Resin composition and printed circuit board using the same
Assignee: Sumitomo Bakelite Co Ltd
•
Filing: 1997-03-04
•
Granted: 1998-03-10
•
Expires: 2017-03-04
Abstract
Abstract The present invention provides a rein composition comprising the following components (a), (b), (c), (d) and (e) as essential components; and an excellent multilayer printed circuit board obtained by using the resin composition: (a) a polyfunctional epoxy resin having an epoxy equivalent of 120-500, (b) a modified phenol novolac obtained by reacting 20-60 mole % of the phenolic hydroxyl groups of a phenol novolac obtained by condensing a phenol compound with formaldehyde in the presence of an acidic catalyst, with a glycidyl group-containing acrylate or methacrylate, (c) an epoxy acrylate or epoxy methacrylate compound, (d) a diluent consisting of a polyfunctional monomer having a plurality of photosensitive functional groups or a polyfunctional monomer having a photosensitive functional group and a heat-sensitive functional group, or a diluent consisting of a combination of the two monomers, and (e) a photopolymerization initiator.
Inventors
- 👤 Takeshi Hosomi
- 👤 Hiroshi Hayai
- 👤 Takayuki Baba
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 11:30
CPC Classifications
C; C08; C08F; C08F290/00; C08F290/08; C08F290/14; C08F283/00; C08F283/10; C08F290/02; C08F290/06; C08F290/064; Y; Y10; Y10S; Y10S525/00; Y10S525/922
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
122 words
A resin composition comprising the following components (a), (b), (c), (d) and (e) as essential components: (a) a polyfunctional epoxy resin having an epoxy equivalent of 120-500, (b) a modified phenol novolac obtained by reacting 20-60 mole % of the phenolic hydroxyl groups of a phenol novolac obtained by condensing a phenol compound with formaldehyde in the presence of an acidic catalyst, with a glycidyl group-containing acrylate or methacrylate, (c) an epoxy acrylate or epoxy methacrylate compound, (d) a diluent consisting of a polyfunctional monomer having a plurality of photosensitive functional groups or a polyfunctional monomer having a photosensitive functional group and a heat-sensitive functional group, or a diluent consisting of a combination of the two monomers, and (e) a photopolymerization initiator.
Claim 2
Dependent Claim
122 words
A resin composition comprising the following components (a), (b), (c), (d) and (e) as essential components: (a) a polyfunctional epoxy resin having an epoxy equivalent of 120-500, (b) a modified phenol novolac obtained by reacting 20-60 mole % of the phenolic hydroxyl groups of a phenol novolac obtained by condensing a phenol compound with formaldehyde in the presence of an acidic catalyst, with a glycidyl group-containing acrylate or methacrylate, (c) an epoxy acrylate or epoxy methacrylate compound, (d) a diluent consisting of a polyfunctional monomer having a plurality of photosensitive functional groups or a polyfunctional monomer having a photosensitive functional group and a heat-sensitive functional group, or a diluent consisting of a combination of the two monomers, and (e) a photopolymerization initiator.
Claim 3
Dependent Claim
123 words
A resin composition comprising the following components (a), (b), (c), (d) and (e) as essential components: (a) a polyfunctional epoxy resin having an epoxy equivalent of 120-500, (b) a modified bisphenol novolac obtained by reacting 20-60 mole % of the phenolic hydroxyl groups of a bisphenol novolac obtained by condensing bisphenol A or F with formaldehyde in the presence of an acidic catalyst, with a glycidyl group-containing acrylate or methacrylate, (c) an epoxy acrylate or epoxy methacrylate compound, (d) a diluent consisting of a polyfunctional monomer having a plurality of photosensitive functional groups or a polyfunctional monomer having a photosensitive functional group and a heat-sensitive functional group, or a diluent consisting of a combination of the two monomers, and (e) a photopolymerization initiator.
Claim 4
Dependent Claim
123 words
A resin composition comprising the following components (a), (b), (c), (d) and (e) as essential components: (a) a polyfunctional epoxy resin having an epoxy equivalent of 120-500, (b) a modified bisphenol novolac obtained by reacting 20-60 mole % of the phenolic hydroxyl groups of a bisphenol novolac obtained by condensing bisphenol A or F with formaldehyde in the presence of an acidic catalyst, with a glycidyl group-containing acrylate or methacrylate, (c) an epoxy acrylate or epoxy methacrylate compound, (d) a diluent consisting of a polyfunctional monomer having a plurality of photosensitive functional groups or a polyfunctional monomer having a photosensitive functional group and a heat-sensitive functional group, or a diluent consisting of a combination of the two monomers, and (e) a photopolymerization initiator.
Claim 5
Dependent Claim
21 words
A resin composition according to claim 1, wherein the polyfunctional epoxy resin (a) is a bisphenol A or F epoxy resin.
Claim 6
Dependent Claim
21 words
A resin composition according to claim 2, wherein the polyfunctional epoxy resin (a) is a bisphenol A or F epoxy resin.
