Free form fabrication of metallic components
Assignee: Teledyne Scientific and Imaging LLC
•
Filing: 1995-09-19
•
Granted: 1998-04-28
•
Expires: 2015-09-19
Abstract
Abstract A method of free form fabrication of metallic components, typically using computer aided design data, comprises selective laser binding and transient liquid sintering of blended powders. The powder blend includes a base metal alloy, a lower melting temperature alloy, and a polymer binder that constitutes approximately 5-15% of the total blend. A preform part is built up, layer-by-layer, by localized laser melting of the polymer constituent, which rapidly resolidifies to bind the metal particles. The binder is eliminated from the preform part by heating in a vacuum furnace at low atmospheric pressure. The preform part may require support during elimination of the polymer binder and subsequent densification by controlled heat treatment. Densification is performed at a temperature above the melting point of the lower temperature alloy but below the melting point of the base metal alloy to produce transient liquid sintering of the part to near full density with desired shape and dimensional tolerances. The densified part may be subjected to a final hot isostatic pressing (HIP) treatment to close residual porosity and complete the chemical homogenization of the part. Elimination of residual porosity improves fatigue properties of part, and homogenization improves ambient temperature ductility, toughness, and high temperature strength. An advantage of the process is rapid production of complex shaped metal prototypes and complete small batch production runs of high cost metal components without special tooling or machining operations.
Inventors
- 👤 Clifford C. Bampton
- 👤 Robert Burkett
- 👤 Hong-Son Ryang
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 08:28
CPC Classifications
B; B22; B22F; B22F3/00; B22F3/10; B22F1/00; B22F1/09; B22F1/10; B22F10/00; B22F10/10; B22F10/16; B22F10/30; B22F10/34; B22F10/40; B22F10/43; B33; B33Y; B33Y10/00; B33Y40/00; B33Y40/20; B33Y70/00; B22F10/37; B22F10/47; B22F2003/1042; B22F2998/00; B22F2998/10; B29; B29K; B29K2503/00; B29K2503/04; B29K2503/06; Y; Y02; Y02P; Y02P10/00; Y02P10/25
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
119 words
A method of selective sintering of a powder, comprising the steps of: mixing powders of a base metal, a lower melting temperature metal, and a polymer binder to form a powder blend; spreading a layer of said powder blend on a platform; directing a beam of energy onto selected areas of said layer of said powder blend to melt said polymer binder, said polymer binder resolidifying to bind said metal powders in said selected areas; and heating said selected areas of bound metal powders to eliminate said polymer binder and to densify said selected areas by transient liquid sintering and isothermal resolidification at a temperature sufficient to melt said lower melting temperature powder but not said base metal powder.
Claim 2
Independent Claim
119 words
A method of selective sintering of a powder, comprising the steps of: mixing powders of a base metal, a lower melting temperature metal, and a polymer binder to form a powder blend; spreading a layer of said powder blend on a platform; directing a beam of energy onto selected areas of said layer of said powder blend to melt said polymer binder, said polymer binder resolidifying to bind said metal powders in said selected areas; and heating said selected areas of bound metal powders to eliminate said polymer binder and to densify said selected areas by transient liquid sintering and isothermal resolidification at a temperature sufficient to melt said lower melting temperature powder but not said base metal powder.
Claim 3
Dependent Claim
36 words
The method of claim 1, further comprising the step of repeating said steps of spreading said powder blend and directing said energy beam onto selected areas layer-by-layer to build up a preform part of bound powders.
Claim 4
Dependent Claim
27 words
The method of claim 2, wherein said heating step comprises heating said preform part to vaporize and eliminate said polymer binder and to densify said preform part.
Claim 5
Dependent Claim
37 words
The method of claim 3, further comprising the step of supporting said preform part during said heating step in a bed of support powder selected from the group consisting of ceramic powders and ceramic coated metal powders.
Claim 6
Dependent Claim
41 words
The method of claim 4, wherein said step of supporting said preform part in a bed of support powder includes selecting said support powder from the group consisting of yttria, zirconia, silicon nitride, boron nitride, and surface nitrided nickel aluminide powders.
Claim 7
Dependent Claim
30 words
The method of claim 4, wherein said step of supporting said preform part in a bed of support powder includes the step of providing a fluidized bed of support powder.
Claim 8
Dependent Claim
39 words
The method of claim 3, further comprising the steps of: providing preform support shapes; coating said preform support shapes with a release agent; and positioning said coated preform support shapes to support said preform part during said heating step.
Claim 9
Dependent Claim
26 words
The method of claim 7, further comprising the step of placing said preform part and support shapes on a low friction plate during said heating step.
Claim 10
Dependent Claim
27 words
The method of claim 3, further comprising the step of hot isostatic pressing said densified part to close residual porosity and complete chemical homogenization of said part.
Claim 11
Dependent Claim
20 words
The method of claim 1, wherein said polymer binder comprises high purity nylon in the form of fine spherical particles.
