Energy beam casting of metal articles
Assignee: Westinghouse Electric Co LLC
•
Filing: 1987-03-04
•
Granted: 1990-05-22
•
Expires: 2007-03-04
Abstract
Abstract Near net shape metal articles are cast from powder feedstock using a focused high energy beam which melts successive layers of powder as it repetitively traces the shape of the article over a substrate without the necessity for refocusing. Powder is fed into a cavity in which the article is formed at a rate to maintain a depth which provides lateral support for, and therefore forms a mold for, a thick layer of powder which is melted by the energy beam to add each layer to the article. The high energy laser or electron beam has a power density sufficient to penetrate the melted layer of powder and melt the surface of the underlying substrate or layer just enough to provide a good metallurgical bond for the layer being added. A copper fixture which supports the substrate while the article is being formed, serves as a heat sink and forms the cavity which confines the powder to the vicinity of the article being formed. Various shapes can be cast through selected programming of the repetitive pattern of relative motion between the energy beam and the substrate.
Inventors
- 👤 Graham A. Whitlow
- 👤 Gerald J. Bruck
- 👤 James E. Smith
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 03:16
CPC Classifications
B; B22; B22F; B22F10/00; B22F10/20; B22F10/25; B22F10/60; B22F10/66; B22F12/00; B22F12/30; B22F12/37; B22F2998/00; Y; Y02; Y02P; Y02P10/00; Y02P10/25
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
181 words
A method of producing articles from powder metal comprising the steps of: generating a focused energy beam having an energy density sufficient to melt the powder metal; generating relative movement between the energy beam and a substrate such that the energy beam repetitively traces over the substrate the shape of said article and melts the surface of the substrate at the interface of the energy beam and the substrate; and feeding powder metal onto said substrate to maintain a depth of powder metal which laterally supports and forms a mold for a layer of powder metal at the energy beam interface which is melted by the energy beam, the thickness of the layer of powder metal being such that the energy beam penetrates the layer of powder metal and melts the surface of the substrate but only to the extent to wet the substrate sufficiently to bond to the substrate the melted powder metal, which in turn, cools rapidly upon leaving the energy beam interface to form a thick layer of the article which becomes the substrate for the next layer.
Claim 2
Independent Claim
181 words
A method of producing articles from powder metal comprising the steps of: generating a focused energy beam having an energy density sufficient to melt the powder metal; generating relative movement between the energy beam and a substrate such that the energy beam repetitively traces over the substrate the shape of said article and melts the surface of the substrate at the interface of the energy beam and the substrate; and feeding powder metal onto said substrate to maintain a depth of powder metal which laterally supports and forms a mold for a layer of powder metal at the energy beam interface which is melted by the energy beam, the thickness of the layer of powder metal being such that the energy beam penetrates the layer of powder metal and melts the surface of the substrate but only to the extent to wet the substrate sufficiently to bond to the substrate the melted powder metal, which in turn, cools rapidly upon leaving the energy beam interface to form a thick layer of the article which becomes the substrate for the next layer.
Claim 3
Dependent Claim
47 words
The method of claim 1 including the step of focusing the energy beam at a focal point beyond the surface of the substrare such that the energy beam is defocused at the substrate, and maintaining the focus constrant as successive layers of the article are built up.
Claim 4
Dependent Claim
34 words
The method of claim 2 including focusing the energy beam at a point beyond the surface of the substrate at a distance about equal to the height of the article to be built up.
Claim 5
Dependent Claim
46 words
The method of claim 3 including focusing the energy beam at a point about 0.5 inches beyond the surface of the substrate and adding successive layers to the article to build it up to the height of about 0.5 inches above the surface of the substrate.
Claim 6
Dependent Claim
65 words
The method of claim 1 including the step of focusing the energy beam at a focal point above the surface of the substrate such that the energy beam is defocused at the substrate and maintaining the focus constant as successive layers of the article are built-up, said focal point being sufficiently above the substrate such that the energy beam remains defocused at each successive layer.
Claim 7
Dependent Claim
51 words
The method of claim 1 wherein the step of feeding powder metal comprises feeding such powder metal at a rate which maintains a depth of powder metal over the substrate at the energy beam interface sufficient to form a layer of the article having a thickness greater than about 0.1 inches.
