US5877048A
Expired / Lapsed
US
⏱️ 0.0 years remaining
3-D CMOS transistors with high ESD reliability
Assignee: Taiwan Semiconductor Manufacturing Co TSMC Ltd
•
Filing: 1998-03-23
•
Granted: 1999-03-02
•
Expires: 2018-03-23
Abstract
Abstract The present invention discloses a method for manufacturing 3-D transistors with high electrostatic discharge (ESD) reliability. Pad oxide layers are on a silicon substrate and a thick field oxide is on the silicon substrate between the pad oxide layer. An oxygen amorphized region is formed in the substrate by using an ion implantation having oxygen ions as dopants and the field oxide as a hard mask. A high-temperature thermal annealing is implemented to convert the oxygen amorphized region into an oxygen implant-induced oxide regions. Then, the pad oxide layers and the field oxide are removed to form a field oxide region on the substrate and silicon islands on the oxygen implant-induced oxide regions. A thin gate oxide is deposited on the surface of the substrate and the silicon islands to seal the silicon islands. Finally, PMOSFETs are formed on the silicon islands and bulk NMOSFET buffers are formed on the field oxide region of the substrate.
Inventors
- 👤 Shye-Lin Wu
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 10:15
CPC Classifications
H; H10; H10D; H10D84/00; H10D84/01; H10D84/0123; H10D84/0126; H10D84/0165; H10D84/02; H10D84/03; H10D84/038; H10D86/00; H10D86/01; H10D86/201
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
140 words
A method to manufacture 3-D CMOS transistors, the method comprising the steps of: providing a substrate having a field oxide and pad oxide layers on said substrate, said field oxide defining a field oxide region between said pad oxide layers; implementing an ion implantation having oxygen dopant to form an oxygen amorphized region in said substrate below said pad oxide layers, using said field oxide as a hard mask; performing a thermal annealing to convert said oxygen amorphized region into an buried oxide region; removing said pad oxide layers and said field oxide to form silicon islands on said buried oxide region; forming a gate oxide layer on the surface of said silicon islands and said substrate; and forming P channel MOS devices in said silicon islands and N channel MOS devices in said substrate at said field oxide region.
Claim 2
Independent Claim
140 words
A method to manufacture 3-D CMOS transistors, the method comprising the steps of: providing a substrate having a field oxide and pad oxide layers on said substrate, said field oxide defining a field oxide region between said pad oxide layers; implementing an ion implantation having oxygen dopant to form an oxygen amorphized region in said substrate below said pad oxide layers, using said field oxide as a hard mask; performing a thermal annealing to convert said oxygen amorphized region into an buried oxide region; removing said pad oxide layers and said field oxide to form silicon islands on said buried oxide region; forming a gate oxide layer on the surface of said silicon islands and said substrate; and forming P channel MOS devices in said silicon islands and N channel MOS devices in said substrate at said field oxide region.
Claim 3
Dependent Claim
17 words
The method of claim 1, wherein said field oxide has thickness between about 3000 to 10000 angstroms.
Claim 4
Dependent Claim
39 words
The method of claim 1, wherein said ion implantation for forming said oxygen amorphized region is performed with an energy between about 100 to 500 KeV and a dose between about 5×10 16 to 5×10 19 ions/cm 2 .
Claim 5
Dependent Claim
26 words
The method of claim 1, wherein said thermal annealing is achieved in an N 2 ambient with a temperature between about 1050 to 1350 degrees centigrade.
Claim 6
Dependent Claim
29 words
The method of claim 1, wherein said thermal annealing is achieved in an N 2 and O 2 ambient with a temperature between about 1050 to 1350 degrees centigrade.
Claim 7
Dependent Claim
23 words
The method of claim 1, wherein said gate oxide layer and said field oxide are removed by using buffer oxide etching (BOE) solution.
Claim 8
Dependent Claim
21 words
The method of claim 1, wherein said gate oxide layer and said field oxide are removed by using diluted HF solution.
Claim 9
Dependent Claim
18 words
The method of claim 1, wherein said gate oxide layer is grown in an N 2 O ambient.
Claim 10
Dependent Claim
16 words
The method of claim 1, wherein said gate oxide layer is grown in an NO ambient.
Claim 11
Independent Claim
107 words
A method for manufacturing silicon islands on a substrate, the method comprising the steps of: providing a substrate; forming a pad oxide on said substrate; defining field oxide regions on said pad oxide; forming field oxide on said substrate on the said field oxide region; performing an ion implantation containing oxygen ions to form oxygen amorphized regions in said substrate below said pad oxide layers by using field oxide as a hard mask; performing a thermal annealing to convert said oxygen amorphized region into an buried oxide region; and removing said pad oxide layers and said field oxide to form silicon islands on said buried oxide region.
Claim 12
Independent Claim
107 words
A method for manufacturing silicon islands on a substrate, the method comprising the steps of: providing a substrate; forming a pad oxide on said substrate; defining field oxide regions on said pad oxide; forming field oxide on said substrate on the said field oxide region; performing an ion implantation containing oxygen ions to form oxygen amorphized regions in said substrate below said pad oxide layers by using field oxide as a hard mask; performing a thermal annealing to convert said oxygen amorphized region into an buried oxide region; and removing said pad oxide layers and said field oxide to form silicon islands on said buried oxide region.
Claim 13
Dependent Claim
18 words
The method of claim 10, wherein said field oxide has a thickness between about 3000 to 10000 angstroms.
Claim 14
Dependent Claim
31 words
The method of claim 10, wherein said ion implantation is implemented with an energy between 100 to 500 KeV and a dose between 5×10 16 to 5×10 19 ions/cm 2 .
Claim 15
Dependent Claim
24 words
The method of claim 10, wherein said thermal annealing is performed in an N 2 ambient with a temperature 1050 to 1350 degrees centigrade.
Claim 16
Dependent Claim
27 words
The method of claim 10, wherein said thermal annealing is performed in an N 2 and O 2 ambient with a temperature 1050 to 1350 degrees centigrade.
Claim 17
Dependent Claim
22 words
The method of claim 10, wherein said pad oxide and said field oxide are removed by using buffer oxide etching (BOE) solution.
Claim 18
Dependent Claim
20 words
The method of claim 10, wherein said pad oxide and said field oxide are removed by using diluted HF solution.
References Cited (Backward Citations)
US5113236A
Cited
US5338965A
Cited
US5422296A
Cited
US5795809A
Cited
US5795800A
Cited
US5795800B1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2002-03-01 | 2002-08-31 | 2003-03-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2006-03-01 | 2006-08-31 | 2007-03-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2010-03-01 | 2010-08-31 | 2011-03-02 | $7700.00 | Window Closed / Lapsed |