Patent US5686172A successfully refreshed from Google Patents.
US5686172A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Metal-foil-clad composite ceramic board and process for the production thereof
Assignee: Mitsubishi Gas Chemical Co Inc
•
Filing: 1995-11-28
•
Granted: 1997-11-11
•
Expires: 2015-11-28
Abstract
Abstract A metal-foil-clad composite ceramic board produced by impregnating by impregnating a sintered substrate (II) of an inorganic continuously porous sintered body (I) having a true porosity of 12 to 50% and an open porosity of at least 10%, with a thermosetting resin (R) under vacuum, to form a resin-impregnated sintered substrate (IIR), stacking a metal foil on the resin-impregnated sintered substrate (IIR) and press-forming the resultant laminate, wherein the stacked metal foil has a 10-point average surface roughness Rz of 10 mu m or less, and the resin-impregnated sintered substrate (IIR) and the metal foil have substantially no adhesive layer therebetween or have an adhesive layer having a thickness of 10 mu m or less therebetween.
Inventors
- 👤 Kazuyuki Ohya
- 👤 Norio Sayama
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 16:34
CPC Classifications
H; H05; H05K; H05K3/00; H05K3/02; H05K3/022; C; C04; C04B; C04B37/00; C04B37/02; B; B32; B32B; B32B15/00; B32B15/04; H05K1/00; H05K1/02; H05K1/03; H05K1/0306; H05K1/0313; H05K1/0353; H10; H10W; H10W70/00; H10W70/01; H10W70/05; H10W70/60; H10W70/67; H10W70/69; H10W70/692; H05K2201/00; H05K2201/01; H05K2201/0104; H05K2201/0116; H05K2201/03; H05K2201/0332; H05K2201/0335; H05K2201/0355; H05K3/46; H05K3/4611; H05K3/4626; H05K3/4629; Y; Y10; Y10S; Y10S428/00; Y10S428/901; Y10S428/922; Y10S428/9335; Y10S428/94; Y10T; Y10T428/00; Y10T428/249921; Y10T428/249953; Y10T428/249955; Y10T428/249956; Y10T428/249967; Y10T428/249994; Y10T428/26; Y10T428/266; Y10T428/31
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
118 words
A metal-foil-clad composite ceramic board formed of a resin-impregnated sintered substrate (IIR) obtained by impregnating a 0.2 to 10 mm thick sintered substrate (II) portion of an inorganic continuously porous sintered body (I) having a true porosity of 12 to 50% and an open porosity of at least 10%, with a thermosetting resin (R) under vacuum, and a metal foil, the resin-impregnated sintered substrate (IIR) and the metal foil being stacked and press-formed, the stacked metal foil having a 10-point average surface roughness Rz of 10 μm or less, the resin-impregnated sintered substrate (IIR) and the metal foil having substantially no adhesive layer therebetween or having an adhesive layer having a thickness of 10 μm or less therebetween.
Claim 2
Dependent Claim
118 words
A metal-foil-clad composite ceramic board formed of a resin-impregnated sintered substrate (IIR) obtained by impregnating a 0.2 to 10 mm thick sintered substrate (II) portion of an inorganic continuously porous sintered body (I) having a true porosity of 12 to 50% and an open porosity of at least 10%, with a thermosetting resin (R) under vacuum, and a metal foil, the resin-impregnated sintered substrate (IIR) and the metal foil being stacked and press-formed, the stacked metal foil having a 10-point average surface roughness Rz of 10 μm or less, the resin-impregnated sintered substrate (IIR) and the metal foil having substantially no adhesive layer therebetween or having an adhesive layer having a thickness of 10 μm or less therebetween.
Claim 3
Dependent Claim
42 words
A metal-foil-clad composite ceramic board according to claim 1, wherein the inorganic continuously porous sintered body (I) has an open porosity of 15 to 35%, a closed porosity of 2% or less and an average pore diameter of 0.2 to 6 μm.
Claim 4
Dependent Claim
43 words
A metal-foil-clad composite ceramic board according to claim 1, wherein the inorganic continuously porous sintered body (I) has a Shore hardness (HS) of 45 or less, a Vickers hardness (HV) of 300 or less and a flexural strength of at least 50 MPa.
Claim 5
Dependent Claim
77 words
A metal-foil-clad composite ceramic board according to claim 1, wherein the sintered substrate (II) is a substrate obtained by surface-treating a sintered substrate from the inorganic continuously porous sintered body (I) produced from a green sheet produced by an extrusion method, and has a size of at least 500 cm 2 , a thickness of 1.0 to 6.0 mm, and a thickness accuracy, per a distance of 2 mm to 50 mm, of within ±30 μm .
Claim 6
Dependent Claim
70 words
A metal-foil-clad composite ceramic board according to claim 1, wherein the sintered substrate (II) is a substrate obtained by impregnating an at least 10 mm thick block of the inorganic continuously porous sintered body (I) with a liquid organic substance (OR) under vacuum, slicing the block to obtain a board having a predetermined thickness of 0.2 to 6.0 mm, and removing the organic substance (OR) by extraction, gasification or calcining.
Claim 7
Dependent Claim
51 words
A metal-foil-clad composite ceramic board according to claim 5, wherein the sintered substrate (II) has a thickness accuracy of within ±20 μm and a 10-point average surface roughness R, of 30 μm or less, and the metal foil has a 10-point average surface roughness R z of 5 μm or less.
Claim 8
Dependent Claim
71 words
A metal-foil-clad composite ceramic board according to claim 1, wherein the sintered substrate (II) is a substrate having improved affinity with the thermosetting resin (R), obtained by impregnating sintered substrate (II) with an organometal compound (OM1), heat-treating the impregnated sintered substrate (II) at a final maximum heating temperature of 650° to 800° C. to pyrolyze the organometal compound (OM1), thereby forming oxide or composite oxide on the substrate including pore surfaces.
Claim 9
Dependent Claim
58 words
A metal-foil-clad composite ceramic board according to claim 7, wherein the organometal compound (OM1) is at least one selected from an organometal compound of aluminum, an organometal compound of titanium and an organometal compound of silicon, and is used in impregnating substrate (II) as a thin solution having an organometal compound concentration of 0.05 to 10% by weight.
Claim 10
Dependent Claim
67 words
A metal-foil-clad composite ceramic board according to claim 1, wherein the sintered substrate (II) is a substrate having an elevated dielectric constant, obtained by impregnating sintered substrate (II) with an organometal compound (OM2), steam-treating the sintered substrate (II), heat-treating the steam-treated sintered substrate (II) at a maximum temperature of 650° to 900° C. to pyrolyze the organometal compound (OM2), thereby forming oxide or composite oxide in pores.
Claim 11
Dependent Claim
90 words
A metal-foil-clad composite ceramic board according to claim 9, wherein the organometal compound (OM2) is at least one compound selected from an organometal compound of titanium, an organometal compound of tantalum, an organometal compound of aluminum, an organometal compound of zirconium, an organometal compound of barium, an organometal compound of calcium, an organometal compound of strontium, an organometal compound of lead and an organometal compound of magnesium, and is selected to form a pyrolysis product in an amount in the range of from 1 to 20% by weight, in pores.
References Cited (Backward Citations)
EP0196865A2
Cited
US4882455A
Cited
US5144536A
Cited
WO1992018213A1
Cited
US5314740A
Cited
EP0566360A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2000-11-10 | 2001-05-12 | 2001-11-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2004-11-10 | 2005-05-12 | 2005-11-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2008-11-10 | 2009-05-12 | 2009-11-11 | $7700.00 | Window Closed / Lapsed |