Methods for etching fuse openings in a semiconductor device
Assignee: Micron Technology Inc
•
Filing: 1996-01-31
•
Granted: 1999-04-20
•
Expires: 2016-01-31
Abstract
Abstract An etch of a fuse opening in overlying layers above a laser-blowable semiconductor fuse having a silicon nitride cap and silicon nitride spacers begins with a silicon nitride that is enclosed in a polysilicon conductive layer on a semiconductor wafer. The etch is performed by etching first with an etch process that etches silicon nitride and later with an etch process that is selective to silicon nitride. The later etch process etches the silicon nitride of the cap and spacers little or not at all, allowing a wider variation in etch depths without destroying the fuse. Also, a patch may be provided in the overlying layers above the fuse, and an etch process employed at the level of the patch that is selective to a material of the patch, resulting in an etch stop effect at that level. The etch process is then changed to an etch process that is not selective to a material of the patch, resulting in decreased variation in etch depth over the surface of the wafer. The etch of the fuse opening is then completed with an etch process that is selective to silicon nitride, again allowing a wider variation in etch depths without destroying the fuse. The etch process that is not selective to a material of the patch and the etch process that is selective to silicon nitride may optionally be one process.
Inventors
- 👤 David S. Becker
- 👤 Kunal R. Parekh
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 02:28
CPC Classifications
H; H10; H10P; H10P50/00; H10P50/20; H10P50/28; H10P50/282; H10P50/283; Y; Y10; Y10S; Y10S438/00; Y10S438/94
Claims Analysis
Total Claims: 58
Claim 1
Independent Claim
133 words
A method for etching a fuse opening during the manufacture of a semiconductor device, said method comprising the steps of: providing a gate stack to serve as a fuse, said gate stack having spacers and a cap comprised of silicon nitride; depositing overlying layers over said gate stack, said overlying layers having a top planar surface; forming a mask upon said top planar surface; forming an opening in said mask upon the top planar surface; and etching a fuse opening in said overlying layers over said gate stack, including the step of etching an opening in said overlying layers through said opening in said mask on said top planar surface, beginning at some time before the downward progress of the opening reaches the gate stack, with an etch process selective to silicon nitride.
Claim 2
Independent Claim
133 words
A method for etching a fuse opening during the manufacture of a semiconductor device, said method comprising the steps of: providing a gate stack to serve as a fuse, said gate stack having spacers and a cap comprised of silicon nitride; depositing overlying layers over said gate stack, said overlying layers having a top planar surface; forming a mask upon said top planar surface; forming an opening in said mask upon the top planar surface; and etching a fuse opening in said overlying layers over said gate stack, including the step of etching an opening in said overlying layers through said opening in said mask on said top planar surface, beginning at some time before the downward progress of the opening reaches the gate stack, with an etch process selective to silicon nitride.
Claim 3
Dependent Claim
69 words
The method as defined in claim 1, wherein: (a) the step of depositing overlying layers over said gate stack comprises the step of depositing a nitride passivation layer over said gate stack; and (b) the step of etching a fuse opening in said overlying layers further comprises the step of etching an opening in said overlying layers beginning with an etch process that is not selective to silicon nitride.
Claim 4
Dependent Claim
87 words
The method as defined in claim 2, wherein the step of etching an opening in said overlying layers, beginning with an etch process that is not selective to silicon nitride, is performed by etching in a plasma etcher in a mixture of CF 4 , CHF 3 , and argon, following which the step of etching an opening in said overlying layers, beginning at a time before the downward progress of the opening reaches the gate stack, with an etch process selective to silicon nitride is performed.
Claim 5
Dependent Claim
64 words
The method as defined in claim 3, wherein the step of etching an opening in said overlying layers, beginning at a time before the downward progress of the opening reaches the gate stack, with an etch process selective to silicon nitride, comprises etching in a plasma etcher in a mixture of CF 4 , argon, CH 2 F 2 , and CHF 3 .
