Polishing agent and polishing method using the same
Assignee: Toshiba Corp
•
Filing: 1995-07-11
•
Granted: 1998-06-23
•
Expires: 2015-07-11
Abstract
Abstract The present invention provides a polishing method including the steps of forming a film made of material containing a metal as a main component over a substrate having depressed portions on a surface thereof so as to fill the depressed portions with the film, and polishing the film by a chemical mechanical polishing method using a polishing agent containing a chemical agent responsible for forming a protection film on a surface of the film by reacting with the material containing a metal as a main component, thereby forming a conductive film in the depressed portions. The present invention also provides a polishing agent, which is used in forming a film made of material containing a metal as a main component in depressed portions of a substrate having depressed portions on a surface thereof by using a chemical mechanical polishing method, including a chemical agent responsible for forming a protection film on the surface of a substrate to be polished by reacting with the material containing a metal as a main component.
Inventors
- 👤 Yasutaka Sasaki
- 👤 Nobuo Hayasaka
- 👤 Hisashi Kaneko
- 👤 Hideaki Hirabayashi
- 👤 Masatoshi Higuchi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 18:18
CPC Classifications
C; C23; C23F; C23F3/00; H; H10; H10P; H10P52/00; H10P52/40; H10P52/403; H10W; H10W20/00; H10W20/01; H10W20/031; H10W20/062
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
141 words
A polishing method comprising the steps of: forming a film made of material containing a metal as a main component over a substrate having depressed portions on a surface thereof so as to fill said depressed portions with said film; and polishing said film by a chemical mechanical polishing method using a polishing agent containing a chemical agent and an etching agent, said chemical agent being responsible for forming a protection film on the surface of said film by reacting with said material containing a metal as a main component, and said etching agent being for etching said material containing a metal as a main component, thereby forming a conductive film in said depressed portions, wherein said metal is Cu or a Cu alloy and said etching agent includes either aminoacetic acid or amidosulfuric acid, and an oxidizing agent and water.
Claim 2
Dependent Claim
141 words
A polishing method comprising the steps of: forming a film made of material containing a metal as a main component over a substrate having depressed portions on a surface thereof so as to fill said depressed portions with said film; and polishing said film by a chemical mechanical polishing method using a polishing agent containing a chemical agent and an etching agent, said chemical agent being responsible for forming a protection film on the surface of said film by reacting with said material containing a metal as a main component, and said etching agent being for etching said material containing a metal as a main component, thereby forming a conductive film in said depressed portions, wherein said metal is Cu or a Cu alloy and said etching agent includes either aminoacetic acid or amidosulfuric acid, and an oxidizing agent and water.
Claim 3
Dependent Claim
18 words
The method according to claim 1, wherein said chemical agent include at least benzotriazole or a derivative thereof.
Claim 4
Dependent Claim
45 words
The method according to claim 2, wherein said etching agent contains aminoacetic acid or amidosulfuric and an oxidizing agent in a mixing ratio which is controlled so as to etch material containing Cu as a main component at a rate of at least 10 nm/minute.
Claim 5
Dependent Claim
33 words
The method according to claim 2, wherein the molar concentration ratio of said chemical agent to aminoacetic acid or amidosulfuric acid in said etching agent falls within the range of 1/1000 to 3/100.
Claim 6
Dependent Claim
125 words
A polishing method comprising the steps of: forming a film made of material containing a metal as a main component over a substrate having depressed portions on a surface thereof so as to fill said depressed portions with said film; polishing said film by a chemical mechanical polishing method using a first polishing agent containing an etching agent for said material containing a metal as a main component; and polishing said film by a chemical mechanical polishing method using a second polishing agent containing said first polishing agent and a chemical agent responsible for forming a protection film on a surface of said film by reacting with said material containing a metal as a main component, thereby forming a conductive film in said depressed portions.
Claim 7
Dependent Claim
125 words
A polishing method comprising the steps of: forming a film made of material containing a metal as a main component over a substrate having depressed portions on a surface thereof so as to fill said depressed portions with said film; polishing said film by a chemical mechanical polishing method using a first polishing agent containing an etching agent for said material containing a metal as a main component; and polishing said film by a chemical mechanical polishing method using a second polishing agent containing said first polishing agent and a chemical agent responsible for forming a protection film on a surface of said film by reacting with said material containing a metal as a main component, thereby forming a conductive film in said depressed portions.
Claim 8
Dependent Claim
30 words
The method according to claim 5, wherein said metal is Cu or a Cu alloy and an etching agent includes aminoacetic acid or amidosulfuric acid, an oxidizing agent and water.