Claim 12
Independent Claim
153 words
A method of free form fabrication of metallic components, comprising the steps of: blending powders of a base metal, a lower melting temperature metal, and a polymer binder to form a powder blend; spreading a layer of said powder blend on a platform; directing a beam of energy onto selected areas of said layer of blended powder to cause localized melting of said polymer binder, said polymer binder resolidifying to bind said metal powders in said selected areas; repeating said steps of spreading said powder blend and directing said energy beam onto selected areas to build up a preform part of bound powders; providing support for said preform part; heating said preform part to vaporize and eliminate said polymer binder from said preform part; and densifying said preform part by transient liquid sintering and isothermal resolidification at a temperature sufficient to melt said lower melting temperature powder but not said base metal powder.
Claim 13
Independent Claim
153 words
A method of free form fabrication of metallic components, comprising the steps of: blending powders of a base metal, a lower melting temperature metal, and a polymer binder to form a powder blend; spreading a layer of said powder blend on a platform; directing a beam of energy onto selected areas of said layer of blended powder to cause localized melting of said polymer binder, said polymer binder resolidifying to bind said metal powders in said selected areas; repeating said steps of spreading said powder blend and directing said energy beam onto selected areas to build up a preform part of bound powders; providing support for said preform part; heating said preform part to vaporize and eliminate said polymer binder from said preform part; and densifying said preform part by transient liquid sintering and isothermal resolidification at a temperature sufficient to melt said lower melting temperature powder but not said base metal powder.
Claim 14
Dependent Claim
27 words
The method of claim 11, further comprising the step of hot isostatic pressing said densified part to close residual porosity and complete chemical homogenization of said part.
Claim 15
Dependent Claim
35 words
The method of claim 11, wherein said step of providing support comprises supporting said preform part in a bed of support powder selected from the group consisting of ceramic powders and ceramic coated metal powders.
Claim 16
Dependent Claim
30 words
The method of claim 13, wherein said step of supporting said preform part in a bed of support powder includes the step of providing a fluidized bed of support powder.
Claim 17
Dependent Claim
47 words
The method of claim 13, wherein said step of providing support further comprises the steps of: providing preform support shapes; coating said preform support shapes with a release agent; and positioning said coated preform support shapes to support said preform part during said heating and densifying steps.
Claim 18
Dependent Claim
19 words
The method of claim 11, wherein said polymer binder comprises a high purity nylon powder comprising fine spherical particles.
Claim 19
Independent Claim
164 words
A method of free form fabrication of metallic components, comprising the steps of: forming a powder blend comprising powders of a base metal, a lower melting temperature alloy of said base metal, and a high purity nylon binder comprising fine spherical particles; spreading a layer of said powder blend on a platform; directing a laser beam onto selected areas of said layer of blended powder to cause localized melting of said nylon binder, said melted nylon binder resolidifying to bind said metal powders in said selected areas; repeating said steps of spreading said powder blend and directing said laser beam onto selected areas to build up a preform part of bound powders; providing support for said preform part; heating said preform part to vaporize and eliminate said nylon binder from said preform part; and densifying said supported preform part by transient liquid sintering and isothermal resolidification at a temperature sufficient to melt said lower melting temperature alloy powder but not said base metal powder.
Claim 20
Independent Claim
164 words
A method of free form fabrication of metallic components, comprising the steps of: forming a powder blend comprising powders of a base metal, a lower melting temperature alloy of said base metal, and a high purity nylon binder comprising fine spherical particles; spreading a layer of said powder blend on a platform; directing a laser beam onto selected areas of said layer of blended powder to cause localized melting of said nylon binder, said melted nylon binder resolidifying to bind said metal powders in said selected areas; repeating said steps of spreading said powder blend and directing said laser beam onto selected areas to build up a preform part of bound powders; providing support for said preform part; heating said preform part to vaporize and eliminate said nylon binder from said preform part; and densifying said supported preform part by transient liquid sintering and isothermal resolidification at a temperature sufficient to melt said lower melting temperature alloy powder but not said base metal powder.
Claim 21
Dependent Claim
27 words
The method of claim 17, further comprising the step of hot isostatic pressing said densified part to close residual porosity and complete chemical homogenization of said part.
Claim 22
Dependent Claim
42 words
The method of claim 17, wherein said step of providing support comprises supporting said preform part in a bed of powder selected from the group consisting of ceramic coated metal powders and yttria, zirconia, silicon nitride, and surface nitrided nickel aluminide powders.
Claim 23
Dependent Claim
51 words
The method of claim 19, wherein said step of providing support further comprises the steps of: providing preform support shapes; coating said preform support shapes with a release agent; and positioning said coated preform support shapes to support said preform part on a low-friction plate during said heating and densifying steps.
References Cited (Backward Citations)
US5017753A
Cited
US5155324A
Cited
US4927992A
Cited
US4855102A
Cited
US5156697A
Cited
US5182170A
Cited
US5316720A
Cited
US5393482A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2001-04-27 | 2001-10-27 | 2002-04-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2005-04-27 | 2005-10-27 | 2006-04-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2009-04-27 | 2009-10-27 | 2010-04-28 | $7700.00 | Window Closed / Lapsed |