein said ion-implantation of silicon is carried out at a dose of about 1×10 14 cm -2 .
Claim 63
Independent Claim
247 words
A method of forming a MOS field effect transistor comprising the steps of: selectively forming a gate electrode on a gate insulation film which is formed on a surface of a silicon substrate; selectively forming side wall oxide films at opposite sides of said gate electrode; selectively forming impurity-introduced silicon films self-aligned on said silicon substrate by using said gate electrode and said side wall oxide films as masks; selectively forming crystal defects in predetermined shallow and deep regions by such an ion-implantation as to have atoms penetrate through said gate electrode and said side wall oxide films, said predetermined shallow region being positioned in a surface region of said semiconductor substrate under said gate electrode and said side wall oxide films, said predetermined deep regions having a bottom level deeper than said predetermined shallow region; and subjecting said semiconductor substrate to a heat treatment not only to cause a rate-increased vertical diffusion of an impurity from said impurity-introduced silicon films through said predetermined deep regions so as to selectively form source/drain diffusion layers but also to cause a rate-increased lateral diffusion of said impurity from said impurity-introduced silicon films through said predetermined deep and shallow regions so as to selectively form shallow diffusion layers in said semiconductor substrate under said side wall oxide films, so that said shallow diffusion layers laterally extend from lower portions of said source/drain diffusion layers and that said shallow diffusion layers have a bottom level shallower than said source/drain diffusion layers.
Claim 64
Independent Claim
247 words
A method of forming a MOS field effect transistor comprising the steps of: selectively forming a gate electrode on a gate insulation film which is formed on a surface of a silicon substrate; selectively forming side wall oxide films at opposite sides of said gate electrode; selectively forming impurity-introduced silicon films self-aligned on said silicon substrate by using said gate electrode and said side wall oxide films as masks; selectively forming crystal defects in predetermined shallow and deep regions by such an ion-implantation as to have atoms penetrate through said gate electrode and said side wall oxide films, said predetermined shallow region being positioned in a surface region of said semiconductor substrate under said gate electrode and said side wall oxide films, said predetermined deep regions having a bottom level deeper than said predetermined shallow region; and subjecting said semiconductor substrate to a heat treatment not only to cause a rate-increased vertical diffusion of an impurity from said impurity-introduced silicon films through said predetermined deep regions so as to selectively form source/drain diffusion layers but also to cause a rate-increased lateral diffusion of said impurity from said impurity-introduced silicon films through said predetermined deep and shallow regions so as to selectively form shallow diffusion layers in said semiconductor substrate under said side wall oxide films, so that said shallow diffusion layers laterally extend from lower portions of said source/drain diffusion layers and that said shallow diffusion layers have a bottom level shallower than said source/drain diffusion layers.
Claim 65
Dependent Claim
34 words
The method as claimed in claim 57, wherein said crystal defects are formed by an ion-implantation at a dose slightly lower than a critical dose over which crystal semiconductor is made into amorphous semiconductor.
Claim 66
Dependent Claim
29 words
The method as claimed in claim 57, wherein said crystal defects are formed by subjecting said surface of said silicon substrate to an ion-implantation to cause interstitial silicon atoms.
Claim 67
Dependent Claim
30 words
The method as claimed in claim 59, wherein said ion is one selected from the group consisting of Ge, N, F, Sb, In, P, As, Ga, He, Ne and Ar.
Claim 68
Dependent Claim
23 words
The method as claimed in claim 57, wherein said heat treatment is carried out at a temperature in the range of 700-900° C.
Claim 69
Dependent Claim
27 words
The method as claimed in claim 57, wherein said heat treatment is a rapid thermal anneal carried out at a temperature in the range of 900-1150° C.
Claim 70
Dependent Claim
21 words
The method as claimed in claim 57, wherein said shallow diffusion layers have a depth in the range of 10-70 nanometers.
Claim 71
Dependent Claim
11 words
The method of claim 57, wherein said ion-implantation is with silicon.
Claim 72
Dependent Claim
32 words
The method as claimed in claim 64, wherein said ion-implantation of silicon is carried out at a dose in the range of 1×10 13 cm -2 to 5×10 14 cm -2 .
Claim 73
Dependent Claim
25 words
The method as claimed in claim 64, wherein said ion-implantation of silicon is carried out at a dose of about 1×10 14 cm -2 .
References Cited (Backward Citations)
US4216030A
Cited
US4584026A
Cited
JPH01196818A
Cited
US5145794A
Cited
JPH0689870A
Cited
JPH0689869A
Cited
JPH0513430A
Cited
JPH05190848A
Cited
JPH0629315A
Cited
JPH0677247A
Cited
US5395773A
Cited
US5668020A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2002-06-21 | 2002-12-21 | 2003-06-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2006-06-21 | 2006-12-21 | 2007-06-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2010-06-21 | 2010-12-21 | 2011-06-22 | $7700.00 | Window Closed / Lapsed |