Claim 6
Dependent Claim
59 words
The method as defined in claim 2, wherein the step of etching an opening in said overlying layers, beginning at a time before the downward progress of the opening reaches the gate stack, with an etch process selective to silicon nitride, comprises etching in a plasma etcher in a mixture of CF 4 , CHF 3 , and argon.
Claim 7
Dependent Claim
64 words
The method as defined in claim 1, wherein the step of etching an opening in said overlying layers, beginning at a time before the downward progress of the opening reaches the gate stack, with an etch process selective to silicon nitride, comprises etching in a plasma etcher in a mixture of CF 4 , argon, CH 2 F 2 , and CHF 3 .
Claim 8
Dependent Claim
119 words
The method as defined in claim 1, wherein: (a) the step of depositing overlying layers over said gate stack comprises depositing a patch over said gate stack; and (b) the step of etching a fuse opening in said overlying layers further comprises the steps of: (i) etching an opening in said overlying layers, beginning at a time before the downward progress of the opening reaches the patch, with an etch process selective to a material of which said patch is comprised; and (ii) etching an opening in said overlying layers, beginning at a time after the downward progress of the opening reaches the patch, with an etch process not selective to said material of which said patch is comprised.
Claim 9
Dependent Claim
12 words
The method as defined in claim 7, wherein said patch comprises polysilicon.
Claim 10
Dependent Claim
13 words
The method as defined in claim 7, wherein said patch comprises silicon nitride.
Claim 11
Dependent Claim
30 words
The method as defined in claim 1, wherein all of said step of etching a fuse opening in said overlying layers is performed in situ in a single process chamber.
Claim 12
Independent Claim
173 words
A method for etching a fuse opening during the manufacture of a semiconductor device, said method comprising the steps of: providing on a semiconductor substrate a conductive layer of polysilicon enclosed laterally by spacers and upwardly by a cap, said spacers and said cap being comprised of silicon nitride, said layer of polysilicon together with said cap and said spacers comprising a fuse; depositing overlying layers over said fuse, including silicon oxide and silicon nitride passivation layers, said overlying layers having a top planar surface; forming a mask upon said top planar surface; forming an opening in said mask upon said top planar surface; and etching a fuse opening in said overlying layers over said fuse through said opening in said mask on said top planar surface, including the steps of: etching an opening over said fuse for a first duration of time with an etch process not selective to silicon nitride; and etching said opening over said fuse for a second duration of time with an etch process selective to silicon nitride.
Claim 13
Independent Claim
173 words
A method for etching a fuse opening during the manufacture of a semiconductor device, said method comprising the steps of: providing on a semiconductor substrate a conductive layer of polysilicon enclosed laterally by spacers and upwardly by a cap, said spacers and said cap being comprised of silicon nitride, said layer of polysilicon together with said cap and said spacers comprising a fuse; depositing overlying layers over said fuse, including silicon oxide and silicon nitride passivation layers, said overlying layers having a top planar surface; forming a mask upon said top planar surface; forming an opening in said mask upon said top planar surface; and etching a fuse opening in said overlying layers over said fuse through said opening in said mask on said top planar surface, including the steps of: etching an opening over said fuse for a first duration of time with an etch process not selective to silicon nitride; and etching said opening over said fuse for a second duration of time with an etch process selective to silicon nitride.
Claim 14
Dependent Claim
28 words
The method as defined in claim 11, wherein said first duration of time is selected so as to end before said opening extends to said silicon nitride cap.
Claim 15
Dependent Claim
46 words
The method as defined in claim 11, wherein said second duration of time is selected so as to end when the bottom of said opening extends to within the range of about 2000 Angstroms above said substrate to about 3000 Angstroms above said silicon nitride cap.
Claim 16
Dependent Claim
30 words
The method as defined in claim 11, wherein all of said step of etching a fuse opening in said overlying layers is performed in situ in a single process chamber.
