Silylated rubber diene polymer containing organosilane
Assignee: Compagnie Generale des Etablissements Michelin SCA
•
Filing: 1996-04-30
•
Granted: 1998-10-13
•
Expires: 2016-04-30
Abstract
Abstract The present invention relates to a rubber composition reinforced by carbonlack and possibly silica, including at least one diene polymer functionalized or modified by an alkoxysilane derivative and at least one organosilane compound having a primary or secondary amine function or an imine function, which can be used for the manufacture of tires having, in particular, improved hysteresis properties.
Inventors
- 👤 Gerard Labauze
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 12:40
CPC Classifications
C; C08; C08L; C08L9/00; B; B60; B60C; B60C1/00; B60C1/0016; C08C; C08C19/00; C08C19/22; C08C19/25; C08C19/30; C08C19/42; C08C19/44; C08K; C08K3/00; C08K3/02; C08K3/04; C08K3/34; C08K3/36; C08K5/00; C08K5/54; C08K2201/00; C08K2201/002; C08K2201/006
Claims Analysis
Total Claims: 25
Claim 1
Independent Claim
197 words
A sulfur-vulcanizable rubber composition comprising at least one diene polymer terminated at one or more termini by an alkoxysilyl radical, carbon black or a mixture of carbon black and silica as reinforcing filler wherein said silica if present is an amount between 1% and 70% inclusive, by weight, of the total reinforcing filler, and at least one organosilane compound having an amine or imine functional group satisfying the general formula I: Z--R.sup.1 --Si(OR.sup.2).sub.3-n (R.sup.3).sub.n in which: Z represents a primary amine functional group, a cyclic or non-cyclic secondary amine functional group, an imine functional group, or a polyamine functional group; R 1 , R 2 , and R 3 , which may be identical or different, represent an alkyl, aryl, alkaryl or aralkyl radical having from 1 to 12 carbon atoms; n is a whole number selected from among the values of 0, 1, or 2 wherein said alkoxysilyl radical, with which said diene polymer is terminated, is distinct from the organosilane of general formula I and wherein said organosilane of general formula I is present in an amount between 0, 1 and 10 parts, inclusive, by weight to 100 parts of alkoxysilyl radical terminated diene polymers.
Claim 2
Dependent Claim
197 words
A sulfur-vulcanizable rubber composition comprising at least one diene polymer terminated at one or more termini by an alkoxysilyl radical, carbon black or a mixture of carbon black and silica as reinforcing filler wherein said silica if present is an amount between 1% and 70% inclusive, by weight, of the total reinforcing filler, and at least one organosilane compound having an amine or imine functional group satisfying the general formula I: Z--R.sup.1 --Si(OR.sup.2).sub.3-n (R.sup.3).sub.n in which: Z represents a primary amine functional group, a cyclic or non-cyclic secondary amine functional group, an imine functional group, or a polyamine functional group; R 1 , R 2 , and R 3 , which may be identical or different, represent an alkyl, aryl, alkaryl or aralkyl radical having from 1 to 12 carbon atoms; n is a whole number selected from among the values of 0, 1, or 2 wherein said alkoxysilyl radical, with which said diene polymer is terminated, is distinct from the organosilane of general formula I and wherein said organosilane of general formula I is present in an amount between 0, 1 and 10 parts, inclusive, by weight to 100 parts of alkoxysilyl radical terminated diene polymers.
Claim 3
Dependent Claim
29 words
The composition of claim 1, wherein the radical R 2 of the compound of general formula I is a lower alkyl radical having from 1 to 4 carbon atoms.
Claim 4
Dependent Claim
128 words
The composition of claim 1, wherein the diene polymer terminated at one or more termini by an alkoxysilyl radical has the general formula II: (Y)--R.sup.5 --Si(OR.sup.4).sub.2 --P (II) in which: Y represents a halogen, alkyl, epoxy, glycidyloxy, vinyl, or allyl radical; R 5 and R 4 , which are identical or different, represent an alkyl, aryl, alkylaryl or aralkyl radical having from 1 to 12 carbon atoms; and P represents the chain of a diene polymer selected from the group represented by any homopolymer obtained by polymerization of a conjugated diene monomer having from 4 to 12 carbon atoms, or any copolymer obtained by copolymerization of one or more dienes conjugated with each other or with one or more aromatic vinyl compounds having 8 to 20 carbon atoms.
