Processing of hydroxylapatite coatings on titanium alloy bone prostheses
Assignee: Los Alamos National Security LLC
•
Filing: 1995-12-01
•
Granted: 1998-10-06
•
Expires: 2015-12-01
Abstract
Abstract Processing of hydroxylapatite sol-gel films on titanium alloy bone prostheses. A method utilizing non-line-of-sight ion beam implantation and/or rapid thermal processing to provide improved bonding of layers of hydroxylapatite to titanium alloy substrates while encouraging bone ingrowth into the hydroxylapatite layers located away from the substrate, is described for the fabrication of prostheses. The first layer of hydroxylapatite is mixed into the substrate by the ions or rapidly thermally annealed, while subsequent layers are heat treated or densified using ion implantation to form layers of decreasing density and larger crystallization, with the outermost layers being suitable for bone ingrowth.
Inventors
- 👤 Michael A. Nastasi
- 👤 Timothy E. Levine
- 👤 James W. Mayer
- 👤 Vincent B. Pizziconi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 22:21
CPC Classifications
A; A61; A61L; A61L27/00; A61L27/28; A61L27/30; A61L27/32; A61F; A61F2/00; A61F2/02; A61F2/30; A61F2/30767; A61L27/02; A61L27/04; A61L27/06; C; C23; C23C; C23C14/00; C23C14/22; C23C14/48; A61F2/3094; A61F2310/00; A61F2310/00005; A61F2310/00011; A61F2310/00023; A61F2310/00389; A61F2310/00592; A61F2310/00796
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
95 words
A method for strengthening the adhesion of hydroxylapatite coatings to titanium alloy prostheses, which comprises the steps of: a. preparing a sol-gel of hydroxylapatite; b. coating the titanium alloy prosthesis with a layer of the sol-gel having a chosen thickness; c. causing the sol-gel layer to densify; and d. intermixing the titanium alloy with hydroxylapatite and further densifying the hardened hydroxylapatite layer using non-line-of-sight ion-implantation; wherein the thickness of the sol-gel layer is chosen such that ions from said ion implantation step can penetrate the densified hydroxylapatite layer and travel into the titanium alloy prosthesis.
Claim 2
Independent Claim
95 words
A method for strengthening the adhesion of hydroxylapatite coatings to titanium alloy prostheses, which comprises the steps of: a. preparing a sol-gel of hydroxylapatite; b. coating the titanium alloy prosthesis with a layer of the sol-gel having a chosen thickness; c. causing the sol-gel layer to densify; and d. intermixing the titanium alloy with hydroxylapatite and further densifying the hardened hydroxylapatite layer using non-line-of-sight ion-implantation; wherein the thickness of the sol-gel layer is chosen such that ions from said ion implantation step can penetrate the densified hydroxylapatite layer and travel into the titanium alloy prosthesis.
Claim 3
Dependent Claim
65 words
The method as described in claim 1, further comprising the steps of: a. coating the ion-implanted titanium alloy prosthesis with a second layer of hydroxylapatite sol-gel; b. curing the prosthesis coated thereby to drive off water; and c. heating the coated and cured prosthesis to densify the second layer of hydroxylapatite, wherein the second layer has a density and crystallization suitable for ingrowth of bone.
Claim 4
Dependent Claim
38 words
The method as described in claim 1, further comprising the step of coating the ion-beam-implanted titanium alloy prosthesis with a second layer of hydroxylapatite, wherein the second layer has a density and crystallization suitable for ingrowth of bone.
Claim 5
Dependent Claim
25 words
The method as described in claim 1, wherein said step of causing the sol-gel layer to harden and density is accomplished using rapid thermal annealing.
Claim 6
Dependent Claim
23 words
The method as described in claim 2, wherein said step of heating the coated and cured prosthesis is accomplished using rapid thermal annealing.
Claim 7
Independent Claim
132 words
A method for strengthening the adhesion of hydroxylapatite coatings to titanium alloy prostheses, which comprises the steps of: a. preparing a first sol-gel of hydroxylapatite having a chosen density; b. coating the titanium alloy prosthesis with the sol-gel; c. curing the coated prosthesis to form a first hard layer of hydroxylapatite; d. densifying the first layer of hydroxylapatite such that the first layer of hydroxylapatite has acceptable binding characteristics to the prosthesis; e. preparing a second sol-gel of hydroxylapatite having a lower density than the first sol-gel thereof; f. coating the densified hydroxylapatite layer with the second layer of hydroxylapatite sol-gel; g. curing the coated prosthesis to form a second hard layer of hydroxylapatite; and h. densifying the second layer of hydroxylapatite such that the second layer is suitable for bone ingrowth.
Claim 8
Independent Claim
132 words
A method for strengthening the adhesion of hydroxylapatite coatings to titanium alloy prostheses, which comprises the steps of: a. preparing a first sol-gel of hydroxylapatite having a chosen density; b. coating the titanium alloy prosthesis with the sol-gel; c. curing the coated prosthesis to form a first hard layer of hydroxylapatite; d. densifying the first layer of hydroxylapatite such that the first layer of hydroxylapatite has acceptable binding characteristics to the prosthesis; e. preparing a second sol-gel of hydroxylapatite having a lower density than the first sol-gel thereof; f. coating the densified hydroxylapatite layer with the second layer of hydroxylapatite sol-gel; g. curing the coated prosthesis to form a second hard layer of hydroxylapatite; and h. densifying the second layer of hydroxylapatite such that the second layer is suitable for bone ingrowth.
Claim 9
Dependent Claim
22 words
The method as described in claim 6, wherein said step of densifying a layer of hydroxylapatite is accomplished using rapid thermal annealing.
Claim 10
Dependent Claim
22 words
The method as described in claim 6, wherein said step of densifying a layer of hydroxylapatite is accomplished using non-line-of-sight ion implantation.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2001-10-05 | 2002-04-06 | 2002-10-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2005-10-05 | 2006-04-06 | 2006-10-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2009-10-05 | 2010-04-06 | 2010-10-06 | $7700.00 | Window Closed / Lapsed |