Claim 17
Independent Claim
187 words
A method for etching a fuse opening during the manufacture of a semiconductor device, said method comprising the steps of: providing on a semiconductor substrate a conductive layer of polysilicon enclosed laterally by spacers and upwardly by a cap, said spacers and said cap being comprised of silicon nitride, said layer of polysilicon together with said cap and said spacers comprising a fuse; depositing overlying layers over said fuse, said overlying layers having a top planar surface, including the step of: depositing a patch over said fuse; forming a mask upon said top planar surface; forming an opening in said mask upon said top planar surface; and etching a fuse opening in said overlying layers over said fuse through said opening in said mask upon said top planar surface, including the steps of: etching an opening over said fuse for a first duration of time with an etch process selective to a material of which said patch is comprised; and etching said opening over said fuse for a second duration of time with an etch process not selective to said material of which said patch is comprised.
Claim 18
Independent Claim
187 words
A method for etching a fuse opening during the manufacture of a semiconductor device, said method comprising the steps of: providing on a semiconductor substrate a conductive layer of polysilicon enclosed laterally by spacers and upwardly by a cap, said spacers and said cap being comprised of silicon nitride, said layer of polysilicon together with said cap and said spacers comprising a fuse; depositing overlying layers over said fuse, said overlying layers having a top planar surface, including the step of: depositing a patch over said fuse; forming a mask upon said top planar surface; forming an opening in said mask upon said top planar surface; and etching a fuse opening in said overlying layers over said fuse through said opening in said mask upon said top planar surface, including the steps of: etching an opening over said fuse for a first duration of time with an etch process selective to a material of which said patch is comprised; and etching said opening over said fuse for a second duration of time with an etch process not selective to said material of which said patch is comprised.
Claim 19
Dependent Claim
81 words
The method as defined in claim 15, wherein: (a) the step of depositing overlying layers over said fuse further includes the step of depositing a nitride passivation layer over said fuse; and (b) the step of etching an opening over said fuse for a first duration of time comprises etching an opening over said fuse for a first duration of time with an etch process selective to a material of which said patch is comprised and not selective to silicon nitride.
Claim 20
Dependent Claim
14 words
The method as defined in claim 15 wherein said patch is comprised of polysilicon.
Claim 21
Dependent Claim
47 words
The method as defined in claim 15 wherein the step of etching a fuse opening in said overlying layers over said fuse further comprises the step of etching said opening over said fuse for a third duration of time with an etch process selective to silicon nitride.
Claim 22
Dependent Claim
30 words
The method as defined in claim 15, wherein all of said step of etching a fuse opening in said overlying layers is performed in situ in a single process chamber.
Claim 23
Independent Claim
216 words
A method for etching a fuse opening during the manufacture of a semiconductor device, said method comprising the steps of: providing on a semiconductor substrate a conductive layer of polysilicon enclosed laterally by spacers and upwardly by a cap, said spacers and said cap being comprised of silicon nitride, said layer of polysilicon together with said cap and said spacers comprising a fuse; depositing overlying layers over said fuse, said overlying layers having a top planar surface, including the step of: depositing a patch over said fuse; and depositing a nitride passivation layer over said fuse; forming a mask upon said top planar surface; forming an opening in said mask upon said top planar surface; and etching a fuse opening in said overlying layers over said fuse through said opening in said mask upon said top planar surface, including the steps of: etching an opening over said fuse for a first duration of time with an etch process that etches silicon nitride; etching said opening over said fuse for a second duration of time with an etch process selective to said material of which said patch is comprised; and etching said opening over said fuse for a third duration of time with an etch process not selective to said material of which said patch is comprised.
Claim 24
Independent Claim
216 words
A method for etching a fuse opening during the manufacture of a semiconductor device, said method comprising the steps of: providing on a semiconductor substrate a conductive layer of polysilicon enclosed laterally by spacers and upwardly by a cap, said spacers and said cap being comprised of silicon nitride, said layer of polysilicon together with said cap and said spacers comprising a fuse; depositing overlying layers over said fuse, said overlying layers having a top planar surface, including the step of: depositing a patch over said fuse; and depositing a nitride passivation layer over said fuse; forming a mask upon said top planar surface; forming an opening in said mask upon said top planar surface; and etching a fuse opening in said overlying layers over said fuse through said opening in said mask upon said top planar surface, including the steps of: etching an opening over said fuse for a first duration of time with an etch process that etches silicon nitride; etching said opening over said fuse for a second duration of time with an etch process selective to said material of which said patch is comprised; and etching said opening over said fuse for a third duration of time with an etch process not selective to said material of which said patch is comprised.
