Assignee: Texas Instruments Inc
•
Filing: 1997-06-03
•
Granted: 1999-01-26
•
Expires: 2017-06-03
Abstract
Abstract A shallow trench isolation (STJ) (10) is used to isolate two active regions (12) from each other. The advantage of STI (10) is that the upper corners (14) are rounded. Rounding of the upper corners (14) is accomplished using an oxide deglaze prior to sidewall oxidation of the trench which undercuts the pad oxide (20) from the pad nitride (22). The allows the sidewall oxidation process to form a thicker oxide at upper corners (14) which in turn, rounds the corners. Rounded corners (14) minimum the electric field strength induced by the geometry. As a result, the Vt lowering that occurs in prior art STI structures is minimized and off-state leakage due to the inherent parasitic transistor at the upper corner is reduced.
Inventors
- 👤 Keith Joyner
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 21:32
CPC Classifications
H; H10; H10W; H10W10/00; H10W10/01; H10W10/011; H10W10/014; H10W10/0145; H10W10/0147; H10W10/10; H10W10/17
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
114 words
A method of forming an isolation structure in a semiconductor body, comprising the steps of: forming a pad oxide on said semiconductor body; forming a pad nitride on said pad oxide; patterning and etching said pad oxide and pad nitride to form a hard mask; undercutting said pad oxide from said pad nitride using an oxide deglaze; etching a trench in said semiconductor body using said hard mask; oxidizing said semiconductor body in the presence of said hard mask to create a sidewall oxide, wherein said oxidizing step creates a thicker oxide at an upper corner of said trench rounding the upper corner of said trench; and filling said trench with a dielectric material.
Claim 2
Independent Claim
114 words
A method of forming an isolation structure in a semiconductor body, comprising the steps of: forming a pad oxide on said semiconductor body; forming a pad nitride on said pad oxide; patterning and etching said pad oxide and pad nitride to form a hard mask; undercutting said pad oxide from said pad nitride using an oxide deglaze; etching a trench in said semiconductor body using said hard mask; oxidizing said semiconductor body in the presence of said hard mask to create a sidewall oxide, wherein said oxidizing step creates a thicker oxide at an upper corner of said trench rounding the upper corner of said trench; and filling said trench with a dielectric material.
Claim 3
Dependent Claim
17 words
The method of claim 1, wherein said undercutting step occurs prior to said etching a trench step.
Claim 4
Dependent Claim
22 words
The method of claim 1, wherein said undercutting step occurs after said etching a trench step and prior to said oxidizing step.
Claim 5
Dependent Claim
28 words
The method of claim 1, wherein said undercutting step undercuts said pad oxide from said pad nitride a distance approximately equal to the thickness of said pad oxide.
Claim 6
Dependent Claim
25 words
The method of claim 1, wherein said undercutting step undercuts said pad oxide from said pad nitride a distance on the order of 10 nm.
Claim 7
Dependent Claim
27 words
The method of claim 1, wherein said oxidizing step comprises oxidation at a temperature on the order of 900° C. in the presence of O2 and HCl.
Claim 8
Dependent Claim
18 words
The method of claim 6, wherein said HCl is used at a concentration on the order of 6%.
Claim 9
Dependent Claim
23 words
The method of claim 1, wherein said oxidizig step comprises a rapid thermal oxidation at a temperature on the order of 1100° C.
Claim 10
Dependent Claim
22 words
The method of claim 1, wherein said undercutting step comprises an oxide deglaze for a duration on the order of 70 seconds.
Claim 11
Dependent Claim
23 words
The method of claim 1, wherein said undercutting step comprises an oxide etch using a 0.49 mole % solution of HF in water.
Claim 12
Dependent Claim
22 words
The method of claim 1, wherein said semiconductor body comprises an SOI substrate and said isolation structure is a mesa isolation structure.
Claim 13
Dependent Claim
15 words
The method of claim 1, wherein said isolation structure is a shallow trench isolation structure.
Claim 14
Independent Claim
127 words
A method of forming a shallow trench isolation structure in a semiconductor body, comprising the steps of: forming a pad oxide on said semiconductor body; forming a pad nitride on said pad oxide; patterning and etching said pad nitride and pad oxide to form a hard mask; etching a trench in said semiconductor body using said hard mask; isotropically etching said pad oxide to undercut the pad oxide from said pad nitride a distance approximately equal to the thickness of said pad oxide; oxidizing said semiconductor body to form a sidewall oxide in said trench, wherein the radius of curvature of an upper corner of said trench is increased during said oxidizing step due to said isotropically etching step; and filling said trench with a dielectric material.
Claim 15
Independent Claim
127 words
A method of forming a shallow trench isolation structure in a semiconductor body, comprising the steps of: forming a pad oxide on said semiconductor body; forming a pad nitride on said pad oxide; patterning and etching said pad nitride and pad oxide to form a hard mask; etching a trench in said semiconductor body using said hard mask; isotropically etching said pad oxide to undercut the pad oxide from said pad nitride a distance approximately equal to the thickness of said pad oxide; oxidizing said semiconductor body to form a sidewall oxide in said trench, wherein the radius of curvature of an upper corner of said trench is increased during said oxidizing step due to said isotropically etching step; and filling said trench with a dielectric material.
Claim 16
Dependent Claim
26 words
The method of claim 13, wherein said isotropically etching step undercuts said pad oxide from said pad nitride a distance on the order of 10 nm.
Claim 17
Dependent Claim
35 words
The method of claim 13, wherein said oxidizing step comprises oxidation at a temperature on the order of 900° C. in the presence of O2 and HCl at a concentration on the order of 6%.
Claim 18
Dependent Claim
23 words
The method of claim 13, wherein said oxidizing step comprises a rapid thermal oxidation at a temperature on the order of 1100° C.
Claim 19
Dependent Claim
34 words
The method of claim 13, wherein said isotropically etching step comprises an oxide etch using an approximately 0.49 mole % solution of HF in water for a duration on the order of 70 seconds.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2002-01-25 | 2002-07-27 | 2003-01-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2006-01-25 | 2006-07-27 | 2007-01-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2010-01-25 | 2010-07-27 | 2011-01-26 | $7700.00 | Window Closed / Lapsed |