Assignee: International Business Machines Corp
•
Filing: 1994-09-30
•
Granted: 1997-07-15
•
Expires: 2014-09-30
Abstract
Abstract A process and apparatus for Al2O3 CVD on silicon wafers using aluminum tri-isopropoxide in a high-volume production environment is presented. The conditions required to use ATI in a production environment and provide maximum utilization of ATI are first of all delivery of ATI via direct evaporation. The ATI source bottle is pumped out (bypassing substrates) until propene and isopropanol signals are reduced to 1% of process pressure before start of aluminum oxide deposition. Either IR spectroscopy or mass spectrometry can be used to provide a control signal to the microprocessor controller. Heating the supplied tetramer to 120 DEG C. for two hours assures complete conversion to trimer. The ATI is stored at 90 DEG C. to minimize decomposition during idle periods and allow recovery of trimer upon return to 120 DEG C. for two hours. During periods of demand, the ATI is held at 120 DEG C. to minimize decomposition.
Inventors
- 👤 Steven George Barbee
- 👤 Jonathan Daniel Chapple-Sokol
- 👤 Richard Anthony Conti
- 👤 Richard Hsiao
- 👤 James Anthony O'Neill
- 👤 Narayana V. Sarma
- 👤 Donald Leslie Wilson
- 👤 Justin Wai-chow Wong
- 👤 Steven Paul Zuhoski
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 01:41
CPC Classifications
C; C23; C23C; C23C16/00; C23C16/22; C23C16/30; C23C16/40; C23C16/403; C23C16/44; C23C16/448; C23C16/4481; C23C16/52
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
246 words
A method of depositing a dense aluminum oxide upon a substrate comprising the steps of: a) providing a vacuum processing chamber, the processing chamber having at least one gas injector nozzle for injection of gas into the chamber, a heated susceptor upon which is placed said substrate, and temperature controllable walls; b) providing a chemical vapor delivery system having a premix chamber connected to the processing chamber, the chemical vapor delivery system controllably generating and delivering a chemical vapor from a source of aluminum tri-isopropoxide (ATI); c) heating the ATI source to a temperature sufficient to provide a flow of the chemical vapor through the chemical vapor delivery system by direct evaporation of ATI; d) pumping out said chemical vapor from the ATI source, bypassing the processing chamber, until a predetermined purity of the chemical vapor is detected; e) controlling the flow of the chemical vapor in the chemical vapor delivery system to the processing chamber at a predetermined flow rate when said predetermined purity is detected; f) maintaining a process pressure within the processing chamber and the chemical vapor delivery system at a prescribed pressure; g) mixing a preheated inert gas with the flow of chemical vapor in the premix chamber to produce a gas mixture, the flow of inert gas being mass flow controlled; and h) injecting the gas mixture into the processing chamber so that the chemical vapor in the gas mixture reacts on the substrate to form an aluminum oxide film thereon.
Claim 2
Independent Claim
246 words
A method of depositing a dense aluminum oxide upon a substrate comprising the steps of: a) providing a vacuum processing chamber, the processing chamber having at least one gas injector nozzle for injection of gas into the chamber, a heated susceptor upon which is placed said substrate, and temperature controllable walls; b) providing a chemical vapor delivery system having a premix chamber connected to the processing chamber, the chemical vapor delivery system controllably generating and delivering a chemical vapor from a source of aluminum tri-isopropoxide (ATI); c) heating the ATI source to a temperature sufficient to provide a flow of the chemical vapor through the chemical vapor delivery system by direct evaporation of ATI; d) pumping out said chemical vapor from the ATI source, bypassing the processing chamber, until a predetermined purity of the chemical vapor is detected; e) controlling the flow of the chemical vapor in the chemical vapor delivery system to the processing chamber at a predetermined flow rate when said predetermined purity is detected; f) maintaining a process pressure within the processing chamber and the chemical vapor delivery system at a prescribed pressure; g) mixing a preheated inert gas with the flow of chemical vapor in the premix chamber to produce a gas mixture, the flow of inert gas being mass flow controlled; and h) injecting the gas mixture into the processing chamber so that the chemical vapor in the gas mixture reacts on the substrate to form an aluminum oxide film thereon.