Claim 25
Dependent Claim
14 words
The method as defined in claim 20 wherein said patch is comprised of polysilicon.
Claim 26
Dependent Claim
48 words
The method as defined in claim 20, wherein the step of etching a fuse opening in said overlying layers over said fuse, further includes the step of: (a) etching said opening over said fuse for a fourth duration of time with an etch process selective to silicon nitride.
Claim 27
Dependent Claim
15 words
The method as defined in claim 20, wherein said patch is comprised of silicon nitride.
Claim 28
Dependent Claim
30 words
The method as defined in claim 20, wherein all of said step of etching a fuse opening in said overlying layers is performed in situ in a single process chamber.
Claim 29
Dependent Claim
97 words
A etching method comprising: providing a fuse composed of a conductive material, the conductive material having thereon spacers and a cap comprised of an insulative material; depositing overlying layers over said fuse, said overlying layers having a top planar surface; forming a mask upon said top planar surface; forming a opening in said mask upon said top planar surface; and etching an opening in said overlying layers through said opening in said mask upon said top planar surface with an etch process selective to said insulative material prior to the opening reaching the cap on the fuse.
Claim 30
Dependent Claim
97 words
A etching method comprising: providing a fuse composed of a conductive material, the conductive material having thereon spacers and a cap comprised of an insulative material; depositing overlying layers over said fuse, said overlying layers having a top planar surface; forming a mask upon said top planar surface; forming a opening in said mask upon said top planar surface; and etching an opening in said overlying layers through said opening in said mask upon said top planar surface with an etch process selective to said insulative material prior to the opening reaching the cap on the fuse.
Claim 31
Dependent Claim
50 words
The method as defined in claim 25, wherein: depositing said overlying layers over said fuse comprises depositing a passivation layer over said fuse; and etching said opening in said overlying layers further comprises beginning etching of said opening with an etch process that is not selective to said insulative material.
Claim 32
Dependent Claim
84 words
The method as defined in claim 25, wherein: depositing said overlying layers over said fuse comprises depositing a patch over said fuse; and etching said opening in said overlying layers further comprises: etching with an etch process selective to a material of which said patch is comprised before the downward progress of the opening reaches the patch; and etching with an etch process not selective to said material of which said patch is comprised after the downward progress of the opening reaches the patch.
Claim 33
Dependent Claim
12 words
The method as defined in claim 27, wherein said patch comprises polysilicon.
Claim 34
Dependent Claim
14 words
The method as defined in claim 27, wherein said patch comprises said insulative material.
Claim 35
Dependent Claim
24 words
The method as defined in claim 1, wherein etching said opening in said overlying layers is performed in situ in a single process chamber.
Claim 36
Dependent Claim
17 words
The method as defined in claim 1, wherein said insulative material is substantially composed of silicon nitride.
Claim 37
Independent Claim
236 words
A method for etching a fuse opening during the manufacture of a semiconductor device, said method comprising the steps of: providing a semiconductor substrate; providing a gate stack upon the semiconductor substrate to serve as a fuse, said gate stack having: an electrically conductive layer having lateral surfaces; a cap layer having an external exposed surface; and a spacer layer upon and in contact with the lateral surfaces of the electrically conductive layer, wherein spacer layer has an external exposed surface and extends from the semiconductor substrate to the cap layer, wherein the cap layer and the spacer layer are composed of silicon nitride, and wherein the spacer layer is adjacent to an exposed surface of the semiconductor substrate; depositing overlying layers over said gate stack, upon the external exposed surface of the cap layer, upon the external exposed surface of the spacer layer, and upon the exposed surface of the semiconductor substrate such that the overlying layers enclose the cap layer and the spacer layer; and etching a fuse opening in said overlying layers over said gate stack, including the step of etching an opening in said overlying layers, beginning at some time before the downward progress of the opening reaches the gate stack, with an etch process selective to silicon nitride such that the spacer layer remains in contact with electrically conductive layer, the electrically conductive layer is not exposed by the fuse opening.
