Balloon catheter
Assignee: Boston Scientific Scimed Inc
•
Filing: 1987-11-30
•
Granted: 1990-10-16
•
Expires: 2007-11-30
Abstract
Abstract An inflatable medical balloon is formed by fabricating a tubular preform having a tapered region at the end of the portion where the main body of the balloon will form to enable the corresponding transition section of the blown balloon to have a separately controllable thickness profile. The preferred method includes providing a tube of a selected resin of wall thickness and diameter suitable for being formed into a balloon, and selectively heating to drawing temperature a defined region of the tube at one or both ends of the portion of the tube from which the balloon is to be formed. Tension is applied in opposite directions to respective ends of the heated region to draw the region to a smaller diameter, thereby providing a preform having, at the end of the portion of the tube, a tapered, relatively small diameter region of material that has substantially no crystallization or molecular orientation. In preferred embodiments a tapered region is provided at both ends of the portion in which the main body of the balloon is to be formed. Thereafter the tubular preform is heated to blowing temperature and, while heated, a balloon is formed by drawing and blowing the preform including the tapered regions. The balloon is mounted to form a balloon catheter device. A dilatation balloon catheter, is also described having wall thickness in the transition region less than 0.001 inch.
Inventors
- 👤 Richard A. Noddin
- 👤 Arthur R. Madenjian
- 👤 Ralph J. Barry, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 02:31
CPC Classifications
A; A61; A61M; A61M25/00; A61M25/10; A61M25/1027; A61M25/1029; A61L; A61L29/00; A61L29/04; A61L29/06; A61M25/104
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
202 words
A method of forming an inflatable medical balloon catheter device comprising (a) providing a tube of a selected resin of wall thickness and diameter suitable for being formed into a balloon, said tube having at least a first region crystallized to render it dimensionally stable under heated conditions, (b) selectively heating to drawing temperature a defined second region of said tube disposed at an end of the portion of the tube from which the balloon is to be formed, between said portion of tube and said first region, (c) applying tension in opposite directions to respective ends of said heated region to draw the second region to a smaller diameter, thereby providing a preform having, at the end of said portion of tube, a tapered, relatively small diameter region comprised of material that has substantially no crystallization or molecular orientation, (d) thereafter heating said tubular preform to blowing temperature and, while heated, forming a balloon by drawing and blowing said preform including said tapered region, and (e) mounting said balloon on a catheter to form a balloon catheter device, said step of preforming said tapered end region enabling the corresponding section of the blown balloon to have a separately controllable thickness profile.
Claim 2
Independent Claim
202 words
A method of forming an inflatable medical balloon catheter device comprising (a) providing a tube of a selected resin of wall thickness and diameter suitable for being formed into a balloon, said tube having at least a first region crystallized to render it dimensionally stable under heated conditions, (b) selectively heating to drawing temperature a defined second region of said tube disposed at an end of the portion of the tube from which the balloon is to be formed, between said portion of tube and said first region, (c) applying tension in opposite directions to respective ends of said heated region to draw the second region to a smaller diameter, thereby providing a preform having, at the end of said portion of tube, a tapered, relatively small diameter region comprised of material that has substantially no crystallization or molecular orientation, (d) thereafter heating said tubular preform to blowing temperature and, while heated, forming a balloon by drawing and blowing said preform including said tapered region, and (e) mounting said balloon on a catheter to form a balloon catheter device, said step of preforming said tapered end region enabling the corresponding section of the blown balloon to have a separately controllable thickness profile.
Claim 3
Independent Claim
204 words
A method of forming an inflatable medical balloon catheter device comprising (a) providing a tube of a selected resin of wall thickness and diameter suitable for being formed into a balloon, said tube having two, spaced apart first regions crystallized to render it stable under heated conditions, (b) selectively heating to drawing temperature two defined second regions of said tube disposed at the respective ends of the portion of the tube from which the balloon is to be formed, between the respective ends of said portion of tube and said second regions, (c) applying tension in opposite directions to respective ends of said heated regions to draw the second regions to smaller diameter, thereby providing a preform having, at the ends of said portion of tube, tapered, relatively small diameter regions comprised of material that has substantially no crystallization or molecular orientation, (d) thereafter heating said tubular preform to blowing temperature and, while heated, forming a balloon by drawing and blowing said preform including said tapered regions, and (e) mounting said balloons on a catheter to form a balloon catheter device, said step of preforming said tapered end regions enabling the corresponding sections of the blown balloon to have a separately controllable thickness profile.
Claim 4
Independent Claim
204 words
A method of forming an inflatable medical balloon catheter device comprising (a) providing a tube of a selected resin of wall thickness and diameter suitable for being formed into a balloon, said tube having two, spaced apart first regions crystallized to render it stable under heated conditions, (b) selectively heating to drawing temperature two defined second regions of said tube disposed at the respective ends of the portion of the tube from which the balloon is to be formed, between the respective ends of said portion of tube and said second regions, (c) applying tension in opposite directions to respective ends of said heated regions to draw the second regions to smaller diameter, thereby providing a preform having, at the ends of said portion of tube, tapered, relatively small diameter regions comprised of material that has substantially no crystallization or molecular orientation, (d) thereafter heating said tubular preform to blowing temperature and, while heated, forming a balloon by drawing and blowing said preform including said tapered regions, and (e) mounting said balloons on a catheter to form a balloon catheter device, said step of preforming said tapered end regions enabling the corresponding sections of the blown balloon to have a separately controllable thickness profile.
Claim 5
Dependent Claim
30 words
The method of claim 1 or 2 wherein said drawing temperature is above the glass transition temperature and below crystallization temperature such that substantially no crystallization or molecular orientation occurs.
Claim 6
Dependent Claim
29 words
The method of claim 1 or 2 wherein said drawing temperature is near or above the melt temperature of said resin and after drawing, said preform is rapidly quenched.
Claim 7
Dependent Claim
28 words
The method of claim 1 or 2 wherein said blowing temperature is approximately the glass transition temperature or above, and substantially below the crystallization temperature of said resin.
Claim 8
Dependent Claim
30 words
The method of claim 5 wherein, for biaxially orienting the balloon, said blowing temperature is below the drawing temperature, in the region of the glass transition temperature of said resin.
Claim 9
Dependent Claim
37 words
The method of claim 1 or 2 wherein said resin is amorphous polyethylene terephthalate, said drawing temperature is between about 105 and 130 degrees centigrade and said blowing temperature is between about 85 and 115 degrees centigrade.
Claim 10
Dependent Claim
54 words
The method of claim 1 or 2 wherein said drawing to form said preform and said step of drawing and blowing said preform are so related that the wall thickness of the main body of the balloon and the wall thickness of a tapered end section of the balloon are of substantially equal value.
Claim 11
Dependent Claim
42 words
The method of claim 1 or 2 wherein said heating of said defined region is performed in such a manner that the portion of the tube from which the main body of the balloon is to be formed is not substantially heated.
Claim 12
Dependent Claim
13 words
A balloon product made according to the method of claim 1 or 2.
Claim 13
Dependent Claim
11 words
A balloon product made according to the method of claim 8.
References Cited (Backward Citations)
US3865666A
Cited
US3950468A
Cited
US4323071A
Cited
US4323071B1
Cited
US4256789A
Cited
US4256789B1
Cited
US4411055A
Cited
US4422447A
Cited
US4490421A
Cited
US4646719A
Cited
US4587975A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-10-15 | 1994-04-16 | 1994-10-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-10-15 | 1998-04-16 | 1998-10-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-10-15 | 2002-04-16 | 2002-10-16 | $7700.00 | Window Closed / Lapsed |