Method of Controlling Reactions between tetrakis dialkylamine titanium and ammonia for producing titanium nitride films
Assignee: Aerospace Corp
•
Filing: 1996-06-25
•
Granted: 1998-06-09
•
Expires: 2016-06-25
Abstract
Abstract Chemical vapor deposition of titanium nitride thin films is based upon the gas phase kinetics of the reaction of a metal-amido precursors, e.g. tetrakis dimethylamido titanium (Ti(NMe 2 ) 4 ), which when reacted with a reagent, for example, NH 3 produces in a transamination reaction, an amine, e.g. HNMe 2 , as a direct product, which when added to the reaction in excess, inhibits the reversible transamination reaction so as to slow and control the rate of reaction to produce titanium nitride films having conformal step coverage over sub-micron integrated circuit features.
Inventors
- 👤 Bruce H. Weiller
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 03:26
CPC Classifications
H; H10; H10W; H10W20/00; H10W20/01; H10W20/031; H10W20/032; H10W20/033; C; C23; C23C; C23C16/00; C23C16/22; C23C16/30; C23C16/34
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
190 words
A method of controlling a rate of a reversible transamination reaction in a gas phase for controlling the rate of deposition of a titanium nitride film, the method comprising the steps of, supplying a partial pressure of a precursor, the precursor is a member of the group consisting of tetrakis dimethylamido titanium and tetrakis diethylamido titanium, supplying a constant partial pressure of an ammonia reagent, supplying a partial pressure of an inhibitor, the inhibitor is a member of the group consisting of dimethylamine and diethylamine, the inhibitor is dimethylamine when the precursor is tetrakis dimethylamido titanium, the inhibitor is diethylamine when precursor is tetrakis diethylamido titanium, mixing the precursor, reagent and inhibitor together, the precursor and reagent reacting together in the reversible transamination reaction producing a dialkylamine product having a chemical composition equal to the inhibitor, the dialkylamine inhibitor is supplied in addition to the produced dialkylamine product, the inhibitor is supplied for controlling the rate of the reversible transamination reaction for controlling the rate of deposition of the titanium nitride film, and exposing a substrate to the reversible transamination reaction to deposit the titanium nitride film on the substrate.
Claim 2
Independent Claim
190 words
A method of controlling a rate of a reversible transamination reaction in a gas phase for controlling the rate of deposition of a titanium nitride film, the method comprising the steps of, supplying a partial pressure of a precursor, the precursor is a member of the group consisting of tetrakis dimethylamido titanium and tetrakis diethylamido titanium, supplying a constant partial pressure of an ammonia reagent, supplying a partial pressure of an inhibitor, the inhibitor is a member of the group consisting of dimethylamine and diethylamine, the inhibitor is dimethylamine when the precursor is tetrakis dimethylamido titanium, the inhibitor is diethylamine when precursor is tetrakis diethylamido titanium, mixing the precursor, reagent and inhibitor together, the precursor and reagent reacting together in the reversible transamination reaction producing a dialkylamine product having a chemical composition equal to the inhibitor, the dialkylamine inhibitor is supplied in addition to the produced dialkylamine product, the inhibitor is supplied for controlling the rate of the reversible transamination reaction for controlling the rate of deposition of the titanium nitride film, and exposing a substrate to the reversible transamination reaction to deposit the titanium nitride film on the substrate.
Claim 3
Dependent Claim
27 words
The method of claim 1 further comprising the step of, carrying the precursor by an inert carrier gas into a mixing chamber prior to the mixing step.
Claim 4
Dependent Claim
32 words
The method of claim 2 further comprising the steps of, controlling the temperature of the precursor, reagent and inhibitor in the mixing chamber during the reversible transamination reaction to a constant temperature.
Claim 5
Dependent Claim
87 words
The method of claim 1 wherein the precursor is a tetrakis dimethylamido titanium gas at less than 0.006 torr partial pressure, the reagent is ammonia gas at a partial pressure of 0.5 torr, and the inhibitor is dimethylamine at a partial pressure of 0.198 torr during the gas phase reaction, the method further comprising the steps of, controlling the temperature of the reaction to 24° C., and carrying the tetrakis dimethylamido titanium gas in a helium gas carrier into a mixing chamber prior to the mixing step.
References Cited (Backward Citations)
No citation records indexed.
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2001-06-08 | 2001-12-08 | 2002-06-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2005-06-08 | 2005-12-08 | 2006-06-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2009-06-08 | 2009-12-08 | 2010-06-09 | $7700.00 | Window Closed / Lapsed |