Claim 38
Independent Claim
236 words
A method for etching a fuse opening during the manufacture of a semiconductor device, said method comprising the steps of: providing a semiconductor substrate; providing a gate stack upon the semiconductor substrate to serve as a fuse, said gate stack having: an electrically conductive layer having lateral surfaces; a cap layer having an external exposed surface; and a spacer layer upon and in contact with the lateral surfaces of the electrically conductive layer, wherein spacer layer has an external exposed surface and extends from the semiconductor substrate to the cap layer, wherein the cap layer and the spacer layer are composed of silicon nitride, and wherein the spacer layer is adjacent to an exposed surface of the semiconductor substrate; depositing overlying layers over said gate stack, upon the external exposed surface of the cap layer, upon the external exposed surface of the spacer layer, and upon the exposed surface of the semiconductor substrate such that the overlying layers enclose the cap layer and the spacer layer; and etching a fuse opening in said overlying layers over said gate stack, including the step of etching an opening in said overlying layers, beginning at some time before the downward progress of the opening reaches the gate stack, with an etch process selective to silicon nitride such that the spacer layer remains in contact with electrically conductive layer, the electrically conductive layer is not exposed by the fuse opening.
Claim 39
Dependent Claim
76 words
The method as defined in claim 32, wherein the overlying layers have a top planar surface, the method further comprising, prior to etching a fuse opening in said overlying layers: forming a mask upon said top planar surface; forming an opening in said mask upon said top planar surface; and wherein etching a fuse opening in said overlying layers further comprises etching the fuse opening through the opening in the mask upon the top planar surface.
Claim 40
Independent Claim
228 words
A method for etching a fuse opening during the manufacture of a semiconductor device, said method comprising the steps of: providing on a semiconductor substrate a conductive layer of polysilicon having lateral surfaces, said conductive layer having spacers on said lateral surfaces extending upwardly to a cap, said spacers and said cap each having an external exposed surface and being composed of silicon nitride, said layer of polysilicon together with said cap and said spacers comprising a fuse, wherein the spacers are adjacent to an exposed surface of the semiconductor substrate; depositing overlying layers over said fuse, including silicon oxide and silicon nitride passivation layers, upon the external exposed surface of the cap layer, upon the external exposed surface of the spacer layer, and upon the exposed surface of the semiconductor substrate such that the overlying layers substantially cover up and enclose the cap layer and the spacer layer; and etching a fuse opening in said overlying layers over said fuse such that the spacers remain in contact with conductive layer and the conductive layer is not exposed by the fuse opening, including the steps of: etching an opening over said fuse for a first duration of time with an etch process not selective to silicon nitride; and etching said opening over said fuse for a second duration of time with an etch process selective to silicon nitride.
Claim 41
Independent Claim
228 words
A method for etching a fuse opening during the manufacture of a semiconductor device, said method comprising the steps of: providing on a semiconductor substrate a conductive layer of polysilicon having lateral surfaces, said conductive layer having spacers on said lateral surfaces extending upwardly to a cap, said spacers and said cap each having an external exposed surface and being composed of silicon nitride, said layer of polysilicon together with said cap and said spacers comprising a fuse, wherein the spacers are adjacent to an exposed surface of the semiconductor substrate; depositing overlying layers over said fuse, including silicon oxide and silicon nitride passivation layers, upon the external exposed surface of the cap layer, upon the external exposed surface of the spacer layer, and upon the exposed surface of the semiconductor substrate such that the overlying layers substantially cover up and enclose the cap layer and the spacer layer; and etching a fuse opening in said overlying layers over said fuse such that the spacers remain in contact with conductive layer and the conductive layer is not exposed by the fuse opening, including the steps of: etching an opening over said fuse for a first duration of time with an etch process not selective to silicon nitride; and etching said opening over said fuse for a second duration of time with an etch process selective to silicon nitride.
