Three-step nitride etching process for better critical dimension and better vertical sidewall profile
Assignee: Taiwan Semiconductor Manufacturing Co TSMC Ltd
•
Filing: 1996-03-25
•
Granted: 1998-12-29
•
Expires: 2016-03-25
Abstract
Abstract This invention describes a three-step process for etching a layer of silicon nitride over a thin layer of silicon dioxide on a semiconductor substrate for producing silicon nitride pattern with nearly vertical sidewalls, very small critical dimension bias and no trenching in the silicon dioxide, comprising a first step of a highly anisotropic etch process with a high etch rate, achieved by adding CHF 3 to the gaseous mixture of SF 6 and He, carried out at a relatively high power and low pressure, used to etch the bulk of the silicon nitride layer, a second step of lower etch anisotropy and etch rate, achieved by replacing CHF 3 with HBr, carried out at higher pressure and lower power, used to etch out the remainder of the nitride layer with a small over-etch beyond the end point, a third step of high Si 3 N 4 /SiO 2 etch selectivity, achieved by adding an oxidant to the reactive gas mixture, used to remove any remaining silicon nitride residues.
Inventors
- 👤 Shih Chang Huang
- 👤 Yuh Da Fan
- 👤 Yung-Jung Chang
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 15:31
CPC Classifications
H; H10; H10P; H10P70/00; H10P70/20; H10P70/23; H10P70/234; H10P50/00; H10P50/20; H10P50/28; H10P50/282; H10P50/283
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
101 words
A three-step method of etching silicon nitride layers over pad oxides in semiconductor integrated circuits, comprising the steps of: a first step of a main etch (ME1) using a reactive gas mixture of SF 6 , CHF 3 and He, to remove 80% to 90% of the silicon nitride layer; a second step of a main etch (ME2) using a reactive gas mixture of HBr, SF 6 and He to remove the remainder, except for any remaining residues, of the silicon nitride layer; and a third step of an over-etch (OE), to remove any of the remaining residues of silicon nitride.
Claim 2
Dependent Claim
101 words
A three-step method of etching silicon nitride layers over pad oxides in semiconductor integrated circuits, comprising the steps of: a first step of a main etch (ME1) using a reactive gas mixture of SF 6 , CHF 3 and He, to remove 80% to 90% of the silicon nitride layer; a second step of a main etch (ME2) using a reactive gas mixture of HBr, SF 6 and He to remove the remainder, except for any remaining residues, of the silicon nitride layer; and a third step of an over-etch (OE), to remove any of the remaining residues of silicon nitride.
Claim 3
Dependent Claim
45 words
The method of claim 1 wherein said first step etch ME1 uses a reactive gas mixture having a composition, as measured by the flow rates of individual gas components, of SF 6 at 180±20 sccm, CHF 3 at 20±2 sccm and He at 250±25 sccm.
Claim 4
Dependent Claim
32 words
The method of claim 1, wherein the process conditions for said first etch step ME1 are: gas pressure at 250±25 mTorr, RF power at 260 W±10%, and electrode gap at 1.05 cm±10%.
Claim 5
Dependent Claim
43 words
The method of claim 1 wherein said second etch step ME2 uses a reactive gas mixture having a composition, as measured by the flow rates of individual gas components, of HBr at 30±3 sccm, SF 6 at 120±12 sccm, He at 250±25 sccm.
Claim 6
Dependent Claim
33 words
The method of claim 1 wherein the process conditions for said second etch step ME2 are: gas pressure at 450±50 mTorr, RF power at 210 W±10%, and the electrode gap at 1.2 cm±10%.
Claim 7
Dependent Claim
33 words
The method of claim 1 wherein said second etch step ME2 is used to etch most of the remainder of the silicon nitride layer, except for any remaining residues to an end point.
Claim 8
Dependent Claim
24 words
The method of claim 1 wherein said third etch step OE uses a reactive gas mixture containing a gas component of O 2 .
Claim 9
Dependent Claim
20 words
The method of claim 1 wherein said third etch step OE uses a gas mixture containing no CHF 3 .
Claim 10
Dependent Claim
45 words
The method of claim 1 wherein said third etch step OE uses a reactive gas mixture having a composition, as measured by the flow rates of individual gas components, of HBr at 20±2 sccm, O 2 at 10±2 sccm, and SF 6 at 120±12 sccm.
Claim 11
Dependent Claim
33 words
The method of claim 1 wherein the process conditions for said third etch step OE are: gas pressure at 650±50 mTorr, RF power at 200±20 W, and the electrode gap at 1.2 cm±10%.
