Process improvements for preparing catheter balloons

Claim 2

In a method of preparing an oriented balloon of thermoplastic material comprising extruding a hollow tube of the thermoplastic material, and subsequently expanding the tube by subjecting the tubing, while in a mold, to an elevated temperature and an increased interior pressure to produce an oriented balloon, the improvement wherein the tube is subjected to a drying step, prior to said expanding step, thereby increasing the strength of the balloon relative to a reference balloon prepared in the same manner, except for said drying step.

Claim 3

A method as in claim 1 wherein the extruded tube is subjected to a stretching step before said expanding step and the tube is dried before said stretching step.

Claim 4

A method of preparing an oriented balloon as in claim 1 wherein the thermoplastic material is a polyethylene terephthalate homopolymer or copolymer.

Claim 7

A method as in claim 5 wherein the tubing is also subjected to a relatively a lower tension while the body portion is blown than while the first and second waist portions are blown.

Claim 8

In a process for forming an elongated balloon having a longitudinal body portion, first and second waist portions of reduced diameter relative to the body portion at opposite ends of the balloon and first and second cone portions connecting corresponding waist portions and respective ends of the longitudinal body portion, the process comprising the steps of placing an extruded and stretched tubular preform in a mold having an internal form corresponding to the desired outer configuration of the balloon, and forming the balloon by applying axial tension and internal pressure to the preform upon dipping of the mold into a heated heat transfer media, the improvement comprising that the forming step comprises: pressurizing the preform to a first pressure in the range of 150-320 psi and applying a first tension in the range of 5-150 g; dipping the mold to a first depth in the range of from the transition (C) from the first waist to the first cone to the transition (D) from the first cone to the body portion of the balloon while maintaining the first tension and the first pressure, and thereby expanding at least one portion of the preform in the mold; pressurizing the preform to a second pressure less than the first pressure and between 80 and 170 psi and setting a second tension in the range of the first tension; dipping the mold to a second depth in the range of from the transition (E) from the body portion to the second cone portion to the transition (F) from the second cone to the second waist while maintaining the second tension and the second pressure; pressurizing the preform to a third pressure higher than the second pressure and between 150 and 320 psi and applying to the preform a third tension, higher than the first tension, and then, dipping the mold to a third depth (H) beyond the depth of the second waist while maintaining the third tension and the third pressure.

Claim 9

In a process for forming an elongated balloon having a longitudinal body portion, first and second waist portions of reduced diameter relative to the body portion at opposite ends of the balloon and first and second cone portions connecting corresponding waist portions and respective ends of the longitudinal body portion, the process comprising the steps of placing an extruded and stretched tubular preform in a mold having an internal form corresponding to the desired outer configuration of the balloon, and forming the balloon by applying axial tension and internal pressure to the preform upon dipping of the mold into a heated heat transfer media, the improvement comprising that the forming step comprises: pressurizing the preform to a first pressure in the range of 150-320 psi and applying a first tension in the range of 5-150 g; dipping the mold to a first depth in the range of from the transition (C) from the first waist to the first cone to the transition (D) from the first cone to the body portion of the balloon while maintaining the first tension and the first pressure, and thereby expanding at least one portion of the preform in the mold; pressurizing the preform to a second pressure less than the first pressure and between 80 and 170 psi and setting a second tension in the range of the first tension; dipping the mold to a second depth in the range of from the transition (E) from the body portion to the second cone portion to the transition (F) from the second cone to the second waist while maintaining the second tension and the second pressure; pressurizing the preform to a third pressure higher than the second pressure and between 150 and 320 psi and applying to the preform a third tension, higher than the first tension, and then, dipping the mold to a third depth (H) beyond the depth of the second waist while maintaining the third tension and the third pressure.

Claim 10

A method as in claim 6 wherein the third tension is in the range of 50 to 700 g.