Claim 3
Dependent Claim
17 words
The method of claim 1, wherein the temperature in step c) is between 115° and 125° C.
Claim 4
Dependent Claim
28 words
The method of claim 2, further comprising the step of maintaining a temperature of the processing chamber to less than 5° C. above the temperature of step c).
Claim 5
Dependent Claim
27 words
The method of claim 3, wherein the temperature in step c) is approximately 120° C. and the temperature of the processing chamber is less than 125° C.
Claim 6
Dependent Claim
20 words
The method of claim 1, wherein the flow of said chemical vapor in step e) is at least 1 sccm.
Claim 7
Dependent Claim
17 words
The method of claim 1, wherein the prescribed pressure in step f) is less than 200 mTorr.
Claim 8
Dependent Claim
16 words
The method of claim 1, wherein a nominal rate of inert gas flow is 200 sccm.
Claim 9
Dependent Claim
11 words
The method of claim 7, wherein the inert gas is Argon.
Claim 10
Independent Claim
187 words
A method to use aluminum tri-isopropoxide (ATI) for chemical vapor deposition (CVD) of aluminum oxide, said method comprising the steps of: a) storing ATI during periods of no production demand at a temperature no less than 90° C. but not greater than 95° C.; b) storing ATI during periods of no production demand under vacuum; c) raising the ATI temperature to a temperature no greater than 125° C. in preparation for a period of production demand; d) maintaining ATI during periods of production demand at a temperature not greater than 125° C.; e) transporting ATI to a CVD reactor via direct evaporation; f) agitating the ATI during periods of production demand; g) directing the ATI to a reactor bypass in lieu of to the CVD reactor during a start up period and maintaining flow to the bypass until the concentration of ATI has reached a predetermined purity; h) directing the ATI to the CVD reactor after the concentration of ATI has reached a predetermined purity for deposition of aluminum oxide; and i) reducing the ATI temperature to about 90° C. after termination of the production demand period.
Claim 11
Independent Claim
187 words
A method to use aluminum tri-isopropoxide (ATI) for chemical vapor deposition (CVD) of aluminum oxide, said method comprising the steps of: a) storing ATI during periods of no production demand at a temperature no less than 90° C. but not greater than 95° C.; b) storing ATI during periods of no production demand under vacuum; c) raising the ATI temperature to a temperature no greater than 125° C. in preparation for a period of production demand; d) maintaining ATI during periods of production demand at a temperature not greater than 125° C.; e) transporting ATI to a CVD reactor via direct evaporation; f) agitating the ATI during periods of production demand; g) directing the ATI to a reactor bypass in lieu of to the CVD reactor during a start up period and maintaining flow to the bypass until the concentration of ATI has reached a predetermined purity; h) directing the ATI to the CVD reactor after the concentration of ATI has reached a predetermined purity for deposition of aluminum oxide; and i) reducing the ATI temperature to about 90° C. after termination of the production demand period.
Claim 12
Dependent Claim
24 words
The method of claim 9, further comprising the step of maintaining the temperature of ATI during delivery prior to the period of production demand.
Claim 13
Dependent Claim
18 words
The method of claim 10, further comprising the step of maintaining the temperature of ATI during steps e-h.
Claim 14
Dependent Claim
19 words
The method of claim 11, wherein the pressure of the CVD reactor is less than an ATI vapor pressure.
References Cited (Backward Citations)
US4187336A
Cited
US4696833A
Cited
US4675089A
Cited
US4997677A
Cited
US5029554A
Cited
US4947789A
Cited
US5173328A
Cited
US5091207A
Cited
US5160542A
Cited
US4999219A
Cited
US5070815A
Cited
US5223305A
Cited
US5356476A
Cited
US5431734A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2000-07-14 | 2001-01-13 | 2001-07-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2004-07-14 | 2005-01-13 | 2005-07-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2008-07-14 | 2009-01-13 | 2009-07-15 | $7700.00 | Window Closed / Lapsed |