Isolation trench with a rounded top edge using an etch buffer layer
Assignee: Taiwan Semiconductor Manufacturing Co TSMC Ltd
•
Filing: 1997-02-20
•
Granted: 1997-10-07
•
Expires: 2017-02-20
Abstract
Abstract The present invention provides a method of manufacturing a trench having rounded top corners 28 in a substrate. The rounded top edges allow the formation of a gate oxide with a uniform thickness around the trench thereby reducing parasitic field FET problems. The method begins by forming a pad layer 14 over a semiconductor substrate 10. Next, an insulating layer 18 composed of silicon nitride is formed over the pad layer 14. A first opening 19 is formed in the insulating layer 18 and the pad layer 14 exposing the surface of the substrate. The first opening is defined by sidewalls of the pad layer 14 and of the insulating layer 18. An etch buffer layer 20 composed of polysilicon is formed over the resultant surface. In one etch step, the etch buffer layer 20 is anisotropically etched forming spacers 22 on the sidewalls of the pad layer 14 and of the insulating layer 18. The same etch step continues by etching the spacers 22 and the exposed substrate in the first opening 19 thereby forming a trench 26 in the substrate 10. Because the etch has to etch through the spacers before it reached the substrate, the trench 26 has rounded top edges 28 near the pad layer 14. Lastly, the pad layer 14 and the first insulating layer 18 are removed thereby forming the trench 26 with rounded top edges 28.
Inventors
- 👤 Chin-Hsiung Ho
- 👤 Chia-Shiung Tsai
- 👤 Cheng-Kai Liu
- 👤 Chaochieh Tsai
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 02:48
CPC Classifications
H; H10; H10P; H10P50/00; H10P50/69; H10P50/691; H10P50/693; H10P50/695; H10W; H10W10/00; H10W10/01; H10W10/011; H10W10/014; H10W10/0145; H10W10/10; H10W10/17; Y; Y10; Y10S; Y10S148/00; Y10S148/05
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
167 words
A method of fabricating trench with rounded corners in a substrate comprising the steps of: a) forming a pad layer over a semiconductor substrate; b) forming an insulating layer over said pad layer; c) forming a first opening in said insulating layer and said pad layer exposing the surface of said substrate; said first opening defined by sidewalls of said pad layer and sidewalls of said insulating layer; d) forming a silicon etch buffer layer over the substrate surface; e) anisotropically etching said etch buffer layer forming spacers on said sidewalls of said pad layer and of said insulating layer and exposed said substrate, and etching said spacers and the exposed substrate in said first opening forming a trench in said substrate; said trench having rounded top edges near said pad layer; and f) removing said pad layer and said first insulating layer thereby forming said trench with rounded top edges wherein the anisotropically etching in step e) comprises a dry etch using Cl 2 and HBr.
Claim 2
Independent Claim
167 words
A method of fabricating trench with rounded corners in a substrate comprising the steps of: a) forming a pad layer over a semiconductor substrate; b) forming an insulating layer over said pad layer; c) forming a first opening in said insulating layer and said pad layer exposing the surface of said substrate; said first opening defined by sidewalls of said pad layer and sidewalls of said insulating layer; d) forming a silicon etch buffer layer over the substrate surface; e) anisotropically etching said etch buffer layer forming spacers on said sidewalls of said pad layer and of said insulating layer and exposed said substrate, and etching said spacers and the exposed substrate in said first opening forming a trench in said substrate; said trench having rounded top edges near said pad layer; and f) removing said pad layer and said first insulating layer thereby forming said trench with rounded top edges wherein the anisotropically etching in step e) comprises a dry etch using Cl 2 and HBr.
Claim 3
Dependent Claim
39 words
The method of claim 1 which further includes: a) filling said trench with a dielectric layer composed of silicon oxide, b) forming a gate oxide over said substrate; and c) forming field effect transistors over said gate oxide layer.
Claim 4
Dependent Claim
26 words
The method of claim 1 wherein said silicon etch buffer layer is composed of a material selected from the group consisting of amorphous silicon and polysilicon.
Claim 5
Dependent Claim
27 words
The method of claim 1 wherein said pad layer is composed of silicon oxide and has thickness in a range of between about 70 and 200 Å.
Claim 6
Dependent Claim
27 words
The method of claim 1 wherein said insulating layer is composed of silicon nitride having a thickness in a range of between about 1000 and 2000 Å.
