US5772754A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Ultrafine particles and production method thereof
Assignee: Toshiba Corp
•
Filing: 1996-02-07
•
Granted: 1998-06-30
•
Expires: 2016-02-07
Abstract
Abstract An electron beam of more than 1×10 19 e/cm 2 ·sec is irradiated to metastable metal oxide particles such as θ-Al 2 O 3 particles or the like disposed on an amorphous carbon film. A phase transformation or the like of the metastable metal oxide particles is occurred by the electron beam irradiation. Thus, stable metal oxide ultrafine particles such as an α-Al 2 O 3 ultrafine particle 2 whose diameter is more tiny than the metastable metal oxide particles used, and a metal ultrafine particle composed of an oxide such as Al ultrafine particles are produced.
Inventors
- 👤 Shun-ichiro Tanaka
- 👤 Bing She Xu
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 06:46
CPC Classifications
B; B22; B22F; B22F9/00; B22F9/16; B22F9/30; B22F1/00; B22F1/05; B22F1/054; B82; B82Y; B82Y30/00; C; C01; C01B; C01B13/00; C01B13/14; C01B13/145; C01F; C01F7/00; C01F7/02; C01F7/021; C01F7/027; B22F2202/00; B22F2202/11; C01P; C01P2004/00; C01P2004/30; C01P2004/32; C01P2004/60; C01P2004/62; C01P2004/64
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
62 words
An ultrafine powder comprising at least one selected from the group consisting of stable ultrafine particles of a metal oxide and nanoparticles of a metal which is a component of the metal oxide, wherein the ultrafine particles and the nanoparticles are produced from metastable particles of the metal oxide by irradiating an electron beam in a vacuum to form the ultrafine powder.
Claim 2
Dependent Claim
62 words
An ultrafine powder comprising at least one selected from the group consisting of stable ultrafine particles of a metal oxide and nanoparticles of a metal which is a component of the metal oxide, wherein the ultrafine particles and the nanoparticles are produced from metastable particles of the metal oxide by irradiating an electron beam in a vacuum to form the ultrafine powder.
Claim 3
Dependent Claim
35 words
The ultrafine powder as set forth in claim 1, wherein the ultrafine particles and the nanoparticles have at least a shape selected form the group consisting of a sphere, a rod and a mushroom shape.
Claim 4
Dependent Claim
38 words
The ultrafine powder as set forth in claim 1, wherein the metastable particles are θ-Al 2 O 3 particles, the stable ultrafine particles are α-Al 2 O 3 ultrafine particles, and the metal nanoparticles are of Al nanoparticles.
Claim 5
Independent Claim
77 words
A method for producing an ultrafine powder comprising at least one selected from the group consisting of ultrafine stable particles of a metal oxide and nanoparticles of a metal which is a component metal of the metal oxide, comprising a step of irradiating an electron beam having an intensity of more than 10 19 e/cm 2 ·sec in a vacuum to metastable particles of the metal oxide, the metastable particles being disposed on an amorphous carbon film.
Claim 6
Independent Claim
77 words
A method for producing an ultrafine powder comprising at least one selected from the group consisting of ultrafine stable particles of a metal oxide and nanoparticles of a metal which is a component metal of the metal oxide, comprising a step of irradiating an electron beam having an intensity of more than 10 19 e/cm 2 ·sec in a vacuum to metastable particles of the metal oxide, the metastable particles being disposed on an amorphous carbon film.
Claim 7
Dependent Claim
60 words
The method as set forth in claim 4, wherein a diameter of the metastable particles is in the range of 90 to 200 nm, a diameter of the ultrafine stable particles of the metal oxide is in the range of 10 to 50 nm, and a diameter of the metal nanoparticles is in the range of 5 to 20 nm.
Claim 8
Dependent Claim
37 words
The method as set forth in claim 4, wherein the metastable particles are θ-Al 2 O 3 particles, the stable ultrafine particles are α-Al 2 O 3 ultrafine particles, and the metal nanoparticles are of Al nanoparticles.
Claim 9
Dependent Claim
33 words
A preferentially growing body of ultrafine particles of a stable metal oxide, wherein the ultrafine particles are grown in a definite crystal direction of the ultrafine particles to form the preferentially growing body.
Claim 10
Dependent Claim
33 words
A preferentially growing body of ultrafine particles of a stable metal oxide, wherein the ultrafine particles are grown in a definite crystal direction of the ultrafine particles to form the preferentially growing body.
Claim 11
Dependent Claim
21 words
The preferentially growing body as set forth in claim 7, wherein the ultrafine particles are α-Al 2 O 3 ultrafine particles.
Claim 12
Independent Claim
124 words
A method for producing a preferentially growing body of ultrafine particles comprising the steps of: disposing metastale metal oxide particles on an amorphous carbon film, irradiating preliminary an electron beam having an intensity of more than 10 19 e/cm 2 ·sec to a portion of the amorphous carbon film surrounding the metastable metal oxide particles, irradiating an electron beam having an intensity of more than 10 19 e/cm 2 ·sec in a vacuum to the metastable metal oxide particles of the metal oxide to the metastable metal oxide particles to form stable metal oxide ultrafine particles, and irradiating continuously to the stable metal oxide particles to form a preferentially growing body which grows in an definite crystal direction of the metal oxide ultrafine particles.
Claim 13
Independent Claim
124 words
A method for producing a preferentially growing body of ultrafine particles comprising the steps of: disposing metastale metal oxide particles on an amorphous carbon film, irradiating preliminary an electron beam having an intensity of more than 10 19 e/cm 2 ·sec to a portion of the amorphous carbon film surrounding the metastable metal oxide particles, irradiating an electron beam having an intensity of more than 10 19 e/cm 2 ·sec in a vacuum to the metastable metal oxide particles of the metal oxide to the metastable metal oxide particles to form stable metal oxide ultrafine particles, and irradiating continuously to the stable metal oxide particles to form a preferentially growing body which grows in an definite crystal direction of the metal oxide ultrafine particles.
Claim 14
Dependent Claim
30 words
The method as set forth in claim 9, wherein the metastable particles are θ-Al 2 O 3 particles, and the stable ultrafine particles are α-Al 2 O 3 ultrafine particles.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2001-06-29 | 2001-12-29 | 2002-06-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2005-06-29 | 2005-12-29 | 2006-06-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2009-06-29 | 2009-12-29 | 2010-06-30 | $7700.00 | Window Closed / Lapsed |