Abstract
Abstract A polyethylene article such as film or fiber having high strength and high elastic modulus is produced by orienting an ultra-high molecular weight polyethylene having an intrinsic viscosity at 135 DEG C. in decalin of 5 to 50 dl/g, said ultra-high molecular weight polyethylene being prepared by homo- or copolymerizing ethylene in the presence of a catalyst system and hydrogen, said catalyst system comprising (1) a solid catalyst component containing at least magnesium, titanium and/or vanadium, (2) an organometallic compound and (3) a compound represented by the following general formula [I]:ogen or a hydrocarbon residue, with the proviso that any two of R1, R2, R3 and R4 may conjointly form a cyclic hydrocarbon residue.
Inventors
- 👤 Takeichi Shiraishi
- 👤 Yoshiyuki Shimo
- 👤 Seizo Kobayashi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 23:34
CPC Classifications
C; C08; C08J; C08J5/00; C08J5/18; B; B29; B29C; B29C55/00; B29C55/02; B29C55/18; C08F; C08F10/00; C08F10/02; D; D01; D01F; D01F6/00; D01F6/02; D01F6/04; B29K; B29K2023/00; B29K2023/04; B29K2023/06; B29K2023/0658; B29K2023/0683; C08F110/00; C08F110/02; C08J2323/00; C08J2323/02; C08J2323/04
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
151 words
A process for producing a polyethylene material of high strength and high elastic modulus, characterized by orienting an ultra-high molecular weight polyethylene having an intrinsic viscosity at 135° C. in decalin of 5 to 50 dl/g by stretching the ultra-high molecular weight polyethylene to a stretch ratio of not lower than 30:1, said ultra high molecular weight polyethylene being prepared by homopolymerizing ethylene or copolymerizing ethylene and an alpha-olefin in the presence of a catalyst system and hydrogen, said catalyst system comprising (1) a solid catalyst component containing at least magnesium and titanium, (2) an organometallic compound and (3) a compound represented by the following general formula I: ##STR5## where R 1 , R 2 , R 3 and R 4 , are each hydrogen or a hydrocarbon radical, provided any two of R 1 , R 2 , R 3 and R 4 may cojointly form a cyclic hydrocarbon radical.
Claim 2
Dependent Claim
151 words
A process for producing a polyethylene material of high strength and high elastic modulus, characterized by orienting an ultra-high molecular weight polyethylene having an intrinsic viscosity at 135° C. in decalin of 5 to 50 dl/g by stretching the ultra-high molecular weight polyethylene to a stretch ratio of not lower than 30:1, said ultra high molecular weight polyethylene being prepared by homopolymerizing ethylene or copolymerizing ethylene and an alpha-olefin in the presence of a catalyst system and hydrogen, said catalyst system comprising (1) a solid catalyst component containing at least magnesium and titanium, (2) an organometallic compound and (3) a compound represented by the following general formula I: ##STR5## where R 1 , R 2 , R 3 and R 4 , are each hydrogen or a hydrocarbon radical, provided any two of R 1 , R 2 , R 3 and R 4 may cojointly form a cyclic hydrocarbon radical.
Claim 3
Dependent Claim
20 words
The process of claim 1, wherein the hydrocarbon residue in the general formula I! has 1 to 18 carbon atoms.
Claim 4
Dependent Claim
34 words
The process of claim 2, wherein the hydrocarbon residue in an alkyl, aryl or aralkyl group, or two hydrocarbon residues form a ring of an indene compound, a cyclopentacyclooctene compound or a fluorene compound.
Claim 5
Dependent Claim
13 words
The process of claim 1, wherein the organometallic compound is an organoaluminum compound.
Claim 6
Dependent Claim
29 words
The process of claim 1, wherein the compound of the general formula I! is used in an amount of 0.01 to 100 moles per mole of the organometallic compound.
Claim 7
Dependent Claim
37 words
The process of claim 1, wherein the polymerization is performed at a temperature of -20° to 120° C., a pressure of 0 to 70 kg/cm 2 .G and a hydrogen concentration of lower than 50 mole %.
Claim 8
Dependent Claim
23 words
The process of claim 1, wherein the copolymerization of ethylene is performed using ethylene and less than 20 mole % of an α-olefin.
Claim 9
Dependent Claim
36 words
The process of claim 1, wherein the ultra-high molecular weight polyethylene is subjected to stretching after going through a rolling step which is carried out at a temperature lower than the melting point of the polyethylene.
Claim 10
Dependent Claim
29 words
The process of claim 8, wherein prior to the rolling step there is performed a compression molding step at a temperature lower than the melting point of said polyethylene.
Claim 11
Dependent Claim
18 words
The process of claim 1, wherein the orientation is performed at a stretch ratio of 30 to 50.