Claim 42
Dependent Claim
76 words
The method as defined in claim 34, wherein the overlying layers have a top planar surface, the method further comprising, prior to etching a fuse opening in said overlying layers: forming a mask upon said top planar surface; forming an opening in said mask upon said top planar surface; and wherein etching a fuse opening in said overlying layers further comprises etching the fuse opening through the opening in the mask upon the top planar surface.
Claim 43
Dependent Claim
157 words
A etching method comprising: providing a semiconductor substrate; providing a fuse situated upon the semiconductor substrate and composed of a conductive material, the conductive material having thereon spacers extending upwardly to a cap, the spacers and the cap each having an external exposed surface and being composed of silicon nitride, wherein the spacers are adjacent to an exposed surface of the semiconductor substrate; depositing overlying layers upon the external exposed surface of the cap layer, upon the external exposed surface of the spacer layer, and upon the exposed surface of the semiconductor substrate such that the overlying layers enclose the cap layer and the spacer layer; and etching an opening in said overlying layers with an etch process selective to said insulative material prior to the opening reaching the cap on the fuse such that the spacers remain in contact with the conductive material of the fuse and the conductive material is not exposed by the opening.
Claim 44
Dependent Claim
157 words
A etching method comprising: providing a semiconductor substrate; providing a fuse situated upon the semiconductor substrate and composed of a conductive material, the conductive material having thereon spacers extending upwardly to a cap, the spacers and the cap each having an external exposed surface and being composed of silicon nitride, wherein the spacers are adjacent to an exposed surface of the semiconductor substrate; depositing overlying layers upon the external exposed surface of the cap layer, upon the external exposed surface of the spacer layer, and upon the exposed surface of the semiconductor substrate such that the overlying layers enclose the cap layer and the spacer layer; and etching an opening in said overlying layers with an etch process selective to said insulative material prior to the opening reaching the cap on the fuse such that the spacers remain in contact with the conductive material of the fuse and the conductive material is not exposed by the opening.
Claim 45
Dependent Claim
77 words
The method as defined in claim 36, wherein the overlying layers have a top planar surface, the method further comprising, prior to etching an opening in said overlying layers: forming a mask upon said top planar surface; forming an opening in said mask upon said top planar surface; and wherein etching an opening in said overlying layers further comprises etching the opening in said overlying layers through the opening in the mask upon the top planar surface.
Claim 46
Independent Claim
165 words
A method for forming an opening to a fuse, the method comprising: providing a semiconductor substrate; providing a fuse on the semiconductor substrate, the fuse including an electrically conductive material, and the fuse having an exposed external surface thereon; forming a covering composed of silicon nitride over the fuse and extending to the semiconductor substrate so as to cover the exposed external surface of the fuse, wherein: the covering is in contact with the electrically conductive material; the covering has an exposed external surface thereon that is adjacent to an exposed surface of the semiconductor substrate; forming overlying layers upon the external exposed surface of the covering and upon the exposed surface of the semiconductor substrate such that the overlying layers enclose the covering; forming an opening in said overlying layers such that: the covering remains in contact with the electrically conductive material of the fuse; the conductive material is not exposed by the opening; and the semiconductor substrate is not exposed by the opening.
Claim 47
Independent Claim
165 words
A method for forming an opening to a fuse, the method comprising: providing a semiconductor substrate; providing a fuse on the semiconductor substrate, the fuse including an electrically conductive material, and the fuse having an exposed external surface thereon; forming a covering composed of silicon nitride over the fuse and extending to the semiconductor substrate so as to cover the exposed external surface of the fuse, wherein: the covering is in contact with the electrically conductive material; the covering has an exposed external surface thereon that is adjacent to an exposed surface of the semiconductor substrate; forming overlying layers upon the external exposed surface of the covering and upon the exposed surface of the semiconductor substrate such that the overlying layers enclose the covering; forming an opening in said overlying layers such that: the covering remains in contact with the electrically conductive material of the fuse; the conductive material is not exposed by the opening; and the semiconductor substrate is not exposed by the opening.
