Valvular annuloplasty rings of a biocompatible low elastic modulus titanium-niobium-zirconium alloy
Assignee: Smith and Nephew Inc
•
Filing: 1995-10-12
•
Granted: 1997-10-07
•
Expires: 2015-10-12
Abstract
Abstract An annuloplasty ring of low elastic modulus Ti--Nb--Zr alloy to provide enhanced biocompatibility, hemocompatibility, flexibility and strength. Components of the annuloplasty ring can be surface hardened by oxygen or nitrogen diffusion or by depositing a tightly adherent, hard, wear-resistant, hemocompatible ceramic coating by physical vapor deposition and chemical vapor deposition. The Ti--Nb--Zr alloy can be used as a fabrication material for any annuloplasty ring component that either comes into contact with blood, thereby demanding high levels of hemocompatibility, or that is subject to microfretting, corrosion, or other wear such that a low elastic modulus metal with a corrosion-resistant, hardened surface would be desirable.
Inventors
- 👤 James A. Davidson
- 👤 Kenneth P. Daigle
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 15:46
CPC Classifications
A; A61; A61F; A61F2/00; A61F2/02; A61F2/24; A61F2/2442; A61F2/2445; A61F2/2448; A61L; A61L27/00; A61L27/02; A61L27/04; A61L27/06; A61L27/50; A61L27/507; A61L33/00; A61L33/02; A61L33/022; C; C22; C22C; C22C14/00; C22C30/00
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
115 words
An annuloplasty ring for implantation in living body tissue of a patient, the annuloplasty ring having enhanced biocompatibility, comprising: components at least partially fabricated from a metal alloy comprising: (i) titanium; and (ii) from about 10 to about 20 wt. % niobium or from about 35 to about 50 wt. % niobium; wherein the alloy is substantially free of toxic elements, said toxic elements being aluminum, manganese, vanadium, cobalt, nickel, molybdenum and chromium, except such amounts of said toxic elements as may occur as impurities in the alloy and as contaminants as a result of an alloying process, the amounts of said impurities and contaminants being insignificant to cause adverse effect on the patient's body.
Claim 2
Dependent Claim
115 words
An annuloplasty ring for implantation in living body tissue of a patient, the annuloplasty ring having enhanced biocompatibility, comprising: components at least partially fabricated from a metal alloy comprising: (i) titanium; and (ii) from about 10 to about 20 wt. % niobium or from about 35 to about 50 wt. % niobium; wherein the alloy is substantially free of toxic elements, said toxic elements being aluminum, manganese, vanadium, cobalt, nickel, molybdenum and chromium, except such amounts of said toxic elements as may occur as impurities in the alloy and as contaminants as a result of an alloying process, the amounts of said impurities and contaminants being insignificant to cause adverse effect on the patient's body.
Claim 3
Dependent Claim
16 words
The annuloplasty ring of claim 1, wherein said components include a core and a woven sleeve.
Claim 4
Dependent Claim
23 words
The annuloplasty ring of claim 1, wherein said metal alloy further includes an amount of zirconium sufficient to retard the transformation of beta.
Claim 5
Dependent Claim
20 words
The annuloplasty ring of claim 3, wherein the metal alloy includes from about 0.5 to about 20 wt. % zirconium.
Claim 6
Dependent Claim
49 words
The annuloplasty ring of claim 1, further including a hardened outer surface layer on at least a portion of said components, said layer formed on said components by a process selected from the group consisting of oxygen diffusion hardening, nitrogen diffusion hardening, physical vapor deposition, and chemical vapor deposition.
Claim 7
Dependent Claim
49 words
The annuloplasty ring of claim 3, further including a hardened outer surface layer on at least a portion of said components, said layer formed on said components by a process selected from the group consisting of oxygen diffusion hardening, nitrogen diffusion hardening, physical vapor deposition, and chemical vapor deposition.
Claim 8
Dependent Claim
47 words
The annuloplasty ring of claim 1, claim 3, claim 5 or claim 6, wherein surfaces of said components that come into contact with body tissue or fluid are at least partially coated with a composition selected from the group consisting of anticoagulants, antimicrobial agents, antibiotics, and medicaments.
Claim 9
Dependent Claim
51 words
The annuloplasty ring of claim 1, claim 3, claim 5 or claim 6, further including a lower friction wear-resistant outer surface layer on at least a portion of said components, said lower friction wear-resistant outer surface layer produced by a process selected from the group consisting of boronation and silver doping.