Claim 8
Dependent Claim
49 words
The method of claim 1 wherein the step of feeding powder metal comprises feeding such powder metal at a rate which maintains a depth of powder metal at the energy beam interface sufficient to form a layer of the article having a thickness of about 0.03 to 0.05 inches.
Claim 9
Dependent Claim
86 words
The method of claim 1 including the step of surrounding the base substrate at least partially with a heat sink member to conduct away from the base substrate heat produced by the energy beam, said heat sink member defining with the base substrate a cavity in which said article is produced, and wherein the step of feeding powder metal comprises feeding powder metal into said cavity to maintain a depth of powder metal which laterally supports and forms a mold for said layer of powder metal.
Claim 10
Dependent Claim
36 words
The method of claim 1 including the step of adjusting the angle of incidence of the energy beam on the substrate to control the shape of said article built up from layers of melted powder metal.
Claim 11
Dependent Claim
21 words
The method of claim 1 including separating the article made up of layers of melted powder metal from the base substrate.
Claim 12
Dependent Claim
53 words
The method of claim 1 including securing a thin base substrate to a support member, building up said article from layers of melted powder metal with said base substrate secured to said support member, and then separating said rhin base substrate from the support member and removing the base substrate from said article.
Claim 13
Dependent Claim
65 words
The method of claim 1 including providing a guide member having an opening which forms with the base substrate a cavity in which said article is formed, and wherein the step of feeding powder metal comprises feeding powder metal into said cavity at a rate to maintain a depth of powder metal which laterally supports and forms a mold for said layer of powder metal.
Claim 14
Dependent Claim
210 words
Apparatus for forming articles from powder metal comprising: means for generating a focused energy beam having an energy density sufficient to melt the powder metal; a base substrate; means for generating relative movement between the energy beam and the base substrate such that the interface of the energy beam with the base substrate repetitively traces the shape of said article over said base substrate; a guide member supported between the energy beam generating means and the base substrate and forming with the base substrate a cavity in which said article is formed; and means for feeding powder metal into said cavity to maintain a depth of powder metal in the cavity which laterally supports and forms a mold for a layer of powder metal at the energy beam interface which is melted by the energy beam, the thickness of the layer of powder metal being such that the energy beam penetrates the layer of powder metal and melts the surface of the base substrate, but only to the extent to wet the substrate sufficiently to bond to the substrate the melted powder metal, which in turn, cools rapidly upon leaving the energy beam interface to form a thick layer of the article which becomes the substrate for the next layer.
Claim 15
Dependent Claim
210 words
Apparatus for forming articles from powder metal comprising: means for generating a focused energy beam having an energy density sufficient to melt the powder metal; a base substrate; means for generating relative movement between the energy beam and the base substrate such that the interface of the energy beam with the base substrate repetitively traces the shape of said article over said base substrate; a guide member supported between the energy beam generating means and the base substrate and forming with the base substrate a cavity in which said article is formed; and means for feeding powder metal into said cavity to maintain a depth of powder metal in the cavity which laterally supports and forms a mold for a layer of powder metal at the energy beam interface which is melted by the energy beam, the thickness of the layer of powder metal being such that the energy beam penetrates the layer of powder metal and melts the surface of the base substrate, but only to the extent to wet the substrate sufficiently to bond to the substrate the melted powder metal, which in turn, cools rapidly upon leaving the energy beam interface to form a thick layer of the article which becomes the substrate for the next layer.
Claim 16
Dependent Claim
56 words
The apparatus of claim 13 including a support member and a fixture securing said base substrate to the support member, said fixture including said guide member and comprising heat conducting members in intimate contact with said base substrate to form a heat sink to conduct heat generated by the energy beam away from the base substrate.
References Cited (Backward Citations)
US4000392A
Cited
US4125926A
Cited
US4218494A
Cited
US4233720A
Cited
US4323756A
Cited
US4474861A
Cited
US4585619A
Cited
US4575330A
Cited
US4575330B1
Cited
US4730093A
Cited
US4752352A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-05-21 | 1993-11-20 | 1994-05-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-05-21 | 1997-11-20 | 1998-05-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-05-21 | 2001-11-20 | 2002-05-22 | $7700.00 | Window Closed / Lapsed |