Claim 48
Dependent Claim
77 words
The method as defined in claim 38, wherein the overlying layers have a top planar surface, the method further comprising, prior to etching an opening in said overlying layers: forming a mask upon said top planar surface; forming an opening in said mask upon said top planar surface; and wherein etching an opening in said overlying layers further comprises etching the opening in said overlying layers through the opening in the mask upon the top planar surface.
Claim 49
Independent Claim
182 words
A method for forming an opening to a fuse, the method comprising: providing a semiconductor substrate; providing a fuse on the semiconductor substrate, the fuse including an electrically conductive material; forming a covering composed of an electrically insulative material over the fuse and extending to the semiconductor substrate so as to substantially cover the fuse, wherein: the covering is in contact with the electrically conductive material; and the covering has an exposed external surface thereon; forming overlying layers upon the external exposed surface of the covering and upon the semiconductor substrate such that the overlying layers substantially cover up and enclose the covering, the overlying layers having a top planar surface; forming a mask upon said top planar surface; forming an opening in said mask upon said top planar surface; forming an opening in said overlying layers through the opening in the mask upon the top planar surface such that: the covering remains in contact with the electrically conductive material of the fuse; the conductive material is not exposed by the opening; and the semiconductor substrate is not exposed by the opening.
Claim 50
Independent Claim
182 words
A method for forming an opening to a fuse, the method comprising: providing a semiconductor substrate; providing a fuse on the semiconductor substrate, the fuse including an electrically conductive material; forming a covering composed of an electrically insulative material over the fuse and extending to the semiconductor substrate so as to substantially cover the fuse, wherein: the covering is in contact with the electrically conductive material; and the covering has an exposed external surface thereon; forming overlying layers upon the external exposed surface of the covering and upon the semiconductor substrate such that the overlying layers substantially cover up and enclose the covering, the overlying layers having a top planar surface; forming a mask upon said top planar surface; forming an opening in said mask upon said top planar surface; forming an opening in said overlying layers through the opening in the mask upon the top planar surface such that: the covering remains in contact with the electrically conductive material of the fuse; the conductive material is not exposed by the opening; and the semiconductor substrate is not exposed by the opening.
Claim 51
Dependent Claim
40 words
The method as defined in claim 40, wherein the semiconductor substrate has a top most surface upon which the fuse is situated, wherein the opening terminates not less than 2000 Angstroms above the top most surface of the semiconductor substrate.
Claim 52
Dependent Claim
38 words
The method as defined in claim 40, wherein the covering has a top most surface upon which the overlying layer are situated, wherein the opening terminates not more than 3000 Angstroms above top most surface of the covering.
Claim 53
Dependent Claim
67 words
The method as defined in claim 40, wherein: the semiconductor substrate has a top most surface upon which the fuse is situated; the covering has a top most surface upon which the overlying layer are situated; and the opening terminates: not less than 2000 Angstroms above the top most surface of the semiconductor substrate; and not more than 3000 Angstroms above top most surface of the covering.
Claim 54
Dependent Claim
19 words
The method as defined in claim 40, wherein the fuse further comprises a metal silicide layer and oxide layer.
Claim 55
Dependent Claim
36 words
The method as defined in claim 40, forming overlying layers over said covering comprises: forming an insulative layer upon the semiconductor substrate and upon the covering; forming a capacitor plate composed of an electrically conductive material.
Claim 56
Dependent Claim
15 words
The method as defined in claim 45, wherein the capacitor plate is composed of polysilicon.
Claim 57
Dependent Claim
60 words
The method as defined in claim 40, wherein forming overlying layers over said covering comprises: forming an insulative layer composed silicon oxide upon the covering; forming a patch upon the insulative layer, wherein the patch is composed of a material selected from the group consisting of silicon nitride and polysilicon, wherein the insulative layer separates the covering from the patch.
Claim 58
Dependent Claim
15 words
The method as defined in claim 40, wherein the covering is composed of silicon nitride.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2002-04-19 | 2002-10-19 | 2003-04-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2006-04-19 | 2006-10-19 | 2007-04-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2010-04-19 | 2010-10-19 | 2011-04-20 | $7700.00 | Window Closed / Lapsed |