Coating solution for silica-based coating film and method for the preparation thereof
Assignee: Tokyo Ohka Kogyo Co Ltd
•
Filing: 1997-09-23
•
Granted: 1998-08-18
•
Expires: 2017-09-23
Abstract
Abstract Proposed is a coating solution for the formation of a silica-based coating film on the surface of a substrate used in the manufacturing process of semiconductor devices as well as a method for the coating solution, which exhibits excellent storage stability without gelation and is capable of forming a silica-based coating film free from the troubles due to evolution of gases such as crack formation even when the coating film has a relatively large thickness. The coating solution is prepared by the hydrolysis reaction of a trialkoxy silane such as triethoxy silane dissolved in propyleneglycol dimethyl ether in a specified concentration with addition of a specified amount of water followed by removal of the alcohol formed by the hydrolysis reaction of the trialkoxy silane by distillation to such an extent that the content of the alcohol in the coating solution does not exceed 10% by weight or, preferably, 3% by weight.
Inventors
- 👤 Yoshinori Sakamoto
- 👤 Yoshio Hagiwara
- 👤 Toshimasa Nakayama
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 20:22
CPC Classifications
C; C08; C08J; C08J3/00; C08J3/02; C08J3/09; C08J3/091; C08J3/095; C08G; C08G77/00; C08G77/04; C08G77/06; C09; C09D; C09D183/00; C09D183/04; H; H10; H10P; H10P14/00; H10P14/60; C08J2383/00; C08J2383/04
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
193 words
A method for the preparation of a coating solution for the formation of a silica-based coating film on a substrate surface which comprises the steps of: (a) dissolving a trialkoxy silane compound, of which the alkoxy group has 1 to 4 carbon atoms, in an alkyleneglycol dialkyl ether represented by the general formula ##STR3## in which each R is, independently from the other, an alkyl group having 1 to 4 carbon atoms and the subscript n is 3 or 4, as a solvent in a concentration in the range from 1 to 5% by weight calculated as SiO 2 to give a silane solution; (b) adding, to the silane solution, water in an amount in the range from 2.5 to 3.0 moles per mole of the trialkoxy silane compound; (c) adding, to the silane solution, an acid in a catalytic amount as a catalyst for the hydrolysis reaction of the trialkoxy silane compound; and (d) effecting hydrolysis of the trialkoxy silane compound to form a hydrolysis product thereof dissolved in a solvent system comprising the alkyleneglycol dialkyl ether and the alcohol as a by-product of the hydrolysis reaction of the trialkoxy silane compound.
Claim 2
Independent Claim
193 words
A method for the preparation of a coating solution for the formation of a silica-based coating film on a substrate surface which comprises the steps of: (a) dissolving a trialkoxy silane compound, of which the alkoxy group has 1 to 4 carbon atoms, in an alkyleneglycol dialkyl ether represented by the general formula ##STR3## in which each R is, independently from the other, an alkyl group having 1 to 4 carbon atoms and the subscript n is 3 or 4, as a solvent in a concentration in the range from 1 to 5% by weight calculated as SiO 2 to give a silane solution; (b) adding, to the silane solution, water in an amount in the range from 2.5 to 3.0 moles per mole of the trialkoxy silane compound; (c) adding, to the silane solution, an acid in a catalytic amount as a catalyst for the hydrolysis reaction of the trialkoxy silane compound; and (d) effecting hydrolysis of the trialkoxy silane compound to form a hydrolysis product thereof dissolved in a solvent system comprising the alkyleneglycol dialkyl ether and the alcohol as a by-product of the hydrolysis reaction of the trialkoxy silane compound.
Claim 3
Dependent Claim
61 words
The method for the preparation of a coating solution as claimed in claim 1 in which the solution obtained in step (d) is further subjected to: (e) removal of the alcohol in the solvent system by distillation to such an extent that the amount of the alcohol does not exceed 10% by weight based on the total amount of the solution.
Claim 4
Dependent Claim
51 words
The method for the preparation of a coating solution as claimed in claim 2 in which removal of the alcohol by distillation in step (e) is performed to such an extent that the amount of the alcohol does not exceed 8% by weight based on the total amount of the solution.
Claim 5
Dependent Claim
51 words
The method for the preparation of a coating solution as claimed in claim 3 in which removal of the alcohol by distillation in step (e) is performed to such an extent that the amount of the alcohol does not exceed 3% by weight based on the total amount of the solution.
Claim 6
Dependent Claim
60 words
The method for the preparation of a coating solution as claimed in claim 2 in which the distillation of the solution in step (e) is performed to such an extent that the concentration of the hydrolysis product of the trialkoxy silane compound in the solution is in the range from 7 to 13% by weight calculated as SiO 2 .
Claim 7
Dependent Claim
41 words
The method for the preparation of a coating solution as claimed in claim 2 in which the distillation of the solution in step (e) is performed at a temperature in the range from 20° to 50° C. under a reduced pressure.
Claim 8
Dependent Claim
46 words
The method for the preparation of a coating solution as claimed in claim 1 in which the concentration of the trialkoxy silane compound in the silane solution prepared in step (a) is in the range from 2 to 4% by weight calculated as SiO 2 .
Claim 9
Dependent Claim
45 words
The method for the preparation of a coating solution as claimed in claim 1 in which the amount of the water added to the silane solution in step (b) is in the range from 2.8 to 3.0 moles per mole of the trialkoxy silane compound.
Claim 10
Dependent Claim
29 words
The method for the preparation of a coating solution as claimed in claim 1 in which the acid added to the silane solution in step (c) is nitric acid.
Claim 11
Dependent Claim
53 words
The method for the preparation of a coating solution as claimed in claim 9 in which the amount of the nitric acid added to the silane solution in step (c) is in the range from 0.1 to 500 ppm by weight based on the overall amount of the silane solution in step (b).
Claim 12
Dependent Claim
24 words
The method for the preparation of a coating solution as claimed in claim 1 in which the alkyleneglycol dialkyl ether is propyleneglycol dimethyl ether.
Claim 13
Dependent Claim
36 words
The method for the preparation of a coating solution as claimed in claim 1 in which the trialkoxy silane compound is selected from the group consisting of trimethoxy silane, triethoxy silane, tripropoxy silane and tributoxy silane.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2001-08-17 | 2002-02-16 | 2002-08-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2005-08-17 | 2006-02-16 | 2006-08-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2009-08-17 | 2010-02-16 | 2010-08-18 | $7700.00 | Window Closed / Lapsed |