Claim 11

In a process for forming an elongated balloon having a longitudinal body portion, first and second waist portions of reduced diameter relative to the body portion at opposite ends of the balloon and first and second cone portions connecting corresponding waist portions and respective ends of the longitudinal body portion, the process comprising the steps of placing an extruded and stretched tubular preform in a mold having an internal form corresponding to the desired outer configuration of the balloon, and forming the balloon by applying axial tension and internal pressure to the preform upon dipping of the mold into a heated heat transfer media, the improvement comprising that the forming step comprises: pressurizing the preform to a first pressure in the range of 150-320 psi and applying a first tension in the range of 5-150 g; dipping the mold to a first depth in the range of from the transition (C) from the first waist to the first cone to the transition (D) from the first cone to the body portion of the balloon while maintaining the first tension and the first pressure, and thereby expanding at least one portion of the preform in the mold; holding the mold at the first depth for a predetermined first time interval while maintaining the first tension and the first pressure; pressurizing the preform to a second pressure less than the first pressure and between 80 and 170 psi and setting a second tension in the range of the first tension; dipping the mold to a second depth in the range of from the transition (E) from the body portion to the second cone portion to the transition (F) from the second cone to the second waist while maintaining the second tension and the second pressure; holding the mold at the second depth while maintaining the second tension and the second pressure for a predetermined second time interval; pressurizing the preform to a third pressure higher than the second pressure and between 150 and 320 psi and applying to the preform a third tension, higher than the first tension; dipping the mold to a third depth (H) beyond the depth of the second waist while maintaining the third tension and the third pressure, and then holding the mold at the third depth for a predetermined third time interval while maintaining the third tension and third pressure.

Claim 12

In a process for forming an elongated balloon having a longitudinal body portion, first and second waist portions of reduced diameter relative to the body portion at opposite ends of the balloon and first and second cone portions connecting corresponding waist portions and respective ends of the longitudinal body portion, the process comprising the steps of placing an extruded and stretched tubular preform in a mold having an internal form corresponding to the desired outer configuration of the balloon, and forming the balloon by applying axial tension and internal pressure to the preform upon dipping of the mold into a heated heat transfer media, the improvement comprising that the forming step comprises: pressurizing the preform to a first pressure in the range of 150-320 psi and applying a first tension in the range of 5-150 g; dipping the mold to a first depth in the range of from the transition (C) from the first waist to the first cone to the transition (D) from the first cone to the body portion of the balloon while maintaining the first tension and the first pressure, and thereby expanding at least one portion of the preform in the mold; holding the mold at the first depth for a predetermined first time interval while maintaining the first tension and the first pressure; pressurizing the preform to a second pressure less than the first pressure and between 80 and 170 psi and setting a second tension in the range of the first tension; dipping the mold to a second depth in the range of from the transition (E) from the body portion to the second cone portion to the transition (F) from the second cone to the second waist while maintaining the second tension and the second pressure; holding the mold at the second depth while maintaining the second tension and the second pressure for a predetermined second time interval; pressurizing the preform to a third pressure higher than the second pressure and between 150 and 320 psi and applying to the preform a third tension, higher than the first tension; dipping the mold to a third depth (H) beyond the depth of the second waist while maintaining the third tension and the third pressure, and then holding the mold at the third depth for a predetermined third time interval while maintaining the third tension and third pressure.

Claim 13

The method as in claim 8 wherein said first time interval is between 1 and 40 seconds, the second time interval is between 1 and 40 seconds and the third time interval is between 10 and 100 seconds.

Claim 14

The method of claim 8 wherein the difference between said second and third pressures is at least 100 psi.

Claim 15

The method of claim 8 wherein the thermoplastic material is a polyethylene terephthalate homopolymer or copolymer.

Claim 16

The method of claim 11 wherein said heat transfer media is heated to a temperature of 90° C. to 100° C.

Claim 17

The method of claim 6 wherein the extruded tubular preform is dried after being extruded and prior to being stretched.

Claim 18

The method of claim 13 wherein the extruded tubular preform is dried to a moisture content of less than 0.15 weight %.

Claim 19

The method of claim 6 wherein the second tension is the same as the first tension.

Claim 20

The method of claim 6 wherein the second tension is less than the first tension.