Rechargeable alkaline silver-zinc cell with improved negative electrode
Assignee: Yardney Technical Products Inc
•
Filing: 1996-10-02
•
Granted: 1998-06-30
•
Expires: 2016-10-02
Abstract
Abstract Substantial improvements to the cycle life of silverzinc cells were obtained by the addition of small amounts of bismuth oxide (Bi2O3) to the negative zinc electrode, in conjunction with cadmium oxide (CdO) and lead oxide (PbO). These improvements, which can be extended to other zinc-based alkaline batteries, especially nickel-zinc and zinc-air, can also be realized in conjunction with other metal oxides and hydroxides, particularly indium hydroxide [In(OH)3], which, like Bi2O3, has the additional advantage of being non-toxic.
Inventors
- 👤 Jose R. Serenyi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 10:10
CPC Classifications
H; H01; H01M; H01M4/00; H01M4/02; H01M4/24; H01M4/244; H01M10/00; H01M10/24; H01M10/32; H01M50/00; H01M50/40; H01M50/409; H01M50/411; H01M50/414; H01M50/423; H01M50/429; H01M50/449; H01M50/454; H01M50/457; H01M4/62; H01M50/44; Y; Y02; Y02E; Y02E60/00; Y02E60/10
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
119 words
A rechargeable alkaline silver-zinc electrochemical cell comprising, a positive and a negative electrode having a separator therebetween containing an alkaline electrolyte, said positive electrode containing silver as a positive active material, said negative electrode comprising predominantly zinc or zinc oxide as the negative active material and an additive consisting essentially of bismuth oxide and at least one additional oxide or hydroxide of a metal selected from the group consisting of lead, cadmium and indium, the amount of said bismuth oxide ranging from about 2.0% by wt. to about 10% by wt and the amount of said additional oxide or hydroxide in each instance ranging from about 0.25% by wt. to about 2% by wt. of said negative active material.
Claim 2
Dependent Claim
119 words
A rechargeable alkaline silver-zinc electrochemical cell comprising, a positive and a negative electrode having a separator therebetween containing an alkaline electrolyte, said positive electrode containing silver as a positive active material, said negative electrode comprising predominantly zinc or zinc oxide as the negative active material and an additive consisting essentially of bismuth oxide and at least one additional oxide or hydroxide of a metal selected from the group consisting of lead, cadmium and indium, the amount of said bismuth oxide ranging from about 2.0% by wt. to about 10% by wt and the amount of said additional oxide or hydroxide in each instance ranging from about 0.25% by wt. to about 2% by wt. of said negative active material.
Claim 3
Dependent Claim
32 words
A rechargeable alkaline silver-zinc electrochemical cell according to claim 1, wherein the amount of bismuth oxide ranges from about 2% by wt. to about 5% by wt. of said negative active material.
Claim 4
Dependent Claim
33 words
A rechargeable alkaline silver-zinc electrochemical cell according to claim 1, wherein said at least one additional oxide or hydroxide is selected from the group consisting of lead oxide, cadmium oxide, and indium hydroxide.
Claim 5
Dependent Claim
19 words
A rechargeable alkaline silver-zinc electrochemical cell according to claim 3, wherein said additive comprises bismuth oxide and lead oxide.
Claim 6
Dependent Claim
33 words
A rechargeable alkaline silver-zinc electrochemical cell according to claim 4, wherein the amount of said lead oxide ranges from about 0.5% by wt. to about 2% by wt. of said negative active material.
Claim 7
Dependent Claim
19 words
A rechargeable alkaline silver-zinc electrochemical cell according to claim 3, wherein said additive comprises bismuth oxide and cadmium oxide.
Claim 8
Dependent Claim
33 words
A rechargeable alkaline silver-zinc electrochemical cell according to claim 6, wherein the amount of said cadmium oxide ranges from about 1.0% by wt. to about 2% by wt. of said negative active material.
Claim 9
Dependent Claim
19 words
A rechargeable alkaline silver-zinc electrochemical cell according to claim 3, wherein said additive comprises bismuth oxide and indium hydroxide.
Claim 10
Dependent Claim
33 words
A rechargeable alkaline silver-zinc electrochemical cell according to claim 8, wherein the amount of said indium hydroxide ranges from about 0.25% by wt. to about 1% by wt. of said negative active material.
Claim 11
Dependent Claim
25 words
A rechargeable alkaline silver-zinc electrochemical cell according to claim 3, wherein said additive comprises bismuth oxide and a mixture of lead oxide and cadmium oxide.
Claim 12
Dependent Claim
49 words
A rechargeable alkaline silver-zinc electrochemical cell according to claim 10, wherein the amount of lead oxide ranges from about 0.5% by wt. to about 2% by wt. and the amount of cadmium oxide ranges from about 1.0% by wt. to about 2.0% by wt. of said negative active material.
Claim 13
Dependent Claim
42 words
A rechargeable alkaline silver-zinc electrochemical cell according to claim 10, wherein said additive comprises about 5% by wt. bismuth oxide, about 2% by wt. cadmium oxide and about 1% by wt. lead oxide based on the weight of said negative active material.
Claim 14
Dependent Claim
37 words
A rechargeable alkaline silver-zinc electrochemical cell according to claim 10, wherein said separator comprises at least one inner separator layer composed of woven nylon and an outer main separator composed of multiple layers of silver treated cellophane.
Claim 15
Dependent Claim
97 words
A rechargeable alkaline silver-zinc electrochemical cell comprising, a positive and a negative electrode having a separator therebetween containing an alkaline electrolyte, said positive electrode containing silver as the positive active material, said negative electrode comprising predominantly zinc or zinc oxide as the negative active material and an additive consisting essentially of from about 2% by wt. to about 5% by wt. bismuth oxide, from about 0.5% by wt. to about 2% by wt. lead oxide and from about 1.0% by wt. to about 2.0% by wt. cadmium oxide, based on the weight of said negative active material.
Claim 16
Dependent Claim
97 words
A rechargeable alkaline silver-zinc electrochemical cell comprising, a positive and a negative electrode having a separator therebetween containing an alkaline electrolyte, said positive electrode containing silver as the positive active material, said negative electrode comprising predominantly zinc or zinc oxide as the negative active material and an additive consisting essentially of from about 2% by wt. to about 5% by wt. bismuth oxide, from about 0.5% by wt. to about 2% by wt. lead oxide and from about 1.0% by wt. to about 2.0% by wt. cadmium oxide, based on the weight of said negative active material.
References Cited (Backward Citations)
US4327157A
Cited
US5376480A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2001-06-29 | 2001-12-29 | 2002-06-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2005-06-29 | 2005-12-29 | 2006-06-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2009-06-29 | 2009-12-29 | 2010-06-30 | $7700.00 | Window Closed / Lapsed |