Claim 5
Dependent Claim
16 words
The composition of claim 3, wherein (Y)--R 5 --Si(OR 4 )-- 2 represents 3-glycidyloxypropyldimethoxysilyl or 2-(3,4(epoxycyclo-hexyl)-ethyldimethoxysilyl.
Claim 6
Dependent Claim
17 words
The composition of claim 1, wherein said diene polymer is a butadiene-styrene copolymer or a butadiene-styrene-isoprene copolymer.
Claim 7
Dependent Claim
15 words
The composition of claim 1, wherein the carbon black represents all of the reinforcing filler.
Claim 8
Dependent Claim
31 words
The composition of claim 1, wherein the reinforcing filler is formed from a mixture of carbon black and silica, the silica representing up to 70% by weight of the total filler.
Claim 9
Dependent Claim
35 words
The composition of claim 7, wherein the silica is a highly dispersible precipitated silica having a surface area of 450 m 2 /g or less as measured by adsorption of cetyl trimethyl ammonium bromide (CTAB).
Claim 10
Dependent Claim
57 words
The composition of claim 8, wherein the silica has a BET specific surface area of between 100 and 300 m 2 /g, both inclusive, and a ratio of BET specific area to CTAB specific surface area of between 1 and 1.2, both inclusive wherein CTAB specific surface area is measured by adsorption of cetyl trimethyl ammonium bromide.
Claim 11
Independent Claim
227 words
A method of preparing a sulfur-vulcanizable rubber composition having a base of diene elastomer which has improved hysteresis properties, comprising a step of incorporating, by thermo-mechanical working, into a diene elastomer terminated at one or more termini by an alkoxysilyl radical, at least one organosilane compound of general formula I: Z--R.sup.1 --Si(OR.sup.2).sub.3-n --(R.sup.3).sub.n (I) in which: Z represents a primary amine functional group, a cyclic or non-cyclic secondary amine functional group, an imine functional group or a polyamine functional group; R 1 , R 2 , and R 3 , which are identical or different, represent an alkyl, aryl, alkaryl or aralkyl radical having from 1 to 12 carbon atoms; and n is a whole number selected from among the values of 0, 1, or 2, wherein said alkoxysilyl radical is distinct from said organosilane compound of general formula I, and wherein said organosilane of general formula I is present in an amount between 0.1 and 10 parts, inclusive, by weight, to 100 parts of alkoxysilyl radical terminated diene polymers; and a subsequent step of adding and incorporating at least one component comprising a reinforcing filler, a plasticizer, a pigment, an antioxidant, a lengthening oil, a silica coupling agent, a silica bonding agent, and/or a silica covering agent, wherein silica, if present, is an amount between 1% and 70%, inclusive, by weight, of the total reinforcing filler.
Claim 12
Independent Claim
227 words
A method of preparing a sulfur-vulcanizable rubber composition having a base of diene elastomer which has improved hysteresis properties, comprising a step of incorporating, by thermo-mechanical working, into a diene elastomer terminated at one or more termini by an alkoxysilyl radical, at least one organosilane compound of general formula I: Z--R.sup.1 --Si(OR.sup.2).sub.3-n --(R.sup.3).sub.n (I) in which: Z represents a primary amine functional group, a cyclic or non-cyclic secondary amine functional group, an imine functional group or a polyamine functional group; R 1 , R 2 , and R 3 , which are identical or different, represent an alkyl, aryl, alkaryl or aralkyl radical having from 1 to 12 carbon atoms; and n is a whole number selected from among the values of 0, 1, or 2, wherein said alkoxysilyl radical is distinct from said organosilane compound of general formula I, and wherein said organosilane of general formula I is present in an amount between 0.1 and 10 parts, inclusive, by weight, to 100 parts of alkoxysilyl radical terminated diene polymers; and a subsequent step of adding and incorporating at least one component comprising a reinforcing filler, a plasticizer, a pigment, an antioxidant, a lengthening oil, a silica coupling agent, a silica bonding agent, and/or a silica covering agent, wherein silica, if present, is an amount between 1% and 70%, inclusive, by weight, of the total reinforcing filler.