Claim 9
Dependent Claim
19 words
The method according to claim 6, wherein a said chemical agent includes at least benzotriazole or a derivative thereof.
Claim 10
Dependent Claim
46 words
The method according to claim 6, wherein said etching agent contains aminoacetic acid or amidosulfuric acid and an oxidizing agent in a mixing ratio which is controlled so as to etch material containing Cu as a main component at a rate of at least 10 nm/minute.
Claim 11
Dependent Claim
33 words
The method according to claim 6, wherein the molar concentration ratio of said chemical agent to aminoacetic acid or amidosulfuric acid in said etching agent falls within the range of 1/1000 to 3/100.
Claim 12
Dependent Claim
134 words
A polishing method, comprising the steps of: forming a conductive film made of a material containing a metal as a main component on a substrate having depressed portions on a surface thereof, so as to fill said depressed portions with said conductive film to form a depressed surface of said conductive film; and chemically and mechanically polishing said conductive film by applying a slurry comprising a polishing agent containing a chemical agent which forms a protective film on the depressed surfaces of said conductive film by reaction with said material containing a metal as a main component in combination with aminoacetic acid or amidosulfuric acid, and hydrogen peroxide, the molar concentration ratio of said chemical agent to aminoacetic acid or amidosulfuric acid in said polishing agent falling within the range of 1/1000 to 3/100.
Claim 13
Dependent Claim
134 words
A polishing method, comprising the steps of: forming a conductive film made of a material containing a metal as a main component on a substrate having depressed portions on a surface thereof, so as to fill said depressed portions with said conductive film to form a depressed surface of said conductive film; and chemically and mechanically polishing said conductive film by applying a slurry comprising a polishing agent containing a chemical agent which forms a protective film on the depressed surfaces of said conductive film by reaction with said material containing a metal as a main component in combination with aminoacetic acid or amidosulfuric acid, and hydrogen peroxide, the molar concentration ratio of said chemical agent to aminoacetic acid or amidosulfuric acid in said polishing agent falling within the range of 1/1000 to 3/100.
Claim 14
Dependent Claim
19 words
The method according to claim 10, wherein a said chemical agent includes at least benzotriazole or a derivative thereof.
Claim 15
Dependent Claim
27 words
The method according to claim 10, wherein said metal is W or a W alloy and said chemical agent includes at least N-benzoyl-N-phenylhydroxylamine or a derivative thereof.
Claim 16
Dependent Claim
15 words
The method according to claim 10, wherein said metal is Cu or a Cu alloy.
Claim 17
Dependent Claim
44 words
The method according to claim 13 wherein aminoacetic acid or amidosulfuric acid and an oxidizing agent are present in a mixing ratio which is controlled so as to etch material containing Cu as a main component at a rate of at least 10 nm/minute.
Claim 18
Dependent Claim
141 words
A polishing method, comprising the steps of: forming a conductive film made of a material containing a metal as a main component on a substrate having depressed portions on a surface thereof, so as to fill said depressed portions with said conductive film to form a depressed surface of said conductive film; and chemically and mechanically polishing said conductive film using a polishing pad attached to a polishing table while applying a slurry comprising a polishing agent containing a chemical agent which forms a protective film on the depressed surfaces of said conductive film by reaction with said material containing a metal as a main component in combination with aminoacetic acid, amidosulfuric acid, or hydrogen peroxide, said polishing being performed while cooling at least one member selected from the group consisting of the polishing pad, the polishing table and the slurry.
Claim 19
Dependent Claim
141 words
A polishing method, comprising the steps of: forming a conductive film made of a material containing a metal as a main component on a substrate having depressed portions on a surface thereof, so as to fill said depressed portions with said conductive film to form a depressed surface of said conductive film; and chemically and mechanically polishing said conductive film using a polishing pad attached to a polishing table while applying a slurry comprising a polishing agent containing a chemical agent which forms a protective film on the depressed surfaces of said conductive film by reaction with said material containing a metal as a main component in combination with aminoacetic acid, amidosulfuric acid, or hydrogen peroxide, said polishing being performed while cooling at least one member selected from the group consisting of the polishing pad, the polishing table and the slurry.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2001-06-22 | 2001-12-22 | 2002-06-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2005-06-22 | 2005-12-22 | 2006-06-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2009-06-22 | 2009-12-22 | 2010-06-23 | $7700.00 | Window Closed / Lapsed |