Method of making low-k fluorinated amorphous carbon dielectric

Claim 2

A plasma enhanced chemical vapor deposition (PECVD) process for depositing a fluorinated amorphous carbon dielectric material on a substrate for use in interconnect structures of integrated circuits, the method comprising the following steps: a) position the substrate in a PECVD chamber and heat the substrate to a temperature above 200° C.; b) introduce a flow of fluorine containing gas (FCG) and carbon containing gas (CCG) into the chamber under sufficient applied energy to form a fluorine and carbon gas plasma, the flow rate ratio of FCG to CCG being selected to deposit fluorinated amorphous carbon containing 40 or more at. % F on the substrate; and c) introduce a flow of SiH 4 (silane) into the chamber together with the FCG and CCG in step b) the SiH 4 providing H radicals for combining with F atoms to suppress fluorine etchants during fluorinated amorphous carbon deposition, whereby the silane increases the thermal stability of the fluorinated amorphous carbon deposited on the substrate.

Claim 3

A PECVD process as in claim 1 in which the substrate is heated to a temperature in the range of about 200° C. to about 300° C. in step a).

Claim 4

A PECVD process as in claim 1 in which the FCG introduced in step b) is C 4 F 8 .

Claim 5

A PECVD process as in claim 3 in which the CCG introduced in step b) is CH 4 .

Claim 6

A PECVD process as in claim 4 in which the ambient pressure in the PECVD chamber maintained during the introduction of C 4 F 8 , CH 4 , and silane is in the range of about 0.3 Torr to about 2.0 Torr.

Claim 7

A PECVD process as in claim 5 in which the ratio of C 4 F 8 to CH 4 (C 4 F 8 /CH 4 ) introduced into the PECVD chamber during steps b) and c) is between about 1/1 and about 30/1.

Claim 8

A PECVD process as in claim 5 in which the ratio of C 4 F 8 to CH 4 (C 4 F 8 /CH 4 ) introduced into the PECVD chamber during steps b) and c) is between about 5/1 and about 15/1.

Claim 9

A PECVD process as in claim 6 in which the percentage of silane in the C 4 F 8 , CH 4 , and silane gases introduced into the PECVD chamber in steps b) and c) is in the range of about 1% to about 15%.

Claim 10

A PECVD process as in claim 5 in which flow rates of the C 4 F 8 , CH 4 , and silane gases introduced into the PECVD chamber in steps b) and c), per cm 3 of the chamber interior volume, are in the following ranges: about 3000 to about 10,000 sccm of C 4 F 8 per m 3 ; about 300 to about 1100 sccm CH 4 per m 3 ; and about 100 to about 550 sccm of silane per m 3 .

Claim 11

A PECVD process as in claim 1 in which the plasma energy applied in the chamber to form the gas plasma therein includes high-frequency energy at a frequency of 13.56 MHz and an energy level of between 0.5 Watts and 3.0 Watts per square centimeter of substrate surface.

Claim 12

A PECVD process as in claim 10 in which the plasma energy applied in the chamber further includes low-frequency energy at a frequency in the range of about 100 KHz to about 900 KHz and energy level of between 0.5 Watts and 3.0 Watts per square centimeter of substrate surface.

Claim 13

A PECVD process as in claim 1 including continuing the process until a selected thickness of fluorinated amorphous carbon is deposited on the substrate, and further including the step of annealing the substrate at a temperature in the range of about 300° C. to about 550° C.

Claim 14

A plasma enhanced chemical vapor deposition (PECVD) process for depositing fluorinated amorphous carbon dielectric on a substrate for use in interconnect structures of integrated circuits, the method comprising the following steps: a) position the substrate in a PECVD chamber and heat the substrate to a temperature between 200° C. and 300° C.; b) introduce octafluorocyclobutane (C 4 F 8 ), methane (CH 4 ), and silane (SiH 4 ) into the chamber, wherein the percentage of silane in the introduced gases is in the range of about 1% to about 15%; c) apply plasma energy in the chamber to form a gas plasma which includes CF x polymer radicals, wherein x is greater than or equal to 1 and less than or equal to 2, for depositing fluorinated amorphous carbon containing 40 or more at. % fluorine on the substrate; and d) maintain a sufficient flow of octafluorocyclobutane, methane, and silane into the chamber during step b) to provide an interior chamber pressure in the range of about 0.3 Torr to about 2.0 Torr until a selected thickness of the fluorinated amorphous carbon is deposited on the substrate, wherein the silane provides H radicals for combining with F atoms to suppress fluorine etchants during the fluorinated amorphous carbon deposition.

Claim 15

A plasma enhanced chemical vapor deposition (PECVD) process for depositing fluorinated amorphous carbon dielectric on a substrate for use in interconnect structures of integrated circuits, the method comprising the following steps: a) position the substrate in a PECVD chamber and heat the substrate to a temperature between 200° C. and 300° C.; b) introduce octafluorocyclobutane (C 4 F 8 ), methane (CH 4 ), and silane (SiH 4 ) into the chamber, wherein the percentage of silane in the introduced gases is in the range of about 1% to about 15%; c) apply plasma energy in the chamber to form a gas plasma which includes CF x polymer radicals, wherein x is greater than or equal to 1 and less than or equal to 2, for depositing fluorinated amorphous carbon containing 40 or more at. % fluorine on the substrate; and d) maintain a sufficient flow of octafluorocyclobutane, methane, and silane into the chamber during step b) to provide an interior chamber pressure in the range of about 0.3 Torr to about 2.0 Torr until a selected thickness of the fluorinated amorphous carbon is deposited on the substrate, wherein the silane provides H radicals for combining with F atoms to suppress fluorine etchants during the fluorinated amorphous carbon deposition.

Claim 16

A PECVD process as in claim 13 in which the plasma energy applied in the chamber further includes high-frequency energy at a frequency of 13.56 MHz and an energy level of between 0.5 Watts and 3.0 Watts per square centimeter of substrate surface.

Claim 17

A PECVD process as in claim 14 in which the plasma energy applied in the chamber further includes low-frequency energy at a frequency in the range of about 100 KHz to about 900 KHz and energy level of between 0.5 Watts and 3.0 Watts per square centimeter of substrate surface.

Claim 18

A PECVD process as in claim 13 in which the ratio of octafluorocyclobutane to methane (C 4 F 8 /CH 4 ) introduced into the PECVD chamber during the process is between about 1/1 and about 30/1.

Claim 19

A PECVD process as in claim 16 in which the percentage of silane in the C 4 F 8 , CH 4 , and silane gases introduced into the PECVD chamber in steps b) and c) is in the range of about 1% to about 15%.

Claim 20

A PECVD process as in claim 13 in which the ratio of octafluorocyclobutane to methane (C 4 F 8 /CH 4 ) introduced into the PECVD chamber during the process is between about 5/1 and about 15/1.

Claim 21

A PECVD process as in claim 18 in which the percentage of silane in the C 4 F 8 , CH 4 , and silane gases introduced into the PECVD chamber in steps b) and c) is in the range of about 1% to about 15%.

Claim 22

A PECVD process as in claim 13 including continuing the process until a selected thickness of fluorinated amorphous carbon is deposited on the substrate, and further including the step of annealing the substrate at a temperature greater than or equal to 440° C.