Claim 12
Independent Claim
142 words
A method of making a pattern with sharp vertical sidewalls and good critical dimensions in first layer film of silicon nitride over a second layer film of oxide, using a three-step etching process, comprising the steps of: a first main etch (ME1) in a plasma using a reactive gas mixture of SF 6 , CHF 3 and He, to remove 80 to 90% of said first layer film of silicon nitride, A second main etch (ME2) in a plasma using a reactive gas mixture of HBr, SF 6 and He to remove the remaining part of said first layer, except for any remaining residues, with an equivalent to 10±5% beyond the end point of the etching of said first layer, and A third etch step to clean up any residues of said first layer material left over on said second layer film.
Claim 13
Independent Claim
142 words
A method of making a pattern with sharp vertical sidewalls and good critical dimensions in first layer film of silicon nitride over a second layer film of oxide, using a three-step etching process, comprising the steps of: a first main etch (ME1) in a plasma using a reactive gas mixture of SF 6 , CHF 3 and He, to remove 80 to 90% of said first layer film of silicon nitride, A second main etch (ME2) in a plasma using a reactive gas mixture of HBr, SF 6 and He to remove the remaining part of said first layer, except for any remaining residues, with an equivalent to 10±5% beyond the end point of the etching of said first layer, and A third etch step to clean up any residues of said first layer material left over on said second layer film.
Claim 14
Dependent Claim
19 words
The method of claim 11 wherein the etch rate of ME1 is higher than the etch rate of ME2.
Claim 15
Dependent Claim
32 words
The method of claim 11 wherein the etch anisotropy, as defined by the ratio of the vertical to the lateral etch rate, for ME1 is larger than the etch anisotropy of ME2.
Claim 16
Dependent Claim
47 words
The method of claim 11 wherein the etch selectivity, as defined by the ratio of the etch rate of said first layer material to the etch rate of said second layer material of the third etch is greater than ME1 and ME2, and is greater than 5.
Claim 17
Independent Claim
113 words
A method of etching silicon nitride layers over pad oxides in semiconductor integrated circuits, comprising the steps of: performing a first etch step of said silicon nitride layer using a reactive gas mixture of SF 6 , CHF 3 and He, to remove a bulk of said silicon nitride layer; performing a second etch step to remove a remainder of said silicon nitride layer, except for any residues, using a reactive gas mixture of HBr, SF 6 and He, using a plasma etch at a higher power and lower pressure than in said first etch step; and performing a final etch step to remove any of the remaining residues of said silicon nitride.
Claim 18
Independent Claim
113 words
A method of etching silicon nitride layers over pad oxides in semiconductor integrated circuits, comprising the steps of: performing a first etch step of said silicon nitride layer using a reactive gas mixture of SF 6 , CHF 3 and He, to remove a bulk of said silicon nitride layer; performing a second etch step to remove a remainder of said silicon nitride layer, except for any residues, using a reactive gas mixture of HBr, SF 6 and He, using a plasma etch at a higher power and lower pressure than in said first etch step; and performing a final etch step to remove any of the remaining residues of said silicon nitride.
Claim 19
Dependent Claim
40 words
The method of claim 15 wherein said first etch step is performed at a flow rate of between 160 and 200 sccm SF 6 , between 18 and 22 sccm CHF 3 , and between 225 and 275 sccm He.
Claim 20
Dependent Claim
41 words
The method of claim 15, wherein said first etch step is performed at a gas pressure of between 225 and 275 mTorr, an RF power of between 234 and 286 W, and an electrode gap of between 0.945 and 1.155 cm.
Claim 21
Dependent Claim
38 words
The method of claim 15 wherein said second etch step is performed at a flow rate of between 27 and 33 sccm HBr, between 108 and 132 sccm SF 6 , and between 225 and 275 sccm He.
Claim 22
Dependent Claim
41 words
The method of claim 15 wherein said second etch step is performed at a gas pressure of between 400 and 500 mTorr, an RF power of between 189 and 231 W, and an electrode gap of between 1.08 and 1.32 cm.
Claim 23
Dependent Claim
24 words
The method of claim 15 wherein said third etch step uses a reactive gas mixture comprising HBr, O 2 , and SF 6 .
References Cited (Backward Citations)
US4374698A
Cited
US4793897A
Cited
US5015331A
Cited
US5013398A
Cited
US5431772A
Cited
US5354417A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2001-12-28 | 2002-06-29 | 2002-12-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2005-12-28 | 2006-06-29 | 2006-12-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2009-12-28 | 2010-06-29 | 2010-12-29 | $7700.00 | Window Closed / Lapsed |