Abstract This invention is directed to a composite composition of particles of highly oriented graphite in the form of flakes having a hexagonal crystal orientation and an aspect ratio of at least 5 to 1 and a polymeric binder which when polymerized under compression forms a solid having a high thermal conductivity and low density and to a method of forming a machinable composite of high thermal conductivity comprising the steps of combining particles of highly oriented graphite flakes having an hexagonal crystal orientation and an aspect ratio of at least 5 to 1 with a polymeric binder to form a composition having at least a 40% graphite particle volume fraction, compressing the composition under a pressure sufficient to substantially align the particles parallel to one another and to the surface of the composition normal to the direction of the applied pressure until said binder polymerizes into a solid thereby forming an electrically conductive solid having a high thermal conductivity.
A method of forming a machinable composite of high thermal conductivity comprising the steps of combining particles of highly oriented graphite flakes having an hexagonal crystal orientation and an aspect ratio of at least 5 to 1 with a thermosetting or thermoplastic polymeric binder to form a composition having at least a 40% graphite particle volume fraction and molding the composition in a compression molding die at elevated pressure in a direction normal to the composition surface to substantially align the particles parallel to one another and normal to the direction of the applied pressure until said binder cures into a solid so that said particles are locked in alignment following solidification thereby forming an electrically conductive solid having a high thermal conductivity greater than 100 watts/meter-k.
Claim 2
Independent Claim
127 words
A method of forming a machinable composite of high thermal conductivity comprising the steps of combining particles of highly oriented graphite flakes having an hexagonal crystal orientation and an aspect ratio of at least 5 to 1 with a thermosetting or thermoplastic polymeric binder to form a composition having at least a 40% graphite particle volume fraction and molding the composition in a compression molding die at elevated pressure in a direction normal to the composition surface to substantially align the particles parallel to one another and normal to the direction of the applied pressure until said binder cures into a solid so that said particles are locked in alignment following solidification thereby forming an electrically conductive solid having a high thermal conductivity greater than 100 watts/meter-k.
Claim 3
Dependent Claim
19 words
A method as defined in claim 1 wherein said highly oriented graphite comprises thermally treated graphite and natural graphite.
Claim 4
Dependent Claim
21 words
A method as defined in claim 2 wherein said composition is formed having at least a 60% graphite particle volume fraction.
Claim 5
Dependent Claim
17 words
A method as defined in claim 3 wherein said applied pressure is above at least 10,000 psi.
Claim 6
Dependent Claim
15 words
A method as defined in claim 1 wherein said polymeric binder is a thermosetting resin.