Claim 10
Dependent Claim
27 words
The annuloplasty ring of claim 3, wherein the metal alloy includes about 74 wt. % titanium, about 13 wt. % niobium, and about 13 wt. % zirconium.
Claim 11
Dependent Claim
29 words
The annuloplasty ring of claim 3, wherein the metal alloy includes titanium, from about 10 to about 20 wt. % niobium, and up to about 20 wt. % zirconium.
Claim 12
Dependent Claim
29 words
The annuloplasty ring of claim 3, wherein the metal alloy includes titanium, from about 35 to about 50 wt. % niobium, and up to about 20 wt. % zirconium.
Claim 13
Dependent Claim
126 words
A annuloplasty ring for implantation in living body tissue of a patient, the annuloplasty ring having enhanced biocompatibility, comprising: components at least partially fabricated from a metal alloy comprising: (i) titanium; and (ii) niobium and tantalum, wherein the combined wt. % of niobium and tantalum is from about 10 to about 20 wt. % or from about 35 to about 50 wt. %; wherein the alloy is substantially free of toxic elements, said toxic elements being aluminum, manganese, vanadium, cobalt, nickel, molybdenum and chromium, except such amounts of said toxic elements as may occur as impurities in the alloy and as contaminants as a result of an alloying process, the amounts of said impurities and contaminants being insignificant to cause adverse effect on the patient's body.
Claim 14
Dependent Claim
126 words
A annuloplasty ring for implantation in living body tissue of a patient, the annuloplasty ring having enhanced biocompatibility, comprising: components at least partially fabricated from a metal alloy comprising: (i) titanium; and (ii) niobium and tantalum, wherein the combined wt. % of niobium and tantalum is from about 10 to about 20 wt. % or from about 35 to about 50 wt. %; wherein the alloy is substantially free of toxic elements, said toxic elements being aluminum, manganese, vanadium, cobalt, nickel, molybdenum and chromium, except such amounts of said toxic elements as may occur as impurities in the alloy and as contaminants as a result of an alloying process, the amounts of said impurities and contaminants being insignificant to cause adverse effect on the patient's body.
Claim 15
Dependent Claim
16 words
The annuloplasty ring of claim 12, wherein said components include a core and a woven sleeve.
Claim 16
Dependent Claim
22 words
The annuloplasty ring of claim 12, wherein said alloy further includes an amount of zirconium sufficient to retard the transformation of beta.
Claim 17
Dependent Claim
20 words
The annuloplasty ring of claim 14, wherein the metal alloy includes from about 0.5 to about 20 wt. % zirconium.
Claim 18
Dependent Claim
49 words
The annuloplasty ring of claim 12, further including a hardened outer surface layer on at least a portion of said components, said layer formed on said components by a process selected from the group consisting of oxygen diffusion hardening, nitrogen diffusion hardening, physical vapor deposition, and chemical vapor deposition.
Claim 19
Dependent Claim
49 words
The annuloplasty ring of claim 14, further including a hardened outer surface layer on at least a portion of said components, said layer formed on said components by a process selected from the group consisting of oxygen diffusion hardening, nitrogen diffusion hardening, physical vapor deposition, and chemical vapor deposition.
Claim 20
Dependent Claim
47 words
The annuloplasty ring of claim 12, claim 14, claim 16 or claim 17, wherein surfaces of said components that come into contact with body tissue or fluid are at least partially coated with a composition selected from the group consisting of anticoagulants, antimicrobial agents, antibiotics, and medicaments.
Claim 21
Dependent Claim
51 words
The annuloplasty ring of claim 12, claim 14, claim 16 or claim 17, further including a lower friction wear-resistant outer surface layer on at least a portion of said components, said lower friction wear-resistant outer surface layer produced by a process selected from the group consisting of boronation and silver doping.
References Cited (Backward Citations)
US2892706A
Cited
US2987352A
Cited
US3408604A
Cited
US3370946A
Cited
US3643658A
Cited
US3677795A
Cited
US3849124A
Cited
US3752664A
Cited
US4040129A
Cited
US3777346A
Cited
US3911783A
Cited
US3906550A
Cited
US4145764A
Cited
DE2703529A1
Cited
US4170990A
Cited
US4197643A
Cited
US4511411A
Cited
US4902359A
Cited
US4983184A
Cited
US4857269A
Cited
EP0437079A1
Cited
US5169597A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2000-10-06 | 2001-04-07 | 2001-10-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2004-10-06 | 2005-04-07 | 2005-10-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2008-10-06 | 2009-04-07 | 2009-10-07 | $7700.00 | Window Closed / Lapsed |