Claim 7
Dependent Claim
23 words
The method of claim 1 wherein said first opening has an open dimension in a range of between about 0.15 and 1.0 μ.
Claim 8
Dependent Claim
27 words
The method of claim 1 wherein said etch buffer layer is composed of polysilicon having a thickness in a range of between about 300 and 500 Å.
Claim 9
Dependent Claim
40 words
The method of claim 1 wherein said pad layer is removed using a dilute HF etch at a temperature between about 175° and 185° C. and said first insulating layer is removed using a hot H 3 PO 4 etch.
Claim 10
Independent Claim
239 words
A method of fabrication a trench with rounded corners in a substrate comprising the steps of: a) forming a pad layer composed of silicon oxide over a semiconductor substrate; said semiconductor substrate having isolation areas and active areas; b) forming an insulating layer composed of silicon nitride over said pad layer; c) forming a first opening in said insulating layer and said pad layer exposing the surface of said substrate over said isolation area, said first opening defined by sidewalls of said pad layer and of said insulating layer; said first opening having an open dimension in a range of between about 0.15 and 1.0 μ; d) forming an etch buffer layer composed of polysilicon over the substrate surface, said etch buffer layer composed of polysilicon having a thickness in a range of between about 300 and 500 Å; e) anisotropically etching said etch buffer layer forming spacers on said sidewalls of said pad layer and of said insulating layer, and etching said spacer and the exposed substrate in said first opening forming a trench in said substrate, said trench having rounded top edges near the pad layer; said trench having a depth in a range of between about 0.3 and 0.5 μm; and f) removing said pad layer and said first insulating layer thereby forming said trench with rounded top edges wherein the anisotropically etching in step e) comprises a dry etch using using Cl 2 and HBr.
Claim 11
Independent Claim
239 words
A method of fabrication a trench with rounded corners in a substrate comprising the steps of: a) forming a pad layer composed of silicon oxide over a semiconductor substrate; said semiconductor substrate having isolation areas and active areas; b) forming an insulating layer composed of silicon nitride over said pad layer; c) forming a first opening in said insulating layer and said pad layer exposing the surface of said substrate over said isolation area, said first opening defined by sidewalls of said pad layer and of said insulating layer; said first opening having an open dimension in a range of between about 0.15 and 1.0 μ; d) forming an etch buffer layer composed of polysilicon over the substrate surface, said etch buffer layer composed of polysilicon having a thickness in a range of between about 300 and 500 Å; e) anisotropically etching said etch buffer layer forming spacers on said sidewalls of said pad layer and of said insulating layer, and etching said spacer and the exposed substrate in said first opening forming a trench in said substrate, said trench having rounded top edges near the pad layer; said trench having a depth in a range of between about 0.3 and 0.5 μm; and f) removing said pad layer and said first insulating layer thereby forming said trench with rounded top edges wherein the anisotropically etching in step e) comprises a dry etch using using Cl 2 and HBr.
Claim 12
Dependent Claim
43 words
The method of claim 9 which further includes: a) filling said trench with an dielectric layer composed of silicon oxide, b) forming a gate oxide over said substrate; and c) forming field effect transistors over said gate oxide layer over said active areas.
Claim 13
Dependent Claim
25 words
The method of claim 9 wherein said etch buffer layer is composed of a material selected from the group consisting of amorphous silicon and polysilicon.
Claim 14
Dependent Claim
27 words
The method of claim 9 wherein said pad layer is composed of silicon oxide and has thickness in a range of between about 70 and 200 Å.
Claim 15
Dependent Claim
23 words
The method of claim 9 wherein said insulating layer is has a thickness in a range of between about 1000 and 2000 Å.
Claim 16
Dependent Claim
40 words
The method of claim 9 wherein said pad layer is removed using a dilute HF etch at a temperature between about 175° and 185° C. and said first insulating layer is removed using a hot H 3 PO 4 etch.
References Cited (Backward Citations)
US4845048A
Cited
US4729815A
Cited
US4857477A
Cited
US4980311A
Cited
JPH0271620A
Cited
US5464794A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2000-10-06 | 2001-04-07 | 2001-10-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2004-10-06 | 2005-04-07 | 2005-10-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2008-10-06 | 2009-04-07 | 2009-10-07 | $7700.00 | Window Closed / Lapsed |