Claim 12
Dependent Claim
17 words
The process of claim 1, wherein the oriented product is in the shape of fiber or film.
Claim 13
Dependent Claim
146 words
A process for producing a polyethylene material of high strength and high elastic modulus, characterized by orienting an ultra-high molecular weight polyethylene having an intrinsic viscosity at 135° C. in decalin of 5 to 50 dl/g, said ultra-high molecular weight polyethylene being prepared by homo- or copolymerizing ethylene in the presence of a catalyst system and hydrogen, said catalyst system comprising (1) a solid catalyst component containing at least magnesium, titanium and/or vandium (2) an organometallic compound and (3) a compound represented by the following general formula I!; ##STR6## where R 1 , R 2 , R 3 and R 4 are each hydrogen or a hydrocarbon residue, provided any two of R 1 , R 2 , R 3 and R 4 may conjointly form a cyclic hydrocarbon residue, and stretching the ultra-high molecular weight polyethylene to a stretch ratio of not lower than 30.
Claim 14
Dependent Claim
146 words
A process for producing a polyethylene material of high strength and high elastic modulus, characterized by orienting an ultra-high molecular weight polyethylene having an intrinsic viscosity at 135° C. in decalin of 5 to 50 dl/g, said ultra-high molecular weight polyethylene being prepared by homo- or copolymerizing ethylene in the presence of a catalyst system and hydrogen, said catalyst system comprising (1) a solid catalyst component containing at least magnesium, titanium and/or vandium (2) an organometallic compound and (3) a compound represented by the following general formula I!; ##STR6## where R 1 , R 2 , R 3 and R 4 are each hydrogen or a hydrocarbon residue, provided any two of R 1 , R 2 , R 3 and R 4 may conjointly form a cyclic hydrocarbon residue, and stretching the ultra-high molecular weight polyethylene to a stretch ratio of not lower than 30.
Claim 15
Dependent Claim
131 words
A process for producing a polyethylene material comprising: (a) providing a catalyst system comprising (1) a solid catalyst component containing at least magnesium, titanium and/or vanadium (2) an organometallic compound and (3) a compound of the formula: ##STR7## where R 1 , R 2 , R 3 and R 4 , are each hydrogen or a hydrocarbon radical, provided any two of R 1 , R 2 , R 3 and R 4 may cojointly form a cyclic hydrocarbon radical; (b) producing an ultra-high molecular weight polyethylene material by material by polymerizing one or more monomers selected from the group consisting of ethylene and alpha-olefins in the presence of hydrogen and the catalyst system; and (c) stretching the ultra-high weight polyethylene material to a stretch ratio of not lower than 30:1.
Claim 16
Dependent Claim
131 words
A process for producing a polyethylene material comprising: (a) providing a catalyst system comprising (1) a solid catalyst component containing at least magnesium, titanium and/or vanadium (2) an organometallic compound and (3) a compound of the formula: ##STR7## where R 1 , R 2 , R 3 and R 4 , are each hydrogen or a hydrocarbon radical, provided any two of R 1 , R 2 , R 3 and R 4 may cojointly form a cyclic hydrocarbon radical; (b) producing an ultra-high molecular weight polyethylene material by material by polymerizing one or more monomers selected from the group consisting of ethylene and alpha-olefins in the presence of hydrogen and the catalyst system; and (c) stretching the ultra-high weight polyethylene material to a stretch ratio of not lower than 30:1.
Claim 17
Dependent Claim
30 words
A process as in claim 13 wherein the ultra-high molecular weight material produced in step (b) has an intrinsic viscosity at 135° C. in decalin of 5 to 50 dl/g.
Claim 18
Dependent Claim
32 words
A process as in claim 13 wherein the one or more monomers polymerized in step (b) are selected from the group consisting of ethylene and alpha-olefins having 3 to 12 carbon atoms.
Claim 19
Dependent Claim
16 words
A film made from a polyethylene material prepared in accordance with the process of claim 1.
Claim 20
Dependent Claim
16 words
A fiber made from a polyethylene material prepared in accordance with the process of claim 1.
Claim 21
Dependent Claim
16 words
A film made from a polyethylene material prepared in accordance with the process of claim 13.
Claim 22
Dependent Claim
16 words
A fiber made from a polyethylene material prepared in accordance with the process of claim 13.
Claim 23
Dependent Claim
29 words
The process of claim 1 for producing a polyethylene material of high strength and high elastic modulus, wherein the alpha-olefin is an alpha-olefin having 3 to 12 carbon atoms.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2001-05-25 | 2001-11-24 | 2002-05-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2005-05-25 | 2005-11-24 | 2006-05-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2009-05-25 | 2009-11-24 | 2010-05-26 | $7700.00 | Window Closed / Lapsed |