Claim 13
Dependent Claim
69 words
The process of claim 10, wherein the organosilane compound of general formula I is placed in the presence of the diene elastomer terminated at one or more termini by an alkoxysilyl radical, wherein said alkoxysilyl radical is distinct from said organosilane compound of general formula I, before any thermo-mechanical work and wherein the organosilane compound of general formula I is then incorporated into the elastomer by the thermo-mechanical working.
Claim 14
Dependent Claim
74 words
The process of claim 10, wherein the organosilane compound of general formula I is placed in the presence of the diene elastomer terminated at one or more termini by an alkoxysilyl radical, wherein said alkoxysilyl radical is distinct from said organosilane compound of general formula I after an initial phase of thermo-mechanical working of said diene elastomer, and wherein the organosilane compound of general formula I is incorporated into the elastomer by thermo-mechanical working.
Claim 15
Dependent Claim
102 words
The process of claim 10, wherein the elastomer, comprising at least one diene polymer terminated at one or more termini by an alkoxysilyl radical, wherein said alkoxysilyl radical is distinct from the organosilane compound of general formula I, the organosilane of formula I, and the carbon black, is subjected to a first phase of thermo-mechanical working, whereupon at least one component comprising a reinforcing filler, a plasticizer, a pigment, an antioxidant, a lengthening oil, a silica coupling agent, a silica bonding agent, and/or a silica covering agent is added, and wherein the thermo-mechanical working is continued for a suitable period of time.
Claim 16
Dependent Claim
126 words
The process of claim 12, wherein the reinforcing filler is formed of carbon black and silica, comprising adding in succession to the elastomer which has undergone an initial phase of thermo-mechanical working, in the following order, the organosilane agent of formula I, then silica and a bonding agent, then a lengthening oil, and finally carbon black with stearic acid and an antioxidizing agent, recovering and cooling the elastomeric block formed, adding and incorporating in a second thermo-mechanical working step at least one component comprising a reinforcing filler, a plasticizer, a pigment, an antioxidant, a lengthening oil, a silica coupling agent, a silica bonding agent, and/or a silica covering agent, recovering the mixture, and in a finishing step, incorporating a vulcanization system and recovering the vulcanizable composition.
Claim 17
Dependent Claim
207 words
A tire having improved resistance to rolling, containing a sulfur-vulcanizable rubber composition comprising at least one diene polymer terminated at one or more termini by an alkoxysilyl radical, carbon black or a mixture of carbon black and silica as reinforcing filler, wherein said silica, if present, is present in an amount between 1% and 70%, inclusive, by weight, of the total reinforcing filler, and at least one organosilane compound comprising an amine or imine function having the general formula I: Z--R.sup.1 --Si(OR.sup.2).sub.3-n (R.sup.3).sub.n (I) in which: Z represents a primary amine functional group, a cyclic or non-cyclic secondary amine functional group or an imine functional group or a polyamine functional group; R 1 , R 2 , and R 3 , which are identical or different, represent an alkyl, aryl, alkaryl or aralkyl radical having from 1 to 12 carbon atoms; and n is a whole number selected from among the values of 0, 1, or 2, wherein the alkoxysilyl radical, with which the diene polymer is terminated is distinct from the organosilane of general formula I, and wherein said organosilane of general formula I is present in an amount between 0.1 and 10 parts, inclusive, by weight, to 100 parts of alkoxysilyl radical terminated diene polymers.
Claim 18
Dependent Claim
207 words
A tire having improved resistance to rolling, containing a sulfur-vulcanizable rubber composition comprising at least one diene polymer terminated at one or more termini by an alkoxysilyl radical, carbon black or a mixture of carbon black and silica as reinforcing filler, wherein said silica, if present, is present in an amount between 1% and 70%, inclusive, by weight, of the total reinforcing filler, and at least one organosilane compound comprising an amine or imine function having the general formula I: Z--R.sup.1 --Si(OR.sup.2).sub.3-n (R.sup.3).sub.n (I) in which: Z represents a primary amine functional group, a cyclic or non-cyclic secondary amine functional group or an imine functional group or a polyamine functional group; R 1 , R 2 , and R 3 , which are identical or different, represent an alkyl, aryl, alkaryl or aralkyl radical having from 1 to 12 carbon atoms; and n is a whole number selected from among the values of 0, 1, or 2, wherein the alkoxysilyl radical, with which the diene polymer is terminated is distinct from the organosilane of general formula I, and wherein said organosilane of general formula I is present in an amount between 0.1 and 10 parts, inclusive, by weight, to 100 parts of alkoxysilyl radical terminated diene polymers.
