Epihalohydrin electrical stress controlling material
Assignee: 3M Co
•
Filing: 1996-08-08
•
Granted: 1998-09-08
•
Expires: 2016-08-08
Abstract
Abstract A non-tacky electrical stress control material comprising a) about 100 parts of a resin component containing 1) from about 20% to about 80% of an epihalohydrin polymer, and 2) correspondingly, from about 80% to about 20% of an insulating silicone polymer having a tan δ of less than one, b) from about 10 to about 200 parts of a filler, said filler being nonconductive at room temperature, selected from the group consisting of barium titanate and hydrated aluminum silicate, and c) from 0 to 30 parts of a plasticizer.
Inventors
- 👤 Thomas J. D. Heyer
- 👤 Robert A. Wandmacher
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 13:18
CPC Classifications
H; H02; H02G; H02G15/00; H02G15/02; H02G15/06; H02G15/064; H02G15/068; C; C08; C08L; C08L71/00; C08L71/02; C08L71/03; C08L83/00; C08L83/04; H01; H01B; H01B3/00; H01B3/18; H01B3/30; H01B3/42; H01B3/427; H01B3/46; C08G; C08G77/00; C08G77/04
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
147 words
A non-tacky electrical stress control material comprising a mixture of a) about 100 parts by weight of a resin component consisting of a blend of 1) from about 20% by weight to about 80% by weight of an epihalohydrin polymer, and 2) correspondingly, from about 80% by weight to about 20% by weight of an insulating silicone polymer having a tan δ of less than one, such silicone being a gum silicone having a durometer of from about 5 to about 30 b) from about 10 to about 200 parts by weight per hundred parts by weight resin component of barium titanate, and c) from 0 to 30 parts by weight of a plasticizer, said material having a permittivity greater than about 15, and a tan δ of less than 4 when tested under electrical stress of from at least about 3 kV to about 20 kV/cm.
Claim 2
Dependent Claim
147 words
A non-tacky electrical stress control material comprising a mixture of a) about 100 parts by weight of a resin component consisting of a blend of 1) from about 20% by weight to about 80% by weight of an epihalohydrin polymer, and 2) correspondingly, from about 80% by weight to about 20% by weight of an insulating silicone polymer having a tan δ of less than one, such silicone being a gum silicone having a durometer of from about 5 to about 30 b) from about 10 to about 200 parts by weight per hundred parts by weight resin component of barium titanate, and c) from 0 to 30 parts by weight of a plasticizer, said material having a permittivity greater than about 15, and a tan δ of less than 4 when tested under electrical stress of from at least about 3 kV to about 20 kV/cm.
Claim 3
Dependent Claim
42 words
A non-tacky electrical stress control material according to claim 1 wherein said resin component consists of about 30% by weight to about 70% by weight of an epihalohydrin polymer, and correspondingly, from about 70% to about 30% of said insulating silicone polymer.
Claim 4
Dependent Claim
26 words
A non-tacky electrical stress control material according to claim 1 wherein said plasticizer comprises from about 5 to about 15 parts per hundred parts resin component.
Claim 5
Dependent Claim
43 words
A non-tacky electrical stress control material according to claim 1 wherein said plasticizer is selected from the group consisting of trimellitates, phthalates, benzoates, fatty acid ester derivatives, fatty acid ester alcohols, dimer acid esters, glutarates, adipates, sebacates, polymeric polyesters, rosin esters, acrylate esters.
Claim 6
Dependent Claim
31 words
A non-tacky electrical stress control material according to claim 1 further comprising from about 1 part to about 15 parts per hundred parts of the resin component, of a metal flake.
Claim 7
Dependent Claim
17 words
A non-tacky electrical stress control material according to claim 5 wherein said metal flake is aluminum flake.
Claim 8
Dependent Claim
21 words
A non-tacky electrical stress control material according to claim 1 wherein said material has a permittivity of at least about 25.
Claim 9
Dependent Claim
53 words
A non-tacky electrical stress control material according to claim 1 wherein said resin component consists of about 20% by weight to about 40% by weight of an epihalohydrin polymer, and correspondingly, from about 80% by weight to about 60% by weight of a silicone polymer having a tan δ of less than one.
References Cited (Backward Citations)
US3515798A
Cited
US3859576A
Cited
US4017652A
Cited
US4017652B1
Cited
US4378463A
Cited
FR2371804A1
Cited
US4203886A
Cited
US4383131A
Cited
US4265800A
Cited
US4363842A
Cited
US4412029A
Cited
EP0279414A2
Cited
US5010137A
Cited
EP0424090B1
Cited
EP0435554A2
Cited
US5455383A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2001-09-07 | 2002-03-09 | 2002-09-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2005-09-07 | 2006-03-09 | 2006-09-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2009-09-07 | 2010-03-09 | 2010-09-08 | $7700.00 | Window Closed / Lapsed |