Method and composition for polishing painted surfaces
Assignee: Illinois Tool Works Inc
•
Filing: 1995-12-22
•
Granted: 1997-10-14
•
Expires: 2015-12-22
Abstract
Abstract A clogging phenomenon in the surface layer of the contact face of a soft plastic-and-abrasive composite for polishing painted surfaces, which reduces the efficiency of the polishing work, is alleviated by mixing into the soft plastic backing material of the composite containing abrasive fine particles, non-abrasive globular particles preferably formed out of bubble material. The globular particles are rotatable in the surface layer of the contact face of the soft backing when the composite is in rubbing contact with the surface to be polished. Water or a surfactant may be interposed between the surface to be polished and the composite. The surface to be polished is rubbed with the composite to remove contaminating substances adhering to the surface to be polished.
Inventors
- 👤 Tadao Kodate
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 09:53
CPC Classifications
B; B24; B24D; B24D11/00; B24D15/00; B24D15/04; B24D3/00; B24D3/02; B24D3/20; B24D3/28; B24D3/34; B24D3/342
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
122 words
A composite for polishing painted surfaces, comprising: a) a soft plastic body having a contact face adapted to contact a surface to be polished; b) abrasive particles embedded in said body at least in proximity to said contact face in an amount effective to polish said surface when said contact face is rubbed against said surface; c) non-abrasive globular particles embedded in said body at least at said contact face in an amount and size effective to move said abrasive particles toward and away from said contact face when said globular particles are rotated in said contact face, said globular particles at said contact face being adapted to rotate in said contact face when said contact face is rubbed against said surface.
Claim 2
Dependent Claim
122 words
A composite for polishing painted surfaces, comprising: a) a soft plastic body having a contact face adapted to contact a surface to be polished; b) abrasive particles embedded in said body at least in proximity to said contact face in an amount effective to polish said surface when said contact face is rubbed against said surface; c) non-abrasive globular particles embedded in said body at least at said contact face in an amount and size effective to move said abrasive particles toward and away from said contact face when said globular particles are rotated in said contact face, said globular particles at said contact face being adapted to rotate in said contact face when said contact face is rubbed against said surface.
Claim 3
Dependent Claim
16 words
The composite of claim 1, in which said body further includes fine fibrous materials dispersed therein.
Claim 4
Dependent Claim
15 words
The composite of claim 1, in which said globular particles consist of synthetic resin material.
Claim 5
Dependent Claim
16 words
The composite of claim 1, in which said composite has a specific gravity less than 1.
Claim 6
Dependent Claim
14 words
The composite of claim 1, in which said globular particles consist of foam material.
Claim 7
Dependent Claim
32 words
The composite of claim 1 in which said globular particles have a particle size which is larger than that of said abrasive particles and is substantially 3 mm or less in diameter.
Claim 8
Dependent Claim
15 words
The composite of claim 1 in which said body is mainly composed of polyolefin polyol.
Claim 9
Dependent Claim
15 words
The composite of claim 1 in which said body is mainly composed of visco-elastic material.
Claim 10
Dependent Claim
21 words
The composite of claim 1 in which said abrasive fine particles have a particle size of substantially 3 to 50 μm.
Claim 11
Dependent Claim
115 words
A polishing method, comprising the steps of: a) placing a contact face of a composite in contact with a painted surface to be polished, the composite comprising a soft plastic body containing a dispersion of abrasive particles in an amount effective to polish said surface and non-abrasive globular particles said globular particles being rotatable in said contact face when said contact face is in rubbing contact with a surface to be polished; and b) rubbing said composite on said surface to be polished with a substance selected from the group consisting of water or surfactant present on said surface and said contact face, whereby extraneous substances adhering to the surface to be polished are removed.
Claim 12
Dependent Claim
115 words
A polishing method, comprising the steps of: a) placing a contact face of a composite in contact with a painted surface to be polished, the composite comprising a soft plastic body containing a dispersion of abrasive particles in an amount effective to polish said surface and non-abrasive globular particles said globular particles being rotatable in said contact face when said contact face is in rubbing contact with a surface to be polished; and b) rubbing said composite on said surface to be polished with a substance selected from the group consisting of water or surfactant present on said surface and said contact face, whereby extraneous substances adhering to the surface to be polished are removed.
Claim 13
Dependent Claim
32 words
The method of claim 10, in which said substance is applied to said surface to be polished and said composite is pressed against said surface to be polished for rubbing the same.
Claim 14
Dependent Claim
36 words
The method of claim 10, in which said substance is applied to at least said contact face of said composite, and said surface to be polished is rubbed with said composite while pressing said composite thereagainst.
Claim 15
Dependent Claim
11 words
The method of claim 10, in which said substance is water.
Claim 16
Dependent Claim
11 words
The method of claim 10, in which said substance is surfactant.
Claim 17
Dependent Claim
37 words
The composite of claim 1, in which said abrasive particles are dispersed in said body adjacent said contact face in the ratio of substantially 700 g of abrasive particles per 150 g of said soft plastic body.
Claim 18
Dependent Claim
25 words
The composite of claim 1, in which said abrasive particles are selected from the group consisting of silica sand, calcium carbonate, alumina, and green carborundum.
Claim 19
Dependent Claim
27 words
The composite of claim 1, in which the material of said nonabrasive globular particles is chosen from the group consisting of synthetic resin, rubber and foam materials.
References Cited (Backward Citations)
JPH0411335A
Cited
US5209760A
Cited
US5203883A
Cited
US5273558A
Cited
US5514192A
Cited
US5551960A
Cited
US5489233A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2000-10-13 | 2001-04-14 | 2001-10-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2004-10-13 | 2005-04-14 | 2005-10-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2008-10-13 | 2009-04-14 | 2009-10-14 | $7700.00 | Window Closed / Lapsed |