Demetallization of polymer/metal multilayer films by etching
Assignee: Medtronic Inc
•
Filing: 1996-06-11
•
Granted: 1998-02-10
•
Expires: 2016-06-11
Abstract
Abstract A method of improving the breakdown strength of polymer multi-layer (PML) capacitors is provided. The method comprises removing metal, specifically, aluminum, from the cut edge. This is done by either etching back the metal electrode layers in either basic or acidic solution or by anodizing the metal to cover that portion of the metal at the edge with an oxide. Removing the metal from the cut edge increases the breakdown strength of the PML capacitors by a factor of two or more.
Inventors
- 👤 Angelo Yializis
- 👤 John G. Keimel
- 👤 Alvin S. Rhorer
- 👤 Trey W. Huntoon
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 01:20
CPC Classifications
H; H01; H01G; H01G4/00; H01G4/002; H01G4/005; H01G4/012; H01G13/00; H01G13/06; H01G4/30
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
166 words
A method of improving the breakdown strength of polymer multi-layer capacitors comprising a plurality of interleaved metal electrodes forming two plates of each of said capacitors, said metal electrodes separated by a dielectric coating, said method comprising: (a) terminating a first set of metal electrodes on a first face of each of said capacitors; (b) terminating a second set of electrodes on a second face of each of said capacitors, wherein said first and second faces are formed on opposite sides of each of said capacitors; (c) initially forming said capacitors as a stack; (d) slicing said stack into straps along a first direction; (e) slicing said straps into individual said capacitors along a second direction which is orthogonal to said first direction to form said first and second faces; (f) applying termination strips along said first and second faces of said capacitors, to leave exposed metal electrode edges from said slicing along said first direction; and (g) removing metal from said exposed metal electrode edges.
Claim 2
Independent Claim
166 words
A method of improving the breakdown strength of polymer multi-layer capacitors comprising a plurality of interleaved metal electrodes forming two plates of each of said capacitors, said metal electrodes separated by a dielectric coating, said method comprising: (a) terminating a first set of metal electrodes on a first face of each of said capacitors; (b) terminating a second set of electrodes on a second face of each of said capacitors, wherein said first and second faces are formed on opposite sides of each of said capacitors; (c) initially forming said capacitors as a stack; (d) slicing said stack into straps along a first direction; (e) slicing said straps into individual said capacitors along a second direction which is orthogonal to said first direction to form said first and second faces; (f) applying termination strips along said first and second faces of said capacitors, to leave exposed metal electrode edges from said slicing along said first direction; and (g) removing metal from said exposed metal electrode edges.
Claim 3
Dependent Claim
15 words
The method of claim 1 wherein said dielectric coating comprises a cross-linked, radiation-curable acrylic monomer.
Claim 4
Dependent Claim
10 words
The method of claim 2 wherein said metal comprises aluminum.
Claim 5
Dependent Claim
20 words
The method of claim 3 wherein said aluminum has a thickness within a range of about 50 to 500 Å.
Claim 6
Dependent Claim
20 words
The method of claim 3 wherein said aluminum is etched back into said first and second faces about 100 μm.
Claim 7
Dependent Claim
20 words
The method of claim 3 wherein said removal of aluminum is accomplished by etching said aluminum back from said edge.
Claim 8
Dependent Claim
18 words
The method of claim 6 wherein said etching is performed in a liquid etchant having a basic pH.
Claim 9
Dependent Claim
19 words
The method of claim 7 wherein said liquid etchant is selected from the group consisting of KOH and NaOH.
Claim 10
Dependent Claim
25 words
The method of claim 7 wherein said etching is performed for a period of time within the range of about 1 minute to 24 hours.
Claim 11
Dependent Claim
18 words
The method of claim 6 wherein said etching is performed in a liquid etchant having an acidic pH.
Claim 12
Dependent Claim
28 words
The method of claim 10 wherein said liquid etchant is selected from the group consisting of HF, H 3 SO 4 , and phosphoric acid and combinations thereof.
Claim 13
Dependent Claim
25 words
The method of claim 10 wherein said etching is performed for a period of time within the range of about 1 minute to 24 hours.
References Cited (Backward Citations)
CA574985A
Cited
US2673792A
Cited
US4490774A
Cited
US4499520A
Cited
US4513349A
Cited
US4515931A
Cited
US4533710A
Cited
US5018048A
Cited
US5097800A
Cited
US4613518A
Cited
US4685197A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2001-02-09 | 2001-08-11 | 2002-02-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2005-02-09 | 2005-08-11 | 2006-02-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2009-02-09 | 2009-08-11 | 2010-02-10 | $7700.00 | Window Closed / Lapsed |