Claim 19
Dependent Claim
21 words
(Twice Amended) The tire of claim 15, wherein the tire comprises a tread formed at least in part from the composition.
Claim 20
Dependent Claim
204 words
A tire tread comprising a sulfur-vulcanizable rubber composition comprising at least one diene polymer terminated at one or more termini by an alkoxysilyl radical, carbon black or a mixture of carbon black and silica as reinforcing filler, wherein said silica, if present, is present in an amount between 1% and 70% inclusive, by weight, of the total reinforcing filler, and at least one organosilane compound comprising an amine or imine functional group of a general formula I: Z--R.sup.1 --Si(OR.sup.2).sub.3-n (R.sup.3).sub.n (I) in which: Z represents a primary amine functional group, a cyclic or non-cyclic secondary amine functional group, or an imine functional group, or a polyamine functional group; R 1 , R 2 , and R 3 , which are identical or different, represent an alkyl, aryl, alkaryl or aralkyl radical having from 1 to 12 carbon atoms; and n is a whole number selected from among the values of 0, 1, or 2, wherein the alkoxysilyl radical, with which the diene polymer is terminated is distinct from the organosilane of general formula I, and wherein said organosilane of general formula I is present in an amount between 0.1 and 10 parts, inclusive, by weight, to 100 parts of alkoxysilyl radical terminated diene polymers.
Claim 21
Dependent Claim
204 words
A tire tread comprising a sulfur-vulcanizable rubber composition comprising at least one diene polymer terminated at one or more termini by an alkoxysilyl radical, carbon black or a mixture of carbon black and silica as reinforcing filler, wherein said silica, if present, is present in an amount between 1% and 70% inclusive, by weight, of the total reinforcing filler, and at least one organosilane compound comprising an amine or imine functional group of a general formula I: Z--R.sup.1 --Si(OR.sup.2).sub.3-n (R.sup.3).sub.n (I) in which: Z represents a primary amine functional group, a cyclic or non-cyclic secondary amine functional group, or an imine functional group, or a polyamine functional group; R 1 , R 2 , and R 3 , which are identical or different, represent an alkyl, aryl, alkaryl or aralkyl radical having from 1 to 12 carbon atoms; and n is a whole number selected from among the values of 0, 1, or 2, wherein the alkoxysilyl radical, with which the diene polymer is terminated is distinct from the organosilane of general formula I, and wherein said organosilane of general formula I is present in an amount between 0.1 and 10 parts, inclusive, by weight, to 100 parts of alkoxysilyl radical terminated diene polymers.
Claim 22
Dependent Claim
41 words
The composition according to claim 1, 3, 4, 5, 6, 7, 8, or 9 wherein the radicals R 1 , R 2 , and R 3 , which may be identical or different, each have from one to four carbon atoms.
Claim 23
Dependent Claim
38 words
The process according to claim 10, 11, 12, 13, or 14 wherein the radicals R 1 , R 2 , and R 3 , which may be identical or different, each have from one to four carbon atoms.
Claim 24
Dependent Claim
35 words
The tire according to claim 15, or 16 wherein the radicals R 1 , R 2 , and R 3 , which may be identical or different, each have from one to four carbon atoms.
Claim 25
Dependent Claim
34 words
The tire tread according to claim 17 wherein the radicals R 1 , R 2 , and R 3 , which may be identical or different, each have from one to four carbon atoms.
References Cited (Backward Citations)
US3135716A
Cited
US3244644A
Cited
US3281383A
Cited
US3595830A
Cited
US3773732A
Cited
US4185042A
Cited
US4550142A
Cited
US5066721A
Cited
US4820751A
Cited
US5017636A
Cited
US5409969A
Cited
US5496883A
Cited
US5496883B1
Cited
US5159009A
Cited
US5227425A
Cited
US5401789A
Cited
US5508333A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2001-10-12 | 2002-04-13 | 2002-10-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2005-10-12 | 2006-04-13 | 2006-10-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2009-10-12 | 2010-04-13 | 2010-10-13 | $7700.00 | Window Closed / Lapsed |