Method of making a sintered article
Assignee: Federal Mogul Coventry Ltd
•
Filing: 1995-03-16
•
Granted: 1998-07-21
•
Expires: 2015-03-16
Abstract
Abstract A method of making a sintered article is disclosed, the method comprising the steps of mixing a prealloyed ferrous powder having a composition in the following ranges in weight %: carbon 0.7-2.7/chromium 3-6/cobalt 5-10/vanadium 0.5-3/molybdenum 6-11/silicon 0.3-2/ others total 2 max/balance iron and optionally up to 3 wt % tungsten, with an addition of carbon powder of at least 0.1 wt %, compacting said powder mixture by uniaxial pressing to form a green compact of near net shape, sintering said green compact in a continuous gas atmosphere sintering furnace at a temperature in the range from 1130° C. to 1250° C. such that the final density of said sintered material is greater than 95% of the theoretical density as a result of the sintering operation alone.
Inventors
- 👤 Charles Grant Purnell
- 👤 Leslie John Farthing
- 👤 David Holme
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 09:15
CPC Classifications
C; C22; C22C; C22C33/00; C22C33/02; C22C33/0257; C22C33/0278; C22C33/0285; B; B22; B22F; B22F3/00; B22F3/10; B22F3/1003; B22F3/1007; B22F2201/00; B22F2201/01; B22F2201/013; B22F2201/02; B22F2998/00; B22F2999/00; Y; Y10; Y10S; Y10S75/00; Y10S75/95
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
134 words
A method of making a sintered article, the method comprising the steps of mixing a prealloyed ferrous powder having a composition in the following ranges in weight %: carbon 0.7-2.7 / chromium 3-6 / cobalt 5-10 / vanadium 0.5-3 / molybdenum 6-11 / silicon 0.3-2 / others total 2 max/balance iron and optionally up to 3 wt % of tungsten, with an addition of carbon powder of at least 0.10 wt %, compacting said powder mixture by uniaxial pressing to form a green compact, sintering said green compact in a continuous sintering furnace, having a gas atmosphere, at a temperature in the range from 1130° C. to 1250° C. such that the final density of said sintered material is greater than 95% of the theoretical density as a result of the sintering operation alone.
Claim 2
Independent Claim
134 words
A method of making a sintered article, the method comprising the steps of mixing a prealloyed ferrous powder having a composition in the following ranges in weight %: carbon 0.7-2.7 / chromium 3-6 / cobalt 5-10 / vanadium 0.5-3 / molybdenum 6-11 / silicon 0.3-2 / others total 2 max/balance iron and optionally up to 3 wt % of tungsten, with an addition of carbon powder of at least 0.10 wt %, compacting said powder mixture by uniaxial pressing to form a green compact, sintering said green compact in a continuous sintering furnace, having a gas atmosphere, at a temperature in the range from 1130° C. to 1250° C. such that the final density of said sintered material is greater than 95% of the theoretical density as a result of the sintering operation alone.
Claim 3
Dependent Claim
18 words
A method according to claim 1 wherein the prealloyed powder contains a minimum of 0.1 wt % tungsten.
Claim 4
Dependent Claim
39 words
A method according to claim 1 wherein the composition of the prealloyed powder lies in the ranges in wt %: carbon 0.7-1.6/ chromium 3-4.25/ cobalt 7.5-8.5/ vanadium 1-1.3/ tungsten 1-2/ molybdenum 9-10/silicon 0.3-1.5/ others total 2 max/ balance iron.
Claim 5
Dependent Claim
19 words
A method according to claim 1 wherein the total carbon content of the sintered article is 1-2.0 wt %.
Claim 6
Dependent Claim
20 words
A method according to claim 1 wherein the powder mixture contains a minimum of 0.3 wt % additional carbon powder.
Claim 7
Dependent Claim
17 words
A method according to claim 1 wherein the maximum addition of free carbon is 0.8 wt. %.
Claim 8
Dependent Claim
17 words
A method according to claim 1 further including a pre-sintering step at temperatures up to 1120° C.
Claim 9
Dependent Claim
25 words
A method according to claim 1 wherein the sintering step is carried out under a continuous gas atmosphere comprising a mixture of hydrogen and nitrogen.
Claim 10
Dependent Claim
17 words
A method according to claim 8 wherein said gas atmosphere comprises up to 30 volume % hydrogen.
Claim 11
Dependent Claim
19 words
A method according to claim 1 wherein the green density of the article is less than 85% of theoretical.
Claim 12
Dependent Claim
23 words
A method according to claim 1 wherein the density of the final sintered article is greater than about 97% of full theoretical density.
Claim 13
Dependent Claim
31 words
A method according to claim 1 further including the step of heat treating the article after sintering to produce a predominantly pearlitic structure having a uniform distribution of free carbides therein.
Claim 14
Dependent Claim
15 words
A method according to claim 12 wherein the heat treatment is an isothermal heat treatment.
Claim 15
Dependent Claim
66 words
A sintered iron-based alloy article when made by claim from 1, the article comprising a composition lying in the ranges in weight % of: carbon 0.8-3/ chromium 3-6/ cobalt 5-10/ vanadium 0.5-3/ molybdenum 6-11/ silicon 0.3-2/ others total 2 max/ balance iron and optionally up to 3 wt % tungsten, the article having a sintered density of greater than 95% of the alloy's full theoretical density.
Claim 16
Dependent Claim
16 words
A sintered article according to claim 14 further including a minimum of 0.1 wt % tungsten.
Claim 17
Dependent Claim
23 words
A sintered article according to claim 14 wherein the microstructure contains free carbides having a size range from 1 μm to 1 μm.
Claim 18
Dependent Claim
7 words
A sintered article according to claim 14.
Claim 19
Dependent Claim
18 words
A sintered article according to claim 17 and having a hardness of from 35 HRC to 45 HRC.
Claim 20
Dependent Claim
21 words
A sintered article according to claim 14 wherein the sintered article is a valve seat insert for an internal combustion engine.
References Cited (Backward Citations)
US4909843A
Cited
US4985309A
Cited
US4970049A
Cited
US5462573A
Cited
US5403371A
Cited
US5009842A
Cited
US5356453A
Cited
US5571305A
Cited
US5522914A
Cited
US5498483A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2001-07-20 | 2002-01-19 | 2002-07-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2005-07-20 | 2006-01-19 | 2006-07-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2009-07-20 | 2010-01-19 | 2010-07-21 | $7700.00 | Window Closed / Lapsed |