Claim 7
Dependent Claim
50 words
A resin composition according to claim 1, wherein the modified phenol novolac (b) is obtained by reacting 40-50 mole % of the phenolic hydroxyl groups of a phenol novolac obtained by condensing a phenol compound with formaldehyde in the presence of an acidic catalyst, with glycidyl acrylate or glycidyl methacrylate.
Claim 8
Dependent Claim
65 words
A resin composition according to claim 1, wherein the epoxy acrylate or epoxy methacrylate compound (c) is obtained by reacting an epoxy compound selected from the group consisting of a bisphenol A epoxy compound, a bisphenol F epoxy compound, a bisphenol S epoxy compound, a phenol novolac epoxy compound, a cresol novolac epoxy compound and an aliphatic epoxy compound, with acrylic acid or methacrylic acid.
Claim 9
Dependent Claim
65 words
A resin composition according to claim 2, wherein the epoxy acrylate or epoxy methacrylate compound (c) is obtained by reacting an epoxy compound selected from the group consisting of a bisphenol A epoxy compound, a bisphenol F epoxy compound, a bisphenol S epoxy compound, a phenol novolac epoxy compound, a cresol novolac epoxy compound and an aliphatic epoxy compound, with acrylic acid or methacrylic acid.
Claim 10
Dependent Claim
120 words
A resin composition according to claim 1, wherein the epoxy acrylate or epoxy methacrylate compound (c) is obtained by reacting the epoxy group of an epoxy compound selected from the group consisting of a bisphenol A epoxy compound, a bisphenol F epoxy compound, a bisphenol S epoxy compound, a phenol novolac epoxy compound, a cresol novolac epoxy compound and an aliphatic epoxy compound, with acrylic acid or methacrylic acid completely or partially and then reacting the reaction product with a dicarboxylic acid compound having an acid value of 5-100 selected from the group consisting of oxalic acid, malonic acid, succinic acid, glutamic acid, adipic acid, maleic acid, fumaric acid, phthalic acid and terephthalic acid, or with an acid anhydride thereof.
Claim 11
Dependent Claim
111 words
A resin composition according to claim 2, wherein the epoxy acrylate or epoxy methacrylate compound (c) is obtained by reacting the epoxy group of an epoxy compound selected from the group consisting of a compound, a bisphenol epoxy compound, a phenol novolac epoxy compound, a cresol novolac epoxy compound and an aliphatic epoxy compound, with acrylic acid or methacrylic acid completely or partially and then reacting the reaction product with a dicarboxylic acid compound having an acid value of 5-100 selected from the group consisting of oxalic acid, malonic acid, succinic acid, glutamic acid, adipic acid, maleic acid, fumaric acid, phthalic acid and terephthalic acid, or with an acid anhydride thereof.
Claim 12
Dependent Claim
37 words
A resin composition according to claim 1, wherein the diluent (d) consisting of a polyfunctional monomer having a plurality of photosensitive functional groups is a compound having, in the molecule, at least two acryloyl or methacryloyl groups.
Claim 13
Dependent Claim
35 words
A resin composition according to claim 10, wherein the compound having, in the molecule, at least two acryloyl or methacryloyl groups is selected from the group consisting of trimethylolpropane triacrylate, pentaerythritol triacrylate and pentaerythritol tetraacrylate.
Claim 14
Dependent Claim
37 words
A resin composition according to claim 2, wherein the diluent (d) consisting of a polyfunctional monomer having a plurality of photosensitive functional groups is a compound having, in the molecule, at least two acryloyl or methacryloyl groups.
Claim 15
Dependent Claim
35 words
A resin composition according to claim 12, wherein the compound having, in the molecule, at least two acryloyl or methacryloyl groups is selected from the group consisting of trimethylolpropane triacrylate, pentaerythritol triacrylate and pentaerythritol tetraacrylate.
Claim 16
Dependent Claim
47 words
A resin composition according to claim 1, wherein the diluent (d) consisting of a polyfunctional monomer having a photosensitive functional group and a heat-sensitive functional group is an acrylate or methacrylate compound having at least one hydroxyl group in the molecule, or glycidyl acrylate or glycidyl methacrylate.
Claim 17
Dependent Claim
47 words
A resin composition according to claim 2, wherein the diluent (d) consisting of a polyfunctional monomer having a photosensitive functional group and a heat-sensitive functional group is an acrylate or methacrylate compound having at least one hydroxyl group in the molecule, or glycidyl acrylate or glycidyl methacrylate.
Claim 18
Dependent Claim
12 words
A resin composition according to claim 1, further comprising a heat-curing accelerator.
Claim 19
Dependent Claim
12 words
A resin composition according to claim 2, further comprising a heat-curing accelerator.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2001-03-09 | 2001-09-08 | 2002-03-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2005-03-09 | 2005-09-08 | 2006-03-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2009-03-09 | 2009-09-08 | 2010-03-10 | $7700.00 